doi:10.3724/SP.J.1077.2008.00491

无机材料学报

碳纳米管/ZnS复合材料的制备及其性能表征

焦志辉, 张孝彬, 程继鹏, 陶新永, 贺狄龙

(浙江大学材料科学与工程系, 硅材料国家重点实验室, 杭州 310027)

收稿日期:2007-06-08 修回日期:2007-09-11 出版日期:2008-05-20 网络出版日期:2008-05-20

Preparation and Characterization of Carbon Nanotubes/ZnS composite

JIAO Zhi-Hui, ZHANG Xiao-Bin, CHENG Ji-Peng, TAO Xin-Yong, HE Di-Long

(State Key Laboratory of Silicon Materials, Department of Materials Science and Engineering, Zhejiang University, Hangzhou 310027, China)

Received:2007-06-08 Revised:2007-09-11 Published:2008-05-20 Online:2008-05-20

摘要/Abstract

摘要：

碳纳米管用氨水、乙二胺四乙酸(EDTA)进行表面改性, 然后通过硫代乙酰胺、醋酸锌、水和表面改性的碳纳米管在水浴超声条件下发生溶液化学反应, 在碳纳米管表面包裹了一层分布均匀、致密的ZnS纳米晶粒. 用XRD、TEM、SAED、SEM、FTIR、PL等表征手段对材料进行了结构及性能表征. 研究结果表明: 对碳纳米管进行乙二胺四乙酸处理是实现ZnS纳米晶粒在碳纳米管表面均匀、致密包裹的重要因素, 碳纳米管/ZnS复合材料的光致发光性较之相同方法合成的ZnS, 俘获态发射峰蓝移6nm, 而能带边缘发射峰蓝移16nm. 通过对FTIR及不同表面改性碳纳米管的对比试验研究, 给出了碳纳米管/ZnS复合材料的形成机理.

关键词: 碳纳米管, ZnS, 包裹, 光致发光

Abstract: Carbon nanotubes were modified by NH₃·H₂O and EDTA, respectively. Then, ZnS nanoparticles were densely and
uniformly coated on modified surfaces of carbon nanotubes through reaction of thioacetamide and zinc acetate in water solution. The samples were characterized by XRD, TEM, SAED, SEM, FTIR and PL spectroscope. Experimental results indicate
that EDTA treatment of the carbon nanotubes is a key factor for the formation of carbon nanotubes/ZnS composite. The PL spectra show that the photoluminescence peaks of the carbon nanotubes/ZnS composite have a small blue shift in comparison with the as-prepared ZnS. A possible formation mechanism is proposed for the carbon nanotubes/ZnS composite．

Key words: carbon nanotube, ZnS, coating, photoluminescence

中图分类号:

TQ050

焦志辉,张孝彬,程继鹏,陶新永,贺狄龙. 碳纳米管/ZnS复合材料的制备及其性能表征[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2008.00491.

JIAO Zhi-Hui,ZHANG Xiao-Bin,CHENG Ji-Peng,TAO Xin-Yong,HE Di-Long. Preparation and Characterization of Carbon Nanotubes/ZnS composite[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2008.00491.

参考文献

[1] Iijima S. Nature, 1991, 354 (7): 56-58.
[2] Kang Yoonmook, Kim Donghwan. Sensors and Actuators A, 2006, 125 (2): 114-117.
[3] Li W Z, Xie S S, Qian L X, et al. Science, 1996, 274 (5293): 1701-1703.
[4] Yao Z, Postma H W C, Balents L, et al. Nature, 1999, 402 (6759): 273-276.
[5] Kong J, Franklin N R, Zhou C, et al. Science, 2000, 287 (5453): 622-625.
[6] Choi W B, Chae S, Bae E, et al. Appl. Phys. Lett., 2003, 82 (2): 275-277.
[7] Han W Q, Zettl A. Nano Lett., 2003, 3 (5): 681-683.
[8] Shi J H, Qin Y J, Wu W, et al. Carbon, 2004, 42 (2): 455-458.
[9] Banerjee S, Wong S S. Nano Lett., 2002, 2 (3): 195-200.
[10] Ravindran S, Chaudhary S, Colburn B, et al. Nano Lett., 2003, 3 (4): 447-453.
[11] Haremza J M, Hahn M A, Krauss T D, et al. Nano Lett., 2002, 2 (11): 1253-1258.
[12] Banerjee S, Wong S S. J. Am. Chem. Soc., 2003, 125 (34): 10342-10350.
[13] Sun J, Gao L, Iwasa M. Chem. Commun., 2004, (7): 832-833.
[14] Kim H, Sigmund W. Appl. Phys. Lett., 2002, 81 (11): 2085-2087.
[15] Wu H Q, Wei X W, Shao M W, et al. J. Crystal Growth, 2004, 265 (1-2): 184-189.
[16] Lee S W, Sigmund W M. Chem. Commun., 2003, (6): 780-781.
[17] Jung K H, Hong J S, Vittal R, et al. Chem. Lett., 2002, (8): 864-865.
[18] Vincent P, Brioude A, Journet C, et al. J. Non-Cryst. Solids, 2002, 311 (2): 130-137.
[19] Li X H, Niu J L, Zhang J, et al. J. Phys. Chem. B., 2003, 107 (11): 2453-2458.
[20] Sun J, Iwasa M, Gao L, et al. Carbon, 2004, 42 (4): 895-899.
[21] Fu Q, Lu C, Liu J. Nano Lett., 2002, 2 (4): 329-332.
[22] Seeger T, Kohler T, Frauenheim T, et al. Chem. Commun., 2002, (1): 34-35.
[23] Fu L, Liu Z M, Liu Y Q, et al. Adv. Mater., 2004, 16 (4): 350.
[24] Cao H Q, Hong G Y, Yan J H, et al. Chem. Lett., 2003, 14 (12): 1293-1295.
[25] Huang MH, Mao S, Feick H, et al. Science, 2001, 292 (5523): 1897-1899.
[26] Quan Zewei, Wang Zhenling, Yang Piaoping, et al. Inorganic Chemistry, 2007, 46 (4): 1354-1360.
[27] Fan D M, Feng S A, Zhu Z P. New Carbon Materials, 2006, 21 (4): 360-364.
[28] Shan Y, Gao L. Journal of the American Ceramic Society, 2006, 89 (2): 759-762.
[29] Xinyu Ye, Ying Fang, Yunsheng Huet, et al. Materials Letters, 2007, DOI:10.1016/j.matlet.2007.03.090.

碳纳米管/ZnS复合材料的制备及其性能表征

Preparation and Characterization of Carbon Nanotubes/ZnS composite

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	张婷婷, 王方园, 刘长友, 张国荣, 吕佳辉, 宋宇晨, 介万奇. 水热-烧结法制备Cr²⁺:ZnSe/ZnSe核壳结构纳米孪晶[J]. 无机材料学报, 2024, 39(4): 409-415.
[2]	陈海燕, 唐志鹏, 尹良君, 张林博, 徐鑫. CIPs@Mn_0.8Zn_0.2Fe₂O₄-CNTs复合材料低频吸波性能研究[J]. 无机材料学报, 2024, 39(1): 71-80.
[3]	李乾利, 黎乃鑫, 李育成, 刘慎业, 程帅, 杨光, 任宽, 王峰, 赵景泰. 辐射光致发光材料及其应用研究进展[J]. 无机材料学报, 2023, 38(7): 731-749.
[4]	田煜彬, 田超凡, 李森, 赵永鑫, 邢涛, 李智, 陈萧如, 向帅蓉, 代鹏程. 高导电性生物质碳布的制备及其燃料电池气体扩散层性能[J]. 无机材料学报, 2023, 38(11): 1316-1322.
[5]	柳琪, 朱璨, 谢贵震, 王俊, 张东明, 邵刚勤. Ce掺杂SrMgF₄超结构多晶体的吸收/光致发光光谱[J]. 无机材料学报, 2022, 37(8): 897-902.
[6]	关旭峰, 李桂芳, 卫云鸽. Na_1-_xM_xCaEu(WO₄)₃ (M=Li, K)红色荧光粉的微观结构与热猝灭特性研究[J]. 无机材料学报, 2022, 37(6): 676-682.
[7]	吴秋琴, 姚奋发, 金传洪, 郑遗凡. 碳纳米管内填充生长超细一维亚化学计量比氧化钨纳米线[J]. 无机材料学报, 2022, 37(4): 413-419.
[8]	张国庆, 秦鹏, 黄富强. 空间限域铅离子与钙钛矿纳米晶间的可逆转换与信息存储应用[J]. 无机材料学报, 2022, 37(4): 445-451.
[9]	杜傲宸, 杜琪源, 刘欣, 杨益民, 夏晨阳, 邹军, 李江. 高光效、大功率LEDs/LDs用Ce:YAG透明陶瓷[J]. 无机材料学报, 2021, 36(8): 883-892.
[10]	刘芳芳, 传秀云, 杨扬, 李爱军. 氮/硫共掺杂对纤水镁石模板碳纳米管电化学性能的影响[J]. 无机材料学报, 2021, 36(7): 711-717.
[11]	王东海,侯文涛,李纳,李东振,徐晓东,徐军,王庆国,唐慧丽. 导模法生长蓝宝石单晶光纤的缺陷和光学特性研究[J]. 无机材料学报, 2020, 35(9): 1053-1058.
[12]	董龙浩,张海军,张俊,吴文浩,贾全利. 碳纳米管改性海泡石多孔陶瓷及其高效油水分离性能研究[J]. 无机材料学报, 2020, 35(6): 689-696.
[13]	罗燚,冯军宗,冯坚,姜勇刚,李良军. 新型碳材料质子交换膜燃料电池Pt催化剂载体的研究进展[J]. 无机材料学报, 2020, 35(4): 407-415.
[14]	孙顶, 丁彦妍, 孔令炜, 张玉红, 郭秀娟, 魏立明, 张力, 张立新. Mg掺杂Cu₂ZnSnS₄的第一性原理研究[J]. 无机材料学报, 2020, 35(11): 1290-1294.
[15]	刘甜甜, 王庆华, 刘希莉, 高凤, 汪庆祥. 近球状钼酸镍/多壁碳纳米管复合材料的制备及其赝电容性能[J]. 无机材料学报, 2018, 33(7): 735-740.