TiO2负载锶铁氧体磁性材料光催化性能及表征

doi:10.3724/SP.J.1077.2008.00652

无机材料学报

TiO₂负载锶铁氧体磁性材料光催化性能及表征

储金宇, 于琦, 吴春笃, 曹常乐, 李宁

江苏大学环境学院, 镇江 212013

收稿日期:2007-09-06 修回日期:2007-12-14 出版日期:2008-07-20 网络出版日期:2008-07-20

Preparation and Characterization of Magnetic Photocatalysts TiO₂ Loaded with Strontium Ferrite

CHU Jin-Yu, YU Qi, WU Chun-Du, CAO Chang-Le, LI Ning

School of Environment, Jiangsu University, Zhenjiang 212013, China

Received:2007-09-06 Revised:2007-12-14 Published:2008-07-20 Online:2008-07-20

摘要/Abstract

摘要： 采用溶胶-凝胶法合成了TiO₂负载锶铁氧体光催化剂, 通过XRD、TEM、UV-Vis、VSM等方法对催化剂结构进行了表征, 并以高压汞灯为光源, 亚甲基兰为目标降解物, 对其光催化活性进行了研究. 结果表明, TiO₂负载锶铁氧体为复合型光催化剂, 负载后的复合光催化剂保持了良好的磁性能; 锶铁氧体的负载拓宽了催化剂的光响应区域, 光吸收带进入可见光区; 在负载量为20％, 催化剂用量1.5g/L条件下, 催化降解亚甲基兰的效率可达99.1％.

关键词: 锶铁氧体, 负载, 光催化, 二氧化钛

Abstract: The photocatalyst of TiO₂loaded with strontium ferrite were synthesized via sol-gel technology and characterized by X-ray powder diffraction (XRD), electron microscope (TEM), UV-Vis diffused
reflectance spectroscope (DRS) and vibrating sample magnetometer(VSM). The photocatalytic activities of the samples were evaluated by decolorization of methylene blue(MB) under UV irradiation. The results indicate that the TiO₂ loaded strontium ferrite photocatalyst is responsive to the visible light region according to DRS analysis. It is also found that the composite has good magnetic property. About 99.1％ MB can be removed at the catalyst dosage of 1.5g/L under UV irradiation for 300 min, when the catalyst is loaded with 20％ strontium ferrite.

Key words: strontium ferrite, load, photocatalysis, TiO₂

中图分类号:

O643

储金宇,于琦,吴春笃,曹常乐,李宁. TiO₂负载锶铁氧体磁性材料光催化性能及表征[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2008.00652.

CHU Jin-Yu,YU Qi,WU Chun-Du,CAO Chang-Le,LI Ning. Preparation and Characterization of Magnetic Photocatalysts TiO₂ Loaded with Strontium Ferrite[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2008.00652.

参考文献

[1] Serpone N. Solar Energy Mater Solar Cells, 1995, 38 (3): 369--379.
[2] Sodergren S, Hagfeldt A, Olsson J, et al. Journal of Physical Chemistry, 1994, 98 (21): 5552--5556.
[3] Kang M, Hong W J, Park M S. Applied Catalysis B: Environmental, 2004, 53 (3): 195--205.
[4] Li X S, Fryxell G E, Engelhard M H, et al. Inorganic Chemistry Communications, 2007, 10 (6): 639--641.
[5] Bideau M, Claudel B, Dubien C, et al. Journal of Photochemistry and Photobiology A: Chemistry, 1995, 91 (2): 137--144.
[6] Mazzarino I, Piccinini P, Spinelli L. Catalysis Today, 1999, 48 (4): 315--321. [7] Beydoun D, Amal R. Materials Science and Engineering, 2002, 94 (1): 71--81.
[8] Watson S, Beydoun D, Amal R. Journal of Photochemistry and Photobiology, 2002, 148 (3): 303--313.
[9] Fu W Y, Yang H B, Li M H, et al. Materials Letters, 2005, 59 (27): 3530--3534.
[10] Beydoun D, Amal R, Low G, et al. Journal of Molecular Catalysis A: Chemical, 2002, 180 (2): 193--200.
[11] Rana S, Srivastava R S, Sorensson M M, et al. Materials Science and Engineering, 2005, 119 (2): 144--151.
[12] Xu S H, Shangguan W F, Yuan J, et al. Science and Technology of Advanced Materials, 2007, 8 (1-2): 40--46.
[13] Cheng P, Li W, Zhou T L, et al. Journal of Photochemistry and Photobiology A: Chemistry, 2004, 168 (1-2): 97--101.
[14] Yuan Z H, You W, Jia J H, et al. Chinese Physics Letters, 1998, 15 (7): 535--536.
[15] Liu J J, Lu G X, He H L, et al. Mater. Res. Bull., 1996, 31 (9): 1049--1056.
[16] 袁志好, 孙永昌, 王玉红, 等. 高等学校化学学报, 2004, 25 (10): 1875--1878.
[17] 廖振华, 陈建军, 姚可夫, 等(LIAO Zhen-Hun, et al). 无
机材料学报(Journal of Inorganic Materials), 2004, 19 (4): 749--754.
[18] 尹京花, 赵莲花, 武伦鹏, 等. 分子催化, 2006, 20 (6): 569--573.

TiO₂负载锶铁氧体磁性材料光催化性能及表征

Preparation and Characterization of Magnetic Photocatalysts TiO₂ Loaded with Strontium Ferrite

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	马彬彬, 钟婉菱, 韩涧, 陈椋煜, 孙婧婧, 雷彩霞. ZIF-8/TiO₂复合介观晶体的制备及光催化活性[J]. 无机材料学报, 2024, 39(8): 937-944.
[2]	曹青青, 陈翔宇, 吴健豪, 王筱卓, 王乙炫, 王禹涵, 李春颜, 茹菲, 李兰, 陈智. SiO₂增强自敏性氮化碳微球可见光降解盐酸四环素的研究[J]. 无机材料学报, 2024, 39(7): 787-792.
[3]	王兆阳, 秦鹏, 蒋胤, 冯小波, 杨培志, 黄富强. 三明治结构钌插层二氧化钛光催化四环素降解性能研究[J]. 无机材料学报, 2024, 39(4): 383-389.
[4]	叶茂森, 王耀, 许冰, 王康康, 张胜楠, 冯建情. II/Z型Bi₂MoO₆/Ag₂O/Bi₂O₃异质结可见光催化降解四环素[J]. 无机材料学报, 2024, 39(3): 321-329.
[5]	李秋实, 殷广明, 吕伟超, 王怀尧, 李婧琳, 杨红光, 关芳芳. Na⁺/g-C₃N₄材料的制备及光催化降解亚甲基蓝机理[J]. 无机材料学报, 2024, 39(10): 1143-1150.
[6]	李跃军, 曹铁平, 孙大伟. S型异质结Bi₄O₅Br₂/CeO₂的制备及其光催化CO₂还原性能[J]. 无机材料学报, 2023, 38(8): 963-970.
[7]	伍林, 胡明蕾, 王丽萍, 黄少萌, 周湘远. TiHAP@g-C₃N₄异质结的制备及光催化降解甲基橙[J]. 无机材料学报, 2023, 38(5): 503-510.
[8]	凌洁, 周安宁, 王文珍, 贾忻宇, 马梦丹. Cu/Mg比对Cu/Mg-MOF-74的CO₂吸附性能的影响[J]. 无机材料学报, 2023, 38(12): 1379-1386.
[9]	孙晨, 赵昆峰, 易志国. 甲烷完全催化氧化研究进展[J]. 无机材料学报, 2023, 38(11): 1245-1256.
[10]	王梦桃, 索军, 方东, 易健宏, 刘意春, Olim RUZIMURADOV. ITO/TiO₂纳米管阵列复合材料的可见光催化性能[J]. 无机材料学报, 2023, 38(11): 1292-1300.
[11]	贾鑫, 李晋宇, 丁世豪, 申倩倩, 贾虎生, 薛晋波. Pd纳米颗粒协同氧空位增强TiO₂光催化CO₂还原性能[J]. 无机材料学报, 2023, 38(11): 1301-1308.
[12]	马润东, 郭雄, 施凯旋, 安胜利, 王瑞芬, 郭瑞华. MoS₂/g-C₃N₄ S型异质结的构建及光催化性能研究[J]. 无机材料学报, 2023, 38(10): 1176-1182.
[13]	马心全, 李喜宝, 陈智, 冯志军, 黄军同. S型异质结BiOBr/ZnMoO₄的构建及光催化降解性能研究[J]. 无机材料学报, 2023, 38(1): 62-70.
[14]	陈瀚翔, 周敏, 莫曌, 宜坚坚, 李华明, 许晖. CoN/g-C₃N₄ 0D/2D复合结构及其光催化制氢性能研究[J]. 无机材料学报, 2022, 37(9): 1001-1008.
[15]	薛虹云, 王聪宇, MAHMOOD Asad, 于佳君, 王焱, 谢晓峰, 孙静. 二维g-C₃N₄与Ag-TiO₂复合光催化剂降解气态乙醛抗失活研究[J]. 无机材料学报, 2022, 37(8): 865-872.