具有可见光催化活性的MoS2量子点/NH2-MIL-125复合材料的制备及性能表征

doi:10.15541/jim20190010

摘要/Abstract

摘要：

采用水热法合成金属-有机骨架材料NH₂-MIL-125, 并修饰硫化钼量子点, 从而构筑具有增强电荷分离的二硫化钼量子点/NH₂-MIL-125复合光催化材料(MoS₂ QDs/NH₂-MIL-125)。利用XRD、HRTEM、DRS、PL对材料性能进行分析, 通过降解甲基橙MO染料测试MoS₂ QDs/NH₂-MIL-125复合材料的光催化性能。结果表明：尺寸约 4 nm的MoS₂ QDs均匀分散在NH₂-MIL-125上, 在可见光照射下, MoS₂ QDs/NH₂-MIL-125复合材料的光催化性能极大优于单一的Bulk MoS₂和NH₂-MIL-125, 降解常数分别是它们的5.8和7.4倍。循环光催化实验结果表明, MoS₂ QDs/NH₂-MIL-125复合材料的光催化能力具有良好的稳定性。DRS和PL的测试结果表明, MoS₂ QDs/NH₂-MIL-125复合材料优异的可见光催化性能主要归因于异质结构的形成, 抑制了光生电子-空穴的复合, 进而提高了光催化性能。

关键词: 二硫化钼量子点, 金属-有机骨架材料, 异质结构, 光催化

Abstract:

MoS₂ quantum dots (QDs) decorated NH₂-MIL-125 (MoS₂ QDs/NH₂-MIL-125) heterostructures were successfully fabricated by a facile method. XRD results exhibit that NH₂-MIL-125 and MoS₂ form crystals in the synthesis process of MoS₂ QDs/NH₂-MIL-125 heterojunctions. TEM results demonstrated clearly that the MoS₂ Quantum dots with size of about 4 nm successfully disperse on the surface of NH₂-MIL-125 plate. Compared with bulk MoS₂ and NH₂-MIL-125, the MoS₂ QDs/NH₂-MIL-125 heterostructures exhibit enhanced photocatalytic performance in degradation of methyl orange under visible light irradiation, about 5.8 and 7.4 times higher that of pure bulk MoS₂ and NH₂-MIL-125, respectively. Meanwhile, MoS₂ QDs/NH₂-MIL-125 composites exhibit good stability and reusability during cycle experiment. The excellent photocatalytic activity of MoS₂ QDs/NH₂-MIL-125 heterostructures is attributed to the formation of heterojunctions between MoS₂ QDs and NH₂-MIL-125, Tacilitating separation of the photogenerated charge carries. PL results prove that MoS₂ QDs/NH₂-MIL-125 composites own lower recombination of photogenerated electrons and holes, resulting in superior photocatalytic ability.

Key words: MoS₂ quantum dots(QDs), metal-organic frameworks, heterojunction, photocatalysis

中图分类号:

TB34

韩丽, 张晓敏, 吴德勇. 具有可见光催化活性的MoS₂量子点/NH₂-MIL-125复合材料的制备及性能表征[J]. 无机材料学报, 2019, 34(11): 1205-1209.

HAN Li, ZHANG Xiao-Min, WU De-Yong. MoS₂ Quantum Dots Decorated NH₂-MIL-125 Heterojunction: Preparation and Visible Light Photocatalytic Performance[J]. Journal of Inorganic Materials, 2019, 34(11): 1205-1209.

图/表 5

Fig. 1 TEM images (a, b), HRTEM images (c, d) and the partial element mappings (e, f) of MoS2 QDs/NH2-MIL-125 composites

Fig. 2 XRD patterns of bulk MoS2, NH2-MIL-125 and MoS2 QDs/NH2-MIL-125 composites

Fig. 3 (a) Photocatalytic activity and (b) plot of -ln(C/C0) of bulk MoS2, NH2-MIL-125 and MoS2 QDs/NH2-MIL-125 composites over MO as a function of irradiation time

Fig. 4 UV-Vis diffuse reflectance spectra (a) and PL spectra (b) of NH2-MIL-125 and MoS2 QDs/NH2-MIL-125 composites

Fig. 5 Stability test of MoS2 QDs/NH2-MIL-125 composites for MO degradation under visible light irradiation

参考文献 22

[1]	GOGOI C, YOUSUFUDDIN M, BISWAS S . A new 3D luminescent Zn(II)-organic framework containing a quinoline-2,6-dicarboxylate linker for the highly selective sensing of Fe(III) ions. Dalton Trans., 2019,48(5):1766-1773.
[2]	LIU D X, GU J J, LIU Q L , et al. Metal-organic frameworks reactivate deceased diatoms to be efficient CO₂ absorbents. Adv. Mater., 2014,26(8):1229-1234.
[3]	JIANG D, XU P, WANG H , et al. Strategies to improve metal organic frameworks photocatalyst's performance for degradation of organic pollutants. Coord. Chem. Rev., 2018,376:449-466.
[4]	YANG Y F, WANG W J, LI H , et al. NH₂-MIL-53(Al) nanocrystals anchored on the surface of RGO hollow spheres and its visible light degradation of methylene blue. Mater. Lett., 2017,197:17-20.
[5]	KHANDAN F M, AFZALI D, SARGAZI G , et al. Novel uranyl-curcumin-MOF photocatalysts with highly performance photocatalytic activity toward the degradation of phenol red from aqueous solution: effective synthesis route, design and a controllable systematic study. J. Mater. Sci: Mater. El., 2018,29(21):18600-18613.
[6]	HU S, LIU M, LI K Y , et al. Surfactant-assisted synthesis of hierarchical NH₂-MIL-125 for the removal of organic dyes. RSC Adv., 2017,7(1):581-587.
[7]	ZHANG Z J, XU J Y, ZENG H B , et al. Carbon quantum dots/BiPO₄ nanocomposites with enhanced visible-light absorption and charge separation. J. Inorg. Mater., 2018,33(5):582-586.
[8]	CORRIEA F C, CALHEIROS M, MARQUES J , et al. Synthesis of Bi₂O₃/TiO₂ nanostructured films for photocatalytic applications. Ceram. Int., 2018,44(18):22638-22644.
[9]	ABDLHAMEED R M, TOBALDI D M, KARMAOUI M . 2018. Engineering highly effective and stable nanocomposite photocatalyst based on NH₂-MIL-125 encirclement with Ag₃PO₄ nanoparticles. J. Photoch. Photobio. a-Chem., 2018,351:50-58.
[10]	WANG M, YANG L, YUAN J , et al. Heterostructured Bi₂S₃@NH₂-MIL-125(Ti) nanocomposite as a bifunctional photocatalyst for Cr(VI) reduction and rhodamine B degradation under visible light. RSC Adv., 2018,8(22):12459-12470.
[11]	ZHU S R, LIU P F, W M K , et al. Enhanced photocatalytic performance of BiOBr/NH₂-MIL-125(Ti) composite for dye degradation under visible light. Dalton Trans., 2016,45(43):17521-17529.
[12]	CHEN W, GU J, LIU Q , et al. Quantum dots of 1T phase transitional metal dichalcogenides generated via electrochemical Li intercalation. ACS Nano, 2018,12(1):308-316.
[13]	SHI L, HE Z, LIU S Q . MoS₂ quantum dots embedded in g-C₃N₄ frameworks: a hybrid 0D-2D heterojunction as an efficient visible- light driven photocatalyst. Appl. Surf. Sci., 2018,457:30-40.
[14]	ZHAO F F, RONG Y F, WAN J M , et al. MoS₂ quantum dots@TiO₂ nanotube composites with enhanced photoexcited charge separation and high-efficiency visible-light driven photocatalysis. Nanotechnology, 2018,29(10):105403.
[15]	MENG X C, LI Z Z, ZENG H M , et al. MoS₂ quantum dots-interspersed Bi₂WO₆ heterostructures for visible light-induced detoxification and disinfection. Appl. Catal. B-Environ., 2017,210:160-172.
[16]	ZHANG B X, ZHANG J L, TAN X N , et al. MIL-125-NH₂@TiO₂ core-shell particles produced by a post-solvothermal route for high-performance photocatalytic H₂ production. ACS Appl. Mat. Interfaces, 2018,10(19):16418-16423.
[17]	GU W, YAN Y, CAO X , et al. A facile and one-step ethanol- thermal synthesis of MoS₂ quantum dots for two-photon fluorescence imaging. J. Mater. Chem. B, 2016,4(1):27-31.
[18]	WU D, WU C, TAN H . Facile synthesis of novel I-doped Bi₄O₅Br₂ nanosheets with enhanced visible light photocatalytic activity. J. Mater. Sci: Mater. El., 2018,29(13):11090-11095.
[19]	WU Z Y, HUANG X B, ZHENG H Y , et al. Aromatic heterocycle- grafted NH₂-MIL-125(Ti) via conjugated linker with enhanced photocatalytic activity for selective oxidation of alcohols under visible light. Appl. Catal. B-Environ., 2018,224:479-487.
[20]	CARVALHO K T G, NOGUEIRA A E, LOPES O F , et al. Synthesis of g-C₃N₄/Nb₂O₅ heterostructures and their application in the removal of organic pollutants under visible and ultraviolet irradiation. Ceram. Int., 2017,43(4):3521-3530.
[21]	YE F, LI H F, YU H T , et al. Hydrothermal fabrication of few-layer MoS₂ nanosheets within nanopores on TiO₂ derived from MIL-125(Ti) for efficient photocatalytic H₂ evolution. Appl. Surf. Sci., 2017,426:177-184.
[22]	WANG F Z, LI W J, GU S N , et al. Facile fabrication of direct Z-scheme MoS₂/Bi₂WO₆ heterojunction photocatalyst with superior photocatalytic performance under visible light irradiation. J. Photoch. Photobio. A-Chem., 2017,335:140-148.

具有可见光催化活性的MoS₂量子点/NH₂-MIL-125复合材料的制备及性能表征

MoS₂ Quantum Dots Decorated NH₂-MIL-125 Heterojunction: Preparation and Visible Light Photocatalytic Performance

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

图/表 5

参考文献 22

相关文章 15

编辑推荐

Metrics

本文评价

[1]	陈莉波, 盛盈, 伍明, 宋季岭, 蹇建, 宋二红. Na和O元素共掺杂氮化碳高效光催化制氢[J]. 无机材料学报, 2025, 40(5): 552-562.
[2]	范小暄, 郑永炅, 徐丽荣, 姚子敏, 曹硕, 王可心, 王绩伟. 基于富氧空位LiYScGeO₄: Bi³⁺长余辉光催化剂的自激活余辉驱动有机污染物芬顿降解[J]. 无机材料学报, 2025, 40(5): 481-488.
[3]	贾相华, 张辉霞, 刘艳凤, 左桂鸿. 湿化学法制备Cu₂O/Cu空心球异质结光催化剂[J]. 无机材料学报, 2025, 40(4): 397-404.
[4]	马彬彬, 钟婉菱, 韩涧, 陈椋煜, 孙婧婧, 雷彩霞. ZIF-8/TiO₂复合介观晶体的制备及光催化活性[J]. 无机材料学报, 2024, 39(8): 937-944.
[5]	曹青青, 陈翔宇, 吴健豪, 王筱卓, 王乙炫, 王禹涵, 李春颜, 茹菲, 李兰, 陈智. SiO₂增强自敏性氮化碳微球可见光降解盐酸四环素的研究[J]. 无机材料学报, 2024, 39(7): 787-792.
[6]	王兆阳, 秦鹏, 蒋胤, 冯小波, 杨培志, 黄富强. 三明治结构钌插层二氧化钛光催化四环素降解性能研究[J]. 无机材料学报, 2024, 39(4): 383-389.
[7]	叶茂森, 王耀, 许冰, 王康康, 张胜楠, 冯建情. II/Z型Bi₂MoO₆/Ag₂O/Bi₂O₃异质结可见光催化降解四环素[J]. 无机材料学报, 2024, 39(3): 321-329.
[8]	李秋实, 殷广明, 吕伟超, 王怀尧, 李婧琳, 杨红光, 关芳芳. Na⁺/g-C₃N₄材料的制备及光催化降解亚甲基蓝机理[J]. 无机材料学报, 2024, 39(10): 1143-1150.
[9]	李跃军, 曹铁平, 孙大伟. S型异质结Bi₄O₅Br₂/CeO₂的制备及其光催化CO₂还原性能[J]. 无机材料学报, 2023, 38(8): 963-970.
[10]	伍林, 胡明蕾, 王丽萍, 黄少萌, 周湘远. TiHAP@g-C₃N₄异质结的制备及光催化降解甲基橙[J]. 无机材料学报, 2023, 38(5): 503-510.
[11]	凌洁, 周安宁, 王文珍, 贾忻宇, 马梦丹. Cu/Mg比对Cu/Mg-MOF-74的CO₂吸附性能的影响[J]. 无机材料学报, 2023, 38(12): 1379-1386.
[12]	孙晨, 赵昆峰, 易志国. 甲烷完全催化氧化研究进展[J]. 无机材料学报, 2023, 38(11): 1245-1256.
[13]	贾鑫, 李晋宇, 丁世豪, 申倩倩, 贾虎生, 薛晋波. Pd纳米颗粒协同氧空位增强TiO₂光催化CO₂还原性能[J]. 无机材料学报, 2023, 38(11): 1301-1308.
[14]	马润东, 郭雄, 施凯旋, 安胜利, 王瑞芬, 郭瑞华. MoS₂/g-C₃N₄ S型异质结的构建及光催化性能研究[J]. 无机材料学报, 2023, 38(10): 1176-1182.
[15]	马心全, 李喜宝, 陈智, 冯志军, 黄军同. S型异质结BiOBr/ZnMoO₄的构建及光催化降解性能研究[J]. 无机材料学报, 2023, 38(1): 62-70.