等离子喷涂Cr3C2-NiCr及其表面化学镀Ni涂层的摩擦学特性

无机材料学报

等离子喷涂Cr₃C₂-NiCr及其表面化学镀Ni涂层的摩擦学特性

李剑锋; 黄静琪; 丁传贤

中国科学院上海硅酸盐研究所, 上海 200050

收稿日期:2000-01-28 修回日期:2000-02-28 出版日期:2001-01-20 网络出版日期:2001-01-20

Tribological Properties of Plasma-Sprayed Cr₃C₂-NiCr Coating without or with Electroless Plated Ni

LI Jian-Feng; HUANG Jing-Qi; DING Chuan-Xian

Shanghai Institute of Ceramics; Chinese Academy of Sciences; Shanghai 200050; China

Received:2000-01-28 Revised:2000-02-28 Published:2001-01-20 Online:2001-01-20

摘要/Abstract

摘要： 考察了等离子喷涂Ｃｒ_３Ｃ_２－ＮｉＣｒ涂层及其表面化学镀Ｎｉ镀层通过不同配副组成摩擦副的摩擦学特性，并应用ＳＥＭ、ＸＲＤ和ＸＰＳ对磨痕进行了分析．结果发现：等离子喷涂Ｃｒ_３Ｃ_２－ＮｉＣｒ涂层及其表面化学镀Ｎｉ镀层自配副组成摩擦副，均表现出较大的摩擦系数和磨损系数；但是，Ｃｒ_３Ｃ_２－ＮｉＣｒ涂层表面化学镀Ｎｉ镀层与Ｃｒ_３Ｃ_２－ＮｉＣｒ涂层配副组成摩擦副，在于摩擦条件下，能达到０．１２的摩擦系数和接近１０^－６ｍｍ³（Ｎｍ）^－１的磨损系数．上述结果是由于Ｃｒ_３Ｃ_２－ＮｉＣｒ涂层的磨损机理从强烈的层状颗粒剥落转变为沿气孔和微裂纹等处的颗粒断裂．

关键词: 等离子喷涂, Cr₃C₂-NiCr涂层, 化学镀Ni, 摩擦学特性

Abstract: Tribological properties of plasma-sprayed Cr₃C₂-NiCr coatings without or with electroless plated
Ni were investigated, and the worn surfaces were analyzed by employing SEM, XRD and XPS. It was found that both the self-mated rubbing pairs consisting
of the Cr₃C₂-NiCr coating and the Cr₃C₂-NiCr coating electroless plated with Ni displayed higher friction coefficient and wear coefficient.
However, The rubbing pair of the Cr₃C₂-NiCr coating electroless plated with Ni against the Cr₃C₂-NiCr coating had a friction
coefficient of 0.12 and a wear coefficient close to 10^-6mm³(Nm)^-1 even if under dry sliding. The improvement in tribological properties
could be attributed to that the wear mechanism of Cr₃C₂-NiCr coating transformed to particle fracturing along pores and microcracks from the
intensive spalling along splat interfaces.

Key words: plasma spraying, Cr₃C₂-NiCr coating, electroless Ni plating, tribological property

中图分类号:

TQ174

李剑锋,黄静琪,丁传贤. 等离子喷涂Cr₃C₂-NiCr及其表面化学镀Ni涂层的摩擦学特性[J]. 无机材料学报.

LI Jian-Feng,HUANG Jing-Qi,DING Chuan-Xian. Tribological Properties of Plasma-Sprayed Cr₃C₂-NiCr Coating without or with Electroless Plated Ni[J]. Journal of Inorganic Materials.

参考文献

[1] Hirvonen J-P, Koskinen J, Jervis J R, et al. Surface and Coatings Technology, 1996, 80: 139--150.
[2] Barbezat G, Moens J R, Nicoll A R. Materials & Design, 1992, 13 (3): 145--148.
[3] Takeuchi J, Muratay Y, Haraday Y, et al. Proceedings of the 15th International Thermal Spray Conference. Nice, France, 1998. 1425--1430.
[4] 金元生, 夏为民, 程华. 清华大学学报, 1992, 32 (5): 17--25.
[5] Mohanty M, Smith R W, Bonte M D, et al. Wear, 1996, 198: 251--266.
[6] Li J F, Ding C X, Huang J Q, et al. Wear, 1997, 211: 177--184.
[7] Czichos H, Klaffke D, Santner E, et al. Wear, 1995, 190: 155--161.
[8] Jin Y S, Li M Y, Wang Y. Wear, 1994, 172: 147--154.
[9] Corte C D, Sliney H E. Tribological Transactions, 1995, 38 (4): 845--850.
[10] Hajdu J. Plating & Surface Finishing, 1996, 83 (9): 29--33.
[11] 余来贵, 张绪寿. 摩擦学学报，1992, 12 (2): 123--130.
[12] Dennis J K, Sheikh S T, Silverstone E C. Transactions of the Institute of Metal Finishing, 1981, 59: 118--122.
[13] 吴玉程, 黄录官, 邓宗钢, 等. 摩擦学学报, 1992, 12 (2): 144--152.
[14] 刘颍, 陈家钊, 涂铭旌, 等. 摩擦学学报, 1998, 18 (1): 71--74.
[15] Li J, Zhang Y, Huang J, et al. Journal of Thermal Spray Technology, 1998, 7 (2): 242--246.
[16] 王世中, 臧鑫士. 现代材料研究方法. 北京：北京航空航天大学出?版社. 1991. 259--260.
[17] Su Y S, Lin J S. Wear, 1993, 166: 27--35.
[18] Li C, Ohmori A, Mcpherson R. Journal of Materials Science, 1997, 32: 997--1004.
[19] Smith R W, Novak R. Powder Metallurgy International, 1991, 23 (3): 147--152.
[20] Ahn H S, Roylance B J. Tribology International, 1992, 25 (4): 227--236.
[21] 迪安 A J. 兰氏化学手册[M]. 尚方久，操时杰，辛无名, 等译. 北京：科学?出版社，1991. 4--12.
[22] Wang Y, Jin Y, Wen S. Wear, 1988, 128: 277--290.

等离子喷涂Cr₃C₂-NiCr及其表面化学镀Ni涂层的摩擦学特性

Tribological Properties of Plasma-Sprayed Cr₃C₂-NiCr Coating without or with Electroless Plated Ni

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	梁锐辉, 钟鑫, 洪督, 黄利平, 牛亚然, 郑学斌. Yb₂O₃改性硅黏结层的环境障涂层体系耐高温水氧腐蚀行为研究[J]. 无机材料学报, 2025, 40(4): 425-432.
[2]	马文, 申喆, 刘琪, 高元明, 白玉, 李荣星. 悬浮液等离子喷涂制备Y₂O₃涂层及耐等离子刻蚀性[J]. 无机材料学报, 2024, 39(8): 929-936.
[3]	李捷, 罗志新, 崔阳, 张广珩, 孙鲁超, 王京阳. 大气等离子喷涂Y₃Al₅O₁₂/Al₂O₃陶瓷涂层的CMAS腐蚀抗力[J]. 无机材料学报, 2024, 39(6): 671-680.
[4]	潘洋洋, 梁波, 洪督, 祁志祥, 牛亚然, 郑学斌. TiAl合金表面TiAlCrY/YSZ涂层高温长时间服役性能[J]. 无机材料学报, 2023, 38(1): 105-112.
[5]	洪督, 牛亚然, 李红, 钟鑫, 郑学斌. 等离子喷涂TiC-Graphite复合涂层摩擦磨损性能[J]. 无机材料学报, 2022, 37(6): 643-650.
[6]	代钊,王铭,王双,李静,陈翔,汪大林,祝迎春. 氧化锆基微量元素共掺杂羟基磷灰石增韧涂层研究[J]. 无机材料学报, 2020, 35(2): 179-186.
[7]	范佳锋,张小锋,周克崧,刘敏,邓畅光,邓春明,牛少鹏,邓子谦. 镀铝改性对PS-PVD 7YSZ热障涂层抗CMAS腐蚀影响机制[J]. 无机材料学报, 2019, 34(9): 938-946.
[8]	谢玲玲, 牛亚然, 王亮, 陈文亮, 郑学斌, 黄贞益. 等离子喷涂ZrC基涂层逐道逐层沉积残余应力模拟与实验验证[J]. 无机材料学报, 2019, 34(7): 768-774.
[9]	周炎哲, 刘敏, 杨焜, 曾威, 宋进兵, 邓春明, 邓畅光. 大气等离子喷涂MoSi₂-30Al₂O₃电热涂层的组织结构及性能[J]. 无机材料学报, 2019, 34(6): 646-652.
[10]	陈书赢, 马国政, 何鹏飞, 刘喆, 刘明, 邢志国, 王海斗, 王海军. 基于粒子飞行特性及铺展行为的WC-10Co4Cr涂层孔隙形成机理研究[J]. 无机材料学报, 2018, 33(8): 895-902.
[11]	张小锋, 周克崧, 刘敏, 邓春明, 牛少鹏, 许世鸣. 等离子喷涂-物理气相沉积Si/莫来石/Yb₂SiO₅环境障涂层[J]. 无机材料学报, 2018, 33(3): 325-330.
[12]	孙旭轩, 陈宏飞, 杨光, 刘斌, 高彦峰. YSZ-Ti₃AlC₂热障涂层及其高温自愈合行为[J]. 无机材料学报, 2017, 32(12): 1269-1274.
[13]	于方丽, 白宇, 吴秀英, 王海军, 吴九汇. 等离子喷涂镍基可磨耗封严涂层抗腐蚀及耐磨性能分析[J]. 无机材料学报, 2016, 31(7): 687-693.
[14]	毛金元, 刘敏, 毛杰, 邓春明, 曾德长, 徐林. 等离子喷涂制备ZrB₂-MoSi₂复合涂层及其抗氧化性能[J]. 无机材料学报, 2015, 30(3): 282-286.
[15]	张小锋, 周克崧, 宋进兵, 邓春明, 牛少鹏, 邓子谦. 等离子喷涂-物理气相沉积7YSZ热障涂层沉积机理及其CMAS腐蚀失效机制[J]. 无机材料学报, 2015, 30(3): 287-293.