多壁碳纳米管/环氧有机硅树脂吸波涂层的介电和吸波性能研究

doi:10.3724/SP.J.1077.2010.00181

摘要/Abstract

摘要：

研究了不同直径和含量多壁碳纳米管填充环氧有机硅树脂吸波涂层在2～18GHz频率范围内的介电和吸波性能. 可以得到吸波涂层的介电常数随着碳纳米管含量的增加而增大. 当碳纳米管含量相同时, 吸波涂层介电常数随着碳纳米管直径的增加而增大. 当碳纳米管含量大于5wt%时, 吸波涂层的介电常数在低频急剧增加,且随频率增大而减少, 出现频散效应. 反射率测试结果表明：当涂层中多壁碳纳米管含量为10wt%、厚度为2mm时, 吸波涂层的最大吸收峰随碳纳米管直径的增大向低频移动. 多壁碳纳米管填充环氧有机硅树脂吸波涂层的吸波性能在7～14GHz范围内可达到-10dB, 具有较好的吸波效果.

关键词: 多壁碳纳米管, 介电性能, 吸波性能, 环氧有机硅树脂

Abstract:

Multi-walled carbon nanotubes as dielectric absorber and epoxy-silicone resin as matrix were used to fabricate multi-walled carbon nanotubes/epoxy-silicone resin coatings. The effects of multi-walled carbon nanotubes content and diameter on dielectric and microwave absorbing properties of the coatings were investigated in the frequency range from 2GHz to 18GHz. The results indicate that both of the real and imaginary part of the permittivity are enhanced with increasing multi-walled carbon nanotubes content and diameter. When the multi-walled carbon nanotubes content is 2wt%, the complex permittivity of the coatings keep almost constant in the frequency range from 2GHz to 18GHz, and are independent on the multi-walled carbon nanotubes diameter. As the multiwalled carbon nanotubes content increases to 5wt%, the complex permittivity of the coatings decreases with the increase of frequency, and also exhibits visible frequency-dependence dielectric response. The minimum reflection loss of the coatings shifts to the low frequency region (from 12.8GHz to 10.8GHz) as the multi-walled carbon nanotubes diameter increasing. The results of the microwave absorbing properties show that the good microwave absorption ability (below -10dB) can be obtained in a frequency range from 7GHz to 14GHz when the multi-walled carbon nanotubes content is 10wt% and the coating thickness is 2mm.

Key words: multi-walled carbon nanotubes, dielectric property, microwave absorbing property, epoxy-silicone resin

中图分类号:

TB332

卿玉长,周万城,罗发,朱冬梅. 多壁碳纳米管/环氧有机硅树脂吸波涂层的介电和吸波性能研究[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2010.00181.

QING Yu-Chang,ZHOU Wan-Cheng,LUO Fa,ZHU Dong-Mei. Electromagnetic and Absorbing Properties of Multi-walled Carbon Nanotubes/Epoxy-silicone Coatings
[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2010.00181.

参考文献

［1］Yusoff A N, Abdullah M H, Ahmad S H, et al. Electromagnetic and absorption properties of some microwave absorbers. J. App. Phys., 2002, 92(2): 876-882.

［2］Dresselhaus M S. Applied physics nanotube antennas.Nature, 2004, 432(7020): 959-960.

［3］Martel R, Schmidt T, Shea H R, et al. Single- and multi-wall carbon nanotube fieldeffect transistors. Appl. Phys. Lett., 1998, 73(17): 2447-2449.

［4］Andrews R, Jacques D, Qian D, et al. Purification and structural annealing of multiwalled carbon nanotubes at graphitization temperatures. Carbon, 2001, 39(11): 1681-1687.

［5］Makeiff Darren A, Huber Trisha. Microwave absorption by polyanilinecarbon nanotube composites.Synthetic Met., 2006,156(7/8):497-505.

［6］李建婷, 曹全喜, 姚娇艳, 等. 热酸氧化及镀镍对碳纳米管吸波性能的影响.功能材料与器件学报, 2007, 13(5): 443-448.

［7］林海燕, 朱红, 郭洪范, 等. Fe填充碳纳米管微波吸收材料的研究.北京交通大学学报, 2007, 31(3): 97-104.

［8］Watts P C P, Ponnampalam D R, Hsu W K, et al. The complex permittivity of multiwalled carbon nanotube-polystyrene composite films in X-band. Chem. Phys. Lett., 2003, 378(5/6): 609-614.

［9］Yang Y, Gupta M C, Dudley K L,et al. A comparative study of EMI shielding properties of carbon nanofiber and multi-walled carbon nanotube filled polymer composites. J. Nanosci. Nanotech., 2005, 5(6): 927-931.

［10］Mdarhri A, Carmona F, Brosseau C, et al. Direct current electrical and microwave properties of polymer-multiwalled carbon nanotubes composites. J. Appl. Phys., 2008, 103(5): 054303-1-9

［11］Li N, Huang Y, Du F, et al. Electromagnetic interference (EMI) shielding of single-walled carbon nanotube epoxy composites. Nano Lett., 2006, 6(6): 1141-1145.

［12］赵东林, 沈曾民 (ZHAO Dong-Lin, et al). 螺旋形手征碳纤维的微波介电特性. 无机材料学报(Journal of Inorganic Materials), 2003, 18(5): 1057-1062.

[1]	张育育, 吴轶城, 孙佳, 付前刚. 聚合物转化SiHfCN陶瓷的制备及其吸波性能[J]. 无机材料学报, 2024, 39(6): 681-690.
[2]	陈雷, 胡海龙. 柔性PDMS基介电复合材料的电场及击穿损伤形貌演变规律研究[J]. 无机材料学报, 2023, 38(2): 155-162.
[3]	韦婷婷, 徐华蕊, 朱归胜, 龙神峰, 张秀云, 赵昀云, 江旭鹏, 宋金杰, 郭宁杰, 龚祎鹏. BaTiO₃陶瓷的低温冷烧结制备及性能研究[J]. 无机材料学报, 2022, 37(8): 903-910.
[4]	姚晓刚, 彭海益, 顾忠元, 何飞, 赵相毓, 林慧兴. 聚苯醚/钙镧钛微波复合基板[J]. 无机材料学报, 2022, 37(5): 493-498.
[5]	叶芬, 江向平, 陈云婧, 黄枭坤, 曾仁芬, 陈超, 聂鑫, 成昊. (0.96NaNbO₃-0.04CaZrO₃)-xFe₂O₃反铁电陶瓷的介电及储能性能研究[J]. 无机材料学报, 2022, 37(5): 499-506.
[6]	孙扬善, 杨治华, 蔡德龙, 张正义, 柳琪, 房树清, 冯良, 石丽芬, 王友乐, 贾德昌. 粉末烧结法制备α-堇青石基玻璃陶瓷的析晶动力学和性能[J]. 无机材料学报, 2022, 37(12): 1351-1357.
[7]	张晓燕, 刘馨玥, 闫金华, 谷耀行, 齐西伟. 钙钛矿型(La_0.2Li_0.2Ba_0.2Sr_0.2Ca_0.2)TiO₃高熵氧化物陶瓷的制备及性能研究[J]. 无机材料学报, 2021, 36(4): 379-385.
[8]	武志红, 邓悦, 蒙真真, 张国丽, 张路平, 王宇斌. 含SiC阵列改性涂层的新型SiC/C_f复合材料吸波性能研究[J]. 无机材料学报, 2021, 36(3): 306-312.
[9]	王通,王渊浩,杨海波,高淑雅,王芬,鲁雅文. BaTiO₃-ZnNb₂O₆陶瓷介电及储能性能研究[J]. 无机材料学报, 2020, 35(4): 431-438.
[10]	简刚, 刘美瑞, 张晨, 邵辉. 用于高介电复合材料的全包裹Ag@TiO₂填充颗粒的制备[J]. 无机材料学报, 2019, 34(6): 641-645.
[11]	甘慧, 王传彬, 沈强, 张联盟. La₂NiMnO₆双钙钛矿陶瓷的等离子活化烧结[J]. 无机材料学报, 2019, 34(5): 541-545.
[12]	黄龙, 丁士华, 张晓云, 严欣堪, 李超, 朱惠. Li₂O-B₂O₃-SiO₂玻璃相对BaAl₂Si₂O₈结构及微波介电性能的影响[J]. 无机材料学报, 2019, 34(10): 1091-1096.
[13]	韩林材, 丁士华, 宋天秀, 黄龙, 张晓云, 熊中. ZBAS对BaAl₂Si₂O₈结构与微波介电性能的影响[J]. 无机材料学报, 2018, 33(8): 883-888.
[14]	刘甜甜, 王庆华, 刘希莉, 高凤, 汪庆祥. 近球状钼酸镍/多壁碳纳米管复合材料的制备及其赝电容性能[J]. 无机材料学报, 2018, 33(7): 735-740.
[15]	穆阳, 邓佳欣, 李皓, 周万城. 两种连续SiC纤维的高温介电及吸波性能对比[J]. 无机材料学报, 2018, 33(4): 427-433.