有机-无机自组装制备类荷叶结构超疏水涂层及其性能研究

doi:10.3724/SP.J.1077.2010.00765

无机材料学报 ›› 2010, Vol. 25 ›› Issue (7): 765-769.DOI: 10.3724/SP.J.1077.2010.00765 CSTR: 32189.14.SP.J.1077.2010.00765

有机-无机自组装制备类荷叶结构超疏水涂层及其性能研究

狄志勇, 何建平, 周建华, 孙盾, 王涛

(南京航空航天大学材料科学与技术学院, 南京210016)

收稿日期:2009-11-16 修回日期:2010-01-21 出版日期:2010-07-20 网络出版日期:2010-06-10
基金资助:
国家自然科学基金(50871053)

Fabrication and Anticorrosion Property of Superhydrophobic Surfaces with Hierarchical Structure through an Organic-inorganic Self-assemble Process

DI Zhi-Yong, HE Jian-Ping, ZHOU Jian-Hua, SUN Dun, WANG Tao

(College of Material Science and Technology, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China)

Received:2009-11-16 Revised:2010-01-21 Published:2010-07-20 Online:2010-06-10

摘要/Abstract

摘要：

以g-氨丙基三乙氧基硅烷(硅烷偶联剂KH550)为连接剂, 利用硅氧烷水解形成硅羟基的自组装功能, 将聚四氟乙烯(PTFE)烧结形成的纳米级纤维与硅氧烷团聚的微米级粒子结合, 制备了具有类荷叶表面形貌的超疏水涂层, 其静态水接触角达152°, 滚动角约为5°. 通过扫描电镜观察涂层的表面微观形貌, 发现该涂层具有微/纳米二级结构. 利用Cassie方程, 探讨了表面微观结构和涂层疏水性能之间的关系. 用电化学交流阻抗谱(EIS)分析覆有涂层的试样在模拟腐蚀环境下的腐蚀行为, 结果表明该试样的腐蚀电流比裸钢片降低了3~4个数量级, 说明该涂层具有较好的防腐性能.

关键词: 超疏水涂层, 微纳米结构, 自组装, 防腐蚀

Abstract:

A superhydrophobic surface was obtained by using g-aminopropyltriethoxylsilane (KH550) as a linker from organic-inorganic self-assemble process. By utilizing silane with amine functional group and Si-hydroxy functional group, bionic superhydrophobic surfaces with hierarchical microsphere/nanofiber structures were prepared on metal surfaces. The corrosion behavior of the composite film was investigated by electrochemicial impedance spectroscope (EIS). The maximal contact angle for water on the composite film is about 152°. Scanning electron microscope (SEM). Test result shows that the lotus-like film has microsphere/nanofiber hierarchical structure. The surface of the film forms a composite framework which plays an essential role in trapping air between the solid substrate and the liquid droplets to get high contact angle and low roll angle. Electrochemical corrosion measurements results indicate that the composite film has excellent corrosion protection for mild steel. The corrosion current of mild steel is nearly 1´10⁴ times than that of the sample coated with the composite film, while the corrosion impedance increases dramatically. It suggests that the superdrophobic film has good corrosion resistance.

Key words: superhydrophobic, hierarchical structure, self-assemble, anticorrosion

中图分类号:

O647

狄志勇, 何建平, 周建华, 孙盾, 王涛. 有机-无机自组装制备类荷叶结构超疏水涂层及其性能研究[J]. 无机材料学报, 2010, 25(7): 765-769.

DI Zhi-Yong, HE Jian-Ping, ZHOU Jian-Hua, SUN Dun, WANG Tao. Fabrication and Anticorrosion Property of Superhydrophobic Surfaces with Hierarchical Structure through an Organic-inorganic Self-assemble Process[J]. Journal of Inorganic Materials, 2010, 25(7): 765-769.

参考文献

[1]Nakajima A, Saiki C, Hashimoto K, et al. Processing of roughened silica film by colloidal silica for super-hydrophobic coating. J. Mater. Sci. Lett., 2001, 20(21): 1975-1977.
[2]Pilotek S, Schmidt H K. Wettability of microstructured hydrophobic Sol-Gel coatings. Journal of Sol-Gel and Technology, 2003, 26(1): 789-792.
[3]Shirtcliffe N J, McHale G, Newton M I, et al. Wetting and wetting transitions on copper-based super-hydrophobic surfaces. Langmuir, 2005, 21(3): 937-943.
[4]Wu Y, Bekke M, Moue Y, et al. Mechanical durability of ultrawater-repellent thin film with microwave plasma-enhanced CVD. Thin Solid Films, 2004, 457(1): 122-127.
[5]Liu H, Feng L, Zhai J, et al. Reversible wettability of a chemical vapor deposition prepared ZnO film between superhydrophobicity and superhydrophilicity. Langmuir, 2004, 20(14): 5659-5661.
[6]Erbil Y H, Demirei A L, Avci Y, et al. Transformation of a simple plastic into a superhydrophobic surface. Science, 2003, 299(5611): 1377-1380.
[7]Song X, Zhai J, Wang Y, et al. Fabrication of superhydrophobic surfaces by self-assembly and their water-adhesion properties. J. Phys. Chem. B, 2005, 109(9): 4048-4052.
[8]Jung D H, Park I J, Choi Y K, et al. Perfluorinated polymer monolayers on porous silica for materials with super liquid repellentp roperties. Langmuir, 2002, 18(16): 6133-6139.
[9]Tadanaga K, Kitamuro K, Matsuda A, et al. Formation of superhydrophobic alumina coating films with high transparency on polymer substrates by the Sol-Gel method. Journal of Sol-Gel and Technology, 2003, 26(1): 705-708.
[10]Shang H M, Wang Y, Limmer S J, et al. Optically transparent superhydrophobic silica-based films. Thin Solid Films, 2005, 472(1): 37-43.
[11]Nakajima A, Abe K, Hashimoto K, et al. Preparation of hardsuper-hydrophobic films with visible light transmission. Thin Solid Films, 2000, 376(1): 140-143.
[12]Barthlott W, Neinhuis C. Purity of the sacred lotus, or escape from contamination in biological surfaces.Plant,1997, 202(1):1-8
[13]Kock K, Bhushan B, Jung Y C, et al. Fabrication of artificial lotus leaves and significance of hierarchical structure for superhydrophobicity and low adhesion. Soft Matter, 2009, 5: 1386-1393
[14]翟锦, 李欢军, 李英顺, 等(ZHAI Jin, et al). 碳纳米管阵列超双疏性质的发现. 物理(Physics), 2002, 31(8): 483-485.
[15]Cassie A B D, Baxter S. Large contact angles of plant and animal surfaces. Nature, 1945, 155: 21-22.
[16]Luo Z Z, Zhang Z Z, Hu L T, et al. Stable bionic superhydrophobic coating surface fabricated by a conventional curing process. Advanced Materials, 2008, 20(5): 970-974.
[17]Michele M, Alessandro C, Luisa D M, et al. Durable superhydrophobic and antireflective surfaces by trimethylsilanized silica nanoparticles-based Sol-Gel processing. Langmuir, 2009, 25(11): 6357-6362.
[18]曹楚南, 张鉴清. 电化学阻抗谱导论. 北京: 科学出版社, 2002: 20-36.

有机-无机自组装制备类荷叶结构超疏水涂层及其性能研究

Fabrication and Anticorrosion Property of Superhydrophobic Surfaces with Hierarchical Structure through an Organic-inorganic Self-assemble Process

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	赵睿, 毛飞, 钱晖, 杨晓, 朱向东, 张兴栋. 微纳米结构生物材料在骨组织再生修复中的研究进展[J]. 无机材料学报, 2023, 38(7): 750-762.
[2]	张祥松, 刘业通, 王永瑛, 武子瑞, 刘振中, 李毅, 杨娟. 自组装制备PtIr合金气凝胶及其高效电催化氨氧化性能[J]. 无机材料学报, 2023, 38(5): 511-520.
[3]	孟晴, 李江涛. 燃烧合成疏水BN粉体和超疏水涂层的制备及其性能表征[J]. 无机材料学报, 2022, 37(10): 1037-1042.
[4]	李华鑫, 陈俊勇, 肖洲, 乐弦, 余显波, 向军辉. 纳米材料形貌和性能调控的仿生自组装研究进展[J]. 无机材料学报, 2021, 36(7): 695-710.
[5]	彭新村, 王智栋, 曾梦丝, 刘云, 邹继军, 朱志甫, 邓文娟. SiO₂纳米球的粒径均一性研究及其在硅光学共振纳米柱阵列中的应用[J]. 无机材料学报, 2019, 34(7): 734-740.
[6]	佟威, 熊党生. 仿生超疏水表面的发展及其应用研究进展[J]. 无机材料学报, 2019, 34(11): 1133-1144.
[7]	王景平, 成方媛, 杜显锋, 徐友龙. 表面自组装法制备高比容Al₂O₃/TiO₂复合膜[J]. 无机材料学报, 2018, 33(6): 617-622.
[8]	范闻, 武利民. 硅油两步脱水法可控制备纳米二氧化钛透镜[J]. 无机材料学报, 2018, 33(12): 1337-1342.
[9]	罗维, 魏晶, 邓勇辉, 李宇慧, 王连军, 赵涛, 江莞. 新型两亲性嵌段共聚物导向合成有序大孔径介孔材料的研究进展[J]. 无机材料学报, 2017, 32(1): 1-10.
[10]	武萱蓉, 杨巧珍, 赵永祥, 路艳罗. ZnS微球的水热/溶剂热法合成及其光催化性能研究[J]. 无机材料学报, 2016, 31(5): 473-478.
[11]	张文强, 张锌. 厘米级盘形硅藻微粒单层密排研究[J]. 无机材料学报, 2015, 30(11): 1208-1212.
[12]	孙志娟, 陈雪莲, 蒋春跃. 自组装法制备中空二氧化硅纳米粒子减反射薄膜[J]. 无机材料学报, 2014, 29(9): 947-955.
[13]	陈峰, 孙团伟, 漆超, 吴进, 崔大祥, 朱英杰. 微波辅助溶剂热法制备磷酸钙微球和多面体[J]. 无机材料学报, 2014, 29(7): 776-780.
[14]	张辉, 马永军, 王艺程, 文丹丹, 叶飞, 白飞明. 离轴磁控溅射法生长1-3维PZT-NFO纳米复合薄膜[J]. 无机材料学报, 2014, 29(4): 371-376.
[15]	侯维敏, 于云, 胡学兵, 于洋, 米乐, 宋力昕. Al₂O₃微滤膜的超疏水改性研究[J]. 无机材料学报, 2013, 28(8): 864-868.