Effect of SiC Content on B4C-SiC Composites Fabricated by Mechanical Alloying-hot Pressing

doi:10.3724/SP.J.1077.2014.13521

Abstract

Abstract:

Dense B₄C-SiC composite ceramics were fabricated through mechanical alloying using coarser B₄C and SiC powders as starting powders, and subsequent hot pressing sintering at 1950℃ without any sintering aid. The influences of the content of SiC on mechanical properties of the composite ceramics were studied through determining relative density of composite ceramics, Vickers hardness, flexure strength and fracture toughness. Combined with the microstructure and component analysis technologies of XRD, SEM and TEM, the relationship between microstructure and mechanical properties of the composite ceramics was investigated. The results indicate that the relative density and fracture toughness of the composite ceramics are improved with increase of SiC content, and reach the maximum value at 96.1% and 4.6 MPa•m^1/2,respectively, with SiC content of 50wt%. However, with the increase of SiC, the Vickers hardness and flexure strength are enhanced firstly and then decreased. The maximum values are 25.5 GPa and 480 MPa, respectively, with SiC content of 20wt%. Homogeneous dispersion of SiC phase in B₄C matrix is one of the reasons why the composite ceramics possess higher flexure strength. Fracture toughness of the composite ceramics is significantly higher than that of monomeric B₄C. The main reasons are attributed to powerful interfacial bonding between B₄C and SiC as well as the higher fracture toughness of SiC.

Key words: composite ceramics, hot pressing, mechanical alloying, mechanical properties, microstructure

CLC Number:

TQ174

ZHANG Zhi-Xiao, DU Xian-Wu, XING Wei-Hong, WANG Wei-Min, ZHANG Jin-Yong, FU Zheng-Yi. Effect of SiC Content on B₄C-SiC Composites Fabricated by Mechanical Alloying-hot Pressing[J]. Journal of Inorganic Materials, 2014, 29(7): 695-700.

Figures/Tables 8

Fig. 1 SEM images and particle size distributions (insets) of raw materials

Fig. 2 Particle size distributions of milled powders with different contents of SiC

Fig. 3 XRD patterns and SEM images of composite powders before and after milling

Fig. 4 Fractural surface SEM images of the sintered samples with different contents of SiC

Fig. 5 Relative density and Vickers hardness of the sintered samples with different contents of SiC

Fig. 6 Flexure strength and fracture toughness of sintered samples with different contents of SiC

Fig. 7 SEM image of polished surface with crack

Fig. 8 TEM image of B4C-20wt%SiC composite

References 23

[1]	SURI A K, SUBRAMANIAN C, SONBER J K, et al. Synthesis and consolidation of boron carbide: a review. International Materials Reviews, 2010, 55(1): 4-40.
[2]	DOMNICH V, REYNAUD S, HABER R A, et al. Boron carbide: structure, properties, and stability under stress. Journal of the American Ceramic Society, 2011, 94(11): 3605-3628.
[3]	LI AI-JU, ZHEN YU-HUA, ZHANG JI-MING, et al. Microstructures and properties of (SiC,TiB2)/B4C composites. Journal of the Chinese Society, 2006, 34(1): 11-15.
[4]	ZORZI J E, PEROTTONI C A, JORNADA DA J A H. Hardness and wear resistance of B4C ceramics prepared with several additives. Materials Letters, 2005, 59(23): 2932-2935.
[5]	MASHHADI M, TAHERI-NASSAJ E, SGLAVO V M, et al. Effect of Al addition on pressureless sintering of B4C. Ceramics International, 2009, 35(2): 831-837.
[6]	ROCHA DA R M, MELO DE F C L. Sintering of B4C by pressureless liquid phase sintering. Materials Science Forum, 2010, 660-661(10): 170-175.
[7]	DU XIAN-WU, ZHANG ZHI-XIAO, WANG WEI-MIN, et al. Effect of particle size on densification and mechanical properties of hot-pressed boron carbide. Journal of Inorganic Materials, 2013, 28(10): 1062-1066.
[8]	KIM H W, KOH Y H, KIM H E. Densification and mechanical properties of B4C with Al2O3 as a sintering aid. Journal of the American Ceramic Society, 2000, 83(11): 2863-2865.
[9]	MASHHADI M, TAHERI-NASSAJ E, MASHHADI M, et al. Pressureless sintering of B4C-TiB2 composites with Al additions. Ceramics International, 2011, 37(8): 3229-3235.
[10]	MA QIAN-CHENG, ZHANG GUO-JUN, KAN YAN-MEI, et al. De-n----------s--if-ication and mechanical properties of boron carbide ceramics with addition of silicon hexaboride. Journal of Inorganic Materials, 2008, 23(6): 1175-1178.
[11]	SIGL L S. Processing and mechanical properties of boron carbide sintered with TiC. Journal of the European Ceramic Society, 1998,18(11): 1521-1529.
[12]	ZHANG Z, DU X, WANG W, et al. Preparation of B4C-SiC composite ceramics through hot pressing assisted by mechanical alloying. International Journal of Refractory Metals and Hard Materials, 2013,41(11): 270-275.
[13]	OHYANAGI M, YAMAMOTO T, KITAURA H, et al. Consolidation of nanostructured SiC with disorder-order transformation. Scripta Materialia, 2004,50(1): 111-114.
[14]	ZHANG YAN-FENG, WANG LIAN-JUN, JIANG WAN, et al. Combination of high-energy ball milling and spark plasma sintering (SPS). Journal of Inorganic Materials, 2005, 20(6): 1445-1449.
[15]	KODERA Y, TOYOFUKU N, YAMASAKI H, et al. Consolidation of SiC/BN composite through MA-SPS method. Journal of Materials Science, 2008, 43(19): 6422-6428.
[16]	HAYUN S, WEIZMANN A, DARIEL M P, et al. Microstructural evolution during the infiltration of boron carbide with molten silicon. Journal of the European Ceramic Society, 2010, 30(4): 1007-1014.
[17]	SHI XIAO-LEI, ZHANG GONG, TAN YI, et al. Preparation and properties of B4C-SiC composite ceramics. Materials for Mechanical Engineering, 2009, 33(12): 77-80.
[18]	ZHANG ZHI-XIAO, DU XIAN-WU, WANG WEI-MIN, et al. Preparation and sintering of high activity B4C-SiC ultrafine composite powders. Journal of Inorganic Materials, 2014, 29(2): 185-190.
[19]	SURYANARAYANA C, AL-AQEELI N. Mechanically alloyed nanocomposites. Progress in Materials Science, 2013, 58(4): 383-502.
[20]	YIN BANG-YUE, WANG LING-SEN, FANG YAN-CHU. Preparation and sintering of ultrafine B4C powders. Journal of Inorganic Materials, 2002,17(2): 343-348.
[21]	DAVIDGE R W. Mechanical Behaviour of Ceramics. Cambridge: Cambridge University Press, 1979.
[22]	谢志鹏. 结构陶瓷. 北京: 清华大学出版社, 2011: 486-492.
[23]	MOSHTAGHIOUN B M, ORTIZ A L, GÓMEZ-GARCÍA D, et al. Toughening of super-hard ultra-fine grained B4C densified by spark-plasma sintering via SiC addition. Journal of the European Ceramic Society, 2013, 33(8): 1395-1401.

Effect of SiC Content on B₄C-SiC Composites Fabricated by Mechanical Alloying-hot Pressing

RichHTML

PDF (PC)

Knowledge

Cited

Abstract

Cite this article

share this article

Figures/Tables 8

References 23

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	FAN Wugang, CAO Xiong, ZHOU Xiang, LI Ling, ZHAO Guannan, ZHANG Zhaoquan. Anticorrosion Performance of 8YSZ Ceramics in Simulated Aqueous Environment of Pressurized Water Reactor [J]. Journal of Inorganic Materials, 2024, 39(7): 803-809.
[2]	CHEN Qian, SU Haijun, JIANG Hao, SHEN Zhonglin, YU Minghui, ZHANG Zhuo. Progress of Ultra-high Temperature Oxide Ceramics: Laser Additive Manufacturing and Microstructure Evolution [J]. Journal of Inorganic Materials, 2024, 39(7): 741-753.
[3]	JIANG Lingyi, PANG Shengyang, YANG Chao, ZHANG Yue, HU Chenglong, TANG Sufang. Preparation and Oxidation Behaviors of C/SiC-BN Composites [J]. Journal of Inorganic Materials, 2024, 39(7): 779-786.
[4]	ZHENG Yawen, ZHANG Cuiping, ZHANG Ruijie, XIA Qian, RU Hongqiang. Fabrication of Boron Carbide Ceramic Composites by Boronic Acid Carbothermal Reduction and Silicon Infiltration Reaction Sintering [J]. Journal of Inorganic Materials, 2024, 39(6): 707-714.
[5]	XUE Yifan, LI Weijie, ZHANG Zhongwei, PANG Xu, LIU Yu. Process Control of PyC Interphases Microstructure and Uniformity in Carbon Fiber Cloth [J]. Journal of Inorganic Materials, 2024, 39(4): 399-408.
[6]	SUN Chuan, HE Pengfei, HU Zhenfeng, WANG Rong, XING Yue, ZHANG Zhibin, LI Jinglong, WAN Chunlei, LIANG Xiubing. SiC-based Ceramic Materials Incorporating GNPs Array: Preparation and Mechanical Characterization [J]. Journal of Inorganic Materials, 2024, 39(3): 267-273.
[7]	ZHENG Jiaqian, LU Xiao, LU Yajie, WANG Yingjun, WANG Zhen, LU Jianxi. Functional Bioadaptability in Medical Bioceramics: Biological Mechanism and Application [J]. Journal of Inorganic Materials, 2024, 39(1): 1-16.
[8]	HE Danqi, WEI Mingxu, LIU Ruizhi, TANG Zhixin, ZHAI Pengcheng, ZHAO Wenyu. Heavy-Fermion YbAl₃ Materials: One-step Synthesis and Enhanced Thermoelectric Performance [J]. Journal of Inorganic Materials, 2023, 38(5): 577-582.
[9]	WU Shuang, GOU Yanzi, WANG Yongshou, SONG Quzhi, ZHANG Qingyu, WANG Yingde. Effect of Heat Treatment on Composition, Microstructure and Mechanical Property of Domestic KD-SA SiC Fibers [J]. Journal of Inorganic Materials, 2023, 38(5): 569-576.
[10]	XIE Jiaye, LI Liwen, ZHU Qiang. Contrastive Study on in Vitro Antibacterial Property and Biocompatibility of Three Clinical Pulp Capping Agents [J]. Journal of Inorganic Materials, 2023, 38(12): 1449-1456.
[11]	LI Jianbo, TIAN Zhen, JIANG Quanwei, YU Lifeng, KANG Huijun, CAO Zhiqiang, WANG Tongmin. Effects of Different Element Doping on Microstructure and Thermoelectric Properties of CaTiO₃ [J]. Journal of Inorganic Materials, 2023, 38(12): 1396-1404.
[12]	WU Dongjiang, ZHAO Ziyuan, YU Xuexin, MA Guangyi, YOU Zhulin, REN Guanhui, NIU Fangyong. Direct Additive Manufacturing of Al₂O₃-TiC_p Composite Ceramics by Laser Directed Energy Deposition [J]. Journal of Inorganic Materials, 2023, 38(10): 1183-1192.
[13]	ZHANG Ye, ZENG Yuping. Progress of Porous Silicon Nitride Ceramics Prepared via Self-propagating High Temperature Synthesis [J]. Journal of Inorganic Materials, 2022, 37(8): 853-864.
[14]	XIA Qian, SUN Shihao, ZHAO Yiliang, ZHANG Cuiping, RU Hongqiang, WANG Wei, YUE Xinyan. Effect of Boron Carbide Particle Size Distribution on the Microstructure and Properties of Reaction Bonded Boron Carbide Ceramic Composites by Silicon Infiltration [J]. Journal of Inorganic Materials, 2022, 37(6): 636-642.
[15]	HONG Du, NIU Yaran, LI Hong, ZHONG Xin, ZHENG Xuebin. Tribological Properties of Plasma Sprayed TiC-Graphite Composite Coatings [J]. Journal of Inorganic Materials, 2022, 37(6): 643-650.