氟化镁基底上HfO2中间层对Al2O3薄膜微观组织和力学性能的影响

doi:10.15541/jim20160030

摘要/Abstract

摘要：

采用电子束蒸镀技术在氟化镁基底上制备了单层Al₂O₃薄膜和含有HfO₂中间层的HfO₂/Al₂O₃双层薄膜。在空气中对所制备的薄膜进行1 h 600℃的退火处理。通过掠入角X射线衍射仪(GIXRD)、场发射扫描电镜(FE-SEM)、傅里叶变换红外光谱仪(FTIR)、纳米压痕和划痕法对薄膜的微观结构、红外透过率和力学性能进行了表征。结果表明: 退火处理后HfO₂/Al₂O₃双层薄膜中形成了一层树枝状的新层, 这种新层的硬度大于17.5 GPa。这种高硬度的新层能够保护氟化镁基底不被划伤。从GIXRD图谱中只能找到单斜相HfO₂的衍射峰, 而Al₂O₃薄膜仍然保持非晶态。从这些结果中可以推断出HfO₂从非晶态向单斜相的转变促进了这种树枝状新层的产生, 也正是这种新层提高了保护薄膜的力学性能。

关键词: HfO2中间层, Al2O3薄膜, 微观组织, 力学性能, 氟化镁基底

Abstract:

Al₂O₃ thin films with or without HfO₂ interlayer between Al₂O₃ and substrate were deposited on MgF₂ substrates by electron-beam evaporation technique. The as-deposited thin films were then annealed at 600℃ for 1 h to promote crystallization. The microstructure, IR transmittance and mechanical properties of the as-deposited and annealed samples were investigated by field emission scanning electron microscopy (FE-SEM), grazing incidence X-ray diffraction (GIXRD), Fourier Transform Infrared (FTIR) spectrometer, nanoindentation, and scratch tests, respectively. FE-SEM results show that a new branch-like layer is generated in annealed HfO₂/Al₂O₃double-layer thin films. The hardness of the newly formed layer is considered to be larger than 17.5 GPa. Because of the high hardness of the new layer, the MgF₂substrate can be protected from being drown out during scratch test. From GIXRD patterns, Al₂O₃ still remains amorphous while HfO₂ interlayer transforms from amorphous to monoclinic phase after annealing process. It could be deduced that it is the phase transformation of HfO₂ interlayer that promotes the formation of the harder branch-like layer.

Key words: HfO2 interlayer, Al2O3 thin film, microstructure, mechanical properties, MgF2 substrate

中图分类号:

TQ174

宋博, 赵丽丽, 陈笑迎, 游丽君, 宋力昕. 氟化镁基底上HfO₂中间层对Al₂O₃薄膜微观组织和力学性能的影响[J]. 无机材料学报, 2016, 31(7): 779-784.

SONG Bo, ZHAO Li-Li, CHEN Xiao-Ying, YOU Li-Jun, SONG Li-Xin. Effects of HfO₂ Interlayer on Microstructure and Mechanical Property of Al₂O₃ Thin Film on MgF₂ Substrate[J]. Journal of Inorganic Materials, 2016, 31(7): 779-784.

图/表 5

Fig. 1 GIXRD patterns of the as-deposited and annealed samples

Fig. 2 Cross-sectional FE-SEM images of the as-deposited and annealed samples (a) A1; (b) A2; (c) AH1; (d) AH2

Fig. 3 IR transmittance spectra of the uncoated MgF2, as-deposited and annealed samples in the range of 3-5 μm

Fig. 4 Mechanical properties obtained from nanoindentation tests (a) Elastic modulus as a function of penetration depth for as-deposited and annealed samples; (b) Hardness as a function of penetration depth for the same samples

Fig. 5 SEM images of scratch tracks of the as-deposited and annealed samples.(a) A1; (b) A2; (c)AH1; (d) AH2; (e) Higher resolution image of the selected area in Fig. 5(d)

参考文献 22

[1]	MOGHIM M, PAYDAR M.Hot-pressing of bimodally distributed magnesium fluoride powder.Infrared Physics & Technology, 2010, 53(6): 430-433.
[2]	NOFAR M, HOSSEINI H M, SHIVAEE H.The dependency of optical properties on density for hot pressed MgF2.Infrared Physics & Technology, 2008, 51(6): 546-549.
[3]	HI Q, LV F, ZHANG F, et al.Particle erosion of infrared materials.Journal of University of Science and Technology Beijing, Mineral, Metallurgy, Material, 2008, 15(6): 758-763.
[4]	ROBERTSON J.Diamond-like amorphous carbon.Materials Science and Engineering: R: Reports, 2002, 37(4): 129-281.
[5]	KISCHKAT J, PETERS S, GRUSKA B, et al.Mid-infrared optical properties of thin films of aluminum oxide, titanium dioxide, silicon dioxide, aluminum nitride, and silicon nitride.Applied Optics, 2012, 51(28): 6789-6798.
[6]	LI Y P, WANG N, CHE X S, et al.Infrared transmissive and rain-erosion resistant performances of GeC/GaP double-layer thin films on ZnS substrates.Applied Surface Science, 2013, 264: 538-544.
[7]	FENG L, LIU Z, LI Q, et al.Investigation of SiO2/Si3N4 films prepared on sapphire by Rf magnetron reactive sputtering.Applied Surface Science, 2006, 252(12): 4064-4070.
[8]	KOHARA T, TAMAGAKI H, IKARI Y, et al.Deposition of α-Al2O3 hard coatings by reactive magnetron sputtering.Surface and Coatings Technology, 2004, 185(2): 166-171.
[9]	RUPPI S.Deposition, microstructure and properties of texture- controlled CVD α-Al2O3 coatings.International Journal of Refractory Metals and Hard Materials, 2005, 23(4): 306-316.
[10]	ZYWITZKI O, GOEDICKE K, MORGNER H.Structure and properties of Al2O3 layers deposited by plasma activated electron beam evaporation.Surface and Coatings Technology, 2002, 151: 14-20.
[11]	SHAMALA K, MURTHY L, RAO K N.Studies on optical and dielectric properties of Al2O3 thin films prepared by electron beam evaporation and spray pyrolysis method.Materials Science and Engineering: B, 2004, 106(3): 269-274.
[12]	ZHANG L, JIANG H, LIU C, et al.Annealing of Al2O3 thin films prepared by atomic layer deposition. Journal of Physics D: Applied Physics, 2007, 40(12): 3707.
[13]	MUSIL J, BLAŽEK J, ZEMAN P, et al. Thermal stability of alumina thin films containing γ-Al2O3 phase prepared by reactive magnetron sputtering.Applied Surface Science, 2010, 257(3): 1058-1062.
[14]	EKLUND P, SRIDHARAN M, SINGH G, et al.Thermal stability and phase transformations of γ-/amorphous-Al2O3 thin films.Plasma Processes and Polymers, 2009, 6(S1): S907-S1011.
[15]	RUPPI S, LARSSON A, FLINK A.Nanoindentation hardness, texture and microstructure of α-Al2O3 and κ-Al2O3 coatings.Thin Solid Films, 2008, 516(18): 5959-5966.
[16]	JIN P, XU G, TAZAWA M, et al.Low temperature deposition of a-Al2O3 thin films by sputtering using a Cr2O3 template.Journal of Vacuum Science & Technology A Vacuum, Surfaces, and Films, 2002, 20(6): 2134-2136.
[17]	PANG X, GAO K, LUO F, et al.Annealing effects on microstructure and mechanical properties of chromium oxide coatings. Thin Solid Films, 2008, 516(15): 4685-4689.
[18]	LEE S K, LEE S B, PARK S Y, et al.Structure of amorphous aluminum oxide.Physical Review Letters, 2009, 103(9): 095501.
[19]	HE Q, GUO H B, WEI J J, et al.Deposition of HfO2 thin films on ZnS substrates. Thin Solid Films, 2008, 516(15): 4695-4699.
[20]	FISCHER-CRIPPS A C. Critical review of analysis and interpretation of nanoindentation test data.Surface and Coatings Technology, 2006, 200(14): 4153-4165.
[21]	LI X, BHUSHAN B.A review of nanoindentation continuous stiffness measurement technique and its applications.Materials Characterization, 2002, 48(1): 11-36.
[22]	BORRERO-LOPEZ O, HOFFMAN M.Measurement of fracture strength in brittle thin films.Surface and Coatings Technology, 2014, 254: 1-10.

氟化镁基底上HfO₂中间层对Al₂O₃薄膜微观组织和力学性能的影响

Effects of HfO₂ Interlayer on Microstructure and Mechanical Property of Al₂O₃ Thin Film on MgF₂ Substrate

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 5

参考文献 22

相关文章 15

编辑推荐

Metrics

本文评价

[1]	陈义, 邱海鹏, 陈明伟, 徐昊, 崔恒. SiC/SiC复合材料基体硼改性方法及其力学性能研究[J]. 无机材料学报, 2025, 40(5): 504-510.
[2]	崔宁, 张玉新, 王鲁杰, 李彤阳, 于源, 汤华国, 乔竹辉. (TiVNbMoW)C_x高熵陶瓷的单相形成过程与碳空位调控[J]. 无机材料学报, 2025, 40(5): 511-520.
[3]	李紫薇, 弓伟露, 崔海峰, 叶丽, 韩伟健, 赵彤. 前驱体法制备(Zr, Hf, Nb, Ta, W)C-SiC复相陶瓷及性能研究[J]. 无机材料学报, 2025, 40(3): 271-280.
[4]	高晨光, 孙晓亮, 陈君, 李达鑫, 陈庆庆, 贾德昌, 周玉. 基于湿法纺丝技术的SiBCN-rGO陶瓷纤维的组织结构、力学和吸波性能[J]. 无机材料学报, 2025, 40(3): 290-296.
[5]	穆浩洁, 张源江, 喻彬, 付秀梅, 周世斌, 李晓东. ZrO₂掺杂Y₂O₃-MgO纳米复相陶瓷的制备及性能研究[J]. 无机材料学报, 2025, 40(3): 281-289.
[6]	李伟, 许志明, 苟燕子, 尹森虎, 余艺平, 王松. SiC纤维烧结陶瓷的制备及其性能研究[J]. 无机材料学报, 2025, 40(2): 177-183.
[7]	范武刚, 曹雄, 周响, 李玲, 赵冠楠, 张兆泉. 8YSZ陶瓷在模拟压水堆水环境中的耐腐蚀性能[J]. 无机材料学报, 2024, 39(7): 803-809.
[8]	王伟明, 王为得, 粟毅, 马青松, 姚冬旭, 曾宇平. 以非氧化物为烧结助剂制备高导热氮化硅陶瓷的研究进展[J]. 无机材料学报, 2024, 39(6): 634-646.
[9]	孙海洋, 季伟, 王为民, 傅正义. TiB-Ti周期序构复合材料设计、制备及性能研究[J]. 无机材料学报, 2024, 39(6): 662-670.
[10]	蔡飞燕, 倪德伟, 董绍明. 高熵碳化物超高温陶瓷的研究进展[J]. 无机材料学报, 2024, 39(6): 591-608.
[11]	刘国昂, 王海龙, 方成, 黄飞龙, 杨欢. B₄C含量对(Ti_0.25Zr_0.25Hf_0.25Ta_0.25)B₂-B₄C陶瓷力学性能及抗氧化性能的影响[J]. 无机材料学报, 2024, 39(6): 697-706.
[12]	粟毅, 史扬帆, 贾成兰, 迟蓬涛, 高扬, 马青松, 陈思安. 浆料浸渍辅助PIP工艺制备C/HfC-SiC复合材料的微观结构及性能研究[J]. 无机材料学报, 2024, 39(6): 726-732.
[13]	孙川, 何鹏飞, 胡振峰, 王荣, 邢悦, 张志彬, 李竞龙, 万春磊, 梁秀兵. 含有石墨烯阵列的SiC基陶瓷材料的制备与力学性能[J]. 无机材料学报, 2024, 39(3): 267-273.
[14]	李雷, 程群峰. 高性能MXenes纳米复合材料研究进展[J]. 无机材料学报, 2024, 39(2): 153-161.
[15]	刘艳艳, 谢曦, 刘增乾, 张哲峰. MAX相陶瓷增强金属基复合材料: 制备、性能与仿生设计[J]. 无机材料学报, 2024, 39(2): 145-152.