Structure and Water-resistance of Rare-earth Luminescent Materials Coated with Si and Al

doi:10.3724/SP.J.1077.2007.00499

Abstract

Abstract: The rare-earth luminescent materials coated with Si and Al were prepared by the sol-gel route. The result of FL measurement indicates that the coated sample has the similar luminescent properties to that of the uncoated. The compositions, microstructure, texture and surface morphology of the binary films containing Si and Al elements were investigated by SEM,XRD,BET and XPS. Water-resistance of the coated and uncoated samples was evaluated by measuring the pH of water in which the samples were dispersed. The results show that a thin dense binary film containing Si and Al elements forms on the surface of the sample through chemical interactions, which can enhance the uncoated sample’s stability under water-containing conditions.

Key words: rare-earth luminescent materials, sol-gel, coating, structure

CLC Number:

TQ422

LUO Yong-Yue,PENG Lei-Lei,DAN Yi,ZHANG Li,ZHAO Kun. Structure and Water-resistance of Rare-earth Luminescent Materials Coated with Si and Al[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2007.00499.

References

[1] Picht, Friederike, Merikhi, et al. Phosphor composition comprising
fine-grain and coarse-grain SiO2 particles. United States Patent, No. 6,010,779, 2000-1-4.
[2] Picht, Friederike,Bredol, et al. Phosphor composition with a coating of colloidal SiO2 particles and an oxygen compound of magnesium, calcium, barium, zinc or aluminum. United States Patent, No. 6,013,979, 2000-1-11.
[3] 崔洪涛, 张耀文, 洪广言. 功能材料, 2001, 32 (6): 564--569.
[4] ZHANG Jun-ying, CHEN Qing-ming, LIN Yuan-hua, et al. Rear Metals, 2002, 21 (2): 152--155.
[5] 周文华, 刘又年, 吕兴栋, 等. 广州化工, 2004, 32 (4): 31--33.
[6] 吕兴栋, 舒万艮, 谭爱东, 等. (LU Xing-Dong, et al). 无机材料学报(Journal of Inorganic Materials), 2004, 19 (6): 1373--1378.
[7] 罗昔贤, 郑笑全, 段锦霞, 等(LUO Xi-Xian, et al). 硅酸盐学报(Journal of the Chinese Ceramic Society), 2003, 31 (11): 1058--1062.
[8] Kozuka, Ko, Kobayashi, et al. Polymerizable emulsifying agent and
application thereof. United States Patent. No. 3, 980, 622, 1976-9-14.
[9] Goebel K H, Stahler K, von Berlepsch H. Colloids and Surfaces A: 1994, 87: 143--149.
[10] 李强, 高濂, 严东生(LI Qiang, et al). 无机材料学报(Journal of Inorganic Materials), 1999, 14 (1): 150--154.
[11] 熊蓉春, 曹朋, 王连盛, 等. 北京化工大学学报, 2005, 32 (3): 61--65.
[12] 曹福想, 严坤, 张科元. 南方金属, 2005, 144: 20--23.
[13] 李大东, 钟孝湘编译. 催化剂载体与负载型催化剂, 第一版. 北京: 中国石化出版社, 1992. 15--24.
[14] 熊煜虹, 王东, 陆毅青, 等(XIONG Yu-Hong, et al). 无机材料学报(Journal of Inorganic Materials), 2003, 18 (2): 451--456.
[15] 肖志国, 罗昔贤. 蓄光型发光材料及其制品, 第二版. 北京: 化学工业出版社, 2005. 177.