碳纳米管/微膨石墨复合负极材料的制备及电化学性能研究

doi:10.3724/SP.J.1077.2012.11736

无机材料学报 ›› 2012, Vol. 27 ›› Issue (10): 1035-1041.DOI: 10.3724/SP.J.1077.2012.11736 CSTR: 32189.14.SP.J.1077.2012.11736

碳纳米管/微膨石墨复合负极材料的制备及电化学性能研究

郭德超, 曾燮榕, 邓飞, 邹继兆, 盛洪超

(深圳大学材料学院, 深圳市特种功能材料重点实验室, 深圳 518060)

收稿日期:2011-11-26 修回日期:2012-01-27 出版日期:2012-10-20 网络出版日期:2012-09-17
作者简介:郭德超(1987-), 男, 硕士研究生. E-mail: dechao@163.com
基金资助:
深圳市政府“人才驿站—双百计划”资助项目(Shenfu[2008] 182); 深圳市科技计划资助项目(CXB201005240010A)

Preparation and Electrochemical Performance of Carbon nanotubes/Micro-expanded?Graphite Composite Anodes for Lithium-ion Batteries

GUO De-Chao, ZENG Xie-Rong, DENG Fei, ZOU Ji-Zhao, SHENG Hong-Chao

(Materials School of Shenzhen University, Shenzhen Key Laboratory of Special Functional Materials, Shenzhen 518060, China)

Received:2011-11-26 Revised:2012-01-27 Published:2012-10-20 Online:2012-09-17
About author:GUO De-Chao. E-mail: dechao@163.com
Supported by:
Two Hundred Plan for Talent Station of Shenzhen(Shenfu [2008] 182); Science and Technology R&D Program of Shenzhen (CXB201005240010A)

摘要/Abstract

摘要： 通过对两种天然鳞片石墨进行微膨胀处理得到微膨石墨, 然后以微膨石墨为基体采用化学气相沉积(CVD)法于微膨石墨的孔洞结构中原位生长碳纳米管, 制备了碳纳米管/微膨石墨复合负极材料. 电化学测试结果表明两种复合材料分别具有443和477 mAh/g的首次可逆容量. 两种复合材料在0.2C倍率下循环充放电30次后容量均能保持95%以上; 在1C下循环充放电50次后, 可逆容量分别稳定在259和195 mAh/g. 微膨胀处理形成的微纳米级孔洞以及原位碳纳米管的网络结构, 提供了更多的储锂空间, 并能够有效地缓冲电极材料在充放电时的体积变化; 电解质溶液浸润在纳米孔洞中, 有利于缩短锂离子的扩散路径, 提高倍率循环性能; 同时原位生长的类似常春藤形的碳纳米管可以起到桥梁的作用, 避免“孤岛”的形成, 增强了复合材料的导电性能.

关键词: 微膨石墨, 碳纳米管, 负极材料, 倍率性能, 循环稳定性

Abstract: Micro-expanded?flake?graphite (MEFG) and micro-expanded?spherical?graphite (MESG) were prepared from two kinds of natural graphite by intercalation reaction and rapid heating processes. Then carbon nanotubes/ micro-expanded?graphite (CNTs/MEG) composites were prepared by chemical vapor deposition (CVD) process, for which CNTs were grown in the pores of micro-expanded?graphite. Electrochemical test results?show that first discharge/ charge capacities of CNTs/MEFG and CNTs/MESG could respectively accommodate up to 443 and 477 mAh/g. Both of the prepared CNTs/MEG composites keep more than 95% capacities after 30 cycles at the rate of 0.2C and their capacities are stable at?259 and 195 mAh/g after 50 cycles at 1C rate, respectively. The nanoporous structure and the CNTs network can improve the discharge capacities and effectively?buffer the volumetric change of the composite electrode materials in the charge/discharge process. The diffusion path of Li+ can be reduced because of the electrolyte solution that filled in the nanopores, which significantly improves the rate capability of the electrodes. In addition, the growing ivy-like CNTs could improve the electric conductive property of the composites in the charge/discharge process.

Key words: micro-expanded graphite, carbon nanotubes, anode materials, rate capability, cycle stability

中图分类号:

TM912

郭德超, 曾燮榕, 邓飞, 邹继兆, 盛洪超. 碳纳米管/微膨石墨复合负极材料的制备及电化学性能研究[J]. 无机材料学报, 2012, 27(10): 1035-1041.

GUO De-Chao, ZENG Xie-Rong, DENG Fei, ZOU Ji-Zhao, SHENG Hong-Chao. Preparation and Electrochemical Performance of Carbon nanotubes/Micro-expanded?Graphite Composite Anodes for Lithium-ion Batteries[J]. Journal of Inorganic Materials, 2012, 27(10): 1035-1041.

参考文献

[1] Armand M, Tarascon J M. Building better batteries. Nature, 2008, 451: 652-657.

[2] CHEN Chang-Guo, CHEN Jia, TANG Yan-Qiu, et al. Recent progress in the structure of carbon cathode materials for lithium ion batteries. Journal of Inorganic Materials, 2003, 18(6): 1153-1157.

[3] Landi B J, Ganter M J, Cress C D, et al. Carbon nanotubes for lithium ion batteries. Energy Environ. Sci., 2009, 2: 638-654.

[4] Endo M, Kim Y A, Hayashi T, et al. Vapor-grown carbon fibers (VGCFs) basic properties and their battery applications. Carbon, 2001, 39(9): 1287-1297.

[5] Sethuraman V A, Hardwick L J, Srinivasan V, et al. Surface structural disordering in graphite upon lithium intercalation/deintercalation. J. Power Sources, 2010, 195(11): 3655-3660.

[6] LIU Yu, WANG Bao-Feng, XIE Jing-Ying, et al. Electrochemical characteristic of SEI in secondary lithium batteries. Journal of Inorganic Materials, 2003, 18(2): 307-312.

[7] Lu M, Cheng H, Yang Y. A comparison of solid electrolyte interphase (SEI) on the artificial graphite anode of the aged and cycled commercial lithium ion cells. Electrochimica Acta, 2008, 53: 3539-3546.

[8] Moon S H, Jin W J, Kim T R, et al. Performance-of graphite electrode modified with carbon nanofibers for lithium ion secondary battery. J. Ind. Eng. Chem., 2005, 11(4): 594-602.

[9] LIU Ye-Xiang, ZHOU Xiang-Yang, LI Jie, et al. Li+ intercalation/ deintercalation process in natural graphite. The Chinese Journal of Nonferrous Metals, 2002, 12(6): 1257-1262.

[10] Nozahi H, Nagarka K, Hoshi K, et al. Carbon-coated graphite for anode of lithium ion rechargeable batteries: carbon coating conditions and precursors. J. Power Sources, 2009, 194(1): 486-493.

[11] Jang S M, Miyawaki J,Tsuji U, et al. Preparation of a carbon nanofiber/natural graphite composite and an evaluation of its electrochemical properties as an anode material for a Li-ion battery. New Carbon Materials, 2010, 25(2): 89-95.

[12] ZHOU De-Feng, Ma Yue, ZHAO Yan-Ling, et al. Electrochemical performance of the composite materials of nano-carbon and graphite- carbon. Journal of Inorganic Materials, 2004, 19(5): 1111-1117.

[13] Makovicka J,Sedlarikova M, Arenillas A, et al. Expanded graphite as an intercaltion anode material for lithium systems. J. Solid State Electrochem, 2009, 13(9): 1467-1471.

[14] Yang S B, Song H H, Chen X H. Electrochemical performance of expanded mesocarbon microbeads as anode material for lithium- ion batteries. Electrochem. Commun., 2006, 8(1): 137-142.

[15] 曾燮榕, 王明福, 谢盛辉, 等. 可膨胀石墨的制备方法. 中国发明专利, C01B31/04, 200410027920, 2005.03.16.

[16] YANG Shao-Bin, FEI Xiao-Fei, JIANG Na. Influences of increasing interlayer space on the properties of lithium storage of natural graphite. Acta Chimica Sinica, 2009, 67(17): 1995-2000.

[17] Wei Xing-Hai, Zhang Jin-Xi, Shi Jing-Li, et al. Preparation of sulfur- free highly expanded graphite. New Carbon Materials, 2004, 19(1): 45-47.

[18] Novak P, Ufheil J, Buqa H, et al. The importance of the active surface area of graphite materials in the first lithium intercalation. J. Power Sources, 2007, 174(2): 1082-1085.

[19] Lahiri I, Oh S W, Hwang J Y, et al. High capacity and excellent stability of lithium ion battery anode using interface-controlled binder-free multiwall carbon nanotubes grown on copper. Nano, 2010, 4(6): 3440-3446.

[20] Tokumitsu K, Fujimoto H, Mabuchi A, et al. High capacity carbon anode for Li-ion battery: a theoretical explanation. Carbon, 1999, 37(10): 1599-1605.

[21] Wang G X, Shen X P, Yao J, et al. Graphene nanosheets for enhanced lithium storage in lithium ion batteries. Carbon, 2009, 47(8): 2049-2053.

[22] Abouimrane A, Compton O C, Amine K, et al. Non-annealed graphene paper as a binder-free anode for lithium-ion batteries. J. Phys. Chem. 2010, 114(29): 12800-12804.

[23] Eom J Y, Park J W, Kwon H S. Effects of ball-milling on lithium insertion into multi-walled carbon nanotubes synthesized by thermal chemical vapour deposition. J. Power Sources, 2006, 157(1): 507-514.

[24] Zou L, Kang F Y, Zheng Y P, et al. Modi-ed natural -ake graphite with high cycle performance as anode material in lithium ion batteries. Electrochemical Acta, 2009, 54(15): 3930-3934.

[25] Sawai K, Ohzuku T. Factors affecting rate capability of graphite electrodes for lithium-ion batteries. J. Electrochemical. Soc., 2003, 150(6): A674-1-5.

[26] ZHANG Xu-Gang, LIU Min, WANG Zuo-Ming, et al. Applications of carbon nanotube composite as anode conductive additives in lithium ion batteries. Carbon Techniques, 2008, 27(4): 10-13.

碳纳米管/微膨石墨复合负极材料的制备及电化学性能研究

Preparation and Electrochemical Performance of Carbon nanotubes/Micro-expanded?Graphite Composite Anodes for Lithium-ion Batteries

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	陈海燕, 唐志鹏, 尹良君, 张林博, 徐鑫. CIPs@Mn_0.8Zn_0.2Fe₂O₄-CNTs复合材料低频吸波性能研究[J]. 无机材料学报, 2024, 39(1): 71-80.
[2]	胡梦菲, 黄丽萍, 李贺, 张国军, 吴厚政. 锂/钠离子电池硬碳负极材料的研究进展[J]. 无机材料学报, 2024, 39(1): 32-44.
[3]	田煜彬, 田超凡, 李森, 赵永鑫, 邢涛, 李智, 陈萧如, 向帅蓉, 代鹏程. 高导电性生物质碳布的制备及其燃料电池气体扩散层性能[J]. 无机材料学报, 2023, 38(11): 1316-1322.
[4]	王洋, 范广新, 刘培, 尹金佩, 刘宝忠, 朱林剑, 罗成果. 钾离子掺杂提高锂离子电池正极锰酸锂性能的微观机制[J]. 无机材料学报, 2022, 37(9): 1023-1029.
[5]	江依义, 沈旻, 宋半夏, 李南, 丁祥欢, 郭乐毅, 马国强. 双功能电解液添加剂对锂离子电池高温高电压性能的影响[J]. 无机材料学报, 2022, 37(7): 710-716.
[6]	王禹桐, 张非凡, 许乃才, 王春霞, 崔立山, 黄国勇. 水系锂离子电池负极材料LiTi₂(PO₄)₃的研究进展[J]. 无机材料学报, 2022, 37(5): 481-492.
[7]	吴秋琴, 姚奋发, 金传洪, 郑遗凡. 碳纳米管内填充生长超细一维亚化学计量比氧化钨纳米线[J]. 无机材料学报, 2022, 37(4): 413-419.
[8]	王晶, 徐守冬, 卢中华, 赵壮壮, 陈良, 张鼎, 郭春丽. 钠离子电池中空结构CoSe₂/C负极材料的制备及储钠性能研究[J]. 无机材料学报, 2022, 37(12): 1344-1350.
[9]	李昆儒, 胡省辉, 张正富, 郭玉忠, 黄瑞安. 源于溪木贼的高性能锂离子电池三维多孔生物质硅/碳复合负极材料[J]. 无机材料学报, 2021, 36(9): 929-935.
[10]	刘芳芳, 传秀云, 杨扬, 李爱军. 氮/硫共掺杂对纤水镁石模板碳纳米管电化学性能的影响[J]. 无机材料学报, 2021, 36(7): 711-717.
[11]	付宇坤, 曾敏, 饶先发, 钟盛文, 张慧娟, 姚文俐. 锂离子电池高镍LiNi_0.8Mn_0.2O₂正极材料的微波合成及其Co、Al共改性[J]. 无机材料学报, 2021, 36(7): 718-724.
[12]	曾凡鑫, 刘创, 曹余良. 去合金化制备具有高循环稳定性的纳米多孔Sb/MCNT储钠负极材料[J]. 无机材料学报, 2021, 36(11): 1137-1144.
[13]	湛菁,徐昌藩,龙怡宇,李启厚. 聚丙烯酰胺凝胶法制备Bi₂Mn₄O₁₀及其电化学性能[J]. 无机材料学报, 2020, 35(7): 827-833.
[14]	董龙浩,张海军,张俊,吴文浩,贾全利. 碳纳米管改性海泡石多孔陶瓷及其高效油水分离性能研究[J]. 无机材料学报, 2020, 35(6): 689-696.
[15]	朱泽阳,魏济时,黄健航,董向阳,张鹏,熊焕明. 晶格空位ZnO纳米棒的制备及其在镍锌电池中的应用[J]. 无机材料学报, 2020, 35(4): 423-430.