λ-Ti3O5粉体的制备及其光存储性能的研究

doi:10.3724/SP.J.1077.2013.12309

无机材料学报 ›› 2013, Vol. 28 ›› Issue (4): 425-430.DOI: 10.3724/SP.J.1077.2013.12309 CSTR: 32189.14.SP.J.1077.2013.12309

λ-Ti₃O₅粉体的制备及其光存储性能的研究

刘刚¹, 黄婉霞¹, 易勇²

(1. 四川大学材料科学与工程学院, 成都 610064; 2. 西南科技大学极端条件物质特性实验室, 绵阳 621010)

收稿日期:2012-05-11 修回日期:2012-07-17 出版日期:2013-04-10 网络出版日期:2013-03-20
作者简介:刘刚(1988–), 男, 硕士研究生. E-mail: liugangscu@163.com
基金资助:
极端条件物质特性实验室基金(11zxjk01) Open Foundation of Laboratory for Extreme Conditions Matter Properties (11zxjk01)

Preparation and Optical Storage Properties of λTi₃O₅ Powder

LIU Gang¹, HUANG Wan-Xia¹, YI Yong²

(1. Materials Science and Engineering College, Sichuan University, Chengdu 610064, China; 2. Laboratory of Matter Characteristic Research at Extreme Conditions, Southwest University of Science and Technology, Mianyang 621010, China)

Received:2012-05-11 Revised:2012-07-17 Published:2013-04-10 Online:2013-03-20
About author:LIU Gang. E-mail: liugangscu@163.com

摘要/Abstract

摘要：

采用氢气还原纳米TiO₂粉体制备了Ti₃O₅粉体, 采用FTIR、XRD、SEM、UV-Vis等对原料及产物进行了表征。结果表明: 加大通氢流量有利于还原反应的进行; 以氧化硅包覆的纳米TiO₂粉体(金红石型)为原料, 1150℃下氢气还原1 h可合成单一物相组成的λ-Ti₃O₅粉体。对比自制未包覆处理的纳米TiO₂, TiO₂粉体的氧化硅包覆处理有利于λ-Ti₃O₅的形成; λ-Ti₃O₅与β-Ti₃O₅有较高的光学对比度, 室温下, 经适当的纳秒脉冲激光(532 nm, 20 ns)处理, λ-Ti₃O₅会向β-Ti₃O₅发生转变, 表现出较好的光存储性能。

关键词: λ, -Ti₃O₅, 粉体, 还原, 纳米TiO₂, 光存储

Abstract:

The Ti₃O₅ powder was prepared by reducing TiO₂ nanopartical in H₂ atmosphere. The samples were investigated by powder X-ray diffraction (XRD), Fourier transform infrared spectroscope (FTIR), scanning electron microscope (SEM) and UV-Vis diffusion reflectance spectra (UV-Vis). The results show that, single phase Ti₃O₅ can be obtained by increasing the H₂ flow. When H₂ flow increases from 0.3 mL/min to 0.8 mL/min, the single phase λ-Ti₃O₅ can be synthesized using SiO₂-coated TiO₂ (rutile, nanoparticle) as raw material at 1150℃ for 1 h. While using nano-TiO₂ powders without SiO₂-coated as raw material, the reduction product is multiphases composed of λ-Ti₃O₅ and β-Ti₃O₅. There is a high reflectivity contrast between λ-Ti₃O₅ and β-Ti₃O₅. When the multiphases sample is irradiated with 532 nm 20 ns-pulsed laser light at room temperature, Ti₃O₅ will transit from α phase to β phase, which shows a good optical storage performance.

Key words: &#x003bb, -Ti₃O₅, powder, reduction, nano-TiO₂, optical storage

中图分类号:

TB383

刘刚, 黄婉霞, 易勇. λ-Ti₃O₅粉体的制备及其光存储性能的研究[J]. 无机材料学报, 2013, 28(4): 425-430.

LIU Gang, HUANG Wan-Xia, YI Yong. Preparation and Optical Storage Properties of λTi₃O₅ Powder[J]. Journal of Inorganic Materials, 2013, 28(4): 425-430.

图/表 11

图1 不同温度下反应吉布斯函变与压力商的关系

Fig. 1 Relationship of Gibbs free energy and pressure quotient at different temperature

图2 不同温度下H2还原氧化硅包覆TiO2粉体(金红石)的XRD图谱

Fig. 2 XRD patterns of the SiO2-coated TiO2 powder (rutile) after reduction in H2 atmosphere at different temperatures for 1 h

图3 不同保温时间下H2还原氧化硅包覆TiO2粉体(金红石)的XRD图谱

Fig. 3 XRD patterns of the SiO2-coated TiO2 powder(rutile) after reduction in H2 atmosphere at 1150℃ for different time

Table 1 Effect of raw material and H2 flow on the composition of reduction product

Number	TiO₂	T/℃ t/h	H₂/(L·min^-1)	Composition
1	A	1150 1	0.3	Ti₄O₇,Ti₃O₅
2	R	1150 1	0.3	Ti₄O₇,Ti₃O₅
3	A	1150 1	0.8	Ti₃O₅
4	R	1150 1	0.8	Ti₃O₅

图4 不同纳米TiO2粉体的红外光谱图

Fig. 4 IR spectra of different nano-TiO2

图5 不同纳米TiO2粉体的SEM照片

Fig. 5 SEM images of different nano-TiO2

图6 不同TiO2的氢还原产物的XRD图谱

Fig. 6 XRD patterns of the different nano-TiO2 after reduction in H2 atmosphere at 1150℃ for 1 h

图7 不同TiO2为原料氢还原制备的Ti3O5的SEM照片

Fig. 7 SEM images of different TiO2 powder after reduction in H2 atmosphere at 1150℃ for 1 h

图8 不同相结构的Ti3O5的反射率曲线

Fig. 8 Wavelength dependence of reflection difference between the β-Ti3O5 and λ-Ti3O5

Table 2 Reflectivity contrast between β-Ti3O5(R1) and λ-Ti3O5(R2)

Wavelength/nm	R₁/%	R₂/%	C/%
310	27.8	11.9	79.9
350	12.7	6.0	71.1
480	9.0	4.7	62.1
750	6.6	2.8	82.1

图9 激光处理前后Ti3O5粉体的XRD图谱

Fig. 9 XRD patterns of the Ti3O5 powder before and after 532 nm laser light irradiation at room temperature

参考文献 13

[1]	赵书文, 王淑荣, 张凤兰, 等. Ti3O5反应蒸发镀制TiO2光学膜的材料. 激光与红外, 1985(12): 23-28.
[2]	Park S Y, Mho S Y, Chi E O, et al. Characteristics of Pt thin films on the conducting ceramics TiO and Ebonex (Ti4O7) as electrode materials. Thin Solid Films, 1995, 258(1/2): 5-9.
[3]	Przyluski J, Kolbrecka K. Voltametric behaviour of TinO2n-1 ceramic electrodes close to the hydrogen evolution reaction. Journal of Applied Electrochemistry, 1993, 23(10): 1063-1068.
[4]	Zheng Liaoying, Li Guorong, Xu Tingxian, et al. Preparation and oxygen-sensing properties of α-Ti3O5 thin film. Journal of Inorganic Materials, 2002, 17(6): 1253-1257.
[5]	Masashige Onoda. Phase transitions of Ti3O5. Journal of Solid State Chem, 1998, 136(1): 67-73.
[6]	Åsbrink S, Magnéli A. Crystal structure studies on trititanium pentoxide, Ti3O5. Acta Cryst., 1959, 12(8): 575-581.
[7]	HONG S H, SBRINKS A. The structure of γ-Ti3O5 at 297 K. Acta Cryst., 1982, 38(10): 2570-2576.
[8]	Ohkoshi Shin-ichi, Tsunobuchi Yoshihide, Matsuda Tomoyuki, et al. Synthesis of a metal oxide with a roomtemperature photoreversible phase transition. Nature Chemistry, 2010, 2(7): 539-545.
[9]	Fang Ming, Li Qinghui, Gu Donghong, et al. Research and development of inorganic materials used as blue-laser optical recording media. Progress In Physics, 2003, 23(4): 423-430.
[10]	梁英教,车荫昌. 无机物热力学数据手册. 沈阳: 东北大学出版社, 1994.
[11]	Zhang Qinghong, Gao Lian, Sun Jian. Retarding effect of silica on the growth and anatase-to-rutile transformation of TiO2 nanocrystals. Journal of Inorganic Materials, 2002, 17(3): 415-421.
[12]	Makiura R, Takabayashi Y, Fitch AN, et al. Nanoscale effects on the stability of the λ-Ti3O5 polymorph. Chem. Asian J., 2011, 6(7): 1886-1890.
[13]	干福熹. 数字光盘和光存储材料. 上海: 上海科学技术出版社, 1992.

[1]	余乐洋阳, 赵芳霞, 张舒心, 徐以祥, 牛亚然, 张振忠, 郑学斌. 感应等离子球化技术制备喷涂用高熵硼化物粉体[J]. 无机材料学报, 2025, 40(7): 808-816.
[2]	孙晶, 李翔, 毛小建, 章健, 王士维. 月桂酸改性剂对氮化铝粉体抗水解性能的影响[J]. 无机材料学报, 2025, 40(7): 826-832.
[3]	高晨光, 孙晓亮, 陈君, 李达鑫, 陈庆庆, 贾德昌, 周玉. 基于湿法纺丝技术的SiBCN-rGO陶瓷纤维的组织结构、力学和吸波性能[J]. 无机材料学报, 2025, 40(3): 290-296.
[4]	王悦, 王欣, 于显利. 室温铁磁性还原氧化石墨烯基全碳膜[J]. 无机材料学报, 2025, 40(3): 305-313.
[5]	叶君豪, 周真真, 胡辰, 王雁斌, 荆延秋, 李廷松, 程梓秋, 吴俊林, IVANOV Maxim, HRENIAK Dariusz, 李江. 共沉淀纳米粉体制备Yb:Sc₂O₃透明陶瓷的微结构与光学性能[J]. 无机材料学报, 2025, 40(2): 215-224.
[6]	冯关正, 杨健, 周渡, 陈啟明, 许文涛, 周有福. 水热-碳热合成AlN纳米粉体的机理[J]. 无机材料学报, 2025, 40(1): 104-110.
[7]	刘磊, 郭瑞华, 王丽, 王艳, 张国芳, 关丽丽. Pt₃Co高指数晶面氧还原过程的密度泛函理论研究[J]. 无机材料学报, 2025, 40(1): 39-46.
[8]	杨鑫, 韩春秋, 曹玥晗, 贺桢, 周莹. 金属氧化物电催化硝酸盐还原合成氨研究进展[J]. 无机材料学报, 2024, 39(9): 979-991.
[9]	潘建隆, 马官军, 宋乐美, 郇宇, 魏涛. 燃料还原法原位制备高稳定性/催化活性SOFC钴基钙钛矿阳极[J]. 无机材料学报, 2024, 39(8): 911-919.
[10]	靳宇翔, 宋二红, 朱永福. 3d过渡金属单原子掺杂石墨烯缺陷电催化还原CO₂的第一性原理研究[J]. 无机材料学报, 2024, 39(7): 845-852.
[11]	施桐, 甘乔炜, 刘东, 张莹, 冯浩, 李强. 自支撑Bi@Cu纳米树电极高效电化学还原CO₂制甲酸[J]. 无机材料学报, 2024, 39(7): 810-818.
[12]	刘焱, 覃显鹏, 甘霖, 周国红, 章天金, 王士维, 陈鹤拓. 亚微米球形Y₂O₃粉体及其透明陶瓷的制备[J]. 无机材料学报, 2024, 39(6): 691-696.
[13]	郑雅雯, 张翠萍, 张瑞杰, 夏乾, 茹红强. 硼酸碳热还原-渗硅反应烧结制备碳化硼陶瓷复合材料[J]. 无机材料学报, 2024, 39(6): 707-714.
[14]	李红兰, 张俊苗, 宋二红, 杨兴林. Mo/S共掺杂的石墨烯用于合成氨: 密度泛函理论研究[J]. 无机材料学报, 2024, 39(5): 561-568.
[15]	王艳莉, 钱心怡, 沈春银, 詹亮. 石墨烯基介孔锰铈氧化物催化剂: 制备和低温催化还原NO[J]. 无机材料学报, 2024, 39(1): 81-89.

λ-Ti₃O₅粉体的制备及其光存储性能的研究

Preparation and Optical Storage Properties of λTi₃O₅ Powder

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 11

参考文献 13

相关文章 15

编辑推荐

Metrics

本文评价