热固性硅树脂压注法制备多孔硅基陶瓷型芯研究

doi:10.15541/jim20140280

无机材料学报 ›› 2015, Vol. 30 ›› Issue (2): 147-152.DOI: 10.15541/jim20140280 CSTR: 32189.14.10.15541/jim20140280

热固性硅树脂压注法制备多孔硅基陶瓷型芯研究

杨治刚, 余建波, 李传军, 玄伟东, 张振强, 邓康, 任忠鸣

(上海大学材料科学与工程学院, 上海市现代冶金和材料制备重点实验室, 上海200072)

收稿日期:2014-05-27 修回日期:2014-07-06 出版日期:2015-02-20 网络出版日期:2015-01-27
作者简介:杨治刚(1988–), 男, 博士研究生. E-mail:203yangzhigang@163.com
基金资助:
国家自然科学基金重点项目(50902140);上海市重大专项课题(08DZ1130100)

Preparing Porous Si-based Ceramic Core Using Thermosetting Silicon Resin Injection Method

YANG Zhi-Gang, YU Jian-Bo, LI Chuan-Jun, XUAN Wei-Dong, ZHANG Zhen-Qiang, DENG Kang, REN Zhong-Ming

(Department of Material Science and Engineering, Shanghai University Key Lab of Modern Metallurgy and Processing of Materials, Shanghai 200072, China)

Received:2014-05-27 Revised:2014-07-06 Published:2015-02-20 Online:2015-01-27
About author:YANG Zhi-Gang. E-mail:203yangzhigang@163.com
Supported by:
National Natural Science Foundation of China (50902140);Shanghai Postdoctoral Sustentation Fund, China (08DZ1130100)

摘要/Abstract

摘要：

以石英玻璃粉为基体, 热固性硅树脂为增塑剂, 利用压注方法制备了多孔硅基陶瓷型芯, 研究了烧结温度和保温时间对样品性能的影响。研究结果表明: 随着烧结温度的升高, 反玻璃化进程加快, 在烧结温度1250℃, 随着保温时间的延长, 玻璃相发生了转变, 逐渐析出方石英, 且含量不断增加; 样品的线收缩率和失重随烧结温度的升高略微增加, 但烧结时间的影响较小。样品的失重主要是由于硅树脂的分解引起的。在1250℃烧结10 h后, 得到样品的收缩率为0.93%, 显气孔率为32.8%, 抗弯强度为9.08 MPa。

关键词: 多孔, 硅树脂, 陶瓷型芯, 线收缩率, 抗弯强度, 显气孔率

Abstract:

The porous Si-based ceramic core was prepared using injection method, where quartz glass powders were used as original materials and thermosetting silicon resin was used as plasticizer. The effect of sintering temperature and holding time on the properties of the samples were examined. It was found that the process of devitrification was accelerated with the increase of sintering temperature while the glass phase transforms into cristobalite gradually. When sintering temperature was at 1250℃, the amount of cristobalite increased with the extension of holding time. Linear shrinkage rate and weight loss of the samples slightly increased with the increase of sintering temperature. But the holding time showed less effect on linear shrinkage rate and weight loss of the samples. In fact, the weight loss of the sample was mainly caused by decomposition of silicon resin. The sample sintered at 1250℃ for 10 h showed linear shrinkage of 0.93%, the porosity of 32.8% and bending strength of 9.08 MPa.

Key words: porous, silicon resin, ceramic core, linear shrinkage rate, bending strength, porosity

中图分类号:

TQ174

杨治刚, 余建波, 李传军, 玄伟东, 张振强, 邓康, 任忠鸣. 热固性硅树脂压注法制备多孔硅基陶瓷型芯研究[J]. 无机材料学报, 2015, 30(2): 147-152.

YANG Zhi-Gang, YU Jian-Bo, LI Chuan-Jun, XUAN Wei-Dong, ZHANG Zhen-Qiang, DENG Kang, REN Zhong-Ming. Preparing Porous Si-based Ceramic Core Using Thermosetting Silicon Resin Injection Method[J]. Journal of Inorganic Materials, 2015, 30(2): 147-152.

图/表 11

图1 硅树脂的热失重曲线

Fig. 1 TG analysis of silicone resin

图2 不同条件下制备样品的XRD图谱

Fig. 2 XRD patterns of the samples prepared at different conditions

图3 在1250℃烧结温度下, 不同保温时间制备的样品XRD图谱

Fig. 3 XRD patterns of the samples prepared at 1250℃ holding for 2 h (a), 6 h (b), 8 h (c) and 10 h (d)

图 4 在保温2 h下, 烧结温度对样品收缩率和失重的影响

Fig. 4 Linear shrinkage rate and weight loss of the samples prepared at different sintering temperature holding for 2 h

图 5 在1250℃烧结温度下, 保温时间对样品收缩率和失重的影响

Fig. 5 Linear shrinkage rate and weight loss of the samples prepared at 1250℃ for different holding time

图 6 在保温2 h下, 烧结温度对样品体积密度和显气孔率的影响

Fig. 6 Bulk-density and apparent porosity of the samples prepared at different sintering temperature and holding for 2 h

图 7 在1250℃烧结温度下, 保温时间对样品体积密度和显气孔率的影响

Fig. 7 Bulk-density and apparent porosity of the samples prepared at 1250℃ for different holding time

图 8 在保温2 h下, 烧结温度对样品室温抗弯强度的影响

Fig. 8 Bending strength of the samples prepared at different sintering temperature and holding for 2 h

图 9 在1250℃烧结温度下, 保温时间对样品室温抗弯强度的影响

Fig. 9 Bending strength of the samples prepared at 1250℃ for different holding time

图 10 不同条件下样品的断口形貌

Fig. 10 Fracture micrographs of the samples prepared at different conditions (a) green body; (b) 1200℃ for 2 h; (c) 1250℃ for 2 h; (d) 1300℃ for 2 h

图11 在1250℃烧结温度下, 不同保温时间样品的断口形貌

Fig. 11 Fracture micrographs of the samples prepared at 1250℃ for different holding time (a) 6 h, (b) 8 h and (c)10 h

参考文献 13

[1]	GU GUO-HONG, CAO LA-MEI.Development of ceramic cores for investment casting hollow blades.Foundry technology, 2002, 23(2): 81-83.
[2]	WANG FEI, LI FEI, LIU HE ZHOU, et al. Review of ceramic core for superalloy hollow blade.Aeronautical Manufacturing Technology, 2009(19): 60-64.
[3]	ZHANG LING, LIU JIAN-PING, SUN GE, et al.Preparation and properties of silica-based ceramic core for single crystal blades.Foundry, 2012, 61(8): 941-943.
[4]	LONG YONG-CHENG, LIU ZHI-YI, GUO MIN, et al.Effect of sintering temperature on properties of silica based ceramic core.Materials Science and Engineering of Powder Metallurgy, 2011, 16(4): 591-596.
[5]	CAO LA-MEI. The processing characters of ceramics core used for directional and single crystal blades. Materials Engineering, 1995(5): 20-21.
[6]	JIA MENG-QIU, DENG HAI-FENG.Synthesis of heat-resistant silicone resin.New Chemical Materials, 2007, 7(7) : 146-148.
[7]	MA YUE-XIN, LIU KUN, ZHOU NAN.Research on the per- formance of methyl phenyl silicone and its composite material.Chemistry and Adhesion, 2007, 29(6): 390-395.
[8]	GAO DA-HAI, JIA MENG-QIU, WU CHAO-BO, et al.New synthesis process of methyl phenyl silicone resin.Thermosetting Resin, 2009, 24(1): 1-4.
[9]	XU DONG-YANG, LI DI-CHEN, WU HAI-HUA, et al.Effect of yttrium aluminum garnet on high-temperature properties of alumina-based ceramic cores.Journal of Aeronautical Materials, 2011, 31(2): 67-71.
[10]	PAN JI-YONG, LIU XIAO-FU, HE LI-MING, et al.Research progress of silica-base ceramic core. Foundry, 2012, 61(2): 174-178.
[11]	HAN XIANG-NAN, LIU ZHI-YI, GUO MIN, et al.High-temperature strengthening technology of directional silica based ceramic core.Materials Science and Engineering of Powder Metallurgy. 2011, 16(5): 647-654.
[12]	XU XIAO-QIU, WU CHUAN, ZHANG BAO-HUA, et al.Preparation, structure characterization, and thermal performance of phenyl-Modified MQ silicone resins. Journal of Applied Polymer Science, 2013, 128(6): 4189-4200.
[13]	GARDELLE B, DUQUESNE S, RERAT V, et al.Thermal degradation and fire performance of intumescent silicone-based coatings.Polymers Advanced Technologies., 2013, 24(1): 62-69.

[1]	赵日达, 汤素芳. 多孔碳陶瓷化改进反应熔渗法制备陶瓷基复合材料研究进展[J]. 无机材料学报, 2024, 39(6): 623-633.
[2]	徐州, 刘宇轩, 池俊霖, 张婷婷, 王姝越, 李伟, 马春慧, 罗沙, 刘守新. 双模板-水热炭化制备马蹄形中空多孔炭及其电化学性能[J]. 无机材料学报, 2023, 38(8): 954-962.
[3]	王新玲, 周娜, 田亚文, 周明冉, 韩静茹, 申远升, 胡执一, 李昱. SnS₂/ZIF-8衍生二维多孔氮掺杂碳纳米片复合材料的锂硫电池性能研究[J]. 无机材料学报, 2023, 38(8): 938-946.
[4]	吴振, 李慧芳, 张中晗, 张振, 李阳, 蓝江河, 苏良碧, 武安华. 面向磁光应用的CeF₃晶体生长与性能表征[J]. 无机材料学报, 2023, 38(3): 296-302.
[5]	王鲁凯, 冯军宗, 姜勇刚, 李良军, 冯坚. 直写3D打印陶瓷基多孔结构的研究进展[J]. 无机材料学报, 2023, 38(10): 1133-1148.
[6]	吴松泽, 周洋, 李润丰, 刘晓倩, 李翠伟, 黄振莺. 铁尾矿及其反应烧结多孔陶瓷的制备与性能研究[J]. 无机材料学报, 2023, 38(10): 1193-1199.
[7]	冯锟, 朱勇, 张凯强, 陈长, 刘宇, 高彦峰. 勃姆石纳米片增强锂离子电池隔膜性能研究[J]. 无机材料学报, 2022, 37(9): 1009-1015.
[8]	李萌, 黄海露, 吴甲民, 刘春磊, 吴亚茹, 张景贤, 史玉升. 浆料固相含量对数字光处理成形Si₃N₄陶瓷性能的影响[J]. 无机材料学报, 2022, 37(3): 310-316.
[9]	李乔磊, 顾玥, 于雪华, 张朝威, 邹明科, 梁静静, 李金国. 烧结温度对3D打印硅基陶瓷型芯表面形貌及粗糙度的影响[J]. 无机材料学报, 2022, 37(3): 325-332.
[10]	吴西士, 朱云洲, 黄庆, 黄政仁. 树脂基多孔碳孔结构对C_f/SiC复合材料连接性能的影响[J]. 无机材料学报, 2022, 37(12): 1275-1280.
[11]	张航, 韩坤原, 董兰兰, 李祥. DLP打印β-磷酸三钙/纳米黏土复合支架的制备与表征[J]. 无机材料学报, 2022, 37(10): 1116-1122.
[12]	李昆儒, 胡省辉, 张正富, 郭玉忠, 黄瑞安. 源于溪木贼的高性能锂离子电池三维多孔生物质硅/碳复合负极材料[J]. 无机材料学报, 2021, 36(9): 929-935.
[13]	刘自若, 刘炜, 郝策, 胡金文, 史彦涛. 蜂窝状碳负载铁基单原子催化剂的制备及ORR催化性能研究[J]. 无机材料学报, 2021, 36(9): 943-949.
[14]	王为得, 陈寰贝, 李世帅, 姚冬旭, 左开慧, 曾宇平. 以YbH₂-MgO体系为烧结助剂制备高热导率高强度氮化硅陶瓷[J]. 无机材料学报, 2021, 36(9): 959-966.
[15]	陈力驰, 王耀功, 王文江, 麻晓琴, 杨静远, 张小宁. 电催化金属辅助化学刻蚀法制备硅纳米线/多孔硅复合结构[J]. 无机材料学报, 2021, 36(6): 608-614.

热固性硅树脂压注法制备多孔硅基陶瓷型芯研究

Preparing Porous Si-based Ceramic Core Using Thermosetting Silicon Resin Injection Method

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

图/表 11

参考文献 13

相关文章 15

编辑推荐

Metrics

本文评价