Scalable Preparation and Microwave Absorption of Lightweight Fe3O4/Mesoporous Carbon Microsphere Composites

doi:10.15541/jim20160689

Abstract

Abstract:

Fe₃O₄/mesoporous carbon microspheres (MCMSs) composites were prepared by a facile wet-impregnation method using spray-drying produced MCMSs as carbon substrates. The structure, morphology and microwave absorbing performance were investigated. Results indicate that the composites have good fluidity and low bulk density of 0.24- 0.33 g/m³. The Fe₃O₄nanoparticles are homogeneously dispersed in the mesoporous channels without blocking the porosity of MCMSs. The resulting Fe₃O₄/MCMSs composites have very high BET surface areas of 548-735 m²/g, which promote multiple relaxations. In the frequency range of 2-18 GHz, the microwave loss is primarily derived from dielectric loss. The composite with 40wt% Fe₃O₄ exhibits a maximum reflection loss of -25 dB at 12.6 GHz and a broad absorption band over 4.7 GHz. Such good microwave electromagnetic performances can be ascribed to the synergistic effects of highly dispersed Fe₃O₄nanoparticles and mesoporous channels, which can increase interfacial relaxation and microwave diffraction as well as reduce the reflection of microwave at the interface between air and absorber.

null

Key words: composites, mesoporous carbon microspheres, ferrites, microwave absorption properties

CLC Number:

TM25

LIU Ke, WANG Ji-Tong, LONG Dong-Hui, LING Li-Cheng. Scalable Preparation and Microwave Absorption of Lightweight Fe₃O₄/Mesoporous Carbon Microsphere Composites[J]. Journal of Inorganic Materials, 2017, 32(10): 1023-1028.

Figures/Tables 7

Fig. 1 (a) TG curves and (b) XRD patterns of Fe3O4/MCMSs composites

Fig. 2 (a) SEM , (b), (c) TEM and (e)-(f) SEM mapping images of 40%-Fe3O4-MCMSs

Fig. 3 (a) Nitrogen adsorption-desorption isotherms and (b) BJH pore size distributions of MCMSs and Fe3O4/MCMSs composites

Table 1 Structure parameters of MCMSs and Fe3O4/MCMSs magnetic composites

Sample	S_BET^a/ (m²·g^-1)	V_total^b/ (cm³·g^-1)	Pore size /nm	Tap density /(g·m^-3)
MCMSs	1221	2.4	8.1	0.18
20%-Fe₃O₄-MCMSs	735	1.8	8.1	0.24
40%-Fe₃O₄-MCMSs	548	1.1	8.1	0.33

Fig. 4 Magnetic hysteresis loops at room temperature of Fe3O4/MCMSs composites. Inset is low field hysteresis curves

Fig. 5 Permittivity, permeability and loss tangent of MCMSs and Fe3O4/MCMSs composites

Fig.6 RL curves of (a) MCMSs, (b)20%-Fe3O4-MCMSs and (c) 40%-Fe3O4-MCMSs at different thickness (1-5 nm)

References 22

[1]	ZHOU H, WANG J, ZHUANG J, et al.Synthesis and electromagnetic interference shielding effectiveness of ordered mesoporous carbon filled poly (methylmethacrylate) composite films.RSC Advances, 2013, 3(45): 23715-23721.
[2]	LI B P, WANG C G, WANG W, et al.Progress of electromagnetic wave absorbing materials based on carbon.Materials Review, 2012, 26(7): 9-14.
[3]	DENG L J, HAN M G.Microwave absorbing performances of multiwalled carbon nanotube composites with negative permeability.Applied Physics Letters, 2007, 91(2): 023119.
[4]	LUO F, ZHOU W C, JIAO H, et al.Current study of high temperature radar absorbing materials.Aerospace Materials & Technology, 2002, 32(1): 8-11.
[5]	XU F, XIANG C, LI L C, et al.Preparation and electromagnetic properties of CoFe2O4 and its composites with expanded graphite.Chemical Journal of Chinese Universities, 2013, 34(10): 2254-2261.
[6]	MENG X G, LUO H L, LI Q Y, et al.The application of carbon fibers with magnetic coatings as microwave absorption materials.Safety & EMC, 2011, (6): 67-69.
[7]	LIN H Y, ZHU H, GUO H, et al.Microwave-absorbing properties of Co-filled carbon nanotubes.Materials Research Bulletin, 2008, 43(10): 2697-2702.
[8]	XIN W, SONG Y H.Mesoporous carbons: recent advances in synthesis and typical applications.RSC Advances, 2015, 5(101): 83239-83285.
[9]	JARONIEC M, GORKA J, CHOMA J, et al.Synthesis and properties of mesoporous carbons with high loadings of inorganic species. Carbon, 2009, 47(13): 3034-3040.
[10]	ROBERTS A D, LI X, ZHANG H.Porous carbon spheres and monoliths: morphology control, pore size tuning and their applications as Li-ion battery anode materials.Chemical Society Reviews, 2014, 43(13): 4341-4356.
[11]	LI X, ZHOU J, QIAO W, et al.Large-scale synthesis of mesoporous carbon microspheres with controllable structure and nitrogen doping using a spray drying method.RSC Advances, 2014, 4(107): 62662-62665.
[12]	MCHENRY M E, LAUGHLIN D E.Nano-scale materials development for future magnetic applications.Acta Materialia, 2000, 48(1): 223-238.
[13]	WU L, MENDOZA-GARCIA A, LI Q, et al.Organic phase syntheses of magnetic nanoparticles and their applications.Chemical Reviews, 2016, 116(18): 10473-10512.
[14]	SUN G, DONG B, CAO M, et al.Hierarchical dendrite-like magnetic materials of Fe3O4, γ-Fe2O3, and Fe with high performance of microwave absorption.Chemistry of Materials, 2011, 23(6): 1587-1593.
[15]	LU B, HUANG H, DONG X L, et al.Influence of alloy components on electromagnetic characteristics of core/shell-type Fe-Ni nanoparticles.Journal of Applied Physics, 2008, 104(11): 114313.
[16]	GUO Y J, ZHANG L, HOU J Q, et al.Preparation and wave-absorbing performance of PANI/Fe3O4/CB hollow structured composites.Chemical Journal of Chinese Universities, 2016, 37(6): 1202-1207.
[17]	DUAN Y, LIU Z, JING H, et al.Novel microwave dielectric response of Ni/Co-doped manganese dioxides and their microwave absorbing properties.Journal of Materials Chemistry, 2012, 22(35): 18291-18299.
[18]	LV H, JI G, LIANG X H, et al.A novel rod-like MnO2@Fe loading on graphene giving excellent electromagnetic absorption properties.Journal of Materials Chemistry C, 2015, 3(19): 5056-5064.
[19]	LV H, LIANG X, CHENG Y, et al.Coin-like α-Fe2O3@CoFe2O4 core-shell composites with excellent electromagnetic absorption performance.ACS Applied Materials & Interfaces, 2015, 7(8): 4744-4750.
[20]	WEI W, YUE X G, ZHOU Y, et al.Novel ternary Fe3O4@polyaniline/polyazomethine/polyetheretherketone crosslinked hybrid membranes: fabrication, thermal properties and electromagnetic behaveiors.RSC Advances, 2014, 4(22): 11159-11167.
[21]	CHEN Y J, GAO P, ZHU C L, et al.Synthesis, magnetic and electromagnetic wave absorption properties of porous Fe3O4/Fe/SiO2 core/shell nanorods.Journal of Applied Physics, 2009, 106(5): 054303.
[22]	ZHOU H, WANG J, ZHUANG J, et al.A covalent route for efficient surface modification of ordered mesoporous carbon as high performance microwave absorbers.Nanoscale, 2013, 5(24): 12502-12511.

Scalable Preparation and Microwave Absorption of Lightweight Fe₃O₄/Mesoporous Carbon Microsphere Composites

RichHTML

PDF (PC)

Knowledge

Cited

Abstract

Cite this article

share this article

Figures/Tables 7

References 22

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	WU Jun, XU Peifei, JING Rui, ZHANG Dahai, FEI Qingguo. Experimental Study on Low-velocity Impact and Residual Strength of SiC/SiC Composite Laminates [J]. Journal of Inorganic Materials, 2024, 39(1): 51-60.
[2]	SHI Weigang, ZHANG Chao, LI Mei, WANG Jing, ZHANG Chengyu. 2D-SiC_f/SiC Interlaminar Mode I Fracture Testing and Characterization [J]. Journal of Inorganic Materials, 2024, 39(1): 45-50.
[3]	WANG Bo, YU Jian, LI Cuncheng, NIE Xiaolei, ZHU Wanting, WEI Ping, ZHAO Wenyu, ZHANG Qingjie. Service Stability of Gd/Bi_0.5Sb_1.5Te₃ Thermo-electro-magnetic Gradient Composites [J]. Journal of Inorganic Materials, 2023, 38(6): 663-670.
[4]	ZHANG Shuo, FU Qiangang, ZHANG Pei, FEI Jie, LI Wei. Influence of High Temperature Treatment of C/C Porous Preform on Friction and Wear Behavior of C/C-SiC Composites [J]. Journal of Inorganic Materials, 2023, 38(5): 561-568.
[5]	ZHANG Ye, YAO Dongxu, ZUO Kaihui, XIA Yongfeng, YIN Jinwei, ZENG Yuping. Combustion Synthesis of Si₃N₄-BN-SiC Composites by in-situ Introduction of BN and SiC [J]. Journal of Inorganic Materials, 2022, 37(5): 574-578.
[6]	WEI Tingting, GAO Xiguang, SONG Yingdong. Response of 2D SiC/SiC Composites Resistivity to Service Environments [J]. Journal of Inorganic Materials, 2022, 37(4): 420-426.
[7]	WANG Hongda, FENG Qian, YOU Xiao, ZHOU Haijun, HU Jianbao, KAN Yanmei, CHEN Xiaowu, DONG Shaoming. Microstructure and Corrosion Behavior of Brazed Joints of SiC/SiC Composites and Hastelloy N Alloy Using Cu-Ni Alloy [J]. Journal of Inorganic Materials, 2022, 37(4): 452-458.
[8]	WU Xishi, ZHU Yunzhou, HUANG Qing, HUANG Zhengren. Effect of Pore Structure of Organic Resin-based Porous Carbon on Joining Properties of C_f/SiC Composites [J]. Journal of Inorganic Materials, 2022, 37(12): 1275-1280.
[9]	JU Yinchao, LIU Xiaoyong, WANG Qin, ZHANG Weigang, WEI Xi. Ablation Behavior of Ultra-high Temperature Composite Ceramic Matrix Composites [J]. Journal of Inorganic Materials, 2022, 37(1): 86-92.
[10]	XIONG Jinyan, LUO Qiang, ZHAO Kai, ZHANG Mengmeng, HAN Chao, CHENG Gang. Facilely Anchoring Cu nanoparticles on WO₃ Nanocubes for Enhanced Photocatalysis through Efficient Interface Charge Transfer [J]. Journal of Inorganic Materials, 2021, 36(3): 325-331.
[11]	MAN Xin, WU Nan, ZHANG Mu, HE Hongliang, SUN Xudong, LI Xiaodong. Lu₂O₃-MgO Nano-powder: Synthesis and Fabrication of Composite Infrared Transparent Ceramics [J]. Journal of Inorganic Materials, 2021, 36(12): 1263-1269.
[12]	ZHANG Junmin, CHEN Xiaowu, LIAO Chunjin, GUO Feiyu, YANG Jinshan, ZHANG Xiangyu, DONG Shaoming. Optimizing Microstructure and Properties of SiC_f/SiC Composites Prepared by Reactive Melt Infiltration [J]. Journal of Inorganic Materials, 2021, 36(10): 1103-1110.
[13]	LI Longbin, XUE Yudong, HU Jianbao, YANG Jinshan, ZHANG Xiangyu, DONG Shaoming. Influence of SiC Nanowires on the Damage Evolution of SiC_f/SiC Composites [J]. Journal of Inorganic Materials, 2021, 36(10): 1111-1117.
[14]	ZHANG Bingyu,WANG ling,WANG Xiaomeng,QIU Haipeng. Effect of Precursors on Impregnation Behaviors of C/SiC Composites [J]. Journal of Inorganic Materials, 2020, 35(9): 1017-1022.
[15]	ZHANG Dongshuo,CAI Hao,GAO Kaiyin,MA Zichuan. Preparation and Visible-light Photocatalytic Degradation on Metronidazole of Zn₂SiO₄-ZnO-biochar Composites [J]. Journal of Inorganic Materials, 2020, 35(8): 923-930.