Low-temperature Hydrothermal Synthesis of MnOOH Nanorods

doi:10.3724/SP.J.1077.2006.01249

Abstract

Abstract: MnOOH nanorods were synthesized hydrothermally at 130℃ for 16h, by using KMnO₄ and N₄(CH₂)₆ as main materials. The as-prepared samples were characterized by X-ray powder diffraction (XRD), transmission electron microscope (TEM), and high resolution transmission electron microscope (HRTEM). The effects of both molar ratios between reactants and reaction temperature on the products were investigated. The results show that the as-prepared MnOOH nanorods are with a monoclinic single phase, rod-like morphology and single crystalline nature.

Key words: MnOOH, hydrothermal synthesis, nanorodsenddocument

CLC Number:

O648
TB383

ZHANG Yuan-Guang,CHEN You-Cun. Low-temperature Hydrothermal Synthesis of MnOOH Nanorods[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2006.01249.

References

[1] Kovtyukhova N I, Mallouk T E. Chem. Eur. J., 2002, 8: 4355--4359.
[2] Han W Q, Fan S S, Li Q Q, et al. Science, 1997, 277: 1287--1290.
[3] Martin R. Science, 1994, 266: 1961--1963.
[4] Pacholski C, Kornowski A, Weller H. Angew. Chem., 2002, 114: 1234--1239.
[5] Yang J, Xue C, Yu S H, et al. Angew. Chem., 2002, 114: 4891--4896.
[6] Bach S, Henry M, Baffier N, et al. J. Solid State Chem., 1990, 88: 325--329.
[7] Bach S, Pereira-Ramos J P, Baffier N, et al. Electrochim. Acta, 1991, 36: 1595--1599.
[8] Hunter J. J. Solid State Chem., 1981, 39: 142--145.
[9] Bach S, Pereira-Ramos J P, Baffier N. J. Solid State Chem., 1995, 120: 70--76.
[10] Al-Sagheer F A, Zaki, M I. Colloid Surface, 2000, A 173: 193--197.
[11] Cordoba de Torresi S I, Gorenstein A. Electrochim. Acta, 1992, 37: 2015--2018.
[12] Kanasaku T, Amezawa K, Yamamoto N. Solid State Ionics, 2000, 133: 51--56.
[13] Brock S L, Duan N, Rong T Z, et al. Chem. Mater., 1998, 10: 2619--2623.
[14] Wang X, Li Y D. Chem. Commun., 2002. 764--766.
[15] Wang X, Li Y D. J. Am. Chem. Soc., 2002, 124: 2881--2885.
[16] Xiong Y J, Xie Y. Chem. Eur. J. 2003, 9: 1645--1648.
[17] Wang W Z, Xu C K, Wang G H, et al. Adv. Mater., 2002, 14: 837--843.
[18] 张治安, 杨邦朝, 邓梅根, 等(ZHANG Zhi-An, et al). 无机?
材料学报(Journal of Inorganic Materials), 2005, 20 (3): 529--536.
[19] Shamma P K, Whittingham M S. Mater. Lett., 2001, 48: 319--313.
[20] Ocana M. Colloid Polyn. Sci., 2000, 278: 443--447.
[21] 朱归胜, 徐华蕊, 廖春图, 等 (ZHU Gui-Sheng, et al). 无
机材料学报(Journal of Inorganic Materials), 2005, 20 (2): 479--483.
[22] Zhang Y G, Liu Y, Guo F, et al. Solid State Commun., 2005, 134: 523--527.
[23] 董喜燕, 张兴堂, 程纲, 等(Dong Xi-Yian, et al).
化学学报(Acta Chimica Sinica), 2004, 62: 2441--2443.