脉冲激光沉积MnF2薄膜的电化学性能

doi:10.3724/SP.J.1077.2010.00145

摘要/Abstract

摘要： 采用脉冲激光沉积法在不锈钢基片上制备了纳米结构的MnF₂薄膜. 充放电测试显示该薄膜在2μA/cm²的放电电流下, 前50次循环具有350～530mAh/g的可逆容量.在循环伏安测试中得到了0.5和1.0V的可逆氧化还原峰,分别代表了MnF₂在充放电时的可逆反应. 薄膜的晶体结构和形貌采用X射线衍射仪（XRD）和扫描电子显微镜（SEM）分析, 充放电后薄膜的组成与结构通过高分辨电子显微镜和选区电子衍射来表征. 实验结果揭示了纳米结构MnF₂薄膜与Li的电化学反应机理, LiF在首次放电后形成的纳米粒子在过渡金属Mn颗粒的驱动下, 可以发生可逆的分解和形成. MnF₂薄膜较小的极化和较高的容量使其可用作锂离子电池阳极材料.

关键词: MnF₂, 薄膜, 脉冲激光沉积, 锂离子电池

Abstract: Nanostructured MnF₂ thin films were fabricated by using pulsed laser deposition on stainless steel substrate at room temperature. The reversible discharge capacities of MnF₂ thin film electrode in the ranges from 350mAh/g to 530mAh/g was achieved during the first 50 cycles at the current of 2μA/cm² from cyclic voltammograms curves of Li/MnF₂ cell. Reduction and oxidation peaks at 0.5V and 1.0V were detected which indicated the reversible formation and decomposition of reaction of MnF2. The structure and morphology of the as-deposited films were characterized by X-ray diffraction and scan electronic microscopy. The electrochemical reaction of MnF₂ thin film electrode was investigated by the high-resolution transmission electron microscope and selected-area electron diffraction measurements. The results demonstrated that nanosized manganese particles formed in initial discharge process could reversible drive the decomposition and formation of LiF. The low polarization and high capacity of MnF₂ thin film show that it is a promising lithiumstorage materials for future rechargeable lithium batteries.

Key words: MnF₂, thin film, pulsed laser deposition, lithium-ion batteries

中图分类号:

O646

崔艳华,薛明喆,胡可,李达,汪小琳,苏伟,刘效疆,孟凡明,傅正文. 脉冲激光沉积MnF₂薄膜的电化学性能[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2010.00145.

CUI Yan-Hua,XUE Ming-Zhe,HU Ke,LI Da,WANG Xiao-Lin,SU Wei,LIU Xiao-Jiang,MENG Fan-Ming,FU Zheng-Wen. Electrochemical Properties of MnF₂ Films Fabricated by Pulsed Laser Deposition
[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2010.00145.

参考文献

［1］Poizot P, Laruelle S, Grugeon S, et al. Nano-sizedtransitionmetaloxidesas negative-electrode materials for lithiumion batteries. Nature, 2000, 407: 496-499.

［2］Pereira N, Dupont L, Tarascon J M, et al. Electrochemistry of Cu₃N with lithium a complex system with parallel processes. J. Electrochem. Soc., 2003, 150(9): A1273-1286.

［3］Pereira N, Klein L C, Amatucci G G, et al. The electrochemistry of Zn₃N₂ and LiZnN a lithium reaction mechanism for metal nitride electrodes. J. Electrochem. Soc., 2002, 149(3): A262-A271.

［4］王颖, 刘文元, 傅正文, 等(WANG Ying, et al). Mn₄N薄膜与锂的电化学反应性能.物理化学学报(Acta Phys.-Chim. Sin.), 2006, 22(1): 65-70.

［5］Débart A, Dupont L, Patrice R, et al. Reactivity of transition metal (Co, Ni, Cu) sulphides vs lithium: the intriguing case of the copper sulphide. Solid State Sci., 2006, 8(6): 640-651.

［6］Souza D C S, Pralong V, Jacobson A J, et al. A reversible solid-state crystalline transformation in a metal phosphide induced by redox chemistry. Science, 2002, 296(5575): 2012-2015.

［7］Bichat M P, Politova T, Pascal J L, et al. Electrochemical reactivity of Cu₃P with lithium. J. Electrochem. Soc., 2004, 151(2): A2074-A2081.

［8］Silva D C C, Crosnier O, Ouvrard G., et al. Reversible lithium uptake by FeP2. Electrochem. SolidState Lett., 2003, 6(8): A162-A165.

［9］Gillot F, Boyanov S, Dupont L, et al. On the reactivity of Li_8-yMn_yP₄ toward lithium. Chem. Mater., 2005, 17(25): 3627-3635.

［10］Wang K, Yang J, Xie J Y, et al. Electrochemical reactions of lithium with CuP₂ and Li_1.75Cu_1.25P₂ synthesized by ballmilling. Electrochem. Commun., 2003, 5(6): 480-483.

［11］薛明喆, 傅正文(XUE Ming-Zhe, et al). 脉冲激光沉积法制备FeSe薄膜电极及其电化学性质. 化学学报(Acta Chim. Sinica), 2007, 65(23): 2715-2719.

［12］Xue M Z, Fu Z W. Lithium electrochemistry of NiSe₂: a new kind of storage energy material. Electrochem. Commun., 2006, 8(12): 1855-1862.

［13］Li H, Richter G, Maier J. Reversible formation and decomposition of LiF clusters using transition metal fluorides as precursors and their application in rechargeable Li batteries. Adv. Mater. (Weinheim, Ger.), 2003, 15(19): 736-739.

［14］Li H, Balaya P, Maier J. Listorage via heterogeneous reaction in selected binary metal fluorides and oxides. J. Electrochem. Soc., 2004, 151(11): A1878-A1885.

［15］Badway F, Pereira N, Cosandey F, et al. Carbon metal fluoride nanocomposites high-capacity reversible metal fluoride conversion materials as rechargeable positive electrodes for Li batteries. J. Electrochem. Soc., 2003, 150(10): A1318-A1327.

［16］Badway F, Pereira N, Cosandey F, et al. Carbon-metal fluoride nanocomposites structure and electrochemistry of FeF3∶C. J. Electrochem. Soc., 2003, 150(9): A1209-A1218.

［17］Plitz I, Badway F, AlSharab J, et al. Structure and electrochemistry of carbonmetal fluoride nanocomposites fabricated by solid-state redox conversion reaction. J. Electrochem. Soc., 2005, 152(2): A307-A315.

［18］Badway F, Mansour A N, Pereira N, et al. Structure and electrochemistry of copper fluoride nanocomposites utilizing mixed conducting matrices.Chem. Mater., 2007, 19(17): 4129-4141.

［19］Makimura Y, Rougier A, Laffont L, et al. Electrochemical behaviour of low temperature grown iron fluoride thin films. Electrochem. Commun., 2006, 8(11): 1769-1774.

［20］Makimura Y, Rougier A, Tarascon J M. Pulsed laser deposited iron fluoride thin films for lithium-ion batteries. Appl. Suf. Sci., 2006, 252(13): 4587-4592.

［21］张华, 周永宁, 吴晓京, 等(ZHANG Hua, et al). 脉冲激光沉积CuF₂薄膜的电化学性能. 物理化学学报(Acta Phys.-Chim. Sin.), 2008, 24(07): 1287-1291.

［22］Zhang H, Zhou Y N, Sun Q, et al. Nanostructured nickel fluoride thin film as a new Li storage material. Solid State Sci., 2008, 10(9): 1166-1172.

［23］Fu Z W, Li C L, Liu W Y, et al. Electrochemical reaction of lithium with cobalt fluoride thin film electrode. J. Electrochem. Soc., 2005, 152(2): E50-E55.

［24］Zhou Y N, Zhang H, Xue M Z, et al. The electrochemistry of nanostructured In₂O₃ with lithium. J. Power Sources, 2006, 162(2): 1373-1378.

［25］Laruelle S, Grugeon S, Poizot P, et al. On the origin of the extra electrochemical capacity displayed by MO/Li cells at low potential. J. Electrochem. Soc., 2002, 149(5): A627-A634.

[1]	刘鹏东, 王桢, 刘永锋, 温广武. 硅泥在锂离子电池中的应用研究进展[J]. 无机材料学报, 2024, 39(9): 992-1004.
[2]	赵志翰, 郭鹏, 魏菁, 崔丽, 刘山泽, 张文龙, 陈仁德, 汪爱英. Ti-DLC薄膜压阻性能及载流子输运行为研究[J]. 无机材料学报, 2024, 39(8): 879-886.
[3]	张慧, 许志鹏, 朱从潭, 郭学益, 杨英. 大面积有机-无机杂化钙钛矿薄膜及其光伏应用研究进展[J]. 无机材料学报, 2024, 39(5): 457-466.
[4]	程节, 周月, 罗薪涛, 高美婷, 骆思妃, 蔡丹敏, 吴雪垠, 朱立才, 袁中直. 蛋黄壳结构FeF₃·0.33H₂O@N掺杂碳纳米笼正极材料的构筑及其电化学性能[J]. 无机材料学报, 2024, 39(3): 299-305.
[5]	鲍可, 李西军. 化学气相沉积法制备智能窗用热致变色VO₂薄膜的研究进展[J]. 无机材料学报, 2024, 39(3): 233-258.
[6]	杨志亮, 杨鏊, 刘鹏, 陈良贤, 安康, 魏俊俊, 刘金龙, 吴立枢, 李成明. 热管理用3英寸硅衬底金刚石薄膜的制备[J]. 无机材料学报, 2024, 39(3): 283-290.
[7]	刘松, 张发强, 罗进, 刘志甫. 0.9BaTiO₃-0.1Bi(Mg_1/2Ti_1/2)O₃铁电薄膜制备及储能特性[J]. 无机材料学报, 2024, 39(3): 291-298.
[8]	徐向明, Husam N ALSHAREEF. MXetronics—MXene电子学[J]. 无机材料学报, 2024, 39(2): 171-178.
[9]	任冠源, 李宜冠, 丁冬海, 梁瑞虹, 周志勇. CaBi₂Nb₂O₉铁电薄膜的生长取向调控和性能研究[J]. 无机材料学报, 2024, 39(11): 1228-1234.
[10]	张哲, 孙婷婷, 王连军, 江莞. 不同维度Ag₂Se构筑柔性热电薄膜的性能优化与器件集成研究[J]. 无机材料学报, 2024, 39(11): 1221-1227.
[11]	戴乐, 刘洋, 高轩, 王书豪, 宋雅婷, 唐明猛, 刘丽莎, 汪尧进. 浓度梯度掺杂实现BiFeO₃薄膜自极化[J]. 无机材料学报, 2024, 39(1): 99-106.
[12]	胡梦菲, 黄丽萍, 李贺, 张国军, 吴厚政. 锂/钠离子电池硬碳负极材料的研究进展[J]. 无机材料学报, 2024, 39(1): 32-44.
[13]	胡盈, 李自清, 方晓生. 溶液法制备AgBi₂I₇薄膜及其光电探测性能研究[J]. 无机材料学报, 2023, 38(9): 1055-1061.
[14]	苏楠, 邱介山, 王治宇. 高容量氟掺杂碳包覆纳米硅负极材料: 气相氟化法制备及其储锂性能[J]. 无机材料学报, 2023, 38(8): 947-953.
[15]	杨卓, 卢勇, 赵庆, 陈军. X射线衍射Rietveld精修及其在锂离子电池正极材料中的应用[J]. 无机材料学报, 2023, 38(6): 589-605.

脉冲激光沉积MnF₂薄膜的电化学性能

Electrochemical Properties of MnF₂ Films Fabricated by Pulsed Laser Deposition

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价