Synthesis of Mesoporous Composite Oxides for the Catalysis of NH3-SCR

doi:10.15541/jim20150100

Abstract

Abstract:

A novel mesoporous ZrO₂-TiO₂ (ZT) based multi-component composite oxide catalyst V₂O₅-WO₃-CuO- Al₂O₃/ZrO₂-TiO₂ (VWCuAl/ZT) was successfully synthesized by one-pot hydrothermal method using both Brij-35 and P123 as composite template. The results indicated that the active species of V₂O₅, WO₃, CuO and Al₂O₃ could be homogeneously dispersed into mesoporous ZrO₂-TiO₂ catalyst carrier. Compared with the reference samples of non-mesoporous I-VWCuAl/ZT and the traditional commercial catalyst V₂O₅-WO₃/TiO₂(V-W/Ti), the prepared VWCuAl/ZT showed a superior low-temperature catalytic activity and high stability over the reaction of NH₃-SCR of NO, especially high catalytic efficacy for NO reduction within a wide temperature range of between 200℃ to 500℃.

Key words: hydrothermal, mesoporous ZrO2-TiO2, VWCuAl/ZT, NH3-SCR, NO

CLC Number:

TQ174

CHEN Ying, ZHOU Xiao-Xia, WANG Jin, XIE Zhi-Guo, CHEN Hang-Rong. Synthesis of Mesoporous Composite Oxides for the Catalysis of NH₃-SCR[J]. Journal of Inorganic Materials, 2015, 30(11): 1155-1160.

Figures/Tables 8

Fig. 1 N2 adsorption/desorption isotherms of different catalysts and catalyst support ZT

Table 1 Texture properties of different catalysts and catalyst support ZT

Sample	ZT	VWCuAl/ZT	I-VWCuAl/ZT
S_BET/(m²•g^-1)	99	102	42
Pore size /nm	35.8	14.9	-
V_total/(cm³•g^-1)	0.71	0.36	-

Fig. 2 XRD patterns of mesoporous ZT support and VWCuAl/ ZT catalyst

Fig. 3 Typical TEM images and the corresponding selected area electron diffraction (SAED) pattern (inset) of mesoporous ZT support (a) and VWCuAl/ZT catalyst (b), and EDS spectrum (c) corresponding to (b) as well as elements weight percentage of VWCuAl/ZT (inset)

Fig. 4 (a) SEM image, (b) STEM image and (c) corresponding elements mapping of VWCuAl/ZT catalyst

Fig. 5 H2-TPR profiles of the prepared VWCuAl/ZT and commercial catalysts

Fig. 6 Comparison of NO conversion over the VWCuAl/ ZT, references commercial catalyst and I-VWCuAl/ZT catalyst

Fig. 7 Reusability of the sample VWCuAl/ZT

References 21

[1]	徐海迪, 邱春天, 张秋林, 等. WO3对MnOx-CeO2/ZrO2-TiO2整体式催化剂NH3选择性催化还原NOx性能的影响. 物理化学学报, 2010, 26(9): 2449-2454.
[2]	MONTICELLI O, LOENDERS R, JACOBS P A, et al.NOx removal from exhaust gas from lean burn internal combustion engines through adsorption on fau type zeolites cation exchanged with alkali metals and alkaline earth metals.Appl. Catal. B-Environ, 1999, 21(3): 215-220.
[3]	LIU Z M, WOO S I.Recent advances in catalytic DeNO(X) science and technology.Catal. Rev, 2006, 48(1): 43-89.
[4]	HAN X H, WEI X L, SCHNELL U, et al.Detailed modeling of hybrid reburn/SNCR processes for NOx reduction in coal-fired furnaces.Combust Flame, 2003, 132(3): 374-386.
[5]	BAE S W, ROH S A, KIM S D.NO removal by reducing agents and additives in the selective non-catalytic reduction (SNCR) process.Chemosphere, 2006, 65(1): 170-175.
[6]	TAKAHASHI N, YAMAZAKI K, SOBUKAWA H, et al.The low-temperature performance of NOx storage and reduction catalyst.Appl. Catal. B-Environ., 2007, 70(1/4): 198-204.
[7]	KLEIN J, WU D L, TSCHAMBER V, et al. Carbon-NSR catalyst interaction: Impact on catalyst structure and NOx storage efficiency. Appl. Catal. B-Environ., 2013, 132-133: 527-534.
[8]	杨玲, 李茂, 李建军. SCR催化剂的研究进展. 四川化工, 2012, 15(6): 26-29.
[9]	BRÖER S, HAMMER T. Selective catalytic reduction of nitrogen oxides by combining a non-thermal plasma and a V2O5-WO3/TiO2 catalyst.Appl. Catal. B, 2000, 28(2): 101-111.
[10]	KOBAYASHI M, MIYOSHI K.WO3-TiO2 monolithic catalysts for high temperature SCR of NO by NH3: influence of preparation method on structural and physico-chemical properties, activity and durability.Appl. Catal. B, 2007, 72(3/4): 253-261.
[11]	GARCIA-BORDEJE E, CALVILLO L, LAZARO M J, et al.Vanadium supported on carbon-coated monoliths for the SCR of NO at low temperature: effect of pore structure.Appl. Catal. B, 2004, 50(4): 235-242.
[12]	GROSSALE A, NOVA I, TRONCONI E.Study of a Fe-zeolite-based system as NH3-SCR catalyst for diesel exhaust aftertreatment.Catalysis Today, 2008, 136(1/2): 18-27.
[13]	YAO X., ZHANG L LI L,et al. Investigation of the structure, acidity, and catalytic performance of CuO/Ti0.95Ce0.05O2 catalyst for the selective catalytic reduction of NO by NH3 at low temperature . Appl. Catal. B-Environ., 2014, 150-151: 315-329.
[14]	LIU C X, CHEN L, LI J H, et al.Enhancement of activity and sulfur resistance of CeO2 supported on TiO2-SiO2 for the selective catalytic reduction of NO by NH3.Environ. Sci. Technol., 2012, 46(11): 6182-6189.
[15]	REDDY B M., KHAN A.Recent advances on TiO2-ZrO2 mixed oxides as catalysts and catalyst supports.Catal. Rev., 2005, 47(2): 257-296.
[16]	BENNICI S, GERVASINI A.Catalytic activity of dispersed CuO phases towards nitrogen oxides (N2O, NO, and NO2).Appl. Catal. B, 2006, 62(3/4): 336-344.
[17]	刘仁龙, 邬旭宏, 王文芳, 等. 钒氧化物催化剂上NH3-SCR 反应物的吸附-脱附. 化学通报, 2012, 75(7): 600-605.
[18]	DONOVAN A P, BALU S U, PANAGIOTIS G S.TiO2-supported metal oxide catalysts for low-temperature selective catalytic reduction of NO with NH3: I. Evaluation and characterization of first row transition metals.Journal of Catalysis, 2004, 221(2): 421-431.
[19]	BUSCA G, CENTI G, MARCHETTI L, et al.Chemical and spectroscopic study of the nature of a vanadium oxide monolayer supported on a high-surface-area TiO2 anatase.Langmuir, 1986, 2(5): 568-577.
[20]	EIGENMANN F, MACIEJEWSKI M, BAIKER A.Selective reduction of NO by NH3 over manganese-cerium mixed oxides: relation between adsorption, redox and catalytic behavior.Appl. Catal. B-Environ, 2006, 62(3): 311-318.
[21]	IMAGAWA H, TANAKA T, TAKAHASHI N, et al.Titanium-doped nanocomposite of Al2O3 and ZrO2-TiO2 as a support with high sulfur durability for NOx storage-reduction catalyst.Appl. Catal. B-Environ, 2009, 86(1/2): 63-68.

Synthesis of Mesoporous Composite Oxides for the Catalysis of NH₃-SCR

RichHTML

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

Figures/Tables 8

References 21

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	QU Boxuan, TAN Ji, CHEN Shuhan, LIU Xuanyong. Enhanced ROS Scavenging Property of Polyoxometalates by Manganese Doping for Cytoprotection [J]. Journal of Inorganic Materials, 2026, 41(6): 839-846.
[2]	FENG Hengyang, WEI Tianran, QIU Pengfei, SHI Xun. Ultra-large Macroscopic Plastic Deformation and Metalworking in Inorganic Semiconductors [J]. Journal of Inorganic Materials, 2026, 41(6): 681-688.
[3]	HU Yang, XIE Min, ZHANG Xiaoyi, LI Xiang, GUO Xinwei, JIANG Nan, ZHOU Wenhan, ZHANG Shengli, ZENG Haibo. Research Progress on Computational and Data-driven Environmental-friendly Luminescent Materials [J]. Journal of Inorganic Materials, 2026, 41(6): 704-722.
[4]	HONG Enliu, TU Xinchen, LI Ziqing, FANG Xiaosheng. Two-dimensional Perovskite Single Crystal Nanosheets: Floating Growth and Optoelectronic Performance [J]. Journal of Inorganic Materials, 2026, 41(6): 787-794.
[5]	WANG Jinwen, YANG Zhen, ZHOU Huan, XIA Dan, YANG Lei. Biomedical Applications of Injectable Inorganic Biomaterials [J]. Journal of Inorganic Materials, 2026, 41(6): 751-763.
[6]	LI Hantao, SHEN Qiang, LUO Guoqiang, WANG Xuefei, GAO Ming, CHEN Chen. Research Progress on Structure and Performance Regulation of Silicon-based Anode Materials via Mechanical Ball Milling [J]. Journal of Inorganic Materials, 2026, 41(5): 561-572.
[7]	WANG Haoyu, KE Xue, GUAN Shiwei, QIAN Shi, LIU Xuanyong. Fe Doped Ti-MOFs for Enhanced Antibacterial Sonodynamic Therapy of Periodontitis [J]. Journal of Inorganic Materials, 2026, 41(4): 527-535.
[8]	MA Xiaojia, GENG Xinyu, ZHANG Weike. Boron and Nitrogen Co-doped Biomass Carbon Sphere Anode Material: Preparation and Sodium Storage Properties for Sodium-ion Batteries [J]. Journal of Inorganic Materials, 2026, 41(4): 469-478.
[9]	XUE Xinyan, ZHANG Xiaowei, LU Heng, LI Shijie, ZHANG Weike, CHAN Siewhwa. Co-Mg Synergistic Carbon Nano Onions Catalyst: Preparation and Low-temperature Catalytic Hydrogen Production from Ammonia Decomposition [J]. Journal of Inorganic Materials, 2026, 41(4): 500-508.
[10]	WEI Lianjin, QI Zhijie, WANG Xin, ZHU Junwu, FU Yongsheng. Modification of Nanodiamond and Its Application in Electrocatalytic Oxygen Reduction Reaction [J]. Journal of Inorganic Materials, 2026, 41(3): 273-288.
[11]	LI Peng, QIU Pengfei, JIANG Binbin, XIAO Jie, SHI Xun. Thermomagnetic Performance of Polycrystalline TaSb₂ [J]. Journal of Inorganic Materials, 2026, 41(3): 303-310.
[12]	ZHANG Yunbo, WANG Bing, LI Wei, SONG Quzhi, DU Yi’ang, WANG Yingde. Size Effect of Nanosheet on BN Fibers Derived from BNNS/Polyborazine Hybrid Precursor [J]. Journal of Inorganic Materials, 2026, 41(3): 359-369.
[13]	LI Hao, QI Yuan, GAO Xiangdong, ZHANG Xingxing, WANG Jinmin. High Temperature Resistant Calcium-doped Silica Aerogels with Enhanced Thermal Insulation via Sol-Gel Hydrothermal Route [J]. Journal of Inorganic Materials, 2026, 41(2): 262-272.
[14]	ZHANG Xiaomin, TONG Liangyu, GAO Hongjie, CHEN Xu, YAN Huhu, GAO Yang. 3D Network-structured Fly Ash Microbeads@Carbon Nanotubes Composites for Electromagnetic Wave Absorption [J]. Journal of Inorganic Materials, 2026, 41(2): 208-216.
[15]	ZHU Jianhua, YANG Xin, RU Lingjie. 2D/2D Coupled ZnIn₂S₄/TiO₂Heterojunction and Its Enhanced Photocatalytic Reduction of CO₂ [J]. Journal of Inorganic Materials, 2026, 41(2): 177-185.