Y2O3与Gd2O3共掺杂SrZrO3热障涂层材料的热物理性能

doi:10.3724/SP.J.1077.2012.00209

无机材料学报 ›› 2012, Vol. 27 ›› Issue (2): 209-213.DOI: 10.3724/SP.J.1077.2012.00209 CSTR: 32189.14.SP.J.1077.2012.00209

Y₂O₃与Gd₂O₃共掺杂SrZrO₃热障涂层材料的热物理性能

马文¹, 宋峰雨¹, 董红英², 许萍¹, 伦文山¹, 郑学斌³

(1. 内蒙古工业大学材料科学与工程学院, 呼和浩特 010051; 2. 内蒙古工业大学化工学院, 呼和浩特 010051; 3. 中国科学院上海硅酸盐研究所, 特种无机涂层重点实验室, 上海 200050)

收稿日期:2011-02-12 修回日期:2011-03-23 出版日期:2012-02-10 网络出版日期:2012-01-05
基金资助:
国家自然科学基金(51062012);教育部重点项目(210035);内蒙古自然科学基金(2009BS0802);中国科学院特种无机涂层重点实验室开放课题基金

Thermophysical Properties of Y₂O₃ and Gd₂O₃ Co-doped SrZrO₃ Thermal Barrier Coating Material

MA Wen¹, SONG Feng-Yu¹, DONG Hong-Ying², XU Ping¹, LUN Wen-Shan¹, ZHENG Xue-Bin³

(1. School of Materials Science and Engineering, Inner Mongolia University of Technology, Huhhot 010051, China; 2. School of Chemistry Engineering, Inner Mongolia University of Technology, Huhhot 010051, China; 3. Key Laboratory of Inorganic Coating Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China)

Received:2011-02-12 Revised:2011-03-23 Published:2012-02-10 Online:2012-01-05
Supported by:
National Natural Science Foundation of China (51062012);Key Project of Chinese Ministry of Education (210035);Natural Science Foundation of Inner Mongolia (2009BS0802);Opening Project of Key Laboratory of Inerganic Cating Materials, Chinese Academy of Sciences

摘要/Abstract

摘要：

采用固相反应法合成了5mol% Y₂O₃与5mol% Gd₂O₃共掺杂SrZrO₃(Sr(Zr_0.9Y_0.05Gd_0.05)O_2.95, SZYG)粉末. 采用X射线衍射(XRD)和差示扫描量热仪(DSC)分别研究了SZYG粉末在1450℃长期热处理后以及200~1400℃范围内的相稳定性. 采用高温热膨胀仪测量了SZYG块材的热膨胀系数, 结果表明: 通过Y₂O₃与Gd₂O₃共掺杂改性可以明显抑制SrZrO₃的相转变. 在1000℃下SZYG块材的热导率是~1.36 W/(m·K), 与SrZrO₃和8YSZ 块材相比降低~35% SZYG分别与8YSZ和Al₂O₃在1250℃热处理24 h表现出很好的化学相容性.

关键词: 热障涂层, 钙钛矿, 热物理性能, 稀土氧化物

Abstract:

Y₂O₃ (5mol%) and Gd₂O₃ (5mol%) co-doped SrZrO₃ (Sr(Zr_0.9Y_0.05Gd_0.05)O_2.95, SZYG) was synthesized by solid state reaction method. The phase stability of the SZYG powder synthesized at high temperature of 1450℃ for a long period and at temperature range of 200-1400℃ was characterized by XRD and DSC, respectively. The coefficients of thermal expansion (CTEs) of bulk SZYG recorded by a high-temperature dilatometer show that the phase transitions of SrZrO₃ is suppressed remarkably by co-doping Y₂O₃ and Gd₂O₃. The thermal conductivity of bulk SZYG at 1000℃ is 1.36 W/(m·K), which is 35% lower than that of bulk SrZrO₃ and 8YSZ. The good chemical compatibility of SZYG with 8YSZ and Al₂O₃, is detected after heat-treatment at 1250℃ for 24 h.

Key words: thermal barrier coatings, perovskite, thermophysical properties, rare earth oxides

中图分类号:

TG174

马文, 宋峰雨, 董红英, 许萍, 伦文山, 郑学斌. Y₂O₃与Gd₂O₃共掺杂SrZrO₃热障涂层材料的热物理性能[J]. 无机材料学报, 2012, 27(2): 209-213.

MA Wen, SONG Feng-Yu, DONG Hong-Ying, XU Ping, LUN Wen-Shan, ZHENG Xue-Bin. Thermophysical Properties of Y₂O₃ and Gd₂O₃ Co-doped SrZrO₃ Thermal Barrier Coating Material[J]. Journal of Inorganic Materials, 2012, 27(2): 209-213.

图/表 6

图1 SZYG粉末1450℃烧结不同时间后产物的XRD图谱

Fig. 1 XRD patterns of SZYG powder sintered at 1450℃ for different times

图2 SZYG与SrZrO3粉末的DSC曲线

Fig. 2 DSC curves of as-synthesized SZYG and SrZrO3 powders

图3 SZYG、Sr(Zr0.8Gd0.2)O2.9与SrZrO3块材的热膨胀系数

Fig. 3 Coefficients of thermal expansion of bulk SZYG, Sr(Zr0.8Gd0.2)O2.9 and SrZrO3

图4 SZYG、Sr(Zr0.8Gd0.2)O2.9与SrZrO3块材的热扩散系数

Fig. 4 Thermal diffusivities of bulk SZYG, Sr(Zr0.8Gd0.2)O2.9 and SrZrO3

图5 SZYG、Sr(Zr0.8Gd0.2)O2.9与SrZrO3块材的热导率

Fig. 5 Thermal conductivities of bulk SZYG, Sr(Zr0.8Gd0.2)O2.9 and SrZrO3

图6 SZYG+8YSZ(a)与SZYG+Al2O3(b)混合粉末在1250℃热处理24 h后的XRD图谱

Fig. 6 XRD patterns of SZYG+8YSZ (a) and SZYG+Al2O3 (b) mixtures after heat-treated at 1250℃ for 24 h

参考文献 29

[1]	Milller R. Thermal barrier coatings for aircraft engines: history and directions. J. Therm. Spray Technol., 1997, 6(1): 35-42.
[2]	Padture NP, Gell M, Jordan E. Thermal barrier coatings for gas-turbine engine applications. Science, 2002, 296(5566): 280-284.
[3]	Schulz U, Leyens C, Fritscher K, et al. Some recent trends in research and technology of advanced thermal barrier coatings. Aerosol Sci. Technol., 2003, 7(1): 73-80.
[4]	Rabiei A, Evans A. Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings. Acta Mater., 2000, 48(15): 3963-3976.
[5]	Clark D R, Levi C G. Materials design for the next generation thermal barrier coatings. Annu. Rev. Mater. Res., 2003, 33: 383-417.
[6]	Ilavsky J, Stalick J. Phase composition and its changes during annealing of plasma-sprayed YSZ. Surf. Coat. Technol., 2000, 127(2/3): 120-129.
[7]	Schulz U. Phase transformation in EB-PVD yttria partially stabilized zirconia thermal barrier coatings during annealing. J. Am. Ceram. Soc., 2000, 83(4): 904-910.
[8]	Levi CG. Emerging materials and processes for thermal barrier systems. Curr. Opin. Solid State Mater. Sci., 2004, 8(1): 77-91.
[9]	Zhu D, Fox DS, Bansal NP, et al. Advanced Oxide Material Systems for 1650℃ Thermal/environmental Barrier Coating Applications. NASA/TM-2004-213219, 2004.
[10]	Suresh G, Seenivasan G, Krishnaiah M, et al. Investigation of the thermal conductivity of selected compounds of lanthanum, samarium and europium. J. Alloy Compounds, 1998, 269(1/2): L9-L12.
[11]	Maloney M. Thermal Barrier Coating Systems and Materials. US Patent 6177200B1, 2001.
[12]	Vassen R, Cao X, Tietz F, et al. Zirconates as new materials for thermal barrier coatings. J. Am. Ceram. Soc., 2000, 83(8): 2023-2028.
[13]	Lehmann H, Pitzer D, Pracht G, et al. Thermal conductivity and thermal expansion coefficients of the lanthanum rare-earth-element zirconate system. J. Am. Ceram. Soc., 2003, 86(8): 1338-1344.
[14]	Padture N, Klemens P. Low thermal conductivity in garnets. J. Am. Ceram. Soc., 1997, 80(4): 1018-1020.
[15]	Sudre O, Cheung J, Marshall D, et al. Thermal Insulation Coatings of LaPO4. The 25th Annual International Conference on Composites, Advance Ceramics, Materials, and Structures, 2001: 367-374.
[16]	Gadow R, Lischka M. Lanthanum hexaaluminate — novel thermal barrier coatings for gas turbine applications — materials and process development. Surf. Coat. Technol., 2002, 151-152: 392-399.
[17]	Ma W, Gong S, Xu H, et al. The thermal cycling behavior of lanthanum cerium oxide thermal barrier coating prepared by EB-PVD. Surf. Coat. Technol., 2006, 200(16/17): 5113-5118.
[18]	Cao X, Vassen R, Fischer W, et al. Lanthanum-cerium oxide as a thermal barrier-coating material for high-temperature applications. Adv. Mater., 2003, 15(17): 1438-1442.
[19]	Ma W, Mack D, Vassen R, et al. Perovskite-type strontium zirconate as a new material for thermal barrier coatings. J. Am. Ceram. Soc., 2008, 91(8): 2630-2635.
[20]	Howard CJ, Knight KS, Kennedy B, et al. The structural phase transitions in strontium zirconate revisited. J. Phys.: Condens. Matter, 2000, 12(45): L677-L683.
[21]	Carlsson L. High-temperature phase transitions in SrZrO3. Acta Cryst., 1967, 23: 901-905.
[22]	Zhao Y, Weidner DJ. Thermal expansion of SrZrO3 and BaZrO3 perovskites. Phys. Chem. Minerals, 1991, 18(5): 294-301.
[23]	Ligny D, Richet P. High-temperature heat capacity and thermal expansion of SrTiO3 and SrZrO3 perovskites. Phys. Rev. B, 1996, 53(6): 3013-3022.
[24]	Ma W, Mack D, Malzbender J, et al. Yb2O3 and Gd2O3 doped strontium zirconate for thermal barrier coatings. J. Eur. Ceram. Soc., 2008, 28(16): 3071-3081.
[25]	Hayashi H, Saitou T, Maruyama N, et al. Thermal expansion coefficient of yttria stabilized zirconia for various yttria contents. Solid State Ionics, 2005, 176(5/6): 613-619.
[26]	Liu ZG, Ouyang JH, Zhou Y. Influence of gadolinia on thermal expansion property of ZrO2-4.5mol%Y2O3 ceramics. J. Alloys Compd., 2009, 473(1/2): L17-L19.
[27]	Schlichting K, Padture N, Klemens P. Thermal conductivity of dense and porous yttria-stabilized zirconia. J. Mater. Sci., 2001, 36(12): 3003-3010.
[28]	Zhu D, Miller R. Thermal Conductivity and Sintering Behavior of Advanced Thermal Barrier Coatings. NASA TM-2002-211481, 2002.
[29]	Zhu D, Miller R. Development of Advanced Low Conductivity Thermal Barrier Coatings. NASA TM-2004-212961, 2004.

Y₂O₃与Gd₂O₃共掺杂SrZrO₃热障涂层材料的热物理性能

Thermophysical Properties of Y₂O₃ and Gd₂O₃ Co-doped SrZrO₃ Thermal Barrier Coating Material

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

图/表 6

参考文献 29

相关文章 15

编辑推荐

Metrics

本文评价

[1]	瞿牡静, 张淑兰, 朱梦梦, 丁浩杰, 段嘉欣, 代恒龙, 周国红, 李会利. CsPbBr₃@MIL-53纳米复合荧光粉的合成、性能及其白光LEDs应用[J]. 无机材料学报, 2024, 39(9): 1035-1043.
[2]	肖梓晨, 何世豪, 邱诚远, 邓攀, 张威, 戴维德仁, 缑炎卓, 李金华, 尤俊, 王贤保, 林俍佑. 钙钛矿太阳能电池纳米纤维改性电子传输层研究[J]. 无机材料学报, 2024, 39(7): 828-834.
[3]	张慧, 许志鹏, 朱从潭, 郭学益, 杨英. 大面积有机-无机杂化钙钛矿薄膜及其光伏应用研究进展[J]. 无机材料学报, 2024, 39(5): 457-466.
[4]	陈甜, 罗媛, 朱刘, 郭学益, 杨英. 有机-无机共添加增强柔性钙钛矿太阳能电池机械弯曲及环境稳定性能[J]. 无机材料学报, 2024, 39(5): 477-484.
[5]	于嫚, 高荣耀, 秦玉军, 艾希成. 上转换发光纳米材料对钙钛矿太阳能电池迟滞效应和离子迁移动力学的影响[J]. 无机材料学报, 2024, 39(4): 359-366.
[6]	陈正鹏, 金芳军, 李明飞, 董江波, 许仁辞, 徐韩昭, 熊凯, 饶睦敏, 陈创庭, 李晓伟, 凌意瀚. 双钙钛矿Sr₂CoFeO₅₊_δ阴极材料的制备及其中温固体氧化物燃料电池性能研究[J]. 无机材料学报, 2024, 39(3): 337-344.
[7]	周泽铸, 梁子辉, 李静, 吴聪聪. 基于挥发性溶剂制备MAPbI₃钙钛矿太阳能电池/模组[J]. 无机材料学报, 2024, 39(11): 1197-1204.
[8]	厉佥元, 李纪伟, 张钰涵, 刘焱康, 孟阳, 储余, 朱一佳, 徐诺言, 朱亮, 张传香, 陶海军. PbTiO₃修饰和极化处理提升钙钛矿太阳能电池性能[J]. 无机材料学报, 2024, 39(11): 1205-1211.
[9]	代晓栋, 张露伟, 钱奕成, 任智鑫, 曹焕奇, 印寿根. 锡铅混合钙钛矿太阳能电池垂直组分梯度的溶剂工程调控[J]. 无机材料学报, 2023, 38(9): 1089-1096.
[10]	董思吟, 帖舒婕, 袁瑞涵, 郑霄家. 低维卤化物钙钛矿直接型X射线探测器研究进展[J]. 无机材料学报, 2023, 38(9): 1017-1030.
[11]	王润, 相恒阳, 曾海波. 钙钛矿多色级联发光二极管中多中心载流子均衡分布调控研究[J]. 无机材料学报, 2023, 38(9): 1062-1068.
[12]	王马超, 唐扬敏, 邓明雪, 周真真, 刘小峰, 王家成, 刘茜. 共沉淀法制备Cs₂Ag_0.1Na_0.9BiCl₆:Tm³⁺双钙钛矿及其近红外发光性能[J]. 无机材料学报, 2023, 38(9): 1083-1088.
[13]	韩旭, 姚恒大, 吕梅, 陆红波, 朱俊. 单分子液晶添加剂在甲脒铅碘钙钛矿太阳能电池中的应用[J]. 无机材料学报, 2023, 38(9): 1097-1102.
[14]	方万丽, 沈黎丽, 李海艳, 陈薪羽, 陈宗琦, 寿春晖, 赵斌, 杨松旺. NiO_x介孔层的成膜过程对碳电极钙钛矿太阳能电池性能的影响[J]. 无机材料学报, 2023, 38(9): 1103-1109.
[15]	蔡凯, 靳志文. 基于二维钙钛矿(PEA)₂PbI₄的光电探测器[J]. 无机材料学报, 2023, 38(9): 1069-1075.