基于双硅氧烷先驱体制备的氧化硅基气凝胶研究进展

doi:10.15541/jim20150223

无机材料学报 ›› 2015, Vol. 30 ›› Issue (12): 1243-1253.DOI: 10.15541/jim20150223 CSTR: 32189.14.10.15541/jim20150223

基于双硅氧烷先驱体制备的氧化硅基气凝胶研究进展

何飞^1,2, 郁万军^1,2, 方旻翰^1,2, 赫晓东^1,2, 李明伟³

(哈尔滨工业大学 1. 特种环境复合材料国防科技重点实验室; 2. 复合材料与结构研究所; 3. 金属精密热加工国防科技重点实验室, 哈尔滨 150001)

收稿日期:2015-05-11 修回日期:2015-06-10 出版日期:2015-12-20 网络出版日期:2015-11-24
作者简介:何飞(1978–), 男, 副教授. E-mail: hefei@hit.edu.cn
基金资助:
特种环境复合材料技术国防科技重点实验室开放基金(9140C490208140C49003)

An Overview on Silica Aerogels Synthesized by Siloxane Co-precursors

(1. Key Laboratory of Science and Technology on Advanced Composites, Harbin Institute of Technology, Harbin 150001, China; 2. Center for Composite Materials, Harbin Institute of Technology, Harbin 150001, China; 3. Key Laboratory for Precision Hot Processing of Materials, Harbin Institute of Technology, Harbin Institute of Technology, Harbin 150001, China)

Received:2015-05-11 Revised:2015-06-10 Published:2015-12-20 Online:2015-11-24
About author:HE Fei. E-mail: hefei@hit.edu.cn
Supported by:
Key Laboratory Opening Funding of Key Laboratory of Science and Technology on Advanced Composites (9140C490208140C49003)

摘要/Abstract

摘要：

气凝胶材料具有高比表面积、高孔隙率、低密度、低热导率和高透过率等特性, 在隔热、隔声和光学等领域具有广泛的应用前景。但该类材料纤细骨架构成的多孔结构所呈现的高脆性是限制其应用的主要因素。本文依据硅氧烷先驱体含有不可水解基团数量的特征, 综述了采用全水解双先驱体、全/部分水解双先驱体和部分水解双先驱体等三类采用双硅氧烷先驱体制备气凝胶材料的研究现状, 分析了这三类气凝胶所呈现出的组织结构特征及其在力学、热学、光学和疏水性等方面的性能特点。通过对硅氧烷先驱体类型的选择和组合, 可以设计气凝胶材料的组织结构与性能, 为改善气凝胶材料的力学行为提出了新思路。

关键词: 氧化硅气凝胶, 双硅氧烷先驱体, 力学性能, 溶胶-凝胶法, 综述

Abstract:

Due to their unique features, such as high specific surface area, high porosity, low density, low thermal conductivity, and high transmittance, aerogels can be widely applied in the fields of thermal insulation, sound insulation and optics. However, aerogels usually tend to be destructive collapse, due to their porous structures constituted by slightly brittle skeletons, which is a negative factor to restrict their applications. According to the number and variety of non-hydrolytic groups in siloxane precursors, an overview of the literatures is presented on silica aerogels synthesized by three kinds of siloxane co-precursors, i.e. integral hydrolytic co-precursors, integral/partial and partial hydrolytic co-precursors. The characteristics of porous structures and properties in mechanics, thermal insulation, optics, and hydrophobicity are analyzed. It is an effective method by choosing appropriate precursors to realize the designs and improve mechanical behaviors of aerogels in respect of structures and properties.

Key words: silica aerogels, siloxane co-precursors, mechanical properties, Sol-Gel method, review

中图分类号:

TB303

何飞, 郁万军, 方旻翰, 赫晓东, 李明伟. 基于双硅氧烷先驱体制备的氧化硅基气凝胶研究进展[J]. 无机材料学报, 2015, 30(12): 1243-1253.

HE Fei, YU Wan-Jun, FANG Min-Han, HE Xiao-Dong, LI Ming-Wei. An Overview on Silica Aerogels Synthesized by Siloxane Co-precursors[J]. Journal of Inorganic Materials, 2015, 30(12): 1243-1253.

图/表 9

表1 含有不同数量不可水解有机基团的有机硅醇盐[5]

Table 1 Organic siloxane precursors containing different non-hydrolytic groups[5]

图1 超级疏水复合材料的制备流程和油水分离实验[31]

Fig. 1 Preparation and application of superhydrophobic materials[31]

图2 不同氧化硅气凝胶制备流程图[49]

Fig. 2 Flow chart illustrating the preparation of different silica aerogels[49]

图3 以MTMS和DMDMS作为双先驱体常压干燥制备出的柔性气凝胶照片[6]

Fig. 3 Digital camera image of the flexible xerogel derived from MTMS and DMDMS co-precursor system[6]

图4 MTMS+DMDMS双先驱体制备的气凝胶三点弯曲试验(a)及实验曲线(b)[54]

Fig. 4 (a) Photograph and (b) stress-strain curves of a 3-point bending test on the MTMS-DMDMS gel[54]

图5 不同类型双先驱体制备泡沫状气凝胶的流程[54]

Fig. 5 Facile synthesis of marshmallow-like gels derived from di- and tri-functional alkoxysilanes as co-precursors[54]

图6 超双疏气凝胶制备流程和反应原理示意图[55]

Fig. 6 Synthetic approach of superamphiphobic aerogels[55] (a) The synthesis for the VTMS+VMDMS marshmallow-like gel (MG1); (b) Synthetic approach for the superamphiphobic aerogels (MG2)

图7 (a)先驱体合成过程和(b)气凝胶真空干燥过程示意图[57]

Fig. 7 (a) Synthesis of the precursor and (b) procedures of vacuum-drying to obtain aerogels[57]

表2 不同先驱体制备的氧化硅基气凝胶性能参数比较

Table 2 Comparison of performance parameters of silica aerogels prepared by different precursors

Precursors	Strength/ MPa	Elastic modulus/ MPa	Density/ (g·cm^-3)	Contact angle/(°)	Thermal conductivity/ (W·m^-1·K^-1)	Thermostability /℃
TMOS	0.031,compressed, crushed^[2]	-	0.12^[2]	Hydrophilic^[2]	0.01~0.03^[2]	600^[2]
MTMS	>9 MPa, compressed 80%, recovered^[50]	0.034~0.062 ^[1]	0.04~0.1^[1]	158~164^[1]	-	257^[1]
TMOS+PTES ^a	-	-	0.15^[5]	132^[5]	-	520^[5]
TMOS+PTES^b	-	-	0.11^[5]	121^[5]	-	520^[5]
TEOS+MTMS^a	-	-	0.107^[46]	120^[5]	-	435^[46]
TEOS+PTES^a	-	-	0.33^[5]	129^[5]	-	520^[5]
TEOS +PTES^b	-	-	0.14^[5]	115^[5]	-	520^[5]
TEOS+HMDZ ^b	-	-	0.09^[7]	146^[7]	0.08^[13]	330^[7]
MTMS+ DMDMS	~0.1, compression, recovered	-	-	hydrophobicity	-	320^[6,54]
VTMS+ VMDMS	~0.07, compressed 80%, recovered	-	0.122	150, superamphiphobic	-	170^[55]
MTMS+ GPTMS	~0.17, compressed 35%, recovered	0.46	0.104	-	0.0388	-^[56]
MPTMS+ VTMS	compression, recovered	0.117	0.085	-	0.047	-^[57]

参考文献 57

[1]	RAO A V, BHAGAT S D, HIRASHIMA H, et al.Synthesis of flexible silica aerogels using methyltrimethoxysilane (MTMS) precursor.Journal of Colloid and Interface Science, 2006, 300(1): 279-285.
[2]	RANDALL J P, MEADOR M A B, JANA S C. Tailoring mechanical properties of aerogels for aerospace applications. ACS Applied Materials & Interfaces, 2011, 3(3): 613-626.
[3]	KANAMORI K, NAKANISHI K.Controlled pore formation in organotrialkoxysilane-derived hybrids: from aerogels to hierarchically porous monoliths.Chemical Society Reviews, 2011, 40(2): 754-770.
[4]	MALEKI H, DURÃES L, PORTUGAL A. An overview on silica aerogels synthesis and different mechanical reinforcing strategies.Journal of Non-Crystalline Solids, 2014, 385(2): 55-74.
[5]	RAO A V, PAJONK G M, BHAGAT S D, et al.Comparative studies on the surface chemical modification of silica aerogels based on various organosilane compounds of the type RnSiX4-n.Journal of Non-Crystalline Solids, 2004, 350(12): 216-223.
[6]	HAYASE G, KANAMORI K, NAKANISHI K.New flexible aerogels and xerogels derived from methyltrimethoxysilane/ dimethyldimethoxysilane co-precursors.Journal of Materials Chemistry, 2011, 21(43): 17077-17079.
[7]	GURAV J L, RAO A V, BANGI U K H. Hydrophobic and low density silica aerogels dried at ambient pressure using TEOS precursor. Journal of Alloys and Compounds, 2009, 471(1): 296-302.
[8]	DONATTI D A, VOLLET D R.Study of the hydrolysis of TEOS-TMOS mixtures under ultrasound stimulation.Journal of Non-Crystalline Solids, 1996, 204(3): 301-304.
[9]	VOLLET D R, NUNES L M, DONATTI D A, et al.Structural characteristics of silica sonogels prepared with different proportions of TEOS and TMOS.Journal of Non-Crystalline Solids, 2008, 354(14): 1467-1474.
[10]	LATTHE S S, DHERE S L, KAPPENSTEIN C, et al.Sliding behavior of water drops on Sol-Gel derived hydrophobic silica films. Applied Surface Science, 2010, 256(10): 3259-3264.
[11]	MAHADIK D B, RAO A V, RAO A P, et al.Effect of concentration of trimethylchlorosilane (TMCS) and hexamethyldisilazane (HMDZ) silylating agents on surface free energy of silica aerogels. Journal of Colloid and Interface Science, 2011, 356(1): 298-302.
[12]	MAHADIK D B, RAO A V, KUMAR R S. et al. Reduction of processing time by mechanical shaking of the ambient pressure dried TEOS based silica aerogel granules.Journal of Porous Materials, 2012, 19(1): 87-94.
[13]	GURAV J L, RAO A V, NADARGI D Y.Study of thermal conductivity and effect of humidity on HMDZ modified TEOS based aerogel dried at ambient pressure.Journal of Sol-Gel Science and Technology, 2009, 50(3): 275-280.
[14]	GURAV J L, NADARGI D Y, RAO A V.Effect of mixed catalysts system on TEOS-based silica aerogels dried at ambient pressure.Applied Surface Science, 2008, 255(5): 3019-3027.
[15]	GURAV J L, RAO A V, NADARGI D Y, et al.Ambient pressure dried TEOS-based silica aerogels: good absorbents of organic liquids.Journal of Materials Science, 2010, 45(2): 503-510.
[16]	PARALE V G, MAHADIK D B, MAHADIK S A, et al.Wettability study of surface modified silica aerogels with different silylating agents.Journal of Sol-Gel Science and Technology, 2012, 63(3): 573-579.
[17]	SHEWALE P M, RAO A V, GURAV J L, et al.Synthesis and characterization of low density and hydrophobic silica aerogels dried at ambient pressure using sodium silicate precursor.Journal of Porous Materials, 2009, 16(1): 101-108.
[18]	SHEWALE P M, RAO A V, RAO A P.Effect of different trimethyl silylating agents on the hydrophobic and physical properties of silica aerogels.Applied Surface Science, 2008, 254(19): 6902-6907.
[19]	RAO A P, RAO A V.Modifying the surface energy and hydrophobicity of the low-density silica aerogels through the use of combinations of surface-modification agents.Journal of Materials Science, 2010, 45(1): 51-63.
[20]	RAO A P, RAO A V, PAJONK G M.Hydrophobic and physical properties of the ambient pressure dried silica aerogels with sodium silicate precursor using various surface modification agents.Applied Surface Science, 2007, 253(14): 6032-6040.
[21]	BANGI U K H, RAO A P, HIRASHIMA H, et al. Physico-chemical properties of ambiently dried sodium silicate based aerogels catalyzed with various acids.Journal of Sol-Gel Science and Technology, 2009, 50(1): 87-97.
[22]	GURAV J L, RAO A V, RAO A P, et al.Physical properties of sodium silicate based silica aerogels prepared by single step Sol-Gel process dried at ambient pressure.Journal of Alloys and Compounds, 2009, 476(1): 397-402.
[23]	LATTHE S S, NADARGI D Y, RAO A V.TMOS based water repellent silica thin films by co-precursor method using TMES as a hydrophobic agent.Applied Surface Science, 2009, 255(6): 3600-3604.
[24]	LATTHE S S, IMAI H, GANESAN V, et al.Porous superhydrophobic silica films by Sol-Gel process.Microporous and Mesoporous Materials, 2010, 130(1): 115-121.
[25]	GANBAVLE V V, BANGI U K H, LATTHE S S, et al. Self-cleaning silica coatings on glass by single step Sol-Gel route.Surface & Coatings Technology, 2011, 205(23): 5338-5344.
[26]	PARALE V G, MAHADIK D B, KAVALE M S, et al.Sol-Gel preparation of PTMS modified hydrophobic and transparent silica coatings.Journal of Porous Materials, 2013, 20(4): 733-739.
[27]	LATTHE S S, IMAI H, GANESAN V, et al.Ultrahydrophobic silica films by Sol-Gel process.Journal of Porous Materials, 2010, 17(5): 565-571.
[28]	DHERE S L, LATTHE S S, KAPPENSTEIN C, et al.Transparent water repellent silica films by Sol-Gel process.Applied Surface Science, 2010, 256(11): 3624-3629.
[29]	LATTHE S S, IMAI H, GANESAN V, et al.Superhydrophobic silica films by Sol-Gel co-precursor method.Applied Surface Science, 2009, 256(1): 217-222.
[30]	PARALE V G, MAHADIK D B, MAHADIK S A, et al.OTES modified transparent dip coated silica coatings.Ceramics International, 2013, 39(1): 835-840.
[31]	GUO P, ZHAI S, XIAO Z, et al.One-step fabrication of highly stable, superhydrophobic composites from controllable and low-cost PMHS/TEOS sols for efficient oil cleanup.Journal of Colloid and Interface Science, 2015, 446(5): 155-162.
[32]	ZHANG X, WU Y, HE S, et al.Structural characterization of sol-gel composites using TEOS/MEMO as precursors.Surface & Coatings Technology, 2007, 201(12): 6051-6058.
[33]	MAHADIK S A, KAVALE M S, MUKHERJEE S K, et al.Transparent superhydrophobic silica coatings on glass by Sol-Gel method.Applied Surface Science, 2010, 257(2): 333-339.
[34]	RAO A V, PAJONK G M.Effect of methyltrimethoxysilane as a co-precursor on the optical properties of silica aerogels.Journal of Non-Crystalline Solids, 2001, 285(1): 202-209.
[35]	RAO A V, KULKARNI M M, AMALNERKAR D P, et al.Surface chemical modification of silica aerogels using various alkyl- alkoxy/chloro silanes. Applied Surface Science, 2003, 206(1): 262-270.
[36]	RAO A V, KULKARNI M M.Hydrophobic properties of TMOS-TMES-based silica aerogels.Materials Research Bulletin, 2002, 37(9): 1667-1677.
[37]	RAO A V, Wagh P B.Preparation and characterization of hydrophobic silica aerogels.Materials Chemistry and Physics, 1998, 53(1): 13-18.
[38]	RAO A V, HARANATH D. Effect of methyltrimethoxysilane as a synthesis component on the hydrophobicity and some physical properties of silica aerogels. Microporous and Mesoporous Materials, 1999, 30(2): 267-273.
[39]	BHAGAT S D, RAO A V.Surface chemical modification of TEOS based silica aerogels synthesized by two step (acid-base) Sol-Gel process.Applied Surface Science, 2006, 252(12): 4289-4297.
[40]	NADARGI D Y, KALESH R R, RAO A V.Rapid reduction in gelation time and impregnation of hydrophobic property in the tetraethoxysilane (TEOS) based silica aerogels using NH4F catalyzed single step Sol-Gel process.Journal of Alloys and Compounds, 2009, 480(2): 689-695.
[41]	HEGDE N D, RAO A V.Organic modification of TEOS based silica aerogels using hexadecyltrimethoxysilane as a hydrophobic reagent.Applied Surface Science, 2006, 253(3): 1566-1572.
[42]	RAO A V, HEGDE N D, Shewale P M.Imperviousness of the hydrophobic silica aerogels against various solvents and acids.Applied Surface Science, 2007, 253(9): 4137-4141.
[43]	HUANG S L, CHIN W K, YANG W P.Structural characteristics and properties of silica_poly(2-hydroxyethyl methacrylate) (PHEMA) nanocomposites prepared by mixing colloidal silica or tetraethyloxysilane (TEOS) with PHEMA.Polymer, 2005, 46(6): 1865-1877.
[44]	LI J, CAO J, YANG M, et al.‘Seeded’ growth of silica aerogel by tetraethoxysilane and trimethylchlorosilane co-precursor method.Journal of Non-Crystalline Solids, 2013, 362(1): 216-221.
[45]	LI J, CAO J, HUO L, et al.One-step synthesis of hydrophobic silica aerogel via in situ surface modification.Materials Letters, 2012, 87(11): 146-149.
[46]	LI Z, CHENG X, HE SONG, et al.Preparation of ambient pressure dried MTMS/TEOS co-precursor silica aerogel by adjusting NH4OH concentration.Materials Letters, 2014, 129(8): 12-15.
[47]	ZHOU B, SHEN J, WU Y, et al.Hydrophobic silica aerogels derived from polyethoxydisiloxane and perfluoroalkylsilane.Materials Science and Engineering C, 2007, 27(5-8): 1291-1294.
[48]	AL-OWEINI R, EL-RASSY H.Synthesis and characterization by FTIR spectroscopy of silica aerogels prepared using several Si(OR)4 and R″Si(OR′)3 precursors.Journal of Molecular Structure, 2009, 919(1/2/3): 140-145.
[49]	AL-OWEINI R, EL-RASSY H.Surface characterization by nitrogen adsorption of silica aerogels synthesized from various Si(OR)4 and R″Si(OR′)3 precursors.Applied Surface Science, 2010, 257(1): 276-281.
[50]	KANAMORI K, AIZAWA M, NAKANISHI K, et al.New transparent methylsilsesquioxane aerogels and xerogels with improved mechanical properties.Advanced Materilals, 2007, 19(12): 1589-1593.
[51]	KANAMORI K, AIZAWA M, NAKANISHI K, et al.Elastic organic- inorganic hybrid aerogels and xerogels.Journal of Sol-Gel Science and Technology, 2008, 48(1): 172-181.
[52]	KANAMORI K, NAKANISHI K, HANADA T.Sol-Gel synthesis, porous structure, and mechanical property polymethylsilsesquioxane aerogels.Journal of the Ceramic Society of Japan, 2009, 117(12): 1333-1338.
[53]	KANAMORI K, KODERA Y, HAYASE G, et al.Transition from transparent aerogels to hierarchically porous monoliths in polymethylsilsesquioxane Sol-Gel system.Journal of Colloid and Interface Science, 2011, 357(2): 336-344.
[54]	HAYASE G, KANAMORI K, FUKUCHI M, et al.Facile synthesis of marshmallow-like macroporous gels usable under harsh conditions for the separation of oil and water.Angewandte Chemie, 2013, 125(7): 2040-2043.
[55]	HAYASE G, KANAMORI K, HASEGAWA G, et al.A superamphiphobic macroporous silicone monolith with marshmallow- like flexibility. Angewandte Chemie International Edition, 2013, 52(41): 1-5.
[56]	ARAVIND P R, NIEMEYER P, RATKE L.Novel flexible aerogels derived from methyltrimethoxysilane/3-(2,3-epoxypropoxy) propyltrimethoxysilane co-precursor.Microporous and Mesoporous Materials, 2013, 181(11): 111-115.
[57]	WANG Z, DAI Z, WU J J, et al.Vacuum-dried robust bridged silsesquioxane aerogels.Advanced Materilals, 2013, 25(32): 4494-4497.

基于双硅氧烷先驱体制备的氧化硅基气凝胶研究进展

An Overview on Silica Aerogels Synthesized by Siloxane Co-precursors

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

图/表 9

参考文献 57

相关文章 15

编辑推荐

Metrics

本文评价

[1]	魏相霞, 张晓飞, 徐凯龙, 陈张伟. 增材制造柔性压电材料的现状与展望[J]. 无机材料学报, 2024, 39(9): 965-978.
[2]	杨鑫, 韩春秋, 曹玥晗, 贺桢, 周莹. 金属氧化物电催化硝酸盐还原合成氨研究进展[J]. 无机材料学报, 2024, 39(9): 979-991.
[3]	刘鹏东, 王桢, 刘永锋, 温广武. 硅泥在锂离子电池中的应用研究进展[J]. 无机材料学报, 2024, 39(9): 992-1004.
[4]	黄洁, 汪刘应, 王滨, 刘顾, 王伟超, 葛超群. 基于微纳结构设计的电磁性能调控研究进展[J]. 无机材料学报, 2024, 39(8): 853-870.
[5]	范武刚, 曹雄, 周响, 李玲, 赵冠楠, 张兆泉. 8YSZ陶瓷在模拟压水堆水环境中的耐腐蚀性能[J]. 无机材料学报, 2024, 39(7): 803-809.
[6]	陈乾, 苏海军, 姜浩, 申仲琳, 余明辉, 张卓. 超高温氧化物陶瓷激光增材制造及组织性能调控研究进展[J]. 无机材料学报, 2024, 39(7): 741-753.
[7]	王伟明, 王为得, 粟毅, 马青松, 姚冬旭, 曾宇平. 以非氧化物为烧结助剂制备高导热氮化硅陶瓷的研究进展[J]. 无机材料学报, 2024, 39(6): 634-646.
[8]	孙海洋, 季伟, 王为民, 傅正义. TiB-Ti周期序构复合材料设计、制备及性能研究[J]. 无机材料学报, 2024, 39(6): 662-670.
[9]	蔡飞燕, 倪德伟, 董绍明. 高熵碳化物超高温陶瓷的研究进展[J]. 无机材料学报, 2024, 39(6): 591-608.
[10]	刘国昂, 王海龙, 方成, 黄飞龙, 杨欢. B₄C含量对(Ti_0.25Zr_0.25Hf_0.25Ta_0.25)B₂-B₄C陶瓷力学性能及抗氧化性能的影响[J]. 无机材料学报, 2024, 39(6): 697-706.
[11]	吴晓晨, 郑瑞晓, 李露, 马浩林, 赵培航, 马朝利. SiC_f/SiC陶瓷基复合材料高温环境损伤原位监测研究进展[J]. 无机材料学报, 2024, 39(6): 609-622.
[12]	粟毅, 史扬帆, 贾成兰, 迟蓬涛, 高扬, 马青松, 陈思安. 浆料浸渍辅助PIP工艺制备C/HfC-SiC复合材料的微观结构及性能研究[J]. 无机材料学报, 2024, 39(6): 726-732.
[13]	赵日达, 汤素芳. 多孔碳陶瓷化改进反应熔渗法制备陶瓷基复合材料研究进展[J]. 无机材料学报, 2024, 39(6): 623-633.
[14]	方光武, 谢浩元, 张华军, 高希光, 宋迎东. CMC-EBC损伤耦合机理及一体化设计研究进展[J]. 无机材料学报, 2024, 39(6): 647-661.
[15]	张幸红, 王义铭, 程源, 董顺, 胡平. 超高温陶瓷复合材料研究进展[J]. 无机材料学报, 2024, 39(6): 571-590.