以多孔阳极氧化铝膜为模板制备介孔二氧化硅纳米纤维

doi:10.3724/SP.J.1077.2010.01277

无机材料学报 ›› 2010, Vol. 25 ›› Issue (12): 1277-1280.DOI: 10.3724/SP.J.1077.2010.01277 CSTR: 32189.14.SP.J.1077.2010.01277

以多孔阳极氧化铝膜为模板制备介孔二氧化硅纳米纤维

王巍^1,2, 李晓天²

(1. 吉林化工学院化工与材料工程学院吉林 132022; 2. 吉林大学材料科学与工程学院长春 130012)

收稿日期:2010-03-08 修回日期:2010-05-12 出版日期:2010-12-20 网络出版日期:2010-11-24

Preparation of Mesoporous Silica Fibers in Porous Anodic Aluminum Oxide Template

WANG Wei^1,2, LI Xiao-Tian²

(1. School of Chemical and Material Engineering, Jilin Institute of Chemical Technology, Jilin 132022, China; 2. Department of Material Science and Engineering, Jilin University, Changchun 130012, China)

Received:2010-03-08 Revised:2010-05-12 Published:2010-12-20 Online:2010-11-24

摘要/Abstract

摘要： 以多孔阳极氧化铝膜为模版, 采用溶胶-胶方法, 制备了具有介孔结构的二氧化硅纳米纤维. 利用SEM、XRD、N₂吸附-脱附和TEM等手段对样品进行了表征. 实验结果显示SiO₂纤维的直径和长度分别依赖于所使用的模板(阳极氧化铝膜)的孔直径和膜的厚度. 而介孔SiO₂纤维中纳米孔道的取向可以通过改变陈化环境来控制. 在有水存在的环境下, SiO₂纤维其纳米孔道取向是环绕于纤维轴向的; 而在无水存在的环境下, SiO₂纤维其纳米孔道取向则是平行于纤维的轴向的.

关键词: 阳极氧化铝, 介孔, 二氧化硅, 纤维

Abstract: Mesoporous silica fibers were prepared within porous anodic aluminum oxide membrane (AAO) using a simple Sol-Gel method. The sample was characterized by SEM, XRD, nitrogen adsorption-desorption and TEM. The diameter and the length of the mesoporous silica fibers are depend on the pore diameter and thickness of AAO membrane, respectively. The orientation of the nanochannels in mesoporous silica fibers can be readily controlled by changing the aging environment. For the samples aged with the presence of water, all the nanochannels in the silica fibers are found to be circular around the fibers. However, for the samples aged without water, the nanochannels were found to be parallel along the fiber axes.

Key words: anodic aluminum oxide, mesoporous, silica, fiber

中图分类号:

O611

王巍, 李晓天. 以多孔阳极氧化铝膜为模板制备介孔二氧化硅纳米纤维[J]. 无机材料学报, 2010, 25(12): 1277-1280.

WANG Wei, LI Xiao-Tian. Preparation of Mesoporous Silica Fibers in Porous Anodic Aluminum Oxide Template[J]. Journal of Inorganic Materials, 2010, 25(12): 1277-1280.

参考文献

[1] Marlow F, McGehee M D, Zhao D, et al. Doped mesoporous silica fibers: a new laser material. Adv. Mater., 1999, 11(8): 632-636. [2] Huo Q, Zhao D, Feng J, et al. Room temperature growth of mesoporous silica fibers: a new high-surface-area optical waveguide. Adv. Mater., 1997, 9(12): 974-978. [3] Nguyen T Q, Wu J J, Doan V, et al. Control of energy transfer in oriented conjugated polymer-mesoporous silica composites. Science, 2000, 288(4): 652-656. [4] Wu C G, Bein T. Conducting polyaniline filaments in a mesoporosu channel host. Science, 1994, 264(6): 1757-1759. [5] Zhao D, Sun J, Li Q, et al. Morphological control of highly ordered mesoporous silica SBA-15. Chem. Mater., 2000, 12(2): 275-279. [6] Wang J, Zhang J, Asoo B Y, et al. Structrue-selective synthesis of mesostructured/mesoporous silica nanofibers. J. Am. Chem. Soc., 2003, 125(46): 13966-13967. [7] Marlow F, Spliethoff B, Tesche B, et al. The internal architecture of mesoporous silica fibers. Adv. Mater., 2000, 12(13): 961-965. [8] Bruinsma P J, Kim A Y, Liu J, et al. Mesoporous silica synthesized by solvent evaporation: spun fibers and spray-dried hollow spheres. Chem. Mater., 1997, 9(11): 2507-2512. [9] Yang P D, Zhao D Y, Chmelka B F, et al. Triblock copolymer directed syntheses of large-pore mesoporous silica fibers. Chem. Mater., 1998, 10(8): 2033-2036. [10] Madhugiri S, Zhou W, Ferraris J P, et al. Electrospun mesoporous molecular sieve fibers. Microporous and Mesoporous Materials, 2003, 63(1/2/3): 75-84. [11] Davis S A, Burkett S L, Mendelson N H, et al.-Bacterial templating of ordered macrostructures in silica and silica-surfactant mesophases. Nature, 1997, 385(1): 420-423. [12] Raimondi M E, Maschmeyer T, Templer R H, et al. Synthesis of direct templated aligned mesopoeous silica coatings within capollaries. Chem. Commun, 1997, 19: 1843-1844. [13] Melosh N A, Davidson P, Feng P, et al. Macroscopic shear aligmeat of bulk transparent mesostructured silica. J. Am. Chem. Soc., 2001, 123(6): 1240-1241. [14] Huang L, Wang H, Hayashi C Y, et al. Single-strand spider silk templating for the formation of hierarchically ordered hollow mesoporous silica fibers. J. Mater. Chem., 2003, 13(4): 666-668. [15] Alberius P C A, Frindell K L, Hayward R C, et al. General predictive synthesis of cubic, hexagonal, and lamellar silica and tiatania mesostructured thin films. Chem. Mater., 2002, 14(8): 3284-3294.

编辑推荐 0

Metrics

阅读次数

全文

2165

HTML			PDF

最新录用	在线预览	正式出版	最新录用	在线预览	正式出版
0	0	1	0	0	2164

来源	本网站	其他网站

次数	627	1538
比例	29%	71%

摘要

3012

最新录用	在线预览	正式出版

0	0	3012

来源	本网站	其他网站

次数	102	2910
比例	3%	97%

以多孔阳极氧化铝膜为模板制备介孔二氧化硅纳米纤维

Preparation of Mesoporous Silica Fibers in Porous Anodic Aluminum Oxide Template

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐 0

Metrics

本文评价

[1]	曹青青, 陈翔宇, 吴健豪, 王筱卓, 王乙炫, 王禹涵, 李春颜, 茹菲, 李兰, 陈智. SiO₂增强自敏性氮化碳微球可见光降解盐酸四环素的研究[J]. 无机材料学报, 2024, 39(7): 787-792.
[2]	管皞阳, 张立, 荆开开, 师维刚, 王晶, 李玫, 刘永胜, 张程煜. 国产三代2.5D SiC_f/SiC复合材料的界面力学性能[J]. 无机材料学报, 2024, 39(3): 259-266.
[3]	赵雅文, 屈发进, 汪岩屹, 王智文, 陈初升. 基于硅酸铝纤维的柔性氧敏感元件的制备和性能[J]. 无机材料学报, 2024, 39(10): 1084-1090.
[4]	师维刚, 张超, 李玫, 王晶, 张程煜. 2D-SiC_f/SiC复合材料层间I型断裂试验及表征[J]. 无机材料学报, 2024, 39(1): 45-50.
[5]	李跃军, 曹铁平, 孙大伟. S型异质结Bi₄O₅Br₂/CeO₂的制备及其光催化CO₂还原性能[J]. 无机材料学报, 2023, 38(8): 963-970.
[6]	吴爽, 苟燕子, 王永寿, 宋曲之, 张庆雨, 王应德. 高温热处理对国产KD-SA型SiC纤维组成结构与力学性能的影响[J]. 无机材料学报, 2023, 38(5): 569-576.
[7]	贾玉娜, 曹旭, 焦秀玲, 陈代荣. 无机酸铝体系氧化铝连续纤维的制备技术研究[J]. 无机材料学报, 2023, 38(11): 1257-1264.
[8]	杨代辉, 孙甜, 田合鑫, 史晓斐, 马东伟. 铁氮共掺杂介孔碳材料的简易制备及其氧还原反应催化性能[J]. 无机材料学报, 2023, 38(11): 1309-1315.
[9]	王红宁, 黄丽, 清江, 马腾洲, 黄维秋, 陈若愚. 有机-无机氧化硅空心球的合成及VOCs吸附应用[J]. 无机材料学报, 2022, 37(9): 991-1000.
[10]	王新刚, 杨青青, 林根连, 高巍, 秦福林, 李荣臻, 康庄, 王小飞, 蒋丹宇, 闫继娜. 国产550级连续氧化铝陶瓷纤维的高温拉伸性能研究[J]. 无机材料学报, 2022, 37(6): 629-635.
[11]	李婷婷, 张阳, 陈加航, 闵宇霖, 王久林. 锂硫电池S@pPAN正极用柔性黏结剂研究[J]. 无机材料学报, 2022, 37(2): 182-188.
[12]	陈铖, 丁晶鑫, 王会, 王德平. 掺钕介孔硼硅酸盐生物活性玻璃陶瓷骨水泥的制备与性能表征[J]. 无机材料学报, 2022, 37(11): 1245-1258.
[13]	张文君, 赵雪莹, 吕江维, 曲有鹏. 中空有序介孔有机硅的研究进展: 制备及在肿瘤治疗中的应用[J]. 无机材料学报, 2022, 37(11): 1192-1202.
[14]	张晓山, 王兵, 吴楠, 韩成, 刘海燕, 王应德. 高红外遮蔽SiZrOC纳米纤维膜的制备及其性能研究[J]. 无机材料学报, 2022, 37(1): 93-100.
[15]	储宇星, 刘海瑞, 闫爽. SnO₂/NiO复合半导体纳米纤维的制备及气敏性能研究[J]. 无机材料学报, 2021, 36(9): 950-958.