Processing and Characterization of Graded SiC/C Plasma Facing Composite

Abstract

Abstract: Simultaneous sintering of SiC and C was completed with the powder metallurgical method, and with which a near dense
plasma facing material with 0～100% compositional distributions of SiC---bulk SiC/C FGM was obtained. Well graded composition and structure of that composite
were demonstrated by SEM analysis. SiC/C FGM combines the well erosion resistance of SiC and high thermal-shock resistance of graphite, and has the high
effective thermal conductivity and thermal fatigue resistance. Chemical sputtering and Takamok irradiation experiments indicate that SiC/C FGM has
good high temperature plasma erosion resistance.

Key words: FGM, plasma facing material, thermal conductivity

CLC Number:

TB333

WU An-Hua,CAO Wen-Bin,GE Chang-Chun,LI Jing-Feng,Kawasaki Akira. Processing and Characterization of Graded SiC/C Plasma Facing Composite[J]. Journal of Inorganic Materials.

References

[1] Niino M, Hirai T, Watanabe R. J. Jpn. Soc. Compos. Mater., 1987, 13: 257--264.
[2] Suresh S, Mortensen A. Fundamentals of Functionally Graded Materials.Cambridge, UK: The University Press. 1998. 6--7.
[3] Qian J P, Roth J, Song J R, et al. J. Nucl. Mater., 1998, 258-263: 706--710.
[4] Sasaki M, Suzuki T, Hirai T. J. Mater. Syn. & Pro., 1994, 2 (2): 109--116.
[5] Wang Y, Sasaki M, Goto T, et al. J. Mater. Sci., 1990, 25: 4607--4612.
[6] Wang Y, Sasaki M, Hirai T. J. Mater. Sci., 1991, 26: 6618--6624.
[7] Sohda Y, et al. Carbon/carbon composites coated with SiC/C functionally gradient compositions, Holt J B et al. eds, Ceramic Transaction, 34, Proc.
of the second Int. Symp. On FGM’92. Westerville, OH: American Ceramic Society, 1993. 125--132.
[8] Sasaki M, Hirai T. Proc. of the first Int. Symp. On FGM’90, Yamanouchi M, et al. eds, Functionally Gradient Materials Forum. Tokyo, Japan: the
Society of Non-Traditional Technology, 1990. 83--88.
[9] Tuinstra, Koeing. J. Chem Phys., 1970, 53 (3): 1126--1130.
[10] Hishiyama Y, Inagaki M, Kimura S, et al. Cabon, 1974, 12: 249--258.
[11] Kanematsu H, Kunieda Y, Yokoi J, et al. High Temperature Materials and Processes, 1996, 15 (1-2): 63--72.
[12] 张家. 碳材料工程基础. 北京: 冶金工业出版社, 1992. 57--63.
[13] Jeandin M, Bienvenu Y. Int. Conf. on Advances in Materials and Processes, Ramakrishnan P ed, Proc. Conf., Bombay. New Delhi, India: Oxford & IBH Publishing Co. PVT. Ltd., 1992. 11--18.
[14] 关振铎, 张中太, 焦金生. 无机材料物理性能. 北京: 清华大学出?版社, 1992. 154--159.
[15] 武安华. 博士学位论文. 北京科技大学, 2002. 68--72.
[16] Hirai T. Functionally graded materials, Brook R J ed, Materials Science and Technology, A comprehensive Treatment, V.17B, Processing of
Ceramics, part 2. Weinheim, FRG: VCH publishers, 1996. 289--343.
[17] 凌云汉, 李江涛, 葛昌纯(LING Yun-Han, et al). 无机材料学报 (Journal of Inorganic Materials), 2001, 16 (6): 1121--1127.