Journal of Inorganic Materials ›› 2019, Vol. 34 ›› Issue (10): 1091-1096.DOI: 10.15541/jim20180582
Previous Articles Next Articles
HUANG Long,DING Shi-Hua(),ZHANG Xiao-Yun,YAN Xin-Kan,LI Chao,ZHU Hui
Received:
2018-12-13
Revised:
2018-01-22
Published:
2019-09-23
Online:
2019-05-29
Supported by:
CLC Number:
HUANG Long, DING Shi-Hua, ZHANG Xiao-Yun, YAN Xin-Kan, LI Chao, ZHU Hui. Structure and Microwave Dielectric Property of BaAl2Si2O8 with Li2O-B2O3-SiO2 Glass Addition[J]. Journal of Inorganic Materials, 2019, 34(10): 1091-1096.
Fig. 1 Line shrinkage and density of BAS-xwt%LBS ceramic sample as a function of sintering temperature (a), and the relationship between density and content of LBS glass (b)
x/wt% | 0 | 0.1 | 0.3 | 0.5 | 1.0 | 2.0 |
---|---|---|---|---|---|---|
T/℃ | 1400 | 1350 | 1275 | 1250 | 1200 | 1025 |
Table 1 Content of LBS glass and corresponding sintering temperature
x/wt% | 0 | 0.1 | 0.3 | 0.5 | 1.0 | 2.0 |
---|---|---|---|---|---|---|
T/℃ | 1400 | 1350 | 1275 | 1250 | 1200 | 1025 |
x/wt% | a/nm | b/nm | c/nm | V/nm3 |
---|---|---|---|---|
0.1 | 0.864121 | 1.304721 | 0.720215 | 0.73558 |
0.3 | 0.864383 | 1.304980 | 0.720196 | 0.73612 |
0.5 | 0.864474 | 1.304825 | 0.720159 | 0.73614 |
1.0 | 0.864824 | 1.304541 | 0.720327 | 0.73623 |
2.0 | 0.864586 | 1.305215 | 0.720430 | 0.73656 |
Table 2 Lattice constant and unit cell volume of BAS-xwt%LBS samples
x/wt% | a/nm | b/nm | c/nm | V/nm3 |
---|---|---|---|---|
0.1 | 0.864121 | 1.304721 | 0.720215 | 0.73558 |
0.3 | 0.864383 | 1.304980 | 0.720196 | 0.73612 |
0.5 | 0.864474 | 1.304825 | 0.720159 | 0.73614 |
1.0 | 0.864824 | 1.304541 | 0.720327 | 0.73623 |
2.0 | 0.864586 | 1.305215 | 0.720430 | 0.73656 |
Fig. 7 Q×f value of BAS-xwt%LBS ceramic as a function of sintering temperature (a) and the relationship between Q×f value and content of LBS glass (b)
[1] | LEI W, ANG R, WANG X C , et al.Phase evolution and near-zero shrinkage in BaAl2Si2O8 low-permittivity microwave dielectric ceramics.Materials Research Bulletin, 2014,50(2):235-239. |
[2] | ZHANG Y, DING S H, LIU Y Q , et al.Crystal structure and microwave dielectric property of Ba1-xMgxAl2Si2O8.Journal of Inorganic Materials, 2017,32(1):91-95. |
[3] | HAN L C, DING S H, SONG T X , et al.ZBAS on the structure and dielectric property of BaAl2Si2O8.Journal of Inorganic Materials, 2018,33(8):883-888. |
[4] |
LANSMANN V, JANSEN M . Application of the glass-ceramic process for the fabrication of whisker reinforced celsian-composites. Journal of Materials Science, 2001,36(6):1531-1538.
DOI |
[5] | BAHAT D . Kinetic study on the hexacelsian-celsian phase transformation. Journal of Materials Science, 1970,5(9):805-810. |
[6] | YOSHIKI B, MATSUMOTO K . High-temperature modification of barium feldspar. Journal of the American Ceramic Society, 1951,34(9):283-286. |
[7] | YANG X J, ZHANG Y, DING S H , et al.Structure and dielectric properties of Ca doped BaAl2Si2O8.Ceramics International, 2018,44:S43-S45. |
[8] | FERONE C, ESPOSITO S , DELL'AGLI G, et al.Role of Li in the low temperature synthesis of monoclinic celsian from (Ba, Li)- exchanged zeolite-a precursor.Solid State Sciences, 2005,7(11):1406-1414. |
[9] | SONG X Q, LU W Z, WANG X C , et al.Sintering behaviour and microwave dielectric properties of BaAl2-2x(ZnSi)xSi2O8 ceramics.Journal of the European Ceramic Society, 2018,38(4):1529-1534. |
[10] | SONG X Q, DU K, ZOU Z Y , et al.Temperature-stable BaAl2Si2O8-Ba5Si8O21-based low-permittivity microwave dielectric ceramics for LTCC applications.Ceramics International, 2017,43(16):14453-14456. |
[11] | LEE K T, ASWATH P B . Role of mineralizers on the hexacelsian to celsian transformation in the barium aluminosilicate (BAS) system. Materials Science & Engineering A, 2003,352(1):1-7. |
[12] | CHO I S, KIM D W, KIM J R , et al.Low-temperature sintering and microwave dielectric properties of BaO·(Nd1-xBix)2O3·4TiO2 by the glass additions.Ceramics international, 2004,30(7):1181-1185. |
[13] | SHIN H K, SHIN H, CHO S Y , et al.Phase evolution and dielectric properties of MgTiO3-CaTiO3 based ceramic sintered with lithium borosilicate glass for application to low temperature co-fired ceramics.Journal of the American Ceramic Society, 2005,88(9):2461-2465. |
[14] | PARK J H, CHOI Y J, PARK J G , et al.Low-fire dielectric compositions with permittivity 20-60 for LTCC applications.Materials Chemistry and Physics, 2004,88(2/3):308-312. |
[15] | LI E, NIU N, WANG J , et al.Effect of Li-B-Si glass on the low temperature sintering behaviors and microwave dielectric properties of the Li-modified ss-phase Li2O-Nb2O5-TiO2 ceramics.Journal of Materials Science: Materials in Electronics, 2015,26(5):3330-3335. |
[16] | YOON K H, PARK M S, CHO J Y , et al.Effect of B2O3-Li2O on microwave dielectric properties of (Ca0.275Sm0.4Li0.25)TiO3 ceramics.Journal of the European Ceramic Society, 2003,23(14):2423-2427. |
[17] | ZHANG Q L, YANG H, ZOU J L , et al.Sintering and microwave dielectric properties of LTCC-zinc titanate multilayers.Materials Letters, 2005,59(8/9):880-884. |
[18] | YANG H, LI E, YANG H , et al.Synthesis of Zn0.5Ti0.5NbO4 microwave dielectric ceramics with Li2O-B2O3-SiO2 glass for LTCC application.International Journal of Applied Glass Science, 2018,9(3):392-402. |
[19] | SHIH Y T, JEAN J H . Low-fire processing of microwave (Ca1-xSrx)(Zr1-yMny)O3 dielectric with Li2O-B2O3-SiO2 glass in H2/N2.Ceramics International, 2017,43:S306-S311. |
[20] | BANSAL, NAROTTAM P . SiC fiber-reinforced celsian composites. 2005, ( Chapter 10):227-249. |
[21] | HYATT M J, BANSAL N P . Crystal growth kinetics in BaOAl2O3·2SiO2 and SrOAl2O3·2SiO2 glasses. Journal of Materials Science, 1996,31(1):172-184. |
[22] | BANSAL N P , DRUMMOND III C H . Kinetics of hexacelsian- to-celsian phase transformation in SrAl2Si2O8. Journal of the American Ceramic Society, 1993,76(5):1321-1324. |
[23] | SHANNON R D . Dielectric polarizabilities of ions in oxides and fluorides. Journal of Applied Physics, 1993,73(1):348-366. |
[24] | PARK Y H, RYU J M, SHIN M Y , et al.Effect of Nb2O5/ZnO addition on microwave properties of (Zr0.8Sn0.2)TiO4 ceramics.Journal of the American Ceramic Society, 2001,84(11):2542-2546. |
[25] | GU Y J, HUANG J L, LI L H , et al.Microwave dielectric properties of low temperature fired CaO-Li2O-Sm2O3-TiO2 ceramics with LBS glass addition.Applied Mechanics and Materials. Trans. Tech. Publications, 2012,148:887-890. |
[26] | ZHANG S, SU H, ZHANG H , et al.Microwave dielectric properties of CaWO4-Li2TiO3 ceramics added with LBSCA glass for LTCC applications.Ceramics International, 2016,42(14):15242-15246. |
[1] | HUANG Jianfeng, LIANG Ruihong, ZHOU Zhiyong. Effects of W/Cr Co-doping on the Crystal Structure and Electric Properties of CaBi2Nb2O9 Piezoceramics [J]. Journal of Inorganic Materials, 2024, 39(8): 887-894. |
[2] | SONG Yunxia, HAN Yinglei, YAN Tao, LUO Min. New Ultraviolet Nonlinear Optical Crystal Rb3Hg2(SO4)3Cl [J]. Journal of Inorganic Materials, 2023, 38(7): 778-784. |
[3] | CHEN Lei, HU Hailong. Evolution of Electric Field and Breakdown Damage Morphology for Flexible PDMS Based Dielectric Composites [J]. Journal of Inorganic Materials, 2023, 38(2): 155-162. |
[4] | YE Fen, JIANG Xiangping, CHEN Yunjing, HUANG Xiaokun, ZENG Renfen, CHEN Chao, NIE Xin, CHENG Hao. Dielectric and Energy Storage Property of (0.96NaNbO3-0.04CaZrO3)-xFe2O3 Antiferroelectric Ceramics [J]. Journal of Inorganic Materials, 2022, 37(5): 499-506. |
[5] | ZHAO Wei, XU Yang, WAN Yingjie, CAI Tianxun, MU Jinxiao, HUANG Fuqiang. Metal Cyanamides/Carbodiimides: Structure, Synthesis and Electrochemical Energy Storage Performance [J]. Journal of Inorganic Materials, 2022, 37(2): 140-151. |
[6] | SUN Yangshan, YANG Zhihua, CAI Delong, ZHANG Zhengyi, LIU Qi, FANG Shuqing, FENG Liang, SHI Lifen, WANG Youle, JIA Dechang. Crystallization Kinetics, Properties of α-cordierite Based Glass-ceramics Prepared by Glass Powder Sintering [J]. Journal of Inorganic Materials, 2022, 37(12): 1351-1357. |
[7] | ZHANG Xiaoyan, LIU Xinyue, YAN Jinhua, GU Yaohang, QI Xiwei. Preparation and Property of High Entropy (La0.2Li0.2Ba0.2Sr0.2Ca0.2)TiO3 Perovskite Ceramics [J]. Journal of Inorganic Materials, 2021, 36(4): 379-385. |
[8] | PENG Fan, ZENG Yi. Method of Crystal Structure Identification by Using Kikuchi Diffraction Patterns [J]. Journal of Inorganic Materials, 2021, 36(11): 1193-1198. |
[9] | BAI Jiawei, YANG Jing, LÜ Zhenfei, TANG Xiaodong. Magnetic and Dielectric Properties of Ti 4+-doped M-type Hexaferrite BaFe12-xTixO19 Ceramics [J]. Journal of Inorganic Materials, 2021, 36(1): 43-48. |
[10] | LI Shufang,ZHAO Shuang,ZHOU Xiao,LI Manrong. Crystal Structures, Optical, and Magnetic Properties of Zn3-xMnxTeO6 [J]. Journal of Inorganic Materials, 2020, 35(8): 895-901. |
[11] | LI Shufang, ZHAO Shuang, LI Manrong. Flux Growth of Tungsten Oxychloride Li23CuW10O40Cl5 [J]. Journal of Inorganic Materials, 2020, 35(7): 834-838. |
[12] | HUANG Chong,ZHAO Wei,WANG Dong,BU Kejun,WANG Sishun,HUANG Fuqiang. Synthesis, Crystal Structure, and Electrical Conductivity of Pd-intercalated NbSe2 [J]. Journal of Inorganic Materials, 2020, 35(4): 505-510. |
[13] | WANG Tong,WANG Yuanhao,YANG Haibo,GAO Shuya,WANG Fen,LU Yawen. Dielectric and Energy Storage Property of BaTiO3-ZnNb2O6 Ceramics [J]. Journal of Inorganic Materials, 2020, 35(4): 431-438. |
[14] | Hui GAN, Chuan-Bin WANG, Qiang SHEN, Lian-Meng ZHANG. Preparation of La2NiMnO6 Double-perovskite Ceramics by Plasma Activated Sintering [J]. Journal of Inorganic Materials, 2019, 34(5): 541-545. |
[15] | Xiang-Xiong ZENG, Jin-Chao YANG, Lian ZUO, Ben-Ben YANG, Jun QIN, Zhi-Hang PENG. Li/Ce/La Multidoping on Crystal Structure and Electric Properties of CaBi2Nb2O9 Piezoceramics [J]. Journal of Inorganic Materials, 2019, 34(4): 379-386. |
Viewed | ||||||
Full text |
|
|||||
Abstract |
|
|||||