Calcium Phosphate/ Gelatin Composite Coatings on Titanium Surfaces by ElectrochemicalDepositon

doi:10.3724/SP.J.1077.2011.00061

Abstract

Abstract: Bioactive calcium phosphate (Ca-P)coated titanium is the most promising bone replacement materials. Bioactive calciumphosphate (Ca-P) coated titanium has the advantages of both metal and ceramicsand has been considered as one of the most promising bone replacementmaterials. Gelatin is the denatured form of collagen and is expected to bebeneficial for hard tissue applications. The CaP/gelatin composite coatings couldcombine the bioactivity and osteoconductivity of CaP with the good characteristicsof gelatin. In the present study, The pulsed electrochemicaldeposition method was employed to deposit CaP/gelatin composite coatings ontitanium substrates. The main purpose of the study is to explore the optimumprocessing parameters of the composite coating. Electrolyte was made from themixture of the Ca-P and gelatin aqueous solution with different concentrations.SEM, XRD and FTIR were usedto characterize the composition and morphology of the coating. The coatings prepared underconstant voltage and pulse voltage electrodeposition were compared and it was foundthat the pulse voltage mode was more suitable for preparing CaP/gelatincoatings. The results indicated that Theoptimized experimental conditions were as follows,:pulse voltage range, of 0 to -1.3V, the Ca²⁺ concentrationof 5.0×10^-⁴mol/L; gelatin concentration of,0.5g/L, pH value, of 5.0; temperature of,50℃. Osteoblasts were cultured on the coatings to evaluate the biocompatibilityof coatings. Alamar Blue assay indicated that the composite coatings couldfavor the proliferation of the osteoblasts.

Key words: pulsedelectrochemical deposition, hydroxyapatite, gelatin, composite coating, biocompatibility

CLC Number:

R318

WANG Ying-Bo,LU Xiong*, FENG Bo,QU Shu-Xin, WENG Jie. Calcium Phosphate/ Gelatin Composite Coatings on Titanium Surfaces by ElectrochemicalDepositon[J]. Journal of Inorganic Materials, 2011, 26(1): 61-67.

References

[1] 王英波, 鲁雄, 冯波, 等(WANG Ying-Bo, et al). 脉冲电沉积制备HA/ZrO₂纳米复合涂层的稳定性及生物相容性评价[J]. 高等学校化学学报(Chem. J. ChineseU.), 2010, 31(2): 253-259.
[2] Tian Ang, Wang Chao, Xue Xiangxin, et al. Inhibitory effect of nano-ha particles on humanu87 glioblastoma cells viability[J].Journal of Inorganic Materials, 2010, 25(1): 101-106.
[3] Weiner S, Wagner H D. The material bone: structure-mechanicalfunction relations[J]. Ann. Rev. Mater. Sci., 1998, 28(1): 271-298.
[4] Manso M, Jimenez C, Morant C, etal. Electrodeposition of hydroxyapatite coatings in basic conditions[J].Biomaterials, 2000, 21(17): 1755-1761.
[5] Redepenning J, Mclssac J P. Electrocrystallization of rushite coatinson prosthetic alloys[J]. Chem. Mater., 1990, 2(6): 625-627.
[6] Hu H B, Lin C J, Hu R, et al.A study on hybrid bioceramic coatings of HA/poly (vinyl acetate) co-depositedelectrochemically on Ti-6A1-4V alloy surface[J], Mater. Sci. Eng. C, 2002, 20(1-/2): 209-214.
[7] Mohamed K R, Mostafa A A. Preparation andbioactivity evaluation of hydroxyapatite-titania/chitosan-gelatin polymericbiocomposites[J]. Mater. Sci. Eng.C, 2008, 28(7): 1087-1099.
[8] Fan Y, Duan K, Wang. R. A compositecoating by electrolysis-induced collagen self-assembly and calcium phosphatemineralization[J]. Biomaterials, 2005, 26(14): 1623-1632.
[9] Kuo M C, Yen S K. The process of electrochemical deposited hydroxyapatitecoatings on biomedical titanium at room temperature. Mater. Sci. Eng. C, 2002, 20(1/2): 153-160.
[10] 王英波, 鲁雄, 翁杰, 等(WANG Ying-Bo,et al). 脉冲电化学沉积制备n-HA/ZrO₂复合涂层[J]. 稀有金属材料与工程(Rare Metal Mat. Eng.),2009, 38(6): 1071-1075.
[11] 张柏林, 王英波, 鲁雄, 等(ZHANG Bai-Lin, etal). 脉冲电化学沉积法制备钛基HA/Ag复合涂层[J].稀有金属材料与工程(Rare MetalMat. Eng.), 2010, 39(10): 1835-1839.
[12] Ban S, Maruno S. Effect of temperature on electrochemical depositionof calcium phosphate coatings in a simulated body fluid[J]. Biomaterials,1995, 16(13): 977-981.
[13] Hou X H, Liu X, Xu J M, et al. Aself-optimizing electrodeposition process for fabrication of calcium phosphatecoatings[J]. Mater. Lett.,2001, 50(2-/3): 103-107.
[14]Manara S, Paolucci F, PalazzoB, at et el.Electrochemically-assisted deposition of biomimetic hydroxyapatite–collagencoatings on titanium plate[J]. Inorg. Chim. Acta, 2008, 361(6): 1634-1645.

[1]	LI Chengyu, DING Ziyou, HAN Yingchao. In vitro Antibacterial and Osteogenic Properties of Manganese Doped Nano Hydroxyapatite [J]. Journal of Inorganic Materials, 2024, 39(3): 313-320.
[2]	CHEN Xinli, LI Yan, WANG Weisheng, SHI Zhiwen, ZHU Liqiang. Gelatin/Carboxylated Chitosan Gated Oxide Neuromorphic Transistor [J]. Journal of Inorganic Materials, 2023, 38(4): 421-428.
[3]	XIE Jiaye, LI Liwen, ZHU Qiang. Contrastive Study on in Vitro Antibacterial Property and Biocompatibility of Three Clinical Pulp Capping Agents [J]. Journal of Inorganic Materials, 2023, 38(12): 1449-1456.
[4]	CAI Jia, ZHAO Fangxia, FAN Dong, HUANG Liping, NIU Yaran, ZHENG Xuebin, ZHANG Zhenzhong. Pyrolysis Behavior and Laser Ablation Resistance of PCS in Polycarbosilane Composite Coatings [J]. Journal of Inorganic Materials, 2023, 38(11): 1271-1280.
[5]	LIU Yan, ZHANG Yufan, WANG Ximan, LI Ting, MA Wenting, YANG Fuwei, CHEN Liang, ZHAO Dongyue, YAN Xiaoqin. Consolidation of Fragile Weathered Bone Relics Using Hydroxyapatite Material as Consolidant [J]. Journal of Inorganic Materials, 2023, 38(11): 1345-1354.
[6]	HONG Du, NIU Yaran, LI Hong, ZHONG Xin, ZHENG Xuebin. Tribological Properties of Plasma Sprayed TiC-Graphite Composite Coatings [J]. Journal of Inorganic Materials, 2022, 37(6): 643-650.
[7]	CHEN Yaling, SHU Song, WANG Shaoxin, LI Jianjun. Mn-HAP SCR Catalyst: Preparation and Sulfur Resistance [J]. Journal of Inorganic Materials, 2022, 37(10): 1065-1072.
[8]	ZHU Yutong, TAN Peijie, LIN Hai, ZHU Xiangdong, ZHANG Xingdong. Injectable Hyaluronan/Hydroxyapatite Composite: Preparation, Physicochemical Property and Biocompatibility [J]. Journal of Inorganic Materials, 2021, 36(9): 981-990.
[9]	LIN Ziyang, CHANG Yuchen, WU Zhangfan, BAO Rong, LIN Wenqing, WANG Deping. Different Simulated Body Fluid on Mineralization of Borosilicate Bioactive Glass-based Bone Cement [J]. Journal of Inorganic Materials, 2021, 36(7): 745-752.
[10]	WU Zhongcao, HUAN Zhiguang, ZHU Yufang, WU Chengtie. 3D Printing and Characterization of Microsphere Hydroxyapatite Scaffolds [J]. Journal of Inorganic Materials, 2021, 36(6): 601-607.
[11]	WU Yonghao, LI Xiangfeng, ZHU Xiangdong, ZHANG Xingdong. Construction of Hydroxyapatite Nanoceramics with High Mechanical Strength and Efficiency in Promoting the Spreading and Viability of Osteoblasts [J]. Journal of Inorganic Materials, 2021, 36(5): 552-560.
[12]	SONG Keke, HUANG Hao, LU Mengjie, YANG Anchun, WENG Jie, DUAN Ke. Hydrothermal Preparation and Characterization of Zn, Si, Mg, Fe Doped Hydroxyapatite [J]. Journal of Inorganic Materials, 2021, 36(10): 1091-1096.
[13]	SHAO Yueting, ZHU Yingjie, DONG Liying, CAI Anyong. Nanocomposite “Xuan Paper” Made from Ultralong Hydroxyapatite Nanowires and Cellulose Fibers and Its Anti-mildew Properties [J]. Journal of Inorganic Materials, 2021, 36(1): 107-112.
[14]	SUN Tuanwei,ZHU Yingjie. One-step Solvothermal Synthesis of Strontium-doped Ultralong Hydroxyapatite Nanowires [J]. Journal of Inorganic Materials, 2020, 35(6): 724-728.
[15]	WANG Zhihu,ZHANG Jumei,BAI Lijing,ZHANG Guojun. Mg(OH)₂ Film on Micro-arc Oxidation Ceramic Coating of AZ31 Magnesium Alloy: Preparation and Corrosion Resistance [J]. Journal of Inorganic Materials, 2020, 35(6): 709-716.