Fabrication of Bio-ceramic Bone Model

doi:10.3724/SP.J.1077.2012.00348

Abstract

Abstract:

The process parameters and raw materials of current commercial rapid prototyping (RP) machines are limited, thus the bone model is not easily to fabricate. In order to overcome these disadvantages, a self-developed rapid prototyping machine was used to produce bone model. In this work, the hydroxyapatite (HA), silica sol and suspending agent were mixed as raw materials. By adjusting the suitable process parameter, the bio-ceramic green parts could be formed, and then the specimen green parts were sintered at 1200℃, 1300℃, 1400℃, respectively. The shrinkage, surface roughness and compression strength were tested. Furthermore, the cell activities of the bone model were investigated through the osteoblast MG63 cells culture. The results showed that the green part sintered at 1200℃ exhibits optimum properties with greatly improved compression strength and surface roughness of R_a (12.04 μm), which is suitable for the growth of the osteoblast MG63.

Key words: bio-ceramic, bone model, rapid prototyping, laser

CLC Number:

TQ174

LIU Fwu-Hsing, CHEN Ssu-Han. Fabrication of Bio-ceramic Bone Model[J]. Journal of Inorganic Materials, 2012, 27(4): 348-352.

Figures/Tables 7

Fig. 1 A rapid prototyping machine of selective laser curing

Fig. 2 Schematic of the experimental processes

Fig. 3 Forming range of the selective laser curing

Fig. 4 A finished part of femur bone model

Fig. 5 SEM surface image of femur bone model

Fig. 6 Effect of sintering temperatures on the shrinkage (a), surface roughness (b) and compression strength (c) of specimen

Fig. 7 Optical density of osteoblasts cells cultured for different times

References 14

[1]	Eshraghi S, Das S. Mechanical and microstructure properties of polycaprolactone scaffolds with one-dimensional, two-dimensional, and three-dimensional orthogonally oriented porous architectures produced by selective laser sintering. Acta Biomaterialia., 2010 (6): 2467-2479.
[2]	李武松. 颅颜整形手术用植入物之设计与制作. 桃园: 国立中央大学硕士论文, 1990.
[3]	Peng R S, Wang J B, Yao Q Z. Application study of rapid prototyping manufacturing in media. Chinese Journal of Lasers, 2005, 29(3): 87-88.
[4]	CUI Zhi-Zhong, LI Di-Chen, QIAO Guan-Jun, et al. Peparation of porous carbon template with controllable channels by phenolic resin pyrolyzing. Journal of Inorganic Materials, 2006, 21(4): 848-854.
[5]	Liu F H, Liao Y S. Fabrication of inner complex ceramic parts by selective laser gelling. Journal of the European Ceramic Society. , 2010(30): 3283-3289.
[6]	Liu F H. Manufacturing porous multi-channel ceramics by laser gelling. Ceramics International, 2011(37): 2789-2794.
[7]	赵震锦, 张翀, 张扬, 等. 表面粗糙度对种植体钛片表面成骨细胞的影响. 解剖科学进展, 2008, 14(2): 178-182.
[8]	Goergiou G, Knowles J C. Glass reinforced hydroxyapatite for hard tissue surgery. Biomaterials, 2001(22): 2811-2815.
[9]	Ruys A J, Wei M, Sorrell C C, et al. Sintering effect on the strength of hydroxyapatite. Biomaterials, 1995, 16(5): 409-415.
[10]	ZHANG Lei-Lei, LI He-Jun, LI Ke-Zhi, et al. Effect of surface roughness of carbon/carbon composites on osteoblasts. Journal of Inorganic Materials, 2008, 23(2): 341-345.
[11]	Ponsonnet L, Comte V, Othmane A, et al. Effect of surface topography and chemistry on adhesion, orientation and growth of fibroblasts on nickel-titanium substrates. Materials Science and Engineering C. , 2002, 21(1/2): 157-165.
[12]	Montanaro L, Arciola C R, Campoccia D, et al. In vitro effects on MG63 osteoblast-like cells following contact with two roughness- differing fluorohydroxyapatite-coated titanium alloys. Biomaterials, 2002(23): 3651-3659.
[13]	范震, 贾爽, 苏剑生, 等. 种植体表面粗糙度对成骨细胞增殖及ALP含量的影响. 口腔颌面外科杂志, 2009, 19(2): 128-131.
[14]	Rosa A L, Beloti M M. Rat bone marrow cell response to titanium and titanium alloy with different surface roughness. Clin Oral Implants Res., 2002(14): 43-48.

[1]	ZHAO Kaixuan, LIU Wenpeng, DING Shoujun, DOU Renqin, LUO Jianqiao, GAO Jinyun, SUN Guihua, REN Hao, ZHANG Qingli. Nd:YLF Crystal Growth: Raw Materials Preparation by Melting Method and Property [J]. Journal of Inorganic Materials, 2025, 40(5): 529-535.
[2]	YIN Jie, GENG Jiayi, WANG Kanglong, CHEN Zhongming, LIU Xuejian, HUANG Zhengren. Recent Advances in 3D Printing and Densification of SiC Ceramics [J]. Journal of Inorganic Materials, 2025, 40(3): 245-255.
[3]	CHEN Qian, SU Haijun, JIANG Hao, SHEN Zhonglin, YU Minghui, ZHANG Zhuo. Progress of Ultra-high Temperature Oxide Ceramics: Laser Additive Manufacturing and Microstructure Evolution [J]. Journal of Inorganic Materials, 2024, 39(7): 741-753.
[4]	WANG Kanglong, YIN Jie, CHEN Xiao, WANG Li, LIU Xuejian, HUANG Zhengren. Effect of Particle Grading on Properties of Silicon Carbide Ceramics Prepared by Selective Laser Sintering Printing Combined with Solid-phase Sintering at Atmospheric Pressure [J]. Journal of Inorganic Materials, 2024, 39(7): 754-760.
[5]	TAM YU Puy Mang, XU Yu, GAO Quanhao, ZHOU Haiqiong, ZHANG Zhen, YIN Hao, LI Zhen, LÜ Qitao, CHEN Zhenqiang, MA Fengkai, SU Liangbi. Spectroscopic Properties and Optical Clusters in Erbium-doped CaF₂, SrF₂ and PbF₂ Crystals [J]. Journal of Inorganic Materials, 2024, 39(3): 330-336.
[6]	XU Hao, QIAN Wei, HUA Yinqun, YE Yunxia, DAI Fengze, CAI Jie. Effects of Micro Texture Processed by Picosecond Laser on Hydrophobicity of Silicon Carbide [J]. Journal of Inorganic Materials, 2023, 38(8): 923-930.
[7]	JIN Sai, LIU Xiaogen, QI Shuang, ZHAO Runchang, LI Zhijun. Fused Silica Glass: Laser-induced Damage on Bending Strength Weakening and Safety Design [J]. Journal of Inorganic Materials, 2023, 38(6): 671-677.
[8]	YANG Jiaxue, LI Wen, WANG Yan, ZHU Zhaojie, YOU Zhenyu, LI Jianfu, TU Chaoyang. Spectroscopic and Yellow Laser Features of Dy³⁺: Y₃Al₅O₁₂ Single Crystals [J]. Journal of Inorganic Materials, 2023, 38(3): 350-356.
[9]	WANG Huajin, KOU Huamin, WANG Yongzhe, JIANG Dapeng, ZHANG Bo, QIAN Xiaobo, WANG Jingya, ZHU Linling, ZENG Aijun, YANG Qiuhong, SU Liangbi. Irradiation Damage of CaF₂ with Different Yttrium Concentrations under 193 nm Laser [J]. Journal of Inorganic Materials, 2023, 38(2): 219-224.
[10]	CAI Jia, ZHAO Fangxia, FAN Dong, HUANG Liping, NIU Yaran, ZHENG Xuebin, ZHANG Zhenzhong. Pyrolysis Behavior and Laser Ablation Resistance of PCS in Polycarbosilane Composite Coatings [J]. Journal of Inorganic Materials, 2023, 38(11): 1271-1280.
[11]	WU Dongjiang, ZHAO Ziyuan, YU Xuexin, MA Guangyi, YOU Zhulin, REN Guanhui, NIU Fangyong. Direct Additive Manufacturing of Al₂O₃-TiC_p Composite Ceramics by Laser Directed Energy Deposition [J]. Journal of Inorganic Materials, 2023, 38(10): 1183-1192.
[12]	DENG Taoli, CHEN Hexin, HEI Lingli, LI Shuxing, XIE Rongjun. Achieving High Light Uniformity Laser-driven White Lighting Source by Introducing Secondary Phases in Phosphor Converters [J]. Journal of Inorganic Materials, 2022, 37(8): 891-896.
[13]	CAO Jiwei, WANG Pei, LIU Zhiyuan, LIU Changyong, WU Jiamin, CHEN Zhangwei. Research Progress on Powder-based Laser Additive Manufacturing Technology of Ceramics [J]. Journal of Inorganic Materials, 2022, 37(3): 241-254.
[14]	LIU Haifang, SU Haijun, SHEN Zhonglin, JIANG Hao, ZHAO Di, LIU Yuan, ZHANG Jun, LIU Lin, FU Hengzhi. Research Progress on Ultrahigh Temperature Oxide Eutectic Ceramics by Laser Additive Manufacturing [J]. Journal of Inorganic Materials, 2022, 37(3): 255-266.
[15]	HUANG Longzhi, YIN Jie, CHEN Xiao, WANG Xinguang, LIU Xuejian, HUANG Zhengren. Selective Laser Sintering of SiC Green Body with Low Binder Content [J]. Journal of Inorganic Materials, 2022, 37(3): 347-352.