Wetting Properties and Interface Reaction Mechanism of Ag-Cu Brazes on Dual-phase Membrane Ceramic

doi:10.15541/jim20150551

Abstract

Abstract:

A reactive air brazing Ag-CuO alloy was evaluated for brazing dual phase oxygen membrane Ce_0.8Gd_0.2O_2-_δ- NdBaCo₂O₅₊_δ (CGO-NBCO). Contact angle tests were observed between Ag-Cu brazes and CGO-NBCO in air and the interfacial microstructures of the used samples were evaluated by SEM. The results indicate that the wetting angle decreases from 35° to 20° with the content of Cu increased from 6.6mol% to 15.8mol%. It is found that there are copper oxide-enriched zones formed in the junction of the alloy and substrate. The wettability between Ag-CuO alloy and oxygen membrane CGO-NBCO is improved due to the interfacial reaction between Cu oxides in braze and the surface layers of CGO-NBCO substrates to form compounds of Ba-Cu-O, Co-Cu-O and Nd-Ce-Cu-O oxides. The new formed interface reaction layers promote the wettability of the rest braze.

Key words: Ag-Cu alloy brazing filler, dual-phase membranes ceramic, wettability, interface reaction

CLC Number:

TQ174

ZHANG Li-Li, LI Ke,YU Chen-Chen, ZHANG Yu-Wen, WU Cheng-Zhang, DING Wei-Zhong. Wetting Properties and Interface Reaction Mechanism of Ag-Cu Brazes on Dual-phase Membrane Ceramic[J]. Journal of Inorganic Materials, 2016, 31(6): 607-612.

Figures/Tables 6

Table 1 Composition of Ag-Cu brazes/mol%

Braze	Cu	Ag
Ag	0	100
Ag -6.6Cu	6.6	93.4
Ag -11.0Cu	11.0	89.0
Ag -15.8Cu	15.8	84.2

Fig. 1 XRD pattern of CGO-NBCO

Fig. 2 Contact angles between Ag-Cu and CGO-NBCO as a function of temperature

Fig. 3 Morphologies of the interfaces between Ag-Cu brazes and CGO-NBCO membrane after wetting experiments. (a) Ag; (b) Ag-6.6Cu; (c) Ag-11Cu; (d) Ag-15.8Cu

Fig. 4 EDS analyses of the interface between Ag-Cu brazes and CGO-NBCO membrane

Fig. 5 Pseudobinary Ag-CuO phase diagram[14]

References 14

[1]	WEIL K S, HARDY J S, RICE J P, et al.Brazing as a means of sealing ceramic membranes for use in advanced coal gasiﬁcation processes.Fuel, 2006, 85(2): 156-162.
[2]	SHAO ZONG-PING, XIONG GUO-XING.Mixed conducting oxygen permeative membranes and their application in partial oxidation of methane to syngas process.Process in Chemical, 1999, 11(1): 30-40.
[3]	TONG JIAN-HUA, YANG WEI-SHEN.Methods for selection perovskite-type oxides used as mixed-conducting membranes for oxygen separation.Membrane Science and Technology, 2003, 23(1): 33-42.
[4]	CHUANGANG FAN, WEI LIU, ZENGQIANG DENG, et al.Mechanical stability and transport properties of the Sn-promoted SrCo0.8Fe0.2O3-δ ceramic membrane.Journal of Membrane Science, 2007, 290(1/2): 73-77.
[5]	HARDY J S, KIM J Y, WEIL K S.Joining mixed conducting oxides using an air-fired electrically conductive braze.Journal of the Electrochemical Society, 2004, 151(8): 43-49.
[6]	WEIL K S, KIMJ Y, HARDY J S.Interfacial analysis of (La0.6Sr0.4)(Co0.2Fe0.8)O3-δ substrates wetted by Ag-CuO.Journal of Material Science, 2005(40): 2341-2348.
[7]	DABBARH S, PFAFF A, ZIOMBRA A, et al.Brazing of mice ceramics to high temperature metals.Ceramic Transactions, 2010 (215): 213-223.
[8]	WANG FANG, ZHANG YU-WEN, DING WEI-ZHONG, et al.Pure Cu braze for sealing oxygen-permeable membrane ceramics and stainless steel support.Journal of Functional Materials, 2010, 41(9): 1540-1542.
[9]	WANG FANG, LIU YONG, LU XION-GANG, et al.Effect of Cu content on interface microstructures of oxygen-permeable membrane brazed with Ag-Cu brazing filler.Rare Meterials and Engineering, 2011, 40(10): 1832-1835.
[10]	LIU JIAO, ZHANG YU-WEN, LIU XU, et al.The effect of temperature on the interface reaction and connectivity between Ag-Cu alloy braze and ceramic oxygen-permeable membrane.Journal of Functional Materials, 2011, 42(2): 313-317.
[11]	ZHANG QI-FEI, GENG ZHEN, ZHANG YU-WEN, et al.The wetting and interface reaction mechanism of Ag-Cu-O brazes on BaCo0.7Fe0.2Nb0.1O3-δ oxygen-permeable membrane ceramic.Journal of Functional Materials, 2012, 43(1): 77-80.
[12]	刘蛟. Ag-Cu钎料与透氧膜陶瓷的润湿及界面反应研究. 上海: 上海大学硕士学位论文, 2013.
[13]	NEVRIVA M, KRAUS H, SEDMIDUBSKY D.Phase equilibria study in the partially open Cu-(O) and Me-Cu-, 1995(282/283): 205-224.
[14]	SHAO Z B, LIU K R, LIU Q L, et al.Eauilibrium phase diagrams in the systems PbO-Ag and CuO-Ag.Journal of the American Ceramic Society, 1993, 76(10): 2663-2664.

[1]	SHANGGUAN Li, NIE Xiaoshuang, YE Kuicai, CUI Yuanyuan, QIAO Yuqin. Effects of Surface Wettability of Titanium Oxide Coatings on Osteoimmunomodulatory Properties [J]. Journal of Inorganic Materials, 2023, 38(12): 1457-1565.
[2]	DING Jianxiang,HUANG Peiyan,ZHA Yuhui,WANG Dandan,ZHANG Peigen,TIAN Wubian,SUN Zhengming. High-purity Ti₂AlC Powder: Preparation and Application in Ag-based Electrical Contact Materials [J]. Journal of Inorganic Materials, 2020, 35(6): 729-734.
[3]	ZHAO Zhankui, LI Tao, LU Shuhan, WANG Minggang, ZHANG Jingjing, CHENG Daowen, WU Chen, CHI Yue, WANG Hongli. Magnetic Properties and Resistivity of Soft Magnetic Composites Regulated by SPS Enhanced Interface Reaction Mechanism [J]. Journal of Inorganic Materials, 2020, 35(11): 1223-1226.
[4]	LI Dong, LEI Chao, LAI Hua, LIU Xiao-Lin, YAO Wen-Li, LIANG Tong-Xiang, ZHONG Sheng-Wen. Recent Advancements in Interface between Cathode and Garnet Solid Electrolyte for All Solid State Li-ion Batteries [J]. Journal of Inorganic Materials, 2019, 34(7): 694-702.
[5]	LIANG Yu, LIANG Ling-Yan, WU Wei-Hua, PEI Yu, YAO Zhi-Qiang, CAO Hong-Tao. Microfluidic-method-processed p-type NiO_x Thin-film Transistors [J]. Journal of Inorganic Materials, 2019, 34(1): 79-84.
[6]	CHEN Fan, SHI Kai-Cheng, SUN Shi-Yang, ZHAO Bo-Wen, SHANG Hai-Long, LI Ge-Yang. Direct Brazing of Al/Al₂O₃ without Wettability of Molten Metal [J]. Journal of Inorganic Materials, 2016, 31(6): 602-606.
[7]	LUO Ling-Hong, YU Hui, HUANG Zu-Zhi. Research Progress of the Sealing Glass for Intermediate Temperature Solid Oxide Fuel Cell [J]. Journal of Inorganic Materials, 2015, 30(2): 113-121.
[8]	LU You-Jun, WANG Yan-Min, PAN Zhi-Dong, HUANG Zhen-Kun, WU Lan-Er. Effect of Carbon Nanoparticle Content on Machinability and Wettability of Carbon/Silicon Carbide Ceramics [J]. Journal of Inorganic Materials, 2014, 29(4): 429-432.
[9]	LU Jin-Rong, ZHOU Yang, LI Hai-Yan, ZHENG Yong, LI Shi-Bo, HUANG Zhen-Ying. Wettability and Wetting Process in Cu/Ti₃SiC₂ System [J]. Journal of Inorganic Materials, 2014, 29(12): 1313-1319.
[10]	HUANG Lin, NING Cong-Qin, DING Dong-Yan, BAI Shuo, QIN Rui, LI Ming, MAO Da-Li. Wettability and In Vitro Bioactivity of Doped TiO₂Nanotubes [J]. Journal of Inorganic Materials, 2010, 25(7): 775-779.
[11]	LI Jia-Ke,LIU Lei,LIU Yi-Chun,ZHANG Wen-Long,HU Wen-Bin. Preparation of Ti-Si Eutectic Brazes and its Weldability to SiC [J]. Journal of Inorganic Materials, 2009, 24(1): 204-208.
[12]	LI Da,ZHANG Yue-Li,XIAO Wen-Jia,YANG Yang-Yi,HE Zhen-Hui. Fabrication and Investigation of Superhydrophobic-Hydrophilic CaBi₄Ti₄O₁₅ Coatings [J]. Journal of Inorganic Materials, 2008, 23(4): 745-748.
[13]	YANG Jing,CHEN Jie-Rong,YU Rong. Surface Wettability and Vapour Stability of Silica Membranes Modified by Sol-Gel Method [J]. Journal of Inorganic Materials, 2008, 23(4): 739-744.
[14]	QIAN Bai-Tai,SHEN Zi-Qiu. Super-hydrophobic CuO Nanoflowers by Controlled Surface Oxidation on Copper [J]. Journal of Inorganic Materials, 2006, 21(3): 747-752.
[15]	ZHAO Yan,WANG Bao-Xiang,ZHAO Xiao-Peng. Preparation and Electrorheological Effect of Titanium Oxide/Acrylamide Doped with Cr Ions [J]. Journal of Inorganic Materials, 2006, 21(3): 671-676.