pH值对氮掺杂TiO2物化性质和光催化活性的影响

doi:10.3724/SP.J.1077.2008.00387

摘要/Abstract

摘要： 以TiCl₄为前驱体, 水合肼和氨水的混合溶液为氮源, 采用共沉淀法制备了可见光响应型氮掺杂二氧化钛(N-TiO₂)光催化剂, 重点研究了制备
过程中pH值对催化剂的微结构和光催化活性等物化性质的影响. 采用XRD、BET、UV-vis和XPS等表征方法对光催化剂性质进行了表征. 催化剂主要以锐钛矿相存在, 具有介孔结构和较高的比表面积(～90m²/g). 随着pH值增大, 锐钛矿相(101)面衍射峰逐步增强, 晶粒尺寸逐渐增大, 比表面积逐渐减小. XPS结果表明催化剂掺杂的氮主要以系列氮氧化物形式存在. 氮掺杂小幅降低了禁带宽度, 感光范围拓展到可见光区. 光催化降解实验表明, pH=3.5时, 催化剂的可见光降解效率最高, 为39.65%. 随着pH值增大, 催化剂可见光催化活性逐渐降低; 而在紫外光照射下, pH=9.5时, 催化活性最低; pH=5.5时, 催化活性最高.

关键词: pH值, 二氧化钛, 氮掺杂, 光催化, 可见光

Abstract: Visible-light-driven nitrogen-doped titanium dioxide (N-TiO₂) was synthesized by the method of coprecipitation, in which titanium tetrachloride was used as Ti-precursor and the mixed solution of ammonia and hydrazine hydrate as nitrogen resource. Effects of pH values on the physicochemical properties and the activities of the as-prepared N-TiO₂ catalysts were studied. The obtained photocatalysts are found to be of anatase phase, higher specific area, mesoporous structure and visible response by means of XRD, BET and UV-vis spectra analysis. With increasing pH values, the intensity of anatase (101) peaks enhances, and the crystallite size increases, while the BET specific area decreases. The doped impurities are found to be NO_x species,
which are confirmed by XPS. Minor band-gap narrowing and the visible-light response are due to nitrogen doping. The experiments of photodegradation of 4-chlorophenol show that the degradation ratio (39.65%) of the catalyst prepared at pH=3.5 is the highest under visible light irradiation. The photocatalytic activity decreases when pH values increase. Under UV light
irradiation, the catalyst prepared at pH=5.5 has the highest photocatalytic activity, while that derived from pH=9.5 has the lowest.

Key words: pH value, titanium dioxide, nitrogen-doped, photocatalysis, visible light

中图分类号:

TB383

柏源,孙红旗,金万勤. pH值对氮掺杂TiO₂物化性质和光催化活性的影响[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2008.00387.

BAI Yuan,SUN Hong-Qi,JIN Wan-Qin. Effects of pH Values on the Physicochemical Properties and Photocatalytic Activities of Nitrogen-doped TiO₂[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2008.00387.

参考文献

[1] Asahi R, Morikawa T, Ohwaki T, et al. Science, 2001, 293 (5528): 269--271.
[2] Sakthivel S, Janczarek M, Kisch H. J. Phys. Chem. B, 2004, 108 (50): 19384--19387.
[3] Irie H, Watanabe Y, Hashimoto K. J. Phys. Chem. B, 2003, 107 (23): 5483--5486.
[4] Chen X B, Lou Y B, Samia A C S, et al. Adv. Func. Mater., 2005, 15 (1): 41--49.
[5] Cheng Y P, Sun H Q, Jin W Q, et al. Chem. Eng. J, 2007, 128 (2-3): 127--133.
[6] Sun H Q, Bai Y, Cheng Y P, et al. Ind. Eng. Chem. Res., 2006, 45 (14): 4971--4976.
[7] 孙红旗, 程友萍, 金万勤, 等. 化工学报, 2006, 57 (7): 1570--1574.
[8] 张青红, 高濂, 孙静(ZHANG Qing-Hong, et al). 无机材料学报(Journal of Inorganic Materials), 2002, 17 (3): 415--421.
[9] Yu J G, Su Y R, Cheng B, et al. J. Mol. Catal. A., 2006, 258 (1-2): 104--112.
[10] 李志杰, 侯博, 徐耀, 等. 物理化学学报, 2005, 21 (3): 229--233.
[11] 任学昌, 史载锋, 孔令仁. 催化学报, 2006, 27 (9): 815--822.
[12] Yin S, Aita Y, Komatsu M, et al. J. Mater. Chem., 2005, 15 (6): 674--682.
[13] Yin S, Aita Y, Konmatsu M, et al. J. Eur. Ceram. Soc., 2006, 26 (13): 2735--2742.
[14] 闫鹏飞, 周德瑞, 王建强, 等. 高等学校化学学报, 2002, 23 (12): 2317--2321.
[15] 石金娥, 闫吉昌, 王悦宏, 等. 高等学校化学学报, 2006, 27 (8): 1513--1517.
[16] Hong X T, Wang Z P, Cai W M, et al. Chem. Mater., 2005, 17 (6): 1548--1552.
[17] Pottier A, Chaneca C, Tronca E, et al. J. Mater. Chem., 2001, 11 (4): 1116--1121.
[18] 张青红, 高濂, 郭景坤(ZHANG Qing-Hong, et al). 无机材料学报(Journal of Inorganic Materials), 2000, 15 (6): 992--998.
[19] Yu J C, Yu J G, Ho W K, et al. Chem. Mater., 2002, 14 (9): 3808--3816.
[20] Peng T Y, Song H B, Xiao J R, et al. J. Non-Cryst. Solids, 2006, 352 (30-31): 3167--3174.
[21] Sakthivel S, Kisch H. Angew. Chem. Int. Ed., 2003, 42 (40): 4908--4911.
[22] Yin S, Sato T. Ind. Eng. Chem. Res., 2000, 39 (12): 4526--4530.
[23] Hoffmann M R, Martin S T, Choi W, et al. Chem, Rev., 1995, 95 (1), 69--96.
[24] Nakamura I, Negishi N, Kutsuna S, et al. J. Mol. Catal. A, 2000, 161 (1-2): 205--212.
[25] Diebold U. Surf. Sci. Rep., 2003, 48 (5-8), 53--229.
[26] Nakaoka Y, Nosaka Y. J. Photochem. Photobiol. A, 1997, 110 (3): 299--305.
[27] Kasuga T, Hiramatsu M, Hoson A, et al. Adv. Mater., 1999, 11 (15): 1307--1311.

pH值对氮掺杂TiO₂物化性质和光催化活性的影响

Effects of pH Values on the Physicochemical Properties and Photocatalytic Activities of Nitrogen-doped TiO₂

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	马彬彬, 钟婉菱, 韩涧, 陈椋煜, 孙婧婧, 雷彩霞. ZIF-8/TiO₂复合介观晶体的制备及光催化活性[J]. 无机材料学报, 2024, 39(8): 937-944.
[2]	曹青青, 陈翔宇, 吴健豪, 王筱卓, 王乙炫, 王禹涵, 李春颜, 茹菲, 李兰, 陈智. SiO₂增强自敏性氮化碳微球可见光降解盐酸四环素的研究[J]. 无机材料学报, 2024, 39(7): 787-792.
[3]	王兆阳, 秦鹏, 蒋胤, 冯小波, 杨培志, 黄富强. 三明治结构钌插层二氧化钛光催化四环素降解性能研究[J]. 无机材料学报, 2024, 39(4): 383-389.
[4]	叶茂森, 王耀, 许冰, 王康康, 张胜楠, 冯建情. II/Z型Bi₂MoO₆/Ag₂O/Bi₂O₃异质结可见光催化降解四环素[J]. 无机材料学报, 2024, 39(3): 321-329.
[5]	李秋实, 殷广明, 吕伟超, 王怀尧, 李婧琳, 杨红光, 关芳芳. Na⁺/g-C₃N₄材料的制备及光催化降解亚甲基蓝机理[J]. 无机材料学报, 2024, 39(10): 1143-1150.
[6]	李跃军, 曹铁平, 孙大伟. S型异质结Bi₄O₅Br₂/CeO₂的制备及其光催化CO₂还原性能[J]. 无机材料学报, 2023, 38(8): 963-970.
[7]	王新玲, 周娜, 田亚文, 周明冉, 韩静茹, 申远升, 胡执一, 李昱. SnS₂/ZIF-8衍生二维多孔氮掺杂碳纳米片复合材料的锂硫电池性能研究[J]. 无机材料学报, 2023, 38(8): 938-946.
[8]	伍林, 胡明蕾, 王丽萍, 黄少萌, 周湘远. TiHAP@g-C₃N₄异质结的制备及光催化降解甲基橙[J]. 无机材料学报, 2023, 38(5): 503-510.
[9]	凌洁, 周安宁, 王文珍, 贾忻宇, 马梦丹. Cu/Mg比对Cu/Mg-MOF-74的CO₂吸附性能的影响[J]. 无机材料学报, 2023, 38(12): 1379-1386.
[10]	孙晨, 赵昆峰, 易志国. 甲烷完全催化氧化研究进展[J]. 无机材料学报, 2023, 38(11): 1245-1256.
[11]	王梦桃, 索军, 方东, 易健宏, 刘意春, Olim RUZIMURADOV. ITO/TiO₂纳米管阵列复合材料的可见光催化性能[J]. 无机材料学报, 2023, 38(11): 1292-1300.
[12]	贾鑫, 李晋宇, 丁世豪, 申倩倩, 贾虎生, 薛晋波. Pd纳米颗粒协同氧空位增强TiO₂光催化CO₂还原性能[J]. 无机材料学报, 2023, 38(11): 1301-1308.
[13]	马润东, 郭雄, 施凯旋, 安胜利, 王瑞芬, 郭瑞华. MoS₂/g-C₃N₄ S型异质结的构建及光催化性能研究[J]. 无机材料学报, 2023, 38(10): 1176-1182.
[14]	马心全, 李喜宝, 陈智, 冯志军, 黄军同. S型异质结BiOBr/ZnMoO₄的构建及光催化降解性能研究[J]. 无机材料学报, 2023, 38(1): 62-70.
[15]	陈瀚翔, 周敏, 莫曌, 宜坚坚, 李华明, 许晖. CoN/g-C₃N₄ 0D/2D复合结构及其光催化制氢性能研究[J]. 无机材料学报, 2022, 37(9): 1001-1008.