无定形晶种引导三次生长制备完备性TAPO-5膜

doi:10.15541/jim20140566

无机材料学报 ›› 2015, Vol. 30 ›› Issue (5): 555-560.DOI: 10.15541/jim20140566 CSTR: 32189.14.10.15541/jim20140566

• 研究快报 • 上一篇

无定形晶种引导三次生长制备完备性TAPO-5膜

刘旭光¹，马欣¹，刘勇¹，张宝泉^1,2

(1. 青岛科技大学材料科学与工程学院, 青岛266042; 2. 天津大学化工学院, 化学工程国家重点实验室, 天津 300072)

收稿日期:2014-11-06 修回日期:2014-12-03 出版日期:2015-05-20 网络出版日期:2015-04-28
基金资助:
National Natural Science Foundation of China (21136008); National Ocean Public Project of China (201405008)

Preparation of Perfective TAPO-5 Membrane through Tertiary Growth with Amorphous Seed

LIU Xu-Guang¹, MA Xin¹, LIU Yong¹, ZHANG Bao-Quan^1,2

(1. College of Materials Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042, China; 2. State Key Laboratory of Chemical Engineering, School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China)

Received:2014-11-06 Revised:2014-12-03 Published:2015-05-20 Online:2015-04-28
Supported by:
National Natural Science Foundation of China (21136008); National Ocean Public Project of China (201405008)

摘要/Abstract

摘要：

TAPO-5膜可以通过三次生长法制备。它的完备性与所用晶种以及膜的多晶结构密切相关。393 K下晶化所得无定形晶种有利于引导制备完备性TAPO-5膜。然而, 晶态TAPO-5晶种引导制备的TAPO-5膜存在大量的裂纹(即晶界缺陷), 这破坏了膜的完备性。这些不同结果可以通过SEM、XRD 和单组分气体渗透(He)测试进行说明。它与铺展润湿法所形成的晶种层的不同形式有关。无定形晶种层的典型特征是晶种分散于载体的大孔缺陷中。然而, 晶态TAPO-5将以连续晶种层的形式存在。因此, 无定形晶种更适合引导制备完备性TAPO-5膜。

关键词: 三次生长, 无定形晶种, TAPO-5膜, 铺展润湿法

Abstract:

TAPO-5 membranes were synthesized through a tertiary growth method. Its perfection significantly depends on the adopted seed and itself poly-crystalline structure. Amorphous seed synthesized at a low crystallization temperature (393 K), obviously favors producing the perfective TAPO-5 membrane. TAPO-5 crystal seed, however, induces the growth of its membrane with a larger extent of cracks (i.e., grain boundary defect), destructing itself perfection. Those diverse results are associated with the disparate seeds layers deposited by a spreading-wetting method, and consistently demonstrated by SEM, XRD, and single gas (He) permeation test. A typical feature of the amorphous TAPO-5 seed layer is its dispersive distribution pattern in the macro holes of support. A continuous layer, however, is observed for the TAPO-5 crystal seed layer. The amorphous seed is explained as a prior seed for the perfective TAPO-5 membrane.

Key words: tertiary growth, amorphous seed, TAPO-5 membrane, spreading-wetting method

中图分类号:

TQ174

刘旭光，马欣，刘勇，张宝泉. 无定形晶种引导三次生长制备完备性TAPO-5膜[J]. 无机材料学报, 2015, 30(5): 555-560.

LIU Xu-Guang, MA Xin, LIU Yong, ZHANG Bao-Quan. Preparation of Perfective TAPO-5 Membrane through Tertiary Growth with Amorphous Seed[J]. Journal of Inorganic Materials, 2015, 30(5): 555-560.

参考文献

[1] YU J H, XU R R. Rich structure chemistry in the aluminophosphate family. Accounts of Chemical Research, 2003, 36(7): 481–490.
[2] ZHAO X H, LI X B, CHEN J, et al. Ambient pressure synthesis of hierarchical structured SAPO-5 molecular sieve with special morphology. Journal of Inorganic Materials, 2014, 29(8): 821–826.
[3] SARA M, MUTHUSAMY V, MARIO C, et al. Elucidating the nature and reactivity of Ti ions incorporated in the framework of AlPO4-5 molecular sieves. New evidence from 31P HYSCORE spectroscopy. Journal of the American Chemical Society, 2011, 133(19): 7340–7343.
[4] LEE S O, RAJA R, HARRIS K D M, et al. Mechanistic insights into the conversion of cyclohexene to adipic acid by H2O2 in the presence of a TAPO-5 catalyst. Angewandte Chemie International Edition, 2013, 42(13): 1520–1523.
[5] WANG X B, GUO Y, ZHANG X F, et al. Catalytic properties of benzene hydroxylation by TS-1 film reactor and Pd–TS-1 composite membrane reactor. Catalysis Today, 2010, 156(3/4): 288–294.
[6] CHOI J, JEONG H-K, SNYDER M A, et al. Grain boundary defect elimination in a zeolite membrane by rapid thermal processing. Science, 2009, 325(5940): 590–593.
[7] YANG W S, ZHANG B Q, LIU X F. Synthesis and characterization of SAPO-5 membranes on porous α-Al2O3 substrates. Microporous and Mesoporous Materials, 2009, 117(1/2): 391–394.
[8] WANG X D, YAN J, HUANG W. Preparation and characterization of ultrafine crystal TS-1 films. Journal of Inorganic Materials, 2011, 26(1): 85–90.
[9] WANG J F, LIU X G, ZHANG P P, et al. Synthesis of continuous and dense TAPO-5 molecular sieve membranes by steam-assisted gel conversion method. Journal of Inorganic Materials. 2013, 28(6): 589–593.
[10] STOEGER J A, PALOMINO M, AGRAWAL K V, et al. Oriented CoSAPO-5 membranes by microwave-enhanced growth on TiO2- coated porous alumina. Angewandte Chemie International Edition, 2012, 51(10): 2470–2473.
[11] CARREON M A, LI S, FALCONER J L, et al. Alumina-supported SAPO-34 membranes for CO2/CH4 separation. Journal of the American Chemical Society, 2008, 130(16): 5412–5413.
[12] HUANG A, CARO J. Highly oriented, neutral and cation-free AlPO4 LTA: from a seed crystal monolayer to a molecular sieve membrane. Chemical Communications, 2011, 47(14): 4201–4203.
[13] SATO K, NAKANE T. A high reproducible fabrication method for industrial production of high flux NaA zeolite membrane. Journal of Membrane Science, 2007, 301(1/2): 151–161.
[14] DAS J K, DAS N, BANDYOPADHYAY S. Highly oriented improved SAPO-34 membrane on low cost support for hydrogen gas separation. Journal of Materials Chemistry A, 2013, 1(16): 4966–4973.
[15] ZHOU M, HEDLUND J. Assembly of oriented iron oxide and zeolite crystals via biopolymer films. Journal of Materials Chemistry, 2012, 22(47): 24877–24881.
[16] HUANG A, LIN Y S, YANG W. Synthesis and properties of A-type zeolite membranes by secondary growth method with vacuum seeding. Journal of Membrane Science, 2004, 245(1/2): 41–51.
[17] ALGIERI C, BERNARDO P, BARBIERI G, et al. A novel seeding procedure for preparing tubular NaY zeolite membranes. Microporous and Mesoporous Materials, 2009, 119(1/2/3): 129–136.
[18] LIU X G, XU L, ZHANG B Q, et al.Template removal from AFI aluminophosphate molecular sieve by Pd/SiO2 catalytic hydrocracking at mild temperature. Microporous and Mesoporous Materials, 2014, 193:127–133.
[19] CHEN S B, LIU X G, ZHANG B Q. Preparation and properties of porous α-Al2O3 based ceramic disk substrates. Journal of Inorganic Materials, 2013, 28(6): 599–604.
[20] KARANIKOLOS G N, WYDRA J W, STOEGER J A, et al. Continuous c-oriented AlPO4-5 films by tertiary growth. Chemistry of Materials, 2007, 19(4): 792–797.
[21] LANG L, LIU X F, ZHANG B Q. Synthesis and characterization of (h0h)-oriented silicalite-1 films on α-Al2O3 substrates. Appllied Surface Science, 2008, 254(8): 2353–2358.
[22] KANEZASHI M, O'BRIEN J, LIN Y S. Template-free synthesis of MFI-type zeolite membranes: permeation characteristics and thermal stability improvement of membrane structure. Journal of Membrane Science, 2006, 286(1/2): 213–222.
[23] HU E P, HUANG Y L W, YAN Q, et al. Synthesis of highly c-oriented AFI membranes by epitaxial growth. Microporous and Mesoporous Materials, 2009, 126(1/2): 81–86.
[24] KARANIKOLOS G N, GARCIA H, CORMA A, et al. Growth of AlPO4-5 and CoAPO-5 films from amorphous seeds. Microporous and Mesoporous Materials, 2008, 115(1/2): 11–22.
[25] PENG Y, ZHAN Z Y, SHAN L J, et al. Preparation of zeolite MFI membranes on defective macroporous alumina supports by a novel wetting-rubbing seeding method: role of wetting agent. Journal of Membrane Science, 2013, 444: 60–69.

无定形晶种引导三次生长制备完备性TAPO-5膜

Preparation of Perfective TAPO-5 Membrane through Tertiary Growth with Amorphous Seed

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	王萌萌, 田力, 张俊敏, 李庆刚, 杨金山, 董绍明. 3D打印制备CNT/SiC-SiO₂及其电磁屏蔽性能[J]. 无机材料学报, 2026, 41(6): 831-838.
[2]	洪恩柳, 涂欣晨, 李自清, 方晓生. 二维钙钛矿单晶纳米片的漂浮法制备及其光电探测性能[J]. 无机材料学报, 2026, 41(6): 787-794.
[3]	李涵涛, 沈强, 罗国强, 王雪飞, 高明, 陈晨. 机械球磨法调控硅基负极材料结构与性能的研究进展[J]. 无机材料学报, 2026, 41(5): 561-572.
[4]	钱新宇, 王无敌, 郭俊尧, 任永春, 董建树, 王庆国, 唐慧丽, 张晨波, 徐晓东, 董永军, 华伟, 徐军. Ho:BaF₂晶体在近红外-中红外波段光谱性能分析[J]. 无机材料学报, 2026, 41(5): 595-603.
[5]	李璇, 叶奎材, 冯佳音, 邱家军, 钱文昊, 邢敏. 钛基牙种植体表面改性促进软组织封闭的研究进展[J]. 无机材料学报, 2026, 41(4): 432-444.
[6]	王禹贺, 罗颐秀, 郭会明, 张广珩, 张思岩, 孙鲁超, 王杰民, 王京阳. 高熵稀土氧化物热障涂层材料弹性及热物性的第一性原理研究[J]. 无机材料学报, 2026, 41(4): 445-454.
[7]	朱开煌, 杨世杰, 李欣格, 宋贯卿, 史淦升, 王焱, 任小孟, 陆遥, 徐新宏, 孙静. 基于UiO-66骨架的氧化石墨烯改性金属有机框架凝胶的制备及其对甲苯的高效吸附性能[J]. 无机材料学报, 2026, 41(4): 519-526.
[8]	蒋圣楠, 郑重, 何唯一, 刘涛, 潘秀红, 陈锟, 郭辉, 高攀, 刘春俊, 刘学超. 硼镓共掺氧化锌透明电极的制备及性能优化[J]. 无机材料学报, 2026, 41(4): 479-485.
[9]	徐浩, 顾海涛, 吴鸿辉, 岳晓飞, 林思琪, 金敏. Bi掺杂InSe晶体生长及性能研究[J]. 无机材料学报, 2026, 41(4): 493-499.
[10]	张梦婕, 李智博, 黄瑞楠, 吕向菲, 王伟. 堇青石/硼酸铝晶须/Co_0.8Fe_xCe_0.2-_xCr₂O₄催化剂的制备及其碳烟过滤-催化燃烧性能[J]. 无机材料学报, 2026, 41(4): 509-518.
[11]	隋金洋, 周大雨, 赵文瑾, 童祎, 王新朋. 工作气压对AlScN薄膜结构和电学性能的影响[J]. 无机材料学报, 2026, 41(4): 486-492.
[12]	程澳芃, 王跃文, 许文涛, 刘全伟, 张海涛, 周有福. 吸附-沉淀自组装结合放电等离子烧结法制备石墨烯增强氧化铝复合陶瓷[J]. 无机材料学报, 2026, 41(4): 536-544.
[13]	田洪旺, 罗龙飞, 胡成龙, 闫猛, 庞生洋, 李建, 汤素芳. C/CA表面陶瓷-树脂涂层的简易制备与中温抗氧化性能[J]. 无机材料学报, 2026, 41(3): 401-408.
[14]	李泽熙, 卢文杰, 王朝, 张璐, 李述体, 高芳亮. 基于液态金属镓制备二维氮化镓及其光电性能研究[J]. 无机材料学报, 2026, 41(3): 377-384.
[15]	曹娟, 吴西士, 刘泽华, 裴兵兵, 韩建燊, 刘欢, 杨亦天, 吴海波, 黄政仁. 晶粒尺寸对常压固相烧结SiC陶瓷断裂强度Weibull分布的影响[J]. 无机材料学报, 2026, 41(2): 217-224.