P2O5-BaO-Al2O3-K2O磷酸盐激光玻璃的表面处理

doi:10.3724/SP.J.1077.2010.00196

摘要/Abstract

摘要：

采用化学浸蚀与高温热处理相结合的方法来改善P₂O₅-BaO-Al₂O₃-K₂O磷酸盐玻璃表面平整性、去除玻璃表面杂质, 提高用管棒法制备光纤预制棒时纤芯和包层玻璃的表面质量, 消除由于机械抛光工艺带来的表面缺陷和表面污染. 实验研究了磷酸盐玻璃盐酸浸蚀的特性, 分析了盐酸溶液与磷酸盐玻璃作用机制, 并确定了浸蚀参数，9mol/L的盐酸溶液对此磷酸盐玻璃具有最大浸蚀速率, 浸蚀30min后, 可消除玻璃表面的划痕. 盐酸溶液对玻璃的浸蚀反应使磷酸盐玻璃表面平整, 但在玻璃表面产生了晶化覆盖层. 通过进一步在拉丝温度下热处理, 可使玻璃表面覆盖层重新非晶化, 提高玻璃透过率. 实验结果表明：化学浸蚀和高温热处理的复合方法是一种有效改善磷酸盐玻璃表面质量的途径.

关键词: 磷酸盐玻璃, 表面, 化学腐蚀, 高温处理

Abstract:

The surface of P₂O₅-BaO-Al₂O₃-K₂O phosphate glass was modified by using both a chemical etching process and a subsequent high-temperature heat treatment, which can effectively remove the surface defects of phosphate glass and the surface contaminations caused by traditional polishing technology. The process of etching phosphate glass in hydrochloric acid was studied to investigate the etching mechanism and determine the etching optimum conditions. It is found that the etching reactions between hydrochloric acid and glass make the phosphate glass surface smooth while a crystal layer is formed on the glass surface. The optimum etching process is as follows, etching in a 9mol/L HCl solution for 30min. After further heating the glass at 550℃, the crystal layer can be removed as crystal particles on glass surface melt, which results in the increase of the transmittance of glass. The results show that a process combining chemical etching the phosphate glass with subsequent heating treatment is an effective method to improve the surface quality of the phosphate glass.

Key words: phosphate glass, surface, chemical etching, heating treatment

中图分类号:

TG171

杨刚,钱奇,杨中民. P₂O₅-BaO-Al₂O₃-K₂O磷酸盐激光玻璃的表面处理[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2010.00196.

YANG Gang,QIAN Qi,YANG Zhong-Min. Surface Treatment of P₂O₅-BaO-Al₂O₃-K₂O Phosphate Laser Glass[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2010.00196.

参考文献

［1］Chahine A, Et-tabirou M, Elbenaissi M, et al. Effect of CuO on the structure and properties of (50-x/2)Na₂O-xCuO-(50-x/2)P₂O₅ glasses. Mater. Chem. Phys., 2004, 84(2/3): 341-347.

［2］Zou X L, Itoh K, Toratani H. Transmission loss characteristics of fluorophosphate optical fibers in the ultraviolet to visible wavelength region. J. Non-Cryst. Solids, 1997, 215(1): 11-20.

［3］Petit L, Cardinal T, Videau J J, et al. Effect of niobium oxide introduction on erbium luminescence in borophosphate glasses. Opt. Mater., 2006, 28(3): 172-180.

［4］Brow R K. Review: the structure of simple phosphate glasses. J. NonCryst. Solids, 2000, 263(1-4): 1-28.

［5］Shelby J E. Properties of alkalialkaline earth metaphosphate glasses. J. Non-Cryst. Solids, 2000, 263&264(1/2): 271-276.

［6］Jiang S B, Luo T, Hwang B C, et al. Er³⁺-doped phosphate glasses for fiber amplifiers with high gain per unit length. J. Non-Cryst. Solids, 2000, 263&264(1/2): 364-368.

［7］Polynkin P, Peyghambarian N, Moloney J. Efficient energy extraction from large-mode-area, short, heavily Er: Yb-codoped phosphate-glass fiber for pulsed laser applications. Appl. Phys. Lett., 2008, 92(6): 061115-1-3.

［8］Grobnic D, Mihailov S J, Walker R B, et al. Bragg gratings made with a femtosecond laser in heavily doped Er-Yb phosphate glass fiber. IEEE Photonic Tech. L., 2007, 19(12): 943-945.

［9］Campbell J H, Suratwala T I. Nd-doped phosphate glasses for high-energy/high-peak-power lasers. J. Non-Cryst. Solids, 2000, 263&264(1/2): 318-341.

［10］Lee Y W, Sinha S, Digonnet M J F, et al. 20W single-mode Yb³⁺-doped phosphate fiber laser. Opt. Lett., 2006, 31(22): 3255-3257.

［11］Jiang S B, Myers M, Peyghambarian N. Er³⁺-doped phosphate glasses and lasers. J. Non-Cryst. Solids, 1998, 239(1/2/3): 143-148.

［12］Jeong Y, Sahu J K, Payne D N, et al. Ytterbium-doped large-core fibre laser with 1 kW of continuous-wave output power. Electron. Lett., 2004, 40(8): 470-472.

［13］Jeong Y, Sahu J K, Payne D N, et al. Ytterbium-doped largecore fibre laser with 1 kW of continuous-wave output power. Optics Express, 2004, 12(25): 6088-6092.

［14］余尧楚, 姜中宏 (YU Yao-Chu, et al). 磷酸盐玻璃熔炼时对铂的腐蚀. 无机材料学报(Journal of Inorganic Materials), 1997, 12(3): 265-272.

［15］杨钢锋，邓再德，冯洲明，等. 碱金属离子对掺铒磷酸盐玻璃除水性质的影响. 华南理工大学学报， 2003, 31(12): 54-57.

［16］杨钢锋, 赵三银, 邓再德, 等(YANG Gang-Feng, et al). 掺铒磷酸盐玻璃反应气氛法除水的研究. 无机材料学报 (Journal of Inorganic Materials), 2005, 20(5): 1083-108.

［17］林达愿, 杨钢锋, 邓再德, 等. 玻璃加工质量对有源光纤芯包界面缺陷的影响. 武汉理工大学学报, 2006, 28(1): 4-6.

［18］冯正蓉. 光纤强度与预制棒表面处理技术. 光纤与电缆及其应用技术, 1996(2): 45-49.

［19］Xu S H, Yang Z M, Feng Z M, et al. Gain and noise characteristics of single-mode Er³⁺/Yb³⁺ co-doped phosphate glass fibers. IEEE International Nanoelectroncs Conference, 2008, 1-3: 633-635.

［20］Xu S H, Yang Z M, Feng Z M, et al. Efficient fibre amplifiers based on a highly Er³⁺/Yb³⁺ codoped phosphate glass-fibre. Chinese Phys. Lett., 2009, 26(4): 047806-1-3.

［21］Liu T, Yang Z M, Xu S H. 3-dimensional heat analysis in short-length Er³⁺/Yb³⁺ co-doped phosphate fiber laser with upconversion. Opt. Express, 2009, 17(1): 235-247.

［22］王中俭, 吴纬, 姜波(WANG Zhong-Jian, et al). ZnO-MgO-P₂O₅磷酸盐玻璃酸溶机理研究. 无机材料学报 (Journal of Inorganic Materials), 2008, 23(1): 155-158.

［23］迪安J A, 主编. 兰氏化学手册, 13版. 北京: 科学出版社, 1991.

［24］南京玻璃纤维研究设计院《玻璃测试技术》编写组. 玻璃测试技术. 北京：中国建筑工业出版社, 1987: 284-285.

［25］瞿金蓉, 胡明安, 陈敬中, 等. 纳米粒子的熔点与粒径的关系. 地球科学－中国地质大学学报, 2005, 30(2): 195-198.

［26］王世良, 周杨韬, 侯丽珍, 等. 由Kelvin 方程推导出微小颗粒的熔点与半径的关系. 湖南理工学院学报 (自然科学版), 2008, 21(3): 37-40.

［27］文潮, 刘晓新, 周刚, 等. 纳米金刚石的熔点和德拜特征温度. 西安交通大学学报, 2000, 34(11): 108-110.

[1]	蔡和庆, 韩璐, 杨松松, 薛新玉, 张扣, 孙志成, 刘儒平, 胡堃, 危岩. 小粒径Fe₃O₄-DMSA-PEI磁性纳米颗粒的制备及其基因负载能力研究[J]. 无机材料学报, 2024, 39(5): 517-524.
[2]	李乾利, 黎乃鑫, 李育成, 刘慎业, 程帅, 杨光, 任宽, 王峰, 赵景泰. 辐射光致发光材料及其应用研究进展[J]. 无机材料学报, 2023, 38(7): 731-749.
[3]	上官丽, 聂晓双, 叶奎材, 崔苑苑, 乔玉琴. 氧化钛涂层润湿性对免疫成骨性能的影响规律[J]. 无机材料学报, 2023, 38(12): 1457-1565.
[4]	张瑞阳, 王壹, 欧博文, 周莹. α-Ni(OH)₂表面羟基协同Ni³⁺位点催化氧化甲醛机理研究[J]. 无机材料学报, 2023, 38(10): 1216-1222.
[5]	朱河圳, 王选朋, 韩康, 杨晨, 万睿哲, 吴黎明, 麦立强. 超高镍LiNi_0.91Co_0.06Al_0.03O₂@Ca₃(PO₄)₂正极材料的储锂稳定性的提升机制[J]. 无机材料学报, 2022, 37(9): 1030-1036.
[6]	林啊鸣, 孙宜阳. Cs₂SnI₆低指数晶面稳定性的第一性原理计算研究[J]. 无机材料学报, 2022, 37(6): 691-696.
[7]	肖美霞, 李苗苗, 宋二红, 宋海洋, 李钊, 毕佳颖. 表面端基卤化Ti₃C₂ MXene应用于锂离子电池高容量电极材料的研究[J]. 无机材料学报, 2022, 37(6): 660-668.
[8]	马磊, 黄毅, 邓浩, 银航, 田强, 晏敏皓. 氟磷灰石对酸性水溶液中铀(VI)的去除研究[J]. 无机材料学报, 2022, 37(4): 395-403.
[9]	周港怀, 刘耀, 石原, 刘绍军. 活性氧化铝催化剂载体的光固化浆料制备与成型[J]. 无机材料学报, 2022, 37(3): 297-302.
[10]	李乔磊, 顾玥, 于雪华, 张朝威, 邹明科, 梁静静, 李金国. 烧结温度对3D打印硅基陶瓷型芯表面形貌及粗糙度的影响[J]. 无机材料学报, 2022, 37(3): 325-332.
[11]	郭李娜, 何雪冰, 吕琳, 吴丹, 原弘. 调控CuO表面性质选择性电催化还原CO₂制HCOOH[J]. 无机材料学报, 2022, 37(1): 29-37.
[12]	郭隐犇, 陈子曦, 王宏志, 张青红. 基于无机填料复合薄膜的摩擦纳米发电机研究进展[J]. 无机材料学报, 2021, 36(9): 919-928.
[13]	周帆, 毕辉, 黄富强. 用稻壳制备亚甲基蓝高吸附容量的超高比表面积活性炭[J]. 无机材料学报, 2021, 36(8): 893-903.
[14]	武晓玮, 李佳艳. 多晶硅表面金属催化化学腐蚀法制绒研究现状[J]. 无机材料学报, 2021, 36(6): 570-578.
[15]	李子宜, 章佳佳, 邹小勤, 左家玉, 李俊, 刘应书, 裴有康. 菱沸石分子筛膜的合成调控与气体分离研究进展[J]. 无机材料学报, 2021, 36(6): 579-591.

P₂O₅-BaO-Al₂O₃-K₂O磷酸盐激光玻璃的表面处理

Surface Treatment of P₂O₅-BaO-Al₂O₃-K₂O Phosphate Laser Glass

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价