热蒸发法制备Zn1-xCdxO纳米管及其生长机制研究

doi:10.3724/SP.J.1077.2009.00998

摘要/Abstract

摘要： 采用热蒸发纯Zn粉和Cd粉, 在湿反应气氛中氧化制备得到掺Cd的ZnO纳米管, 其Cd含量为3.3at%. 场发射扫描电镜(FESEM)及高分辨透射电镜(HRTEM)分析表明, 大部分纳米管外径约80~150nm, 长度达数微米, 壁厚约20nm. 通过与相同条件下制备的ZnO纳米结构的室温光致发光谱(PL) 进行对比发现, 由于Cd的掺入, Zn_1-xCd_xO纳米管的紫外近带边峰(UV NBE)从3.26eV红移到3.20eV附近.分析认为，Zn_1-xCd_xO纳米管遵循气液固(VLS)生长机制, 并在此基础上提出Zn_1-xCd_xO纳米管生长过程, 同时指出Kirkendall效应可能对纳米管的形成起到了重要作用.

关键词: Zn_1-xCd_xO, 纳米管, 制备, 生长过程

Abstract: The Cd-doped ZnO nanotubes with Cd content of about 3.3at% were synthesized via a process of evaporating mixture of pure Zn and Cd powders and then oxidating in a wet condition. Field-emission scanning electron microscope (FESEM) and high resolution transmission electron microscope (HRTEM) analysis indicate that most of the nanotubes are of about 80-150nm in outer diameter, several micrometers in length, and about 20nm in wall thickness. Compared with photoluminescence (PL) spectra of the pure ZnO nanostructures prepared in the same condition, the room-temperature ultraviolet (UV) near-band-edge (NBE) emission of the Zn_1-xCd_xO nanotubes exhibite a slight red shift from 3.26eV to 3.20eV, which is attributed to Cd substitution. It is suggested that the growth of the Zn_1-xCd_xO nanotubes follow vapor-liquid-solid (VLS) mechanism, and a possible growth process of the Zn_1-xCd_xO nanotubes is put forward. The Kirkendall effect is considered to play an important role in the formation of the Zn_1-xCd_xO nanotubes.

Key words: Zn_1-xCd_xO, nanotube, fabrication, growth process

中图分类号:

O649

刘勃,王发展,张顾钟,赵超,原思聪. 热蒸发法制备Zn_1-xCd_xO纳米管及其生长机制研究[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2009.00998.

LIU Bo,WANG Fa-Zhan,ZHANG Gu-Zhong,ZHAO Chao,YUAN Si-Cong. Fabrication and Growth Mechanism of Zn_1-xCd_xO Nanotubes by Thermal Evaporation Method[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2009.00998.

参考文献

［1］Pan Z W, Dai Z R, Wang Z L. Science, 2001, 291(5510): 1947-1949.
［2］Wang Z L. J. Phys.: Condens. Mater., 2004, 16(25): R829-R858.
［3］Wang F Z, Ye Z Z, Ma D W, et al. J. Cryst. Growth, 2005, 283(3/4): 373-377.
［4］Yan H Q, He R R, Johnson J, et al. J. Am. Chem. Soc., 2003, 125(16): 4728-4729.
［5］Pan Z W, Mahurin S M, Dai S, et al. Nano Lett., 2005, 5(4): 723-727.
［6］Iijima S. Nature, 1991, 354: 56-58.
［7］Lin Y, Rao A M, Sadanadan B, et al. J. Phys. Chem. B, 2002, 106(6): 1294-1298.
［8］Zhang X H, Xie S Y, Jiang Z Y, et al. J. Phys. Chem. B, 2003, 107(37): 10114-10118.
［9］Li L, Pan S S, Dou X C, et al. J. Phys. Chem. C, 2007, 111(20): 7288-7291.
［10］李长全, 傅敏恭. 无机化学学报, 2006, 22(9): 1669-1670.
［11］Wang H Q, Li G H, Jia L C, et al. J. Phys. Chem. C, 2008, 112(31): 11738-11743.
［12］Fan D H, Shen W Z, Zheng M J, et al. J. Phys. Chem. C, 2007, 111(26): 9116-9121.
［13］Xing Y J, Xi Z H, Zhang X D, et al. Solid State Communication, 2004,129(10): 671-675.
［14］Xu W Z, Ye Z Z, Ma D W, et al. Appl. Phys. Lett., 2005, 87(9): 0931101-3.
［15］Makino T, Segawa Y, Kawasaki M, et al. Appl. Phys. Lett., 2001, 78(9): 1237-1239.
［16］Wang F Z, He H P, Ye Z Z, et al. J. Phys. D: Appl. Phys., 2005, 38(16): 2919-2922.
［17］Tabet-Derraz H, Benramdane N, Nacer D, et al. Sol. Energy Mater. Sol. Cells, 2002, 73(3): 249-259.
［18］张志军, 王发展, 刘勃, 等. 物理化学学报, 2008, 24(10): 1912-1916.
［19］Hu J Q, Bando Y. Appl. Phys. Lett., 2003, 82(9): 1401-1403.
［20］Bae Y S, Seo H W, Park J H. J. Phys. Chem. B, 2004, 108(17): 5206-5210.
［21］Zhou S M, Zhang X H, Meng X M, et al. Mater. Res. Bull., 2006, 41(2): 340-346.
［22］Fan H J, Gsele U, Zacharias M. Small, 2007, 3(10): 1660-1671.
［23］唐鑫, 吕海峰, 马春雨, 等. 物理学报, 2008, 57(02): 1066-1072.
［24］Bylander E G. J. Appl. Phys., 1978, 49(3): 1188-1195.
［25］Vanheusden K, Seager C H, Warren W L, et al. Appl. Phys. Lett., 1996, 68(3): 403-405.
［26］Egelhaaf H J, Oelkrug D. J. Cryst. Growth, 1996, 161(1-4): 190-194.
［27］Meulenkamp E A. J. Phys. Chem. B, 1998, 102(40): 7764-7769.
［28］Li D, Leung Y H, Djurisic A B, et al. Appl. Phys. Lett., 2004, 85(9): 1601-1603.

[1]	潘建隆, 马官军, 宋乐美, 郇宇, 魏涛. 燃料还原法原位制备高稳定性/催化活性SOFC钴基钙钛矿阳极[J]. 无机材料学报, 2024, 39(8): 911-919.
[2]	陈海燕, 唐志鹏, 尹良君, 张林博, 徐鑫. CIPs@Mn_0.8Zn_0.2Fe₂O₄-CNTs复合材料低频吸波性能研究[J]. 无机材料学报, 2024, 39(1): 71-80.
[3]	蔡凯, 靳志文. 基于二维钙钛矿(PEA)₂PbI₄的光电探测器[J]. 无机材料学报, 2023, 38(9): 1069-1075.
[4]	冒爱琴, 陆文宇, 贾洋刚, 王冉冉, 孙静. 柔性压电器件及其可穿戴应用[J]. 无机材料学报, 2023, 38(7): 717-730.
[5]	郭春霞, 陈伟东, 闫淑芳, 赵学平, 杨傲, 马文. 埃洛石纳米管负载锆氧化物吸附水中砷的研究[J]. 无机材料学报, 2023, 38(5): 529-536.
[6]	马婷婷, 汪志鹏, 张梅, 郭敏. 超长稳定的混合阳离子钙钛矿太阳能电池性能优化研究[J]. 无机材料学报, 2023, 38(12): 1387-1395.
[7]	田煜彬, 田超凡, 李森, 赵永鑫, 邢涛, 李智, 陈萧如, 向帅蓉, 代鹏程. 高导电性生物质碳布的制备及其燃料电池气体扩散层性能[J]. 无机材料学报, 2023, 38(11): 1316-1322.
[8]	王梦桃, 索军, 方东, 易健宏, 刘意春, Olim RUZIMURADOV. ITO/TiO₂纳米管阵列复合材料的可见光催化性能[J]. 无机材料学报, 2023, 38(11): 1292-1300.
[9]	韦婷婷, 徐华蕊, 朱归胜, 龙神峰, 张秀云, 赵昀云, 江旭鹏, 宋金杰, 郭宁杰, 龚祎鹏. BaTiO₃陶瓷的低温冷烧结制备及性能研究[J]. 无机材料学报, 2022, 37(8): 903-910.
[10]	吴秋琴, 姚奋发, 金传洪, 郑遗凡. 碳纳米管内填充生长超细一维亚化学计量比氧化钨纳米线[J]. 无机材料学报, 2022, 37(4): 413-419.
[11]	白志强, 赵璐, 白云峰, 冯锋. MXenes的制备、性质及其在肿瘤诊疗中的研究进展[J]. 无机材料学报, 2022, 37(4): 361-375.
[12]	李江, 丁继扬, 黄新友. 稀土离子掺杂Gd₂O₂S闪烁陶瓷的研究进展[J]. 无机材料学报, 2021, 36(8): 789-806.
[13]	刘芳芳, 传秀云, 杨扬, 李爱军. 氮/硫共掺杂对纤水镁石模板碳纳米管电化学性能的影响[J]. 无机材料学报, 2021, 36(7): 711-717.
[14]	李子宜, 章佳佳, 邹小勤, 左家玉, 李俊, 刘应书, 裴有康. 菱沸石分子筛膜的合成调控与气体分离研究进展[J]. 无机材料学报, 2021, 36(6): 579-591.
[15]	方华靖, 赵泽天, 武文婷, 汪宏. 柔性电致变色器件研究进展[J]. 无机材料学报, 2021, 36(2): 140-151.