Visible-light-driven Activation of Persulfate by RGO/g-C3N4 Composites for Degradation of BPA in Wastewater

doi:10.15541/jim20190334

Abstract

Abstract:

Persistent organic pollutants can be effectively removed by photocatalytic oxidation, which reveals potential application prospects in the field of wastewater purification. Binary reduced graphene oxide and graphitic carbon nitride (RGO/g-C₃N₄) visible-light photocatalyst was successfully fabricated by the freeze drying assisted thermal polymerization method with urea and dicyandiamide as raw materials, respectively. The morphologies, structures and optical properties were characterized by various techniques. It was found that g-C₃N₄ and RGO nanostructures formed an intimate contact across the heterojunction interface. The photodegradation performances of catalysts were evaluated by removing bisphenol A (BPA) with the activation of persulfate (PS). The results indicated that the photocatalytic activities of photocatalysts were enhanced with the addition of PS as an oxidant and electron acceptor under visible light irradiation (λ>420 nm). Moreover, BPA was almost completely removed by RGO/g-C₃N₄ prepared with urea as raw material in 40 min. After five recovery tests, the removal efficiency of BPA for the catalyst was up to 80% within 40 min under visible light irradiation, which exhibited superior stability.

Key words: g-C₃N₄, reduced graphene oxide, visible-light photocatalysis, persulfate

CLC Number:

TQ174

ZHANG Sai, ZOU Yingtong, CHEN Zhongshen, LI Bingfeng, GU Pengcheng, WEN Tao. Visible-light-driven Activation of Persulfate by RGO/g-C₃N₄ Composites for Degradation of BPA in Wastewater[J]. Journal of Inorganic Materials, 2020, 35(3): 329-336.

Figures/Tables 10

Fig. 1 XRD patterns of GO, CNU, G-CNU, CND, and G-CND samples

Fig. 2 FT-IR spectra of GO, CNU, G-CNU, CND, and G-CND samples

Fig. 3 TEM images of (a) CND, (b) G-CND, (c) CNU, and (d) G-CNU photocatalysts

Fig. 4 N2 adsorption-desorption isotherms of CND, G-CND, CNU and G-CNU samples

Fig. 5 (a) C1s, (b) N1s and (c) O1s XPS spectra of CND, G-CND, CNU and G-CNU samples

Fig. 6 (a) The UV-Vis DRS and (b) the (αhν)1/2-hν curves of CND, G-CND, CNU and G-CNU photocatalysts

Fig. 7 PL spectra of different photocatalysts

Fig. 8 (a-c) Catalytic activities of photocatalysts for BPA degradation under different conditions, and (d) effects of solutionpH on BPA removal over G-CNU catalysts by activating PS under visible light irradiation (λ>420 nm) (a) Visible light; (b) PS and (c) visible light/PS; Reaction conditions: C0(BPA) = 10 mg·L-1, C0(catalyst) = 0.5 g·L-1, C0(PS) = 1.0 g·L-1

Fig. 9 Cycling tests in degradation of BPA over G-CNU by PS activation under visible light irradiation (λ>420 nm)

Fig. 10 (a) Effect of different radical scavengers on BPA degradation in the G-CNU suspension under visible light irradiation (λ>420 nm) with the addition of PS, and (b) schematic diagram of photodegradation mechanism Reaction conditions: C0(BPA) = 10 mg·L-1, C0(catalyst) = 0.5 g·L-1, C0(PS) = 1.0 g·L-1

References 31

[1]	ZHANG SAI, GU PENG-CHENG, MA RAN , et al. Recent developments in fabrication and structure regulation of visible- light-driven g-C₃N_4-based photocatalysts towards water purification: a critical review. Catalysis Today, 2019,335:65-77.
[2]	LI CUI-XIA, JIN HAI-ZE, YANG ZHI-ZHONG , et al. Preparation and photocatalytic properties of mesoporous RGO/TiO₂ composites. Journal of Inorganic Materials, 2017,32(4):357-364.
[3]	WANG XIN-CHEN, MAEDA K, THOMAS A , et al. A metal-free polymeric photocatalyst for hydrogen production from water under visible light. Nature Materials, 2009,8:76-80.
[4]	ONG W J, TAN L L, NG Y H , et al. Graphitic carbon nitride (g-C₃N₄)-based photocatalysts for artificial photosynthesis and environmental remediation: are we a step closer to achieving sustainability? Chemical Reviews, 2016,116(12):7159-7329.
[5]	YAN XIN, LU JIN-HUA, HUI XIAO-YAN , et al. Preparation and visible light photocatalytic property of g-C₃N₄/MoS₂ nanosheets/ GO ternary composite photocatalyst. Journal of Inorganic Materials, 2018,33(5):515-520.
[6]	XIANG QUAN-JUN, YU JIA-GUO, JARONIEC M . Preparation and enhanced visible-light photocatalytic H₂-production activity of graphene/C₃N₄ composites. The Journal of Physical Chemistry C, 2011,115(15):7355-7363.
[7]	ZHANG SAI, HU CHUN, JI HUAN-HUAN , et al. Facile synthesis of nitrogen-deficient mesoporous graphitic carbon nitride for highly efficient photocatalytic performance. Applied Surface Science, 2019,478:304-312.
[8]	HONG ZHEN-HUA, SHEN BIAO, CHEN YI-LIN , et al. Enhancement of photocatalytic H₂ evolution over nitrogen-deficient graphitic carbon nitride. Journal of Materials Chemistry A, 2013,1(38):11754-11761.
[9]	JIANG LONG-BO, YUAN XING-ZHONG, YANG PAN , et al. Doping of graphitic carbon nitride for photocatalysis: a review. Applied Catalysis B: Environmental, 2017,217:388-406.
[10]	ZHANG SAI, LIU YANG, GU PENG-CHENG , et al. Enhanced photodegradation of toxic organic pollutants using dual-oxygen- doped porous g-C₃N₄: mechanism exploration from both experimental and DFT studies. Applied Catalysis B: Environmental, 2019,248:1-10.
[11]	CHEN WEI, HE ZHI-CAI, HUANG GUO-BO , et al. Direct Z-scheme 2D/2D MnIn₂S₄/g-C₃N₄ architectures with highly efficient photocatalytic activities towards treatment of pharmaceutical wastewater and hydrogen evolution. Chemical Engineering Journal, 2019,359:244-253.
[12]	YANG YING, ZHAO HA-RUI, YANG HONGFEI , et al. In situ fabrication of reduced graphene oxide/mesoporous g-C₃N₄ nanosheets with excellent visible light activity. Journal of Environmental Chemical Engineering, 2018,6:890-897.
[13]	WANG JIAN, ZHU MING-YU, CHEN ZHONG-SHAN , et al. Polyacrylamide modified molybdenum disulfide composites for efficient removal of graphene oxide from aqueous solutions. Chemical Engineering Journal, 2019,361:651-659.
[14]	DONG SHU-YING, DING XU-HUI, GUO TENG , et al. Self- assembled hollow sphere shaped Bi₂WO₆/RGO composites for efficient sunlight-driven photocatalytic degradation of organic pollutants. Chemical Engineering Journal, 2017,316:778-789.
[15]	MONTEAGUDO J M, DURÁN A, SAN MARTÍN I , et al. Effect of sodium persulfate as electron acceptor on antipyrine degradation by solar TiO₂ or TiO₂/rGO photocatalysis. Chemical Engineering Journal, 2019,364:257-268.
[16]	LI YI-BING, ZHANG HAI-MIN, LIU PO-RUN , et al. Cross- linked g-C₃N₄/rGO nanocomposites with tunable band structure and enhanced visible light photocatalytic activity. Small, 2013,9(19):3336-3344.
[17]	GU YONG-PAN, YU YONG-ZHI, ZOU JING-YE , et al. The ultra- rapid synthesis of rGO/g-C₃N₄ composite via microwave heating with enhanced photocatalytic performance. Materials Letters, 2018,232:107-109.
[18]	ZHANG SAI, SONG SHUANG, GU PENG-CHENG , et al. Visible- light-driven activation of persulfate over cyano and hydroxyl group co-modified mesoporous g-C₃N₄ for boosting Bisphenol A degradation. Journal of Materials Chemistry A, 2019,7(10):5552-5560.
[19]	ANDREW LIN KUN-YI, ZHANG ZHI-YU . Degradation of Bisphenol A using peroxymonosulfate activated by one-step prepared sulfur-doped carbon nitride as a metal-free heterogeneous catalyst. Chemical Engineering Journal, 2017,313:1320-1327.
[20]	HUMMERS W S, OFFEMAN R E . Preparation of graphitic oxide. Journal of the American Chemical Society, 1958,80(6):1339-1339.
[21]	XIE YI, CHEN CHANG-LUN, REN XUE-MEI , et al. Coupling g-C₃N₄ nanosheets with metal-organic frameworks as 2D/3D composite for the synergetic removal of uranyl ions from aqueous solution. Journal of Colloid and Interface Science, 2019,550:117-127.
[22]	SHEN CONG-CONG, CHEN CHANG-LUN, WEN TAO , et al. Superior adsorption capacity of g-C₃N₄ for heavy metal ions from aqueous solutions. Journal of Colloid and Interface Science, 2015, 456:7-14.
[23]	LI XIAO-LIN, WANG HAI-LIANG, ROBINSON J T , et al. Simultaneous nitrogen doping and reduction of graphene oxide. Journal of the American Chemical Society, 2009,131(43):15939-15944.
[24]	LI JIANG-HUA, SHEN BIAO, HONG ZHEN-HUA , et al. A facile approach to synthesize novel oxygen-doped g-C₃N₄ with superior visible-light photoreactivity. Chemical Communications, 2012,48:12017-12019.
[25]	ZHANG LI-LI, SHI YI-LUN, WANG LIANG , et al. AgBr- wrapped Ag chelated on nitrogen-doped reduced graphene oxide for water purification under visible light. Applied Catalysis B: Environmental, 2018,220:118-125.
[26]	LAN HUA-CHUN, LI LI-LI, AN XIAO-QIANG , et al. Microstructure of carbon nitride affecting synergetic photocatalytic activity: hydrogen bonds vs. structural defects. Applied Catalysis B: Environmental, 2017,204:49-57.
[27]	WANG YAN-BIN, ZHAO XU, CAO DI , et al. Peroxymonosulfate enhanced visible light photocatalytic degradation Bisphenol A by single-atom dispersed Ag mesoporous g-C₃N₄ hybrid. Applied Catalysis B: Environmental, 2017,211:79-88.
[28]	WEI XIANG-NAN, OU CAI-LING, GUAN XIN-XIN , et al. Facile assembly of CdS-reduced graphene oxide heterojunction with enhanced elimination performance for organic pollutants in wastewater. Applied Surface Science, 2019,469:666-673.
[29]	OH W D, LOK L W, ANDREI V , et al. Enhanced photocatalytic degradation of Bisphenol A with Ag-decorated S-doped g-C₃N₄ under solar irradiation: performance and mechanistic studies. Chemical Engineering Journal, 2018,333:739-749.
[30]	LIU BO-CHUAN, QIAO MENG, WANG YAN-BIN , et al. Persulfate enhanced photocatalytic degradation of Bisphenol A by g-C₃N₄ nanosheets under visible light irradiation. Chemosphere, 2017,189:115-122.
[31]	ZHANG SHOU-WEI, GAO HUI-HUI, LIU XIA , et al. Hybrid 0D-2D Nanoheterostructures: in situ growth of amorphous silver silicates dots on g-C₃N₄ nanosheets for full-spectrum photocatalysis. ACS Applied Materials & Interfaces, 2016,8(51):35138-35149.

Visible-light-driven Activation of Persulfate by RGO/g-C₃N₄ Composites for Degradation of BPA in Wastewater

RichHTML

PDF (PC)

Knowledge

Cited

Abstract

Cite this article

share this article

Figures/Tables 10

References 31

Related Articles 15

Recommended Articles

Metrics

Comments

[1]	LI Qiushi, YIN Guangming, LÜ Weichao, WANG Huaiyao, LI Jinglin, YANG Hongguang, GUAN Fangfang. Preparation of Na⁺/g-C₃N₄ Materials and Their Photocatalytic Degradation Mechanism on Methylene Blue [J]. Journal of Inorganic Materials, 2024, 39(10): 1143-1150.
[2]	WU Lin, HU Minglei, WANG Liping, HUANG Shaomeng, ZHOU Xiangyuan. Preparation of TiHAP@g-C₃N₄ Heterojunction and Photocatalytic Degradation of Methyl Orange [J]. Journal of Inorganic Materials, 2023, 38(5): 503-510.
[3]	MA Rundong, GUO Xiong, SHI Kaixuan, AN Shengli, WANG Ruifen, GUO Ruihua. S-type Heterojunction of MOS₂/g-C₃N₄: Construction and Photocatalysis [J]. Journal of Inorganic Materials, 2023, 38(10): 1176-1182.
[4]	XUE Hongyun, WANG Congyu, MAHMOOD Asad, YU Jiajun, WANG Yan, XIE Xiaofeng, SUN Jing. Two-dimensional g-C₃N₄ Compositing with Ag-TiO₂ as Deactivation Resistant Photocatalyst for Degradation of Gaseous Acetaldehyde [J]. Journal of Inorganic Materials, 2022, 37(8): 865-872.
[5]	HONG Jiahui, MA Ran, WU Yunchao, WEN Tao, AI Yuejie. CoN_x/g-C₃N₄ Nanomaterials Preparation by MOFs Self-sacrificing Template Method for Efficient Photocatalytic Reduction of U(VI) [J]. Journal of Inorganic Materials, 2022, 37(7): 741-749.
[6]	SUN Ming, SHAO Puzhen, SUN Kai, HUANG Jianhua, ZHANG Qiang, XIU Ziyang, XIAO Haiying, WU Gaohui. First-principles Study on Interface of Reduced Graphene Oxide Reinforced Aluminum Matrix Composites [J]. Journal of Inorganic Materials, 2022, 37(6): 651-659.
[7]	LI Hao, TANG Zhihong, ZHUO Shangjun, QIAN Rong. High Performance of Room-temperature NO₂ Gas Sensor Based on ZIF8/rGO [J]. Journal of Inorganic Materials, 2021, 36(12): 1277-1282.
[8]	SHU Mengyang, LU Jialin, ZHANG Zhijie, SHEN Tao, XU Jiayue. CsPbBr₃ Perovskite Quantum Dots/Ultrathin C₃N₄ Nanosheet 0D/2D Composite: Enhanced Stability and Photocatalytic Activity [J]. Journal of Inorganic Materials, 2021, 36(11): 1217-1222.
[9]	LI Neng,KONG Zhouzhou,CHEN Xingzhu,YANG Yufei. Research Progress of Novel Two-dimensional Materials in Photocatalysis and Electrocatalysis [J]. Journal of Inorganic Materials, 2020, 35(7): 735-747.
[10]	XU Shichao,ZHU Tianzhe,QIAO Yang,BAI Xuejian,TANG Nan,ZHENG Chunming. Fabrication of Z-scheme BiVO₄/GO/g-C₃N₄ Photocatalyst with Efficient Visble-light Photocatalytic Performance [J]. Journal of Inorganic Materials, 2020, 35(7): 839-846.
[11]	JIANG Li, GAO Huihui, CAO Ruya, ZHANG Shouwei, LI Jiaxing. Construction of Novel Three Dimensionally Macroporous g-C₃N₄ for Efficient Adsorption/Photocatalytic Reduction of U(VI) [J]. Journal of Inorganic Materials, 2020, 35(3): 359-366.
[12]	WANG Xucong, DENG Hao, JIANG Zhongyi, YUAN Liyong. Photocatalytic Reduction of Re (VII) on Amorphous TiO₂/g-C₃N₄ Derived from Different N Sources [J]. Journal of Inorganic Materials, 2020, 35(12): 1340-1348.
[13]	ZHANG Sheng, JIANG Yi, JI Yuan-Yuan, DU Ying, SHENG Zhen-Huan, YIN Jing-Zhou, LI Qiao-Qi, ZHANG Li-Li. Attapulgite/g-C₃N₄ Composites: Synthesis and Electrocatalytic Oxygen Evolution Property [J]. Journal of Inorganic Materials, 2019, 34(8): 803-810.
[14]	WEI Ju-Meng, LÜ Qiang, WANG Ben-Chi, PAN Jia-Le, YE Xiang-Ju, SONG Chang-Chun. Synthesis of Cubic-relievo Ag₃PO₄ with High Visible-light Photocatalytic Activity [J]. Journal of Inorganic Materials, 2019, 34(7): 786-790.
[15]	Zi-Ya LIU, Ru-Ya CAO, Man-Ying ZHANG. Preparation and Property of Polyethersulfone Ultrafiltration Membranes with Mesoporous-graphitic-C₃N₄/Ag [J]. Journal of Inorganic Materials, 2019, 34(5): 478-486.