Co掺杂改性尖晶石型Li1.035Mn1.965O4的合成及其电化学性能

doi:10.3724/SP.J.1077.2014.14031

摘要/Abstract

摘要：

采用湿化学-后续热处理技术, 合成了掺钴尖晶石锰酸锂材料。X射线衍射(XRD)分析结果表明, 钴的掺入没有改变材料的Fd3m结构。扫描电子显微镜(SEM)分析表明, 所合成的材料颗粒均匀, 形貌规整, 粒径分布较窄。透射电子显微镜(TEM)结果表明, Li_1.035Co_0.035Mn_1.930O₄具有完好的结晶态。充放电测试结果表明, 在室温下钴掺杂能够提高材料的电性能。当产物为Li_1.035Co_0.035Mn_1.930O₄时, 其电性能达到最优: 以0.5C充放电,首次放电容量为113 mAh/g, 经过100次循环后容量保持率为93.8%, 经过4C放电后仍然能够保持0.5C放电容量的76.1%; 而未掺钴的Li_1.035Mn_1.965O₄经过4C放电容量仅保持0.5C放电容量的64.8%。电化学阻抗测试结果表明, 钴离子的掺杂能够提高锰酸锂材料的锂离子扩散速率。

关键词: 锂离子电池, 钴掺杂, 水热法, 尖晶石锰酸锂

Abstract:

Spinel powders of Li_1.035Co_xMn_1.965-_xO₄(x=0-0.100) systems were synthesized by a simple wet chemical process with post heat-treatment. X-ray diffraction (XRD) patterns reveal that the Co doping does not affect the Fd3m space group of the cathode materials. Scanning electron microscope (SEM) images show that the Li_1.035Co_xMn_1.965-_xO₄ cathode materials have a uniform and nearly cubic morphology with a narrow size distribution. Transmission electron microscope (TEM) results demonstrate that the Li_1.035Co_0.035Mn_1.930O₄powder has a good crystalline state. The electrochemical testing results indicate that the prepared Co-doped Li_1.035Co_xMn_1.965-_xO₄ samples show a better cycling ability and rate capability at room temperature than that of Co-free Li_1.035Mn_1.965O₄. In particular, the Li_1.035Co_0.035Mn_1.930O₄ sample delivers a reversible specific capacity of 113 mAh/g in 1^st cycle and retains 93.8% of its initial capacity after 100 cycles at 0.5C rate. When discharging at 4C rate, the Li_1.035Co_0.035Mn_1.930O₄ powder maintains 86 mAh/g, which is 76.1% of the reversible capacity at 0.5C. Comparatively, the Li_1.035Mn_1.965O₄ powder maintains only 64.8% of its reversible capacity at 0.5C discharge rate. The electrochemical impedance spectroscopy results show that Co ion doping can enhance the electrical conductivity and the Li-ion diffusion coefficient. These results indicate a superior cycling and rate performance compared with the pristine one.

Key words: lithium ion batteries, Co doping, hydrothermal method, spinel lithium manganese oxide

中图分类号:

TM912

李运姣, 许虎, 孔龙, 李华成, 李春霞, 章贤臻, 韩强. Co掺杂改性尖晶石型Li_1.035Mn_1.965O₄的合成及其电化学性能[J]. 无机材料学报, 2014, 29(6): 661-666.

LI Yun-Jiao, XU Hu, KONG Long, LI Hua-Cheng, LI Chun-Xia, ZHANG Xian-Zhen, HAN Qiang. Synthesis and Electrochemical Characterizations of Co-doped Lithium
Manganese Oxide Spinel Li_1.035Mn_1.965O₄[J]. Journal of Inorganic Materials, 2014, 29(6): 661-666.

图/表 7

Fig. 1 XRD patterns of Li1.035CoxMn1.965-xO4 samples

Fig. 2 The lattice constant of Li1.035CoxMn1.965-xO4 samples as a function of the Co doping content

Fig. 3 SEM images of the Li1.035CoxMn1.965-xO4 spinel as a function of the Co doping content

Fig. 4 TEM (a), HRTEM (b) and SAED (c) images of the as- prepared Li1.035Co0.035Mn1.930O4 powder

Fig. 5 Discharge curves at 0.1C rate (a), discharge capacity with cycling number at different current rates (b) and cycling <br/>performance at 0.5C (c) of Li1.035CoxMn1.965-x

Fig. 6 Electrochemical impedance spectra (EIS) of the samples in the discharged state (about 3.0 V, vs Li+/Li) after 3 cycles with an equivalent circuit diagram inserted

Table 1 The impedance parameters of Li1.035CoxMn1.965-xO4 samples

Samples	R_s/Ω	R_ct/Ω	W_o-T	L/nm	D_Li⁺/(cm²•s^-1)
x = 0	4.32	129.40	1.976	596	1.81×10^-9
x = 0.035	3.28	79.12	0.121	621	3.19×10^-8
x = 0.065	3.39	91.20	0.286	618	1.37×10^-8
x = 0.100	3.85	102.00	0.547	609	6.85×10^-9

参考文献 33

[1]	LI J, KLOPSCH M C, STAN S. Synthesis and electrochemical performance of the high voltage cathode material Li[Li0.2Mn0.56 Ni0.16Co0.08]O2 with improved rate capability .Journal of Power Sources, 2011, 196(10): 4821-4825.
[2]	PARK O K, CHO Y, LEE S, et al. Who will drive electric vehicles, olivine or spinel?Energy & Environmental Science, 2011, 4: 1621-1633.
[3]	TARASCON J M, ARMAND M. Issues and challenges facing rechargeable lithium batteries. Nature, 2001, 414: 359-367.
[4]	KANG K, MENG Y S, BRÉGER J, et al. Electrodes with high power and high capacity for rechargeable lithium batteries. Science, 2006, 311: 977-980.
[5]	SIMMEN F, HINTENNACH A, HORISBERGER M, et al. Aspects of the surface layer formation on Li1+xMn2O4-δ during electrochemical cycling. Journal of The Electrochemical Society, 2010, 157(9): A1026-A1029.
[6]	XIE J, TANAKA T, IMANISHI N. Li-ion transport kinetics in LiMn2O4 thin films prepared by radio frequency magnetron sputtering. Journal of Power Sources, 2008, 180(1): 576-581.
[7]	WANG Y, CAO G Z. Developments in nanostructured cathode materials for high-performance lithium-ion batteries. Advanced Materials, 2008, 20(12): 2251-2269.
[8]	GUO Y G, HU Y S, SIGLE W. Superior electrode performance of nanostructured mesoporous TiO2 (anatase) through efficient hierarchical mixed conducting networks. Advanced Materials, 2007, 19(16): 2087-2091.
[9]	LIDDLE B J, COLLINS S M, BARTLETT B M. A new one- pot hydrothermal synthesis and electrochemical characterization of Li1+xMn2-yO4 spinel structured compounds.- Energy & Environmental Science, 2010, 3: 1339-1346.
[10]	ARILLO M A, CUELLO G, LÓPEZ M L. Structural characterisation and physical properties of LiMMnO4 (M=Cr, Ti) spinels. Solid State Sciences, 2005, 7(1): 25-32.
[11]	HAYASHI N, IKUTA H, WAKIHARA M. Cathode of LiMgyMn2- yO4 and yMn2-yO4-δ spinel phases for lithium secondary batteries. Journal of The Electrochemical Society, 1999, 146(4): 1351-1354.
[12]	MANDAL S, ROJAS R M, AMARILLA J M, et al. High temperature Co-doped LiMn2O4-based spinels. Structural, electrical, and electrochemical characterization. Chemistry of Materials, 2002, 14(4): 1598-1605.
[13]	IVANOVA S, ZHECHEVA E, STOYANOVA R, et al. High- voltage LiNi1/2Mn3/2O4 spinel: cationic order and particle size distribution. The Journal of Physical Chemistry C, 2011, 115(50): 25170-25182 .
[14]	XIONG L L, XU Y L, ZHANG C, et al. Electrochemical properties of tetravalent Ti-doped spinel LiMn2O4. Journal of Solid State Electrochemistry, 2011, 15(6): 1263-1269.
[15]	MYUNG S T, KOMABA S, HOSOYA K, et al. Synthesis of LiNi0.5Mn0.5-xTixO2 by an emulsion drying method and effect of Ti on structure and electrochemical properties. Chemistry of Materials, 2005, 17(9): 2427-2435.
[16]	TSUJI T, UMAKOSHI H, YAMAMURA Y. Thermodynamic properties of undoped and Fe-doped LiMn2O4 at high temperature. Journal of Physics and Chemistry of Solids, 2005, 66(2/3/4): 283-287.
[17]	LI G H, IKUTA H, UCHIDA T. The spinel phases LiMyMn2-yO4 (M=Co, Cr, Ni) as the cathode for rechargeable lithium batteries. Journal of The Electrochemical Society, 1996, 143(1): 178-182.
[18]	SUNG W O, PARK S H, JUNG E, et al., Improved high-rate capability of Li [Ni0.5CoyMn1.5-y]O4-zFz spinel materials for 5 V lithium secondary batteries. Journal of Industrial and Engineering Chemistry, 2007, 13: 1174-1179.
[19]	THIRUNAKARAN R, SIVASHANMUGAM A, GOPUKUMAR S. Electrochemical behaviour of nano-sized spinel LiMn2O4 and LiAlxMn2-xO4 (x=Al: 0.00-0.40) synthesized via fumaric acid- assisted Sol-Gel synthesis for use in lithium rechargeable batteries. Journal of Physics and Chemistry of Solids, 2008, 69(8): 2082-2090.
[20]	LIU Z L,WANG H B, FANG L. Improving the high-temperature performance of LiMn2O4 spinel by micro-emulsion coating of LiCoO2. Journal of Power Sources, 2002, 104(1): 101-107.
[21]	YOSHIMURA M, BYRAPPA K. Hydrothermal processing of materials: past, present and future. Journal of Materials Science, 2008, 43(7): 2085-2103.
[22]	LI Y J, KONG L, XI X M, et al. Hydrothermal Preparation and Characterization of LiMn2O4 for Li-ion Battery Application. Proceedings of COM 2012, Niagara Falls, Ontario, Canada, 2012.
[23]	AKIMOTO J, TAKAHASHI Y, GOTOH Y, et al. Synthesis, crystal structure, and magnetic property of delithiated LixMnO2 (x < 0.1) single crystals: A novel disordered rocksalt-type manganese dioxide. Chemical of Materials, 2003, 15(15): 2984-2990.
[24]	HE X M, LI J J, CAI Y. Preparation of co-doped spherical spinel LiMn2O4 cathode materials for Li-ion batteries. Journal of Power Sources, 2005, 150: 216-222.
[25]	SHEN C H, LIU R S, GUNDAKARAM R. Effect of Co doping in LiMn2O4. Journal of Power Sources, 2001, 102(1/2): 21-28.
[26]	SHANNON R D. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Crystallographica Section A, 1976, 32: 751-767.
[27]	GAO Y, REIMERS J N, DAHN J R. Changes in the voltage profile of Li/Li1+xMn2-xO4 cells as a function of x. Physical Review B, 1996, 54: 3878.
[28]	JAMES G S. Lange's Handbook of Chemistry. McGraw-Hill, New York, 1992.
[29]	KONG L, LI Y J, LI W J, et al. Synthesis and characterization of Li1.035Mn1.965O4 and Al-doped Li1.035Al0.035Mn1.930O4 as cathode materials for Li-ion batteries by a wet-chemical technique. Journal of Inorganic Materials, 2013, 28(3): 336-340.
[30]	LIANG Y Y, BAO S J, LI H L. A series of spinel phase cathode materials prepared by a simple hydrothermal process for rechargeable lithium batteries . Journal of Solid State Chemistry, 2006, 179(7): 2133-2140.
[31]	HJELM A K, LINDBERGH G. Experimental and theoretical analysis of LiMn2O4 cathodes for use in rechargeable lithium batteries by electrochemical impedance spectroscopy (EIS). Electrochimica Acta, 2002, 47(11): 1747-1759.
[32]	GUO Z P, ZHONG S, WANG G X. Structure and electrochemical characteristics of LiMn0.7M0.3O2(M=Ti, V, Zn, Mo, Co, Mg, Cr). Journal of Alloys and Compounds, 2003, 348(1/2): 231-235.
[33]	SHARMA Y, SHARMA N, SUBBA RAO G V. Lithium-storage and cycleability of nano-CdSnO3 as an anode material for lithium- ion batteries. Journal of Power Sources, 2009, 192(2): 627-635.

Co掺杂改性尖晶石型Li_1.035Mn_1.965O₄的合成及其电化学性能

Synthesis and Electrochemical Characterizations of Co-doped Lithium
Manganese Oxide Spinel Li_1.035Mn_1.965O₄

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 7

参考文献 33

相关文章 15

编辑推荐

Metrics

本文评价

[1]	谭博文, 耿双龙, 张锴, 郑百林. 硅电极组分梯度设计抑制力-化学耦合劣化[J]. 无机材料学报, 2025, 40(7): 772-780.
[2]	刘鹏东, 王桢, 刘永锋, 温广武. 硅泥在锂离子电池中的应用研究进展[J]. 无机材料学报, 2024, 39(9): 992-1004.
[3]	程节, 周月, 罗薪涛, 高美婷, 骆思妃, 蔡丹敏, 吴雪垠, 朱立才, 袁中直. 蛋黄壳结构FeF₃·0.33H₂O@N掺杂碳纳米笼正极材料的构筑及其电化学性能[J]. 无机材料学报, 2024, 39(3): 299-305.
[4]	胡梦菲, 黄丽萍, 李贺, 张国军, 吴厚政. 锂/钠离子电池硬碳负极材料的研究进展[J]. 无机材料学报, 2024, 39(1): 32-44.
[5]	苏楠, 邱介山, 王治宇. 高容量氟掺杂碳包覆纳米硅负极材料: 气相氟化法制备及其储锂性能[J]. 无机材料学报, 2023, 38(8): 947-953.
[6]	李跃军, 曹铁平, 孙大伟. S型异质结Bi₄O₅Br₂/CeO₂的制备及其光催化CO₂还原性能[J]. 无机材料学报, 2023, 38(8): 963-970.
[7]	李光兰, 王天宇, 刘一辰, 路中发. 片状NiFeCo-LDH-Ti₆C_3.75复合催化剂的制备及电催化析氧性能[J]. 无机材料学报, 2023, 38(7): 823-829.
[8]	杨卓, 卢勇, 赵庆, 陈军. X射线衍射Rietveld精修及其在锂离子电池正极材料中的应用[J]. 无机材料学报, 2023, 38(6): 589-605.
[9]	牛海滨, 黄佳慧, 李倩文, 马董云, 王金敏. 多孔NiMoO₄纳米片薄膜的直接水热生长及其电致变色性能[J]. 无机材料学报, 2023, 38(12): 1427-1433.
[10]	姚仪帅, 郭瑞华, 安胜利, 张捷宇, 周国治, 张国芳, 黄雅荣, 潘高飞. 原位负载Pt-Co高指数晶面催化剂的制备及其电催化性能[J]. 无机材料学报, 2023, 38(1): 71-78.
[11]	宿拿拿, 韩静茹, 郭印毫, 王晨宇, 石文华, 吴亮, 胡执一, 刘婧, 李昱, 苏宝连. 基于ZIF-8的三维网络硅碳复合材料锂离子电池性能研究[J]. 无机材料学报, 2022, 37(9): 1016-1022.
[12]	王洋, 范广新, 刘培, 尹金佩, 刘宝忠, 朱林剑, 罗成果. 钾离子掺杂提高锂离子电池正极锰酸锂性能的微观机制[J]. 无机材料学报, 2022, 37(9): 1023-1029.
[13]	朱河圳, 王选朋, 韩康, 杨晨, 万睿哲, 吴黎明, 麦立强. 超高镍LiNi_0.91Co_0.06Al_0.03O₂@Ca₃(PO₄)₂正极材料的储锂稳定性的提升机制[J]. 无机材料学报, 2022, 37(9): 1030-1036.
[14]	冯锟, 朱勇, 张凯强, 陈长, 刘宇, 高彦峰. 勃姆石纳米片增强锂离子电池隔膜性能研究[J]. 无机材料学报, 2022, 37(9): 1009-1015.
[15]	陈莹, 栾伟玲, 陈浩峰, 朱轩辰. 基于应力场的锂离子电池正极多尺度失效研究[J]. 无机材料学报, 2022, 37(8): 918-924.