仿生纳米含硅羟基磷灰石的合成与表征

doi:10.3724/SP.J.1077.2013.12292

摘要/Abstract

摘要：

为了探究仿生纳米含硅羟基磷灰石的合成条件及含硅量对其结晶性能的影响, 以Ca(NO₃)₂、(NH₄)₂HPO₄和Si(OCH₂CH₃)₄(TEOS)为原料, 采用化学沉淀法制备了不同含硅量的羟基磷灰石, 并通过傅里叶变换红外光谱(FTIR)、X射线荧光光谱(XRF)、X射线衍射(XRD)、透射电镜(TEM)对材料进行了表征。结果表明较低温(40℃)时有利于合成纯净的仿生纳米含硅羟基磷灰石, SiO₄^4-取代部分PO₄^3-进入羟基磷灰石的晶格。随着含硅量的增加, 仿生纳米含硅羟基磷灰石的结晶度和晶粒尺寸均降低, 晶胞参数a和c均增大。

关键词: 硅, 羟基磷灰石, 化学沉淀, 仿生

Abstract:

To explore the synthesis condition of the bionic nano-silicon-substituted hydroxyapatite and the impact of the silicon content on its crystallization properties, hydroxyapatite of different silicon content were synthesized from Ca(NO₃)₂, (NH₄)₂HPO₄ and Si(OCH₂CH₃)₄(TEOS) via an aqueous precipitation reaction. Fourier transform infrared spectroscopy (FTIR), X-ray fluorescence spectrum (XRF), X-ray diffraction (XRD) and transmission electron microscopy (TEM) were used for hydroxyapatite characterization. The results show that relative low temperature (40℃) is conducive to obtain pure bionic nano-silicon-substituted hydroxyapatite. Under this condition, SiO₄^4- enters the lattice of hydroxyapatite and replaces part of PO₄^3-. The more the content of silicon is, the lower the crystallinity is, the smaller the grain size is and the higher the lattice parameters a and c are.

Key words: silicon, hydroxyapatite, aqueous precipitation reaction, bionoid

中图分类号:

TQ174

翟倩倩, 赵士贵, 王孝海, 李秀芝, 李文杰, 郑亚森. 仿生纳米含硅羟基磷灰石的合成与表征[J]. 无机材料学报, 2013, 28(1): 58-62.

ZHAI Qian-Qian, ZHAO Shi-Gui, WANG Xiao-Hai, LI Xiu-Zhi, LI Wen-Jie, ZHENG Ya-Sen. Synthesis and Characterization of Bionic Nano-silicon-substituted Hydroxyapatite[J]. Journal of Inorganic Materials, 2013, 28(1): 58-62.

图/表 11

Table 1 Quantities of used reactants

Samples	Ca(NO₃)₂ /mol	(NH₄)₂HPO₄ /mol	TEOS /mol	Expected w(Si)/%	Calculated chemical formula of Si-HA
HA	0.025	0.01500	0.00000	0	Ca₁₀(PO₄)₆(OH)₂
2%Si-HA	0.025	0.01470	0.00030	0.335	Ca₁₀(PO₄)_5.88(SiO₄)_0.12(OH)_1.88
7%Si-HA	0.025	0.01395	0.00105	1.181	Ca₁₀(PO₄)_5.58(SiO₄)_0.42(OH)_1.58
12%Si-HA	0.025	0.01320	0.00180	2.037	Ca₁₀(PO₄)_5.28(SiO₄)_0.72(OH)_1.28
17%Si-HA	0.025	0.01245	0.00255	2.903	Ca₁₀(PO₄)_4.98(SiO₄)_1.02(OH)_0.98

图1 化学沉淀法合成Si-HA流程图

Fig. 1 Flow chart of the preparation of Si-HA by the aqueous precipitation route

图2 不同反应温度条件下12%Si-HA的XRD图谱

Fig. 2 XRD patterns of 12% Si-HA prepared at (a) 40℃, (b) 50℃ and (c) 60℃

图3 HA标准XRD图谱(a)与60℃、陈化24 h的12%Si-HA的XRD图谱(b)

Fig. 3 Standard XRD of HA (a) XRD pattern of 12%Si-HA prepared at 60℃ and aging for 24 h (b)

图4 60℃不同陈化时间条件下12%Si-HA的XRD图谱

Fig. 4 XRD patterns of 12%Si-HA prepared at 60℃ and (a) aging for 24 h (a), 48 h (b) and 72 h (c)

图5 HA和Si-HA的FTIR图谱

Fig. 5 FTIR spectra of (a) HA, (b) 2%Si-HA, (c) 7%Si-HA, (d) 12%Si-HA and (e) 17%Si-HA

Table 2 The content of Ca and Si of Si-HA

Samples	Expected w(Si)/%	Found w(Si)/%	Expected w(Ca)/%	Found w(Ca)/%
HA	0	0	39.84	36.70
2%Si-HA	0.335	0.22	39.90	36.52
7%Si-HA	1.181	0.83	40.18	36.07
12%Si-HA	2.037	1.75	40.42	36.16
17%Si-HA	2.903	2.30	40.67	34.24

图6 不同含硅量的Si-HA的XRD衍射图谱

Fig. 6 XRD patterns of (a) HA, (b) 2%Si-HA, (c) 7%Si-HA, (d) 12%Si-HA and (e) 17%Si-HA

Table 3 Grain size of c-axis and average grain size of Si-HA

Samples	Grain size/nm
Samples	c-axis	Average
HA	27	26.6
2%Si-HA	30.5	23.7
7%Si-HA	21.6	21.1
12%Si-HA	20.1	16.1
17%Si-HA	18.9	13

Table 4 Lattice parameters of HA and Si-HA

Samples	a/nm	c/nm
HA	0.941572	0.686471
2%Si-HA	0.942215	0.690142
7%Si-HA	0.943736	0.686588
12%Si-HA	0.947851	0.686749
17%Si-HA	0.948608	0.687302

图7 Si-HA的TEM照片

Fig.7 TEM images of (a)2%Si-HA and (b)7%Si-HA

参考文献 11

[1]	贡长生,张克立. 新型功能材料. 北京: 化学工业出版社, 2001: 559-560.
[2]	Porter A E, Patel N, Skepper J N, et al. Effect of sintered silicate -substituted hydroxyapatite on remodelling processes at the bone- implant interface. Biomaterials, 2004, 25(16): 3303-3314.
[3]	Thian E S, Huang J, Best S M, et al. Silicon-substituted hydroxyapatite: The next generation of bioactive coatings. Materials Science and Engineering, 2007, 27(2): 251-256.
[4]	Ruys A J. Silicon-doped hydroxyapatite. J. Australas. Ceram. Soc.(Switzerland), 1993, 29(1/2): 71-80.
[5]	Tang X L, Xiao X F, Liu R F. Structural characterization of silicon- substituted hydroxyapatite synthesized by a hydrothermal method. Materials Letters, 2005, 59(29/30): 3841-3846.
[6]	Boyer L, Carpena J, Lacout J L. Synthesis of phosphate-silicate apatites at atmospheric pressure. Solid State lonics, 1997, 95(1/2): 121-129.
[7]	Tian T, Jiang D L, Zhang J X, et al. Synthesis of Si-substituted hydroxyapatite by a wet mechanochemical method. Materials Science and Engineering, 2008, 28(1): 57-63.
[8]	Bianco A, Cacciotti I, Lombardi M, et al. Si-substituted hydroxyapatite nanopowders: synthesis, thermal stability and sinterability. Materials Research Bulletin, 2009, 44(2): 345-354.
[9]	Balas F, Pérez-Pariente J, Vallet-Regí M. In vitro bioactivity of silic on-substituted hydroxyapatites. Journal of Biomedical Materials Research Part A, 2003, 66A(2): 364-375.
[10]	Vallet-Regí M, González-Calbet J M. Calcium phosphates as subst -itution of bone tissues. Progress in Solid State Chemistry, 2004, 32(1/2): 1-31.
[11]	Niwa J. Acceleration of bone-repair using hydroxyapatite. Bone Fracture, 1983, 5: 124-128.

[1]	王浩, 刘学超, 郑重, 潘秀红, 徐锦涛, 朱新锋, 陈锟, 邓伟杰, 汤美波, 郭辉, 高攀. 非本征背照触发平面型4H-SiC光导开关性能研究[J]. 无机材料学报, 2024, 39(9): 1070-1076.
[2]	刘鹏东, 王桢, 刘永锋, 温广武. 硅泥在锂离子电池中的应用研究进展[J]. 无机材料学报, 2024, 39(9): 992-1004.
[3]	王康龙, 殷杰, 陈晓, 王力, 刘学建, 黄政仁. 颗粒级配对选区激光烧结打印结合常压固相烧结制备碳化硅陶瓷性能的影响[J]. 无机材料学报, 2024, 39(7): 754-760.
[4]	李刘媛, 黄开明, 赵秀艺, 刘会超, 王超. RE-Si-Al-O玻璃相对高熵稀土双硅酸盐微结构及耐CMAS腐蚀性能的影响[J]. 无机材料学报, 2024, 39(7): 793-802.
[5]	曹青青, 陈翔宇, 吴健豪, 王筱卓, 王乙炫, 王禹涵, 李春颜, 茹菲, 李兰, 陈智. SiO₂增强自敏性氮化碳微球可见光降解盐酸四环素的研究[J]. 无机材料学报, 2024, 39(7): 787-792.
[6]	张育育, 吴轶城, 孙佳, 付前刚. 聚合物转化SiHfCN陶瓷的制备及其吸波性能[J]. 无机材料学报, 2024, 39(6): 681-690.
[7]	王伟明, 王为得, 粟毅, 马青松, 姚冬旭, 曾宇平. 以非氧化物为烧结助剂制备高导热氮化硅陶瓷的研究进展[J]. 无机材料学报, 2024, 39(6): 634-646.
[8]	郑雅雯, 张翠萍, 张瑞杰, 夏乾, 茹红强. 硼酸碳热还原-渗硅反应烧结制备碳化硼陶瓷复合材料[J]. 无机材料学报, 2024, 39(6): 707-714.
[9]	岳仔豪, 杨小兔, 张正亮, 邓瑞翔, 张涛, 宋力昕. Pb²⁺对掺杂硼硅酸盐玻璃中CsPbBr₃钙钛矿量子点发光性能的影响[J]. 无机材料学报, 2024, 39(4): 449-456.
[10]	孙川, 何鹏飞, 胡振峰, 王荣, 邢悦, 张志彬, 李竞龙, 万春磊, 梁秀兵. 含有石墨烯阵列的SiC基陶瓷材料的制备与力学性能[J]. 无机材料学报, 2024, 39(3): 267-273.
[11]	李承瑜, 丁自友, 韩颖超. 锰掺杂纳米羟基磷灰石的体外抗菌-促成骨性能研究[J]. 无机材料学报, 2024, 39(3): 313-320.
[12]	刘艳艳, 谢曦, 刘增乾, 张哲峰. MAX相陶瓷增强金属基复合材料: 制备、性能与仿生设计[J]. 无机材料学报, 2024, 39(2): 145-152.
[13]	陈梦杰, 王倩倩, 吴成铁, 黄健. 基于DFT的描述符预测生物陶瓷的降解性[J]. 无机材料学报, 2024, 39(10): 1175-1181.
[14]	赵雅文, 屈发进, 汪岩屹, 王智文, 陈初升. 基于硅酸铝纤维的柔性氧敏感元件的制备和性能[J]. 无机材料学报, 2024, 39(10): 1084-1090.
[15]	苏楠, 邱介山, 王治宇. 高容量氟掺杂碳包覆纳米硅负极材料: 气相氟化法制备及其储锂性能[J]. 无机材料学报, 2023, 38(8): 947-953.