Synthesis and Characterization of Cubic P-type Semiconductor Cu1.8S-deposited TiO2 Nanobelts

doi:10.3724/SP.J.1077.2012.00038

Abstract

Abstract:

TiO₂ nanobelts deposited with cubic p-type semiconductor Cu_1.8S particles were prepared using Cu₂O-deposited TiO₂ nanobelts and thiourea as precursors under hydrothermal condition by Cu₂O sacrificial template process. The measurement results show that the reaction temperature, reaction time and thiourea concentration have strong influence on the purity and morphology of Cu_1.8S particles. A mixture phases of Cu_1.8S and Cu₂O on TiO₂ nanobelts were obtained at 120℃ for 25 h within 0.5 mol/L of thiourea concentration. While reaction temperature was raised to 160℃, the Cu_1.8S particles with high purity exhibited obvious aggregation, whereas the Cu_1.8S particles with high purity and well dispersion were prepared under 0.25 mol/L of thiourea concentration. The photocatalytic activities in degradation of Rhodamine B solution demonstrate that the Cu_1.8S or Cu₂O-loading catalysts show lower photodegradation activities as compared with that of pure TiO₂ nanobelts.

Key words: composite, cubic Cu_1.8S, TiO₂nanobelts, photocatalytic activity, p-n heterojunction

CLC Number:

TB381

LI Li, LEI Jing-Guo, JI Tian-Hao, ZHANG Xi-Peng. Synthesis and Characterization of Cubic P-type Semiconductor Cu_1.8S-deposited TiO₂Nanobelts[J]. Journal of Inorganic Materials, 2012, 27(1): 38-44.

Figures/Tables 8

Table 1 Preparation condition of the cubic Cu1.8S-loaded TiO2 nanobelts

Sample	Cu₂O-TiO₂/g	C/(mol·L^-1)	T/℃	t/h
CT-1	3	0.25	160	5
CT-2	3	0.25	160	15
CT-3	3	0.25	160	25
CT-4	3	0.50	120	25
CT-5	3	0.50	160	5
CT-6	3	0.50	160	15
CT-7	3	0.50	160	25

Fig. 1 XRD patterns of Cu2O-TiO2 nanobelts (a), CT-1 (b), CT-2 (c), CT-3 (d), CT-5 (e), CT-6 (f) and CT-7(g)

Fig. 2 Raman spectra of CT-3 (a) and TiO2 nanobelts (b)

Fig. 3 SEM images of Cu2O-TiO2 nanobelts (a), CT-3 (b), CT-4 (c) and CT-7 (d) as well as TEM images of CT-3 (e,f)

Fig. 4 UV-Vis DRS of the products

Fig. 5 N2 adsorption/desorption isotherms of (a) Cu2O-TiO2 nanobelts; (b) CT-3; (c) CT-4; (d) CT-7

Fig. 6 Visible-light photodegradation of Rhodamine B on H-CT-3, CT-3, CT-4 and CT-7 H-CT-3 is made from CT-3 dipping in dilute HCl solution for short time

Fig. 7 Absorption spectra of Rhodamine B solution at different reaction time with the catalysis of CT-3

References 22

[1]	Paulose M, Mor G K, Varghese O K, et al. Visible light photoelectrochemical and water-photoelectrolysis properties of titania nanotube arrays. J. Photochem. Photobiol. A: Chem., 2006, 178(1): 8-15.
[2]	Mor G K, Varghese O K, Paulose M, et al. A review on highly ordered, vertically oriented TiO2 nanotube arrays: fabrication, material properties, and solar energy applications. Sol. Energy Mater. Sol. Cells, 2006, 90(14): 2011-2075.
[3]	ZHANG Zhi-Yu, SANG Li-Xia, LU Li-Ping, et al. Preparation of TiO2 nanotube arrays and their photoelectrochemical properties. Journal of Inorganic Materials, 2010, 25(11): 1145-1149.
[4]	嵇天浩, 周吉. 一维TiO2纳米材料的研究进展. 精细化工, 2010, 27(7): 629-634.
[5]	Zhou W J, Liu H, Wang J Y, et al. Ag2O/TiO2 nanobelts heterostructure with enhanced ultraviolet and visible photocatalytic activity. ACS Appl. Mater. Interfaces, 2010, 2(8): 2385-2392.
[6]	嵇天浩. 锐钛矿型TiO2纳米线/带的大量制备. CN: 101898790A, 2010.12.1.
[7]	Adán C, Bahamonde A, Fernández-García M, et al. Structure and activity of nanosized iron-doped anatase TiO2 catalysts for phenol photocatalytic degradation. Appl. Catal. B: Environ., 2007, 72(1/2): 11-17.
[8]	Albonetti S, Baldi G, Barzanti A, et al. Chlorinated organics total oxidation over V2O5/TiO2 catalysts prepared by polyol-mediated synthesis. Appl. Catal. A: General, 2007, 325(2): 309-315.
[9]	Ashour A. The physical characteristics of Cu2S/CdS thin-film solar cell. J. Optoelectron. Adv. Mater., 2006, 8(4): 1447-1451.
[10]	Mane R S, Lokhande C D. Chemical deposition method for metal chalcogenide thin films. Mater. Chem. Phys., 2000, 65(1): 1-31.
[11]	Yamamoto T, Tanaka K, Kubota E, et al. Deposition of copper sulfide on the surface of poly(ethylene terephthalate) and poly(vinyl alcohol) films in aqueous solution to give electrically conductive films. Chem. Mater., 1993, 5(9): 1352-1357.
[12]	Pfisterer F. The wet-topotaxial process of junction formation and surface treatments of Cu2S-CdS thin-film solar cells. Thin Solid Films, 2003, 431-432(1): 470-476.
[13]	Wu Y, Wadia C, Ma W L, et al. Synthesis and photovoltaic application of copper(I) sulfide nanocrystals. Nano Lett., 2008, 8(8): 2551-2555.
[14]	Reijnen L, Meester B, Goossens A, et al. Nanoporous TiO2/Cu1.8S heterojunctions for solar energy conversion. Mater. Sci. Eng. C, 2002, 19(1/2): 311-314.
[15]	Reijnen L, Feddes B, Vredenberg A M, et al. Rutherford backscattering spectroscopy study of TiO2/Cu1.8S nanocomposites obtained by atomic layer deposition. J. Phys. Chem. B, 2004, 108(26): 9133-9137.
[16]	Cao H L, Qian X F, Wang C, et al. High symmetric 18-facet polyhedron nanocrystals of Cu7S4 with a hollow nanocage. J. Am. Chem. Soc., 2005, 127(46): 16024-16025.
[17]	Xu H L, Wang W Z, Zhu W, et al. Synthesis of octahedral CuS nanocages via a solid-liquid reaction. Nanotechnology, 2006, 17(15): 3649-3654.
[18]	Yang Z H, Zhang D P, Zhang W X, et al. Controlled synthesis of cuprous oxide nanospheres and copper sulfide hollow nanospheres. J. Phys. Chem. Solids, 2009, 70(5): 840-846.
[19]	Zhang H Y, Ji T H, Li L L, et al. Preparation and characterization of room temperature ferromagnetic Ni-doped anatase TiO2 nanobelts. Acta Phys.-Chim. Sin., 2008, 24(4): 607-611.
[20]	Ohsaka T, Izumi F, Fujiki Y. Raman spectrum of anatase TiO2. J. Raman Spectrosc., 1978, 7(6): 321-324.
[21]	Smith J M, Wren J C, Odziemkowski M, et al. The electrochemical response of preoxidized copper in aqueous sulfide solutions. J. Electrochem. Soc., 2007, 154(8): C431-C438.
[22]	Bobrenko Y N, Pavelets S Y, Pavelets A M, et al. Efficient photoelectric converters of ultraviolet radiation based on ZnS and CdS with low-resistivity surface layers. Semiconductor, 2010, 44(8): 1080-1083.

Synthesis and Characterization of Cubic P-type Semiconductor Cu_1.8S-deposited TiO₂Nanobelts

RichHTML

PDF (PC)

Knowledge

Cited

Abstract

Cite this article

share this article

Figures/Tables 8

References 22

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	HE Guoqiang, ZHANG Kaiheng, WANG Zhentao, BAO Jian, XI Zhaochen, FANG Zhen, WANG Changhao, WANG Wei, WANG Xin, JIANG Jiapei, LI Xiangkun, ZHOU Di. Ba(Nd_1/2Nb_1/2)O₃: Au Underrated K40 Microwave Dielectric Ceramic [J]. Journal of Inorganic Materials, 2025, 40(6): 639-646.
[2]	CHEN Yi, QIU Haipeng, CHEN Mingwei, XU Hao, CUI Heng. SiC/SiC Composite: Matrix Boron Modification and Mechanical Properties [J]. Journal of Inorganic Materials, 2025, 40(5): 504-510.
[3]	LI Jianjun, CHEN Fangming, ZHANG Lili, WANG Lei, ZHANG Liting, CHEN Huiwen, XUE Changguo, XU Liangji. Peroxymonosulfate Activation by CoFe₂O₄/MgAl-LDH Catalyst for the Boosted Degradation of Antibiotic [J]. Journal of Inorganic Materials, 2025, 40(4): 440-448.
[4]	MU Shuang, MA Qin, ZHANG Yu, SHEN Xu, YANG Jinshan, DONG Shaoming. Oxidation Behavior of Yb₂Si₂O₇ Modified SiC/SiC Mini-composites [J]. Journal of Inorganic Materials, 2025, 40(3): 323-328.
[5]	YANG Shuqi, YANG Cunguo, NIU Huizhu, SHI Weiyi, SHU Kewei. GeP₃/Ketjen Black Composite: Preparation via Ball Milling and Performance as Anode Material for Sodium-ion Batteries [J]. Journal of Inorganic Materials, 2025, 40(3): 329-336.
[6]	CHEN Guangchang, DUAN Xiaoming, ZHU Jinrong, GONG Qing, CAI Delong, LI Yuhang, YANG Donglei, CHEN Biao, LI Xinmin, DENG Xudong, YU Jin, LIU Boya, HE Peigang, JIA Dechang, ZHOU Yu. Advanced Ceramic Materials in Helicopter Special Structures: Research Progress and Application Prospect [J]. Journal of Inorganic Materials, 2025, 40(3): 225-244.
[7]	MU Haojie, ZHANG Yuanjiang, YU Bin, FU Xiumei, ZHOU Shibin, LI Xiaodong. Preparation and Properties of ZrO₂ Doped Y₂O₃-MgO Nanocomposite Ceramics [J]. Journal of Inorganic Materials, 2025, 40(3): 281-289.
[8]	WANG Yue, WANG Xin, YU Xianli. Room-temperature Ferromagnetic All-carbon Films Based on Reduced Graphene Oxide [J]. Journal of Inorganic Materials, 2025, 40(3): 305-313.
[9]	LUAN Xingang, HE Dianwei, TU Jianyong, CHENG Laifei. 2D Plain and 3D Needle-punched C/SiC Composites: Low-velocity Impact Damage Behavior and Failure Mechanism [J]. Journal of Inorganic Materials, 2025, 40(2): 205-214.
[10]	WANG Wenting, XU Jingjun, MA Ke, LI Meishuan, LI Xingchao, LI Tongqi. Oxidation Behavior at 1000-1300 ℃ in air of Ti₂AlC-20TiB₂ Synthesized by in-situ Reaction/Hot Pressing [J]. Journal of Inorganic Materials, 2025, 40(1): 31-38.
[11]	LIU Pengdong, WANG Zhen, LIU Yongfeng, WEN Guangwu. Research Progress on the Application of Silicon Slurry in Lithium-ion Batteries [J]. Journal of Inorganic Materials, 2024, 39(9): 992-1004.
[12]	QUAN Wenxin, YU Yiping, FANG Bing, LI Wei, WANG Song. Oxidation Behavior and Meso-macro Model of Tubular C/SiC Composites in High-temperature Environment [J]. Journal of Inorganic Materials, 2024, 39(8): 920-928.
[13]	MA Binbin, ZHONG Wanling, HAN Jian, CHEN Liangyu, SUN Jingjing, LEI Caixia. ZIF-8/TiO₂ Composite Mesocrystals: Preparation and Photocatalytic Activity [J]. Journal of Inorganic Materials, 2024, 39(8): 937-944.
[14]	HE Sizhe, WANG Junzhou, ZHANG Yong, FEI Jiawei, WU Aimin, CHEN Yifeng, LI Qiang, ZHOU Sheng, HUANG Hao. Fe/Submicron FeNi Soft Magnetic Composites with High Working Frequency and Low Loss [J]. Journal of Inorganic Materials, 2024, 39(8): 871-878.
[15]	WU Xiangquan, TENG Jiachen, JI Xiangxu, HAO Yubo, ZHANG Zhongming, XU Chunjie. Textured Porous Al₂O₃-SiO₂ Composite Ceramic Platelet-sphere Slurry: Characteristics and Simulation of Light Intensity Distribution [J]. Journal of Inorganic Materials, 2024, 39(7): 769-778.