Influence of Third Component on Preparing Mullite Fibers

doi:10.3724/SP.J.1077.2007.00423

Journal of Inorganic Materials

• Research Paper • Previous Articles Next Articles

Influence of Third Component on Preparing Mullite Fibers

YAO Shu-Yu¹, CHEN Yun-Bo², CUI Hong-Zhi¹, LIU Li-Qiang¹, WANG Shu-Feng¹

1. School of Materials Science and Engineering, Shandong University of Science and Technology, Qingdao 266510, China; 2. Beijing Research Institute of Mechanical & Electrical Technology, Beijing 100083, China

Received:2006-05-26 Revised:2006-08-07 Published:2007-05-20 Online:2007-05-20

Abstract

Abstract: Mullite continuous fibers were prepared in Al₂O₃-SiO₂ system by separately adding FeO, Na₂O and MgO with a melt/drawing method. The forming mechanism of mullite was investigated by using SEM, XRD and SEM-EDS. The results show that the mullite fibers with a needle structure can be prepared from the method. This is a new approach of preparing mullite continuous fibers in industry which comes from producing glass fibers process with a crucible.

Key words: mullite, fiber, prepare, melt/drawing

CLC Number:

TB343

YAO Shu-Yu,CHEN Yun-Bo,CUI Hong-Zhi,LIU Li-Qiang,WANG Shu-Feng. Influence of Third Component on Preparing Mullite Fibers[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2007.00423.

[1]	ZHENG Chen, WANG Xiangning, YUAN Henan, YANG Jiawei, LI Chuanjian, WANG Huadong. Mechanical Property Failure of Alumina Fiber Reinforced Silica Composite [J]. Journal of Inorganic Materials, 2026, 41(3): 331-339.
[2]	ZHANG Yunbo, WANG Bing, LI Wei, SONG Quzhi, DU Yi’ang, WANG Yingde. Size Effect of Nanosheet on BN Fibers Derived from BNNS/Polyborazine Hybrid Precursor [J]. Journal of Inorganic Materials, 2026, 41(3): 359-369.
[3]	YUAN Wang, HU Jianbao, ZHOU Liang, KAN Yanmei, ZHANG Xiangyu, DONG Shaoming. Effect of Argon Atmosphere Heat Treatment on Mechanical Properties and Microstructural Evolution of Shicolon-II SiC Fibers [J]. Journal of Inorganic Materials, 2026, 41(1): 119-128.
[4]	CHEN Bin, REN Ke, WANG Yiguang. Evolution of Mechanical Properties of Mini-SiC_f/SiC Composites at High Temperatures over a Long Period of Time [J]. Journal of Inorganic Materials, 2025, 40(9): 971-980.
[5]	GOU Yanzi, KANG Weifeng, WANG Pengren. Influence of Sintering Conditions on Preparation of Nearly Stoichiometric SiC Fibers with Highly Crystalline Microstructure [J]. Journal of Inorganic Materials, 2025, 40(4): 405-414.
[6]	GAO Chenguang, SUN Xiaoliang, CHEN Jun, LI Daxin, CHEN Qingqing, JIA Dechang, ZHOU Yu. SiBCN-rGO Ceramic Fibers Based on Wet Spinning Technology: Microstructure, Mechanical and Microwave-absorbing Properties [J]. Journal of Inorganic Materials, 2025, 40(3): 290-296.
[7]	WANG Yue, WANG Xin, YU Xianli. Room-temperature Ferromagnetic All-carbon Films Based on Reduced Graphene Oxide [J]. Journal of Inorganic Materials, 2025, 40(3): 305-313.
[8]	LI Wei, XU Zhiming, GOU Yanzi, YIN Senhu, YU Yiping, WANG Song. Preparation and Performance of Sintered SiC Fiber-bonded Ceramics [J]. Journal of Inorganic Materials, 2025, 40(2): 177-183.
[9]	WANG Hongbin, WANG Leying, LUO Linghong, CHENG Liang, XU Xu. Electrolytic CO₂ Performance of La_0.3Sr_0.6Ti_1-_xNi_xO_3-_δ-based Fiber Fuel Electrode for Solid Oxide Electrolysis Cell [J]. Journal of Inorganic Materials, 2025, 40(11): 1212-1220.
[10]	LI Zhenghao, LI Jingming, ZHANG Yuxiang, YUAN Bo, ZHANG Kai, ZHU Xiangdong. Preparation and in vitro Osteogenic Activity Evaluation of Mn/nHA Coated CF/PEEK Composite [J]. Journal of Inorganic Materials, 2025, 40(10): 1145-1152.
[11]	GOU Yanzi, KANG Weifeng, ZHANG Qingyu. Preparation of Nearly Stoichiometric SiC(Ti) Fibers with Highly Crystalline Microstructure from Polytitanocarbosilane [J]. Journal of Inorganic Materials, 2024, 39(12): 1377-1383.
[12]	ZHAO Yawen, QU Fajin, WANG Yanyi, WANG Zhiwen, CHEN Chusheng. Preparation and Properties of Aluminum Silicate Fiber Supported PtTFPP-PDMS Flexible Oxygen Sensing Components [J]. Journal of Inorganic Materials, 2024, 39(10): 1084-1090.
[13]	SHI Weigang, ZHANG Chao, LI Mei, WANG Jing, ZHANG Chengyu. 2D-SiC_f/SiC Interlaminar Mode I Fracture Testing and Characterization [J]. Journal of Inorganic Materials, 2024, 39(1): 45-50.
[14]	LI Yuejun, CAO Tieping, SUN Dawei. Bi₄O₅Br₂/CeO₂ Composite with S-scheme Heterojunction: Construction and CO₂ Reduction Performance [J]. Journal of Inorganic Materials, 2023, 38(8): 963-970.
[15]	WU Shuang, GOU Yanzi, WANG Yongshou, SONG Quzhi, ZHANG Qingyu, WANG Yingde. Effect of Heat Treatment on Composition, Microstructure and Mechanical Property of Domestic KD-SA SiC Fibers [J]. Journal of Inorganic Materials, 2023, 38(5): 569-576.

Influence of Third Component on Preparing Mullite Fibers

PDF (PC)

Knowledge

Cited

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments