掺杂钛催化机理及其再结晶石墨导热性能的研究

无机材料学报

掺杂钛催化机理及其再结晶石墨导热性能的研究

邱海鹏; 宋永忠; 郭全贵; 翟更太; 刘朗

中国科学院山西煤炭化学研究所太原 030001

收稿日期:2001-12-17 修回日期:2002-01-21 出版日期:2003-01-20 网络出版日期:2003-01-20

Thermal Conductivity and Catalytic Mechanism of Recrystallized Graphite by Titanium

QIU Hai-Peng; SONG Yong-Zhong; GUO Quan-Gui; ZHAI Geng-Tai; LIU Lang

Institute of Coal Chemistry; Chinese Academy of Sciences; Taiyuan 030001; China

Received:2001-12-17 Revised:2002-01-21 Published:2003-01-20 Online:2003-01-20

摘要/Abstract

摘要： 用煅烧石油焦作填料、煤沥青作粘结剂、钛粉作添加剂,采用热压工艺制备了一系列不同质量配比的掺杂钛再结晶石墨.考察了不同质量配比的添加钛对再结晶石墨的热导率、抗弯强度的影响以及微观结构的变化.实验结果表明,与相同工艺条件下制备的纯石墨材料相比较,掺杂钛再结晶石墨的热导率、抗弯强度均有较大的提高.室温下,RG-15再结晶石墨的层面方向热导率可达424W/(m·k),抗弯强度可达50.2MPa.微观结构分析表明,少量的掺杂钛,即可使材料达到很高的石墨化度;过多的钛掺杂量不利于材料的热导率以及抗弯强度;原料中掺钛量为15wt％时,再结晶石墨的微晶发育以及排列程度最好,此材料的石墨化度为96.4％,微晶参数La为306nm.XRD物相分析表明,钛元素在再结晶石墨中以碳化钛的形式存在.钛对再结晶石墨制备过程的催化作用可以用液相转化机理来解释.

关键词: 热导率, 再结晶石墨, 微观结构, 催化石墨化机理

Abstract: The recrystallized graphite was prepared from calcined coke, coal-tar pitch and titanium by hot-pressing
progress in order to investigate the effects of the amount of titanium on the thermal conductivity, bending strength and microstructure of
recrystallized graphite. Experimental results show that the recrystallized graphite exhibits higher thermal conductivity and higher bending
strength than the pure graphite prepared by the same process. For the orientation of graphite layers of the present RG-15 materials, the thermal
conductivity and the bending strength are 424W/(m·k) and 50.2MPa at room temperature, respectively. Microstructure analysis reveals that a
little amount of titanium can increase the degree of graphitization of recrystallized graphite, but overlarge amount of titanium dopant makes
basic physical properties worse. For the recrystallized graphite with titanium concentration of 15wt%, the degree of development and arrangement
of graphite crystallite is the best. The degree of graphitization of the present RG-15 material is 96.4% and the value of L_a is 306nm. XRD analysis
indicates that titanium added to carbon substrate is in the form of TiC precipitates. The catalytic role of titanium to preparing recrystallized
graphite can be explained by the liquid phase transition mechanism.

Key words: thermal conductivity, recrystallized graphite, microstructure, catalytic mechanism3

中图分类号:

TB332

邱海鹏,宋永忠,郭全贵,翟更太,刘朗. 掺杂钛催化机理及其再结晶石墨导热性能的研究[J]. 无机材料学报.

QIU Hai-Peng,SONG Yong-Zhong,GUO Quan-Gui,ZHAI Geng-Tai,LIU Lang. Thermal Conductivity and Catalytic Mechanism of Recrystallized Graphite by Titanium[J]. Journal of Inorganic Materials.

参考文献

[1] 孙乐民, 李贺军, 张守阳(SUN Le-Min, et al). 无机材料学?报(Journal of Inorganic Materials), 2000, 15 (6): 1111--1116.
[2] Fitzer E. Carbon, 1987, 25 (2): 163--190.
[3] Hugh O. Pieson, Handbook of Carbon, Graphite,Diamond and Fullenenesroperties, Processing and Application [M]. USA. Noyes Publication, 1993. 51--63.
[4] 王茂章, 贺福. 炭纤维及其复合材料. 北京: 化学工业出版社, 1996. 56.
[5] Garcia Rosales C, Roth J, Behrisch R. Journal of nuclear materials, 1994, (212-215): 1211--1217.
[6] Burtseva T A, Chugunoc O K, Dovguchits E F, et al. Journal of nuclear materials, 1992, (191-194): 309--314.
[7] Enweani B N, Davis J W, Haasz A A. Journal of nuclear materials, 1995, (224): 245--253.
[8] Rubel M, Almqvist N, Wienhold P, et al. Journal of nuclear materials, 1998, (258-263): 787--792.
[9] 邹林华, 黄启忠, 邹自强, 等. 炭素, 1998, (1): 8--11.
[10] 储九荣, 张晓辉, 徐传骧. 高分子材料科学与工程, 2000, 16 (4): 17--21.
[11] Mcquillan A D, Mquillan MK. Titanium [M]. London: Butterworths scientific publications, 1956. 187--190.
[12] Takahashi H, Kuroda H, Akamatu H. Carbon, 1964, 2: 432--433.
[13] Schwartz A S, Bokros J C. Carbon, 1967, 5: 325--330.
[14] Philip L, Walker J. Chemistry and physics of carbon [M]. New York, 1971. 7: 83--104.
[15] 周长江, 魏红, 陈朝辉. 宇航材料工艺, 2001, 1: 15--18.
[16] 中国化工百科全书委员会, 中国化工百科全书 [M]. 北京: 化学工?业出版社, 1998. 15: 754--760.
[17] 麦克格维仑 A D, 麦克格维仑 M K. 钛[M]. 北京: 冶金工业出版社, 1960. 188--191.
[18] 李圣华. 炭和石墨制品 [M]. 北京: 冶金工业出版社, 1983. 36--41.
[19] 谢有赞. 炭石墨材料工艺 [M]. 湖南大学出版社, 1988. 350--352.