相扩散阻挡法制备铁酸钴/改性钛酸铋钠0-3复合多铁性陶瓷

韩权威1, 李 坤1, 彭 松2, 王 雨3, 陈王丽华3   

  1. (1. 江苏工业学院 材料学院, 常州 213164; 2. 南京大学 物理系, 南京 210093; 3. 香港理工大学 应用物理系及材料研究中心, 香港)
  • 收稿日期:2010-07-05 修回日期:2010-10-23 出版日期:2011-05-20 网络出版日期:2011-06-07
  • 作者简介:韩权威(1983-), 男, 硕士研究生. E-mail: hanquanwei@163.com
  • 基金资助:

    Hong Kong PolyU Project, NSFC/RGC N-PolyU501/08 ME Device

Fabrication of the Cobalt Ferrite/Modified Sodium Bismuth Titanate 0-3 Multiferroic Composites via Diffusion-blocking

HAN Quan-Wei1, LI Kun1, PENG Song2, WANG Yu3, CHAN Helen Lai-Wa3   

  1. (1. School of Materials Science and Engineering, Changzhou University, Changzhou, 213016, China; 2. Department of Phisics, Nanjing University, Nanjing 210093, China; 3. Department of Applied Phisics and Materials Research Centre, The Hong Kong Polytechnic University, HongKong, China)
  • Received:2010-07-05 Revised:2010-10-23 Published:2011-05-20 Online:2011-06-07
  • Supported by:

    Hong Kong PolyU Project, NSFC/RGC N-PolyU501/08 ME Device

PDF (PC)

1729

被引次数

11 | 1

摘要： 通过溶胶-凝胶工艺在CoFe2O4(简称CFO)粉体表面包覆二氧化锆陶瓷层来阻挡烧结过程中铁磁相与铁电相之间的离子扩散. 包覆后的CFO与0.92(Bi0.5Na0.5)TiO3-0.02(Bi0.5K0.5)TO3-0.06BaTiO3(简称BNBT) 陶瓷粉体分别按照xCFO/(1-x) BNKLABT (质量分数x = 0.05、0.10、0.15、0.20、0.25、0.30)混合均匀, 并用聚乙烯醇为粘结剂模压成圆片; 再经过1050℃烧结制备了铁磁/铁电0-3型复合材料. XRD分析表明: 二氧化锆在高温烧结过程中对离子扩散具有良好的阻挡作用. 复合陶瓷的耐击穿电压大于75kV/cm. 测量结果表明: 复合陶瓷的压电应变常数、机电耦合系数、介电常数和剩余极化随CFO含量的增加而降低; 磁电耦合系数、介电损耗随CFO含量的增加而有所增大. -35mm×1.5mm的复合陶瓷样品(x=0.05)在谐振频率(90kHz)和199kA/m 偏置磁场下的磁电系数为1.39V/A.

关键词: 磁电效应, 0-3复合, 铁电, 铁磁

Abstract: The ZrO2 buffer layer was coated on CoFe2O4(CFO) powder via a Sol-Gel method. The coated CFO and 0.92(Bi0.5Na0.5)TiO3-0.02(Bi0.5K0.5)TiO3-0.06BaTiO3(BNBT) ceramic powder were mixed according to the chemical formula of xCFO/(1-x) BNBT (weight fraction x = 0.05, 0.10, 0.15, 0.20, 0.25, 0.30). Using polyvinyl alcohol (PVA) as binder, the mixture was pressed into disks. After sintered at 1050℃, the xCFO/(1-x) BNBT 0-3 composite ceramic disks were prepared. The X-ray diffraction results show that the ZrO2 layer can buffer the Fe3+ and Co2+ ions diffusing from CFO to BNBT during the sintering process. The break-down voltage of the co-fired composites is measured to be 75kV/cm. It is found that the piezoelectric constant, electromechanical coefficient, remnant polarization and dielectric permittivity decrease as the CFO content increasing. Magnetoelectric coefficient (ME) and dielectric loss increase with the CFO content increasing. For a composite disk with dimension of -35mm×1.5mm, the ME coefficient at resonance frequency of 90 kHz is 1.39V/A under a DC magnetic bias of 199 kA/m.

Key words: magnetoelectric, 0-3 composite, ferroelectric, ferromagnetic