Bi3NbTiO9的结构与电学性能

章贞; 晏海学; 董显林; 王永龄   

  1. 中国科学院上海硅酸盐研究所 上海 200050
  • 收稿日期:2002-11-05 修回日期:2003-01-21 出版日期:2003-11-20 网络出版日期:2003-11-20

Structural and Electrical Properties of Bi3NbTiO9 Solid Solution

ZHANG Zhen; YAN Hai-Xue; DONG Xian-Lin; WANG Yong-Ling   

  1. Shanghai Institute of Ceramics; Chinese Academy of Sciences; Shanghai 200050; China）
  • Received:2002-11-05 Revised:2003-01-21 Published:2003-11-20 Online:2003-11-20

PDF (PC)

947

摘要： 用传统固相法成功制备出了致密的、相对密度超过95％的Bi3NbTiO9(BNT)压电陶瓷;采用XRD和SEM对陶瓷的结构和晶粒形貌进行了表征;测出了BNT陶瓷在居里温度点附近的介电特性,同时确定了该陶瓷的居里温度Tc为914℃电滞回线的测试显示了该材料典型的硬铁电性,经过高温极化,测出材料的压电常数d33=7pC/N.

关键词: Bi3NbTiO9, 铁电, 压电, 陶瓷

Abstract: Bi3NbTiO9 (BNT) ceramic material with 95%～97% of the theoretical density was prepared by the conventional mixed-oxide method. Its Curie temperature (Tc) of 914℃ was measured to
be almost the highest one among those of all the ceramics known up to date. And obviously, the piezoelectric ceramic can be used at higher
temperatures. The crystal structure of the ceramic was examined by XRD method. Anisometric plate-like crystalline grains were
observed by SEM, which revealed the layered structure of the material. Furthermore, the hysteresis (P-E) loop measurement showed a typical hard
ferroelectricity in the Bi3NbTiO9 ceramics, and the piezoelectric constant (d33) measured was 7pC/N.

Key words: Bi3NbTiO9, ferroelectricity, dielectric properties, ceramics

中图分类号: