Physical Properties of Ba(Ti0.96Sn0.04)O3 Ceramics

doi:10.15541/jim20160038

Abstract

Abstract:

The Ba(Ti_0.96Sn_0.04)O₃ ceramics were prepared through solid-state reaction route. Piezoelectric property, dielectric property, ferroelectric property, and microstructure were investigated. It is found that raw material and processing technique can largely affect the piezoelectric property of the Ba(Ti_0.96Sn_0.04)O₃ ceramics. By comparing with the physical property of pure BaTiO₃ ceramics, Sn doping significantly increases the transition temperature from orthorhombic phase to tetragonal phase (T_O-T) of the Ba(Ti_0.96Sn_0.04)O₃ ceramic to 36.9℃, while the thermal hysteresis at about T_O-T is only 1.8℃. Its microstructure shows complicated domain, mainly composed of simple 90° parallel stripes with a few of different 180° configurations. P-E curve shows ideal square-like and saturated form with remanent polarization P_r of 18.9 μC/cm² and coercive field E_c of 2.5 kV/cm. In addition, it is the non-180°-domain switching that leads large converse piezoelectric constant d₃₃^*, (up to 550 pm/V).

Key words: Ba(Ti0.96Sn0.04)O3, piezoelectric property, dielectric property, ferroelectric property, microstructure

CLC Number:

TQ174

WU Yan-Qing, ZHANG Jia-Liang, LIU Da-Kang, SUN Dan-Dan. Physical Properties of Ba(Ti_0.96Sn_0.04)O₃ Ceramics[J]. Journal of Inorganic Materials, 2016, 31(8): 850-854.

Figures/Tables 8

Table 1 Physical properties of BaTi0.96Sn0.04O3(BTS) and BaTiO3(BTO) ceramics at room temperature

	Fine-BTO	Coarse-BTO	BTS(Ref.[10])	BTS
ρ₀/%	98.1	98.4	97.8	97.8
g/μm	1.2	28.0	5.9	80.0
d₃₃/(pC·N^-1)	413	173	205	300
ε′(at 1 kHz)	3310	2910	3826	1855
T_O-T/℃	28.3	23.1	43.0	36.9
T_C/℃	121.2	123.5	92.2	92.4

Fig. 1 Unipolar electric field-strain S-E curves of BTS ceramics

Fig. 2 XRD patterns of BTS and BTO ceramics

Fig. 3 Variation of d33 with temperature for BTS and BTO ceramics

Fig. 4 ε′ versus temperature curves of the unpoled BTS and BTO ceramics

Fig. 5 Thermal hysteresis curves of the BTS and BTO ceramics

Fig. 6 P-E loops of BTS and BTO ceramics

Fig. 7 Optical images of BTS ceramics (a) Grain size; (b) Domain pattern

References 25

[1]	RÖDEL J, JO W, SEIFERT K T P, et al. Perspective on the development of lead-free piezoceramics.J. Am. Ceram. Soc., 2009, 92(6): 1153-1177.
[2]	JAFFE B, COOK W R, JAFFE H. Piezoelectric Ceramics. London: Academic, 1971: 253-269.
[3]	TAKAHASHI H, NUMAMOTO Y, TANI J, et al.Considerations for BaTiO3 ceramics with high piezoelectric properties fabricated by microwave sintering.Jpn. J. Appl. Phys., 2008, 47(11): 8468-8471.
[4]	KARAKI T, YAN K, MIYAMOTO T, et al.Lead-free piezoelectric ceramics with large dielectric and piezoelectric constants manufactured from BaTiO3 nano-powder.Jpn. J. Appl. Phys., 2007, 46(4-7): L97-L98.
[5]	WADA S, TAKEDA K, MURAISHI T, et al.Preparation of [110] grain oriented barium titanate ceramics by templated grain growth method and their piezoelectric properties.Jpn. J. Appl. Phys., 2007, 46(10S): 372-376.
[6]	SHAO S F, ZHANG J L, ZHANG Z, et.al. High piezoelectric properties and domain configuration in BaTiO3 ceramics obtained through solid-state reaction route. J. Phys D: Appl. Phys., 2008, 41(12): 125408-1-5.
[7]	ZHENG P, ZHANG J L, TAN Y Q, et.al. Grain-size effects on dielectric and piezoelectric properties of poled BaTiO3 ceramics.Acta Mater., 2012, 60(s13/14): 5022-5030.
[8]	ZHANG J L, JI P F, WU Y Q, et al. Strong piezoelectricity exhibited by large-grained BaTiO3 ceramics. Appl. Phys. Lett., 2014, 104(22): 222909-1-4.
[9]	WU Y Q, ZHANG J L, TAN Y Q, et al.Notable grain-size dependence of converse piezoelectric effect in BaTiO3 ceramics.Ceram. Int., 2016, 42: 9815-9820.
[10]	TAN Y Q, ZHANG J L, WU Y Q, et al. Unfolding grain size effects in barium titanate ferroelectric ceramics. Sci. Rep., 2015, 5: 9953-1-9.
[11]	ZHENG P, ZHANG J L, SHAO S F, et al. Piezoelectric properties and stabilities of CuO-modified Ba(Ti, Zr)O3ceramics, Appl. Phys.Lett., 2009, 94(3): 032902-1-4.
[12]	ZHANG J L, ZHANG Z, SHAO S F, et al, High piezoelectric performance and relevant physical mechanism of CuO-modified Ba(Ti0.96Sn0.04)O3 ceramics.J. Adv. Dielectr., 2011, 01(1): 79-84.
[13]	LI W, XU Z J, CHU C Q, et al, Temperature stability in Dy-doped (Ba0.99Ca0.01)(Ti0.98Zr0.02)O3 lead-free ceramics with high piezoelectric coefficient.J. Am. Ceram. Soc., 2011, 94(10): 3181-3183.
[14]	WANG H, WU J.Phase transition, microstructure, and electrical properties of Ca, Zr, and Sn-modified BaTiO3 lead-free ceramics.J. Alloys Compd., 2014, 615(9): 969-974.
[15]	CHEN M, XU Z, CHU R, et al.Y2O3-modified Ba(Ti0.96Sn0.04)O3 ceramics with improved piezoelectricity and raised Curie temperature.Mater. Res. Bull., 2014, 59(16): 305-310.
[16]	关振铎, 张中太, 焦金生. 无机材料物理性能. 北京: 清华大学出版社, 1992: 33-35.
[17]	DEVRIES R C, BURKE J E.Microstructure of barium titanate ceramics.J. Am. Ceram. Soc., 1957, 40(40): 200-206.
[18]	TAKAHASHI H, NUMAMOTO Y, TANI J, et al.Domain properties of high-performance barium titanate ceramics.Jpn. J. Appl. Phys., 2007, 46: 7044-7047.
[19]	ARLT G, SASKO P.Domain configuration and equilibrium size of domains in BaTiO3 ceramics.J. Appl. Phys., 1980, 51(9): 4956-4960.
[20]	ARLT G.Twinning in ferroelectric and ferroelastic ceramics: stress relief.J. Mater. Sci. , 1990, 25(6): 2655-2666.
[21]	ZHANG Q M, WANG H, KIM N, et al.Direct evaluation of domain-wall and intrinsic contributions to the dielectric and piezoelectric response and their temperature dependence on lead zirconate-titanate ceramics. J. Appl.Phys., 1994, 75(1): 454-459 .
[22]	DEMARTIN M, DAMJANOVIC D.Dependence of the direct piezoelectric effect in coarse and fine grain barium titanate ceramics on dynamic and static pressure.Appl. Phys. Lett., 1996, 68(21): 3046-3048.
[23]	GHOSH D, SAKATA A, CARTER J, et al.Domain wall displacement is the origin of superior permittivity and piezoelectricity in BaTiO3 at intermediate grain sizes.Adv. Funct. Mater., 2014, 24: 885-896.
[24]	CHEN DA-REN, LI GUO-RONG, YIN QING-RUI.Piezoelectric constants measurement from converse piezoelectric effect and piezoelectric ceramic actuators.Journal of Inorganic Materials, 1997, 12(6): 861-866.
[25]	TAN Y, ZHANG J, WANG C, et al.Enhancement of electric field-induced strain in BaTiO3 ceramics through grain size optimization.Phys. Status Solidi, 2015, 212(2): 433-438.

Physical Properties of Ba(Ti_0.96Sn_0.04)O₃ Ceramics

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 8

References 25

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	CHEN Xiangjie, LI Ling, LEI Tianfu, WANG Jiajia, WANG Yaojin. Enhanced Piezoelectric Properties of (1-x)(0.8PZT-0.2PZN)-xBZT Ceramics via Phase Boundary and Domain Engineering [J]. Journal of Inorganic Materials, 2025, 40(6): 729-734.
[2]	LI Wenyuan, XU Jianan, DENG Han'ao, CHANG Aimin, ZHANG Bo. Effect of V⁵⁺ Substitution on Microstructure and Microwave Dielectric Properties of LaTaO₄ Ceramics [J]. Journal of Inorganic Materials, 2025, 40(6): 697-703.
[3]	HUANG Zipeng, JIA Wenxiao, LI Lingxia. Crystal Structure and Terahertz Dielectric Properties of (Ti_0.5W_0.5)⁵⁺ Doped MgNb₂O₆ Ceramics [J]. Journal of Inorganic Materials, 2025, 40(6): 647-655.
[4]	YIN Changzhi, CHENG Mingfei, LEI Weicheng, CAI Yiyang, SONG Xiaoqiang, FU Ming, LÜ Wenzhong, LEI Wen. Effect of Ga³⁺ Doping on Crystal Structure Evolution and Microwave Dielectric Properties of SrAl₂Si₂O₈ Ceramic [J]. Journal of Inorganic Materials, 2025, 40(6): 704-710.
[5]	XIONG Siyu, MO Chen, ZHU Xiaowei, ZHU Guobin, CHEN Deqin, LIU Laijun, SHI Xiaodong, LI Chunchun. Low-temperature Sintering of LiB_xAl_1-_xSi₂O₆ Microwave Dielectric Ceramics with Ultra-low Permittivity [J]. Journal of Inorganic Materials, 2025, 40(5): 536-544.
[6]	MU Haojie, ZHANG Yuanjiang, YU Bin, FU Xiumei, ZHOU Shibin, LI Xiaodong. Preparation and Properties of ZrO₂ Doped Y₂O₃-MgO Nanocomposite Ceramics [J]. Journal of Inorganic Materials, 2025, 40(3): 281-289.
[7]	GAO Tianyu, LIU Dong, ZHAO Sixue, DENG Wei, ZHANG Boping, ZHU Lifeng. K_0.5Na_0.5NbO₃-based Piezoelectric Ceramics: Excellent Temperature Stability and Application in Type 1-3 Transducer [J]. Journal of Inorganic Materials, 2025, 40(3): 297-304.
[8]	HUANG Jianfeng, LIANG Ruihong, ZHOU Zhiyong. Effects of W/Cr Co-doping on the Crystal Structure and Electric Properties of CaBi₂Nb₂O₉ Piezoceramics [J]. Journal of Inorganic Materials, 2024, 39(8): 887-894.
[9]	FAN Wugang, CAO Xiong, ZHOU Xiang, LI Ling, ZHAO Guannan, ZHANG Zhaoquan. Anticorrosion Performance of 8YSZ Ceramics in Simulated Aqueous Environment of Pressurized Water Reactor [J]. Journal of Inorganic Materials, 2024, 39(7): 803-809.
[10]	CHEN Qian, SU Haijun, JIANG Hao, SHEN Zhonglin, YU Minghui, ZHANG Zhuo. Progress of Ultra-high Temperature Oxide Ceramics: Laser Additive Manufacturing and Microstructure Evolution [J]. Journal of Inorganic Materials, 2024, 39(7): 741-753.
[11]	JIANG Lingyi, PANG Shengyang, YANG Chao, ZHANG Yue, HU Chenglong, TANG Sufang. Preparation and Oxidation Behaviors of C/SiC-BN Composites [J]. Journal of Inorganic Materials, 2024, 39(7): 779-786.
[12]	ZHENG Yawen, ZHANG Cuiping, ZHANG Ruijie, XIA Qian, RU Hongqiang. Fabrication of Boron Carbide Ceramic Composites by Boronic Acid Carbothermal Reduction and Silicon Infiltration Reaction Sintering [J]. Journal of Inorganic Materials, 2024, 39(6): 707-714.
[13]	XUE Yifan, LI Weijie, ZHANG Zhongwei, PANG Xu, LIU Yu. Process Control of PyC Interphases Microstructure and Uniformity in Carbon Fiber Cloth [J]. Journal of Inorganic Materials, 2024, 39(4): 399-408.
[14]	SUN Chuan, HE Pengfei, HU Zhenfeng, WANG Rong, XING Yue, ZHANG Zhibin, LI Jinglong, WAN Chunlei, LIANG Xiubing. SiC-based Ceramic Materials Incorporating GNPs Array: Preparation and Mechanical Characterization [J]. Journal of Inorganic Materials, 2024, 39(3): 267-273.
[15]	PENG Ping, TAN Litao. Structure and Piezoelectric Properties of CuO-doped (Ba,Ca)(Ti,Sn)O₃ Ceramics [J]. Journal of Inorganic Materials, 2024, 39(10): 1100-1106.