用作关节腔滑膜切除的放射性镝锂硼玻璃微球的性能研究

余 静1, 赵 荻1, 黄文旵1, 周 萘1, 王德平1, 尹 卫2, 陈亚青3   

  1. （1. 同济大学 材料科学与工程学院, 上海 200092; 2. 中国原子能科学研究院 同位素研究所, 北京 102413; 3. 上海市第六人民医院, 上海 200233）
  • 收稿日期:2009-04-21 修回日期:2009-05-31 出版日期:2010-01-24 网络出版日期:2010-01-24

Study on the Performance of Radioactive Dysprosium Lithium Borate Glass
Mircrospheres used for Synovectomy Treatment

YU Jing1, ZHAO Di1, HUANG Wen-Hai1, ZHOU Nai1, WANG De-Ping1, YIN Wei2, CHEN Ya-Qing3   

  1. （1. School of Materials Science and Engineering, Tongji University, Shanghai 200092, China; 2. Institute of Isotope Research, Sinitic Academy of Atomic Energy, Beijing 102413, China; 3. The Sixth Hospital, Shanghai 200233, China）
  • Received:2009-04-21 Revised:2009-05-31 Published:2010-01-24 Online:2010-01-24

PDF (PC)

1504

被引次数

7

摘要： 制备了能用于切除关节腔滑膜的放射性硼酸镝锂（DyLB）玻璃微球, 通过体外试验和动物试验研究了DyLB玻璃微球的降解性和生物相容性. 实验结果表明：DyLB微球在SBF9模拟体液中发生非均匀性溶解, 浸泡7d后, Dy3+的溶出量低于原始玻璃组成中Dy元素总量的0.0026wt%, Li+的溶出量则超过Li元素总量的53wt%. 失重实验表明, DyLB微球具有部分生物可降解性, 对所研究的三个组成, 在SBF9中浸泡1d后, DyLB玻璃微球的总失重量约16%～43％; 浸泡7d后, 微球与SBF9模拟液反应达到平衡, 失重量达到25%～55%. 同时, DyLB微球具有良好的生物相容性, 微球植入小鼠体内2周后, 形貌发生变化并逐渐降解, 期间没有引起组织损伤或异常炎症反应; DyLB微球经中子激活, 活化后核纯度指标大于99.9%, 符合临床应用要求.

关键词: 硼酸盐玻璃, 玻璃微球, 生物降解性, 生物活性, 关节腔滑膜切除

Abstract: The radioactive dysprosium lithium borate glass (DyLB) microspheres used for synovectomy were prepared. The biodegradability and biocompatibility of theses DyLB microspheres were investigated by in-vitro and in-vivo test. The DyLB microspheres reacted nonuniformly in simulated body fluid (SBF9) with more than 53wt% of lithium being dissolved, whereas nearly all of the dysprosium (>99.997wt%) remained in the reacted microspheres, after being immersed in SBF9 at 37℃ for 7d. For three different compositions, the weight loss of DyLB microspheres was 16%－43％ when they were immersed in SBF9 for 1d; After being immersed in SBF9 for 7d, the weight loss of these DyLB microspheres was up to (25%－55%), and the precipitationdissolution reaction reached equilibrium, indicating that the DyLB microspheres were partially biodegradable in SBF9. Furthermore, the DyLB microspheres had good biocompatibility, since no tissue damage or inflammation was detected after being implanted in the liver of rat for two weeks. After being neutron activation, the radionuclide purity of radioactive DyLB microspheres was over 99.9%, which can be used for radiation synovectomy treatment in clinic.

Key words: borate glass microspheres, biodegradability, biocompatibility, radiation synovectomy