Preparation and Luminescence Properties of Flexible Eu3+ Doped SiO2 Fibrous Membranes

doi:10.15541/jim20140659

Abstract

Abstract:

Eu³⁺ doped SiO₂ fibrous membranes were prepared by Sol-Gel and electrospinning methods. The obtained samples were chacterized by SEM, XRD, FT-IR, TG, PL, etc. By heat-treatment, the organic components were removed slowly and the diameters of the Eu³⁺ doped SiO₂ fibers decreased. SEM images exhibit that the surface of the fibers retains smooth and uniform after heat-treatment. By controlling the heating rate, the Eu³⁺ doped SiO₂ fibrous membranes present relatively high tensile strength at about 4.31 MPa after heat-treatment at 750℃. The samples exhibit no cracks after bending and recovering process. By excited by 392.6 nm light, the emission peaks between 570-670 nm are observed, which attributes to the ⁵D₀→⁷F_Jtransition. The strongest emission peak situates at 616 nm results from Eu^{3+ 5}D₀→⁷F₂ transition. The optimal heat-treatment temperature is 750℃. PL spectra also show that the luminescence intensity attains the highest value at the concentration of 8mol% Eu³⁺doped.

Key words: electrospinning, flexible, SiO2 fibrous membranes, luminescence properties

CLC Number:

TB34

ZHANG SHU-XIAN, CUI BO, WANG HONG-ZHI, LI YAO-GANG, ZHANG QING-HONG. Preparation and Luminescence Properties of Flexible Eu³⁺Doped SiO₂ Fibrous Membranes[J]. Journal of Inorganic Materials, 2015, 30(7): 719-724.

Figures/Tables 9

Fig. 1 SEM images of fibrous membranes before (a) and after (b) heating treatment

Fig. 2 X-ray diffraction patterns for fibrous membranes after heat-treatment at different temperatures

Fig. 3 FT-IR spectra of the fibrous membranes before (a) and after (b) heat-treatment at 650℃

Fig. 4 TG curves of hybrid fibrous membranes (a) and PVA powder (b)

Fig. 5 Photographs of the blending sample (a) and the sample for testing (b)

Fig. 6 Strength of fibrous membranes change with heat-treatment temperature (a) and 4% tensile recycle curve of fibrous membranes (b)

Fig. 7 Excitation and emission spectra of fibrous membranes (a) λem=616 nm; (b) λex=392.6 nm

Fig. 8 Emission spectra (a) and intensity ratio of 5D0→7F2 transition to 5D0→7F1 transition (b) of fibrous membranes heat-treated at different temperatures

Fig. 9 Emission spectra of fibrous membranes for different concentrations of Eu3+

References 19

[1]	GU Y, ZHANG Q, WANG H, et al.CaSi2O2N2: Eu nanofiber mat based on electrospinning: facile synthesis, uniform arrangement, and application in white LEDs. Journal of Materials Chemistry, 2011, 21(44): 17790-17797.
[2]	YU H, SONG H, PAN G, et al.Preparation and luminescent properties of europium-doped yttria fibers by electrospinning.Journal of luminescence, 2007, 124(1): 39-44.
[3]	ZHANG P, JIAO X, CHEN D.Fabrication of electrospun Al2O3 fibers with CaO-SiO2 additive.Materials Letters, 2013, 91: 23-26.
[4]	QIANG W, JIAN D, JIANG L, et al.Flexible inorganic nanofibrous membranes with hierarchical porosity for efficient water purification. Chemical Science, 2013, 4(12): 4378-4382.
[5]	CHEN Y, MAO X, SHAN H, et al.Free-standing zirconia nanofibrous membranes with robust flexibility for corrosive liquid filtration.RSC Advances, 2014, 4(6): 2703-2710.
[6]	YANG L, RAZA A, SI Y, et al.Synthesis of superhydrophobic silica nanofibrous membranes with robust thermal stability and flexibility via in situ polymerization.Nanoscale, 2012, 4(20): 6581-6587.
[7]	FRANZO G, VINCIGUERRA V, PRIOLO F.The excitation mechanism of rare-earth ions in silicon nanocrystals.Applied Physics A, 1999, 69(1): 3-12.
[8]	YU M, LIN J, FANG J.Silica spheres coated with YVO4: Eu3+ layers via Sol-Gel process: a simple method to obtain spherical core-shell phosphors.Chemistry of Materials, 2005, 17(7): 1783-1791.
[9]	PETIT L, GRIFFIN J, CARLIE N, et al.Luminescence properties of Eu3+ or Dy3+, Au co-doped SiO2 nanoparticles. Materials Letters, 2007, 61(14): 2879-2882.
[10]	JIN T, TSUTSUMI S, DEGUCHI Y, et al.Preparation and luminescence characteristics of the europium and terbium complexes incorporated into a silica matrix using a Sol-Gel method.Journal of Alloys and Compounds, 1997, 252(1): 59-66.
[11]	BAUMGARTEN P K.Electrostatic spinning of acrylic microfibers. Journal of Colloid and Interface Science, 1971, 36(1): 71-79.
[12]	MUNIR M M, SURYAMAS A B, ISKANDAR F, et al.Scaling law on particle-to-fiber formation during electrospinning.Polymer, 2009, 50(20): 4935-4943.
[13]	SHENOY S L, BATES W D, FRISCH H L, et al.Role of chain entanglements on fiber formation during electrospinning of polymer solutions: good solvent, non-specific polymer-polymer interaction limit.Polymer, 2005, 46(10): 3372-3384.
[14]	THERON S A, ZUSSMAN E, YARIN A L.Experimental investigation of the governing parameters in the electrospinning of polymer solutions.Polymer, 2004, 45(6): 2017-2030.
[15]	INNOCENZI P.Infrared spectroscopy of Sol-Gel derived silica- based films: a spectra-microstructure overview. Journal of Non- Crystalline Solids, 2003, 316(2): 309-319.
[16]	SHAO C, KIM H Y, GONG J, et al.Fiber mats of poly (vinyl alcohol)/silica composite via electrospinning.Materials Letters, 2003, 57(9): 1579-1584.
[17]	CHOI S S, LEE S G, IM S S, et al.Silica nanofibers from electrospinning/Sol-Gel process.Journal of Materials Science Letters, 2003, 22(12): 891-893.
[18]	NOGAMI M, ABE Y.Properties of Sol-Gel-derived Al2O3-SiO2 glasses using Eu3+ ion fluorescence spectra.Journal of Non-crystalline Solids, 1996, 197(1): 73-78.
[19]	孙家跃, 杜海燕, 胡文祥. 固体发光材料. 北京: 化学工业出版社, 2003: 88-94.

Preparation and Luminescence Properties of Flexible Eu³⁺Doped SiO₂ Fibrous Membranes

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 9

References 19

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	WEI Xiangxia, ZHANG Xiaofei, XU Kailong, CHEN Zhangwei. Current Status and Prospects of Additive Manufacturing of Flexible Piezoelectric Materials [J]. Journal of Inorganic Materials, 2024, 39(9): 965-978.
[2]	CHEN Tian, LUO Yuan, ZHU Liu, GUO Xueyi, YANG Ying. Organic-inorganic Co-addition to Improve Mechanical Bending and Environmental Stability of Flexible Perovskite Solar Cells [J]. Journal of Inorganic Materials, 2024, 39(5): 477-484.
[3]	LI La, SHEN Guozhen. 2D MXenes Based Flexible Photodetectors: Progress and Prospects [J]. Journal of Inorganic Materials, 2024, 39(2): 186-194.
[4]	ZHANG Zhe, SUN Tingting, WANG Lianjun, JIANG Wan. Flexible Thermoelectric Films with Different Ag₂Se Dimensions: Performance Optimization and Device Integration [J]. Journal of Inorganic Materials, 2024, 39(11): 1221-1227.
[5]	ZHAO Yawen, QU Fajin, WANG Yanyi, WANG Zhiwen, CHEN Chusheng. Preparation and Properties of Aluminum Silicate Fiber Supported PtTFPP-PDMS Flexible Oxygen Sensing Components [J]. Journal of Inorganic Materials, 2024, 39(10): 1084-1090.
[6]	YANG Yang, CUI Hangyuan, ZHU Ying, WAN Changjin, WAN Qing. Research Progress of Flexible Neuromorphic Transistors [J]. Journal of Inorganic Materials, 2023, 38(4): 367-377.
[7]	LIU Dan, ZHAO Yaxin, GUO Rui, LIU Yantao, ZHANG Zhidong, ZHANG Zengxing, XUE Chenyang. Effect of Annealing Conditions on Thermoelectric Properties of Magnetron Sputtered MgO-Ag₃Sb-Sb₂O₄ Flexible Films [J]. Journal of Inorganic Materials, 2022, 37(12): 1302-1310.
[8]	LIU Cheng, ZHAO Qian, MOU Zhiwei, LEI Jiehong, DUAN Tao. Adsorption Properties of Novel Bismuth-based SiOCNF Composite Membrane for Radioactive Gaseous Iodine [J]. Journal of Inorganic Materials, 2022, 37(10): 1043-1050.
[9]	ZHANG Xiaoshan, WANG Bing, WU Nan, HAN Cheng, LIU Haiyan, WANG Yingde. Infrared Radiation Shielded SiZrOC Nanofiber Membranes: Preparation and High-temperature Thermal Insulation Performance [J]. Journal of Inorganic Materials, 2022, 37(1): 93-100.
[10]	MA Lingling, CHANG Jiang. Nd-doped Calcium Silicate: Photothermal Effect, Fluorescence Performance, and Biological Properties of Its Composite Electrospun Membrane [J]. Journal of Inorganic Materials, 2021, 36(9): 974-980.
[11]	LI Tingting, ZHANG Zhiming, HAN Zhengbo. Research Progress in Polymer-based Metal-organic Framework Nanofibrous Membranes Based on Electrospinning [J]. Journal of Inorganic Materials, 2021, 36(6): 592-600.
[12]	FANG Huajing, ZHAO Zetian, WU Wenting, WANG Hong. Progress in Flexible Electrochromic Devices [J]. Journal of Inorganic Materials, 2021, 36(2): 140-151.
[13]	XU Haifeng,HOU Chengyi,ZHANG Qinghong,LI Yaogang,WANG Hongzhi. Preparation and Thermoelectric Performance of Tellurium Nanowires-based Thin-Film Materials [J]. Journal of Inorganic Materials, 2020, 35(9): 1034-1040.
[14]	ZHU Zhengwang,FENG Rui,LIU Yang,ZHANG Yang,XIE Wenhan,DONG Lijie. Preparation and Property of CoFe₂O₄ Nanofibers with Fishbone-like Structure [J]. Journal of Inorganic Materials, 2020, 35(9): 1011-1016.
[15]	YANG Yi-Na, WANG Ran-Ran, SUN Jing. MXenes in Flexible Force Sensitive Sensors: a Review [J]. Journal of Inorganic Materials, 2020, 35(1): 8-18.