Effects of Vickers Cracks on the Mechanical Properties of Solid-phase-sintered Silicon Carbide Ceramics

doi:10.3724/SP.J.1077.2012.11650

Abstract

Abstract: In order to study the effects of Vickers cracks on the mechanical properties of solid-phase-sintered silicon carbide (SSiC for short) ceramics, the indentation cracks and the crack profiles were observed after loading 0.1–100 N loads on the SSiC samples by SEM. The critical indentation load for Vickers crack initiation in SSiC ceramics lies between 0.1 N and 0.2 N. Indentations by loads lower than 0.5 N have limited influence on bending strength. And if the indentation loads is higher than 10 N, the obtained hardness floats around 24.2 GPa and the cracks are half-coin type. The proper Vickers indentation load range for SSiC ceramic hardness and toughness tests are determined to be 10 N or above.

Key words: silicon carbide ceramic, indentation load, mechanical properties

CLC Number:

TQ174

YANG Xiao, LIU Xue-Jian, HUANG Zheng-Ren, LIU Gui-Ling, YAO Xiu-Min. Effects of Vickers Cracks on the Mechanical Properties of Solid-phase-sintered Silicon Carbide Ceramics[J]. Journal of Inorganic Materials, 2012, 27(9): 965-969.

References

[1] Marro F G, Anglada M. Strengthening of Vickers indented 3Y-TZP by hydrothermal ageing. J. Euro. Ceram. Soc., 2012, 32(2): 317-324.

[2] Yonezu A, Xu B, Chen X. Indentation induced lateral crack in ceramics with surface hardening. Mater. Sci. Eng. A, 2009, 507(1/2): 226-235.

[3] Choi J E, Waddell J N, Swain M V. Pressed ceramics onto zirconia. Part 2: Indentation fracture and influence of cooling rate on residual stresses. Dent. Mater., 2011, 27(11): 1111-1118.

[4] Lube T, Fett T A. Threshold stress intensity factor at the onset of stable crack extension of knoop in-dentation cracks. Eng. Fract. Mech., 2004, 71(16/17): 2263-2269.

[5] Evans A G, Charles E A. Fracture toughness determinations by indentation. J. Am. Ceram. Soc., 1976, 59(7/8): 371-372.

[6] Niihara K, Morena R, Hasselman D P H. Evaluation of KIC of brittle solids by the indentation method with low crack-to-indent ratios. J. Mater. Sci. Lett., 1982, 1(1): 13-16.

[7] Lawn B R, Evans A G, Marshall D B. Elastic/plastic indentation damage in certain ceramics: the median/radial crack system. J. Am. Ceram. Soc., 1980, 63(9/10): 574-581.

[8] Matsumoto R L K. Evaluation of fracture toughness determination methods as applied to Ceria-stabilized tetragonal zirconia polycrystal. J. Am. Ceram. Soc., 1987, 70(12): C366-C368.

[9] Gong Jianghong. Indentation toughness of ceramics: a statistical analysis. Ceram. Int., 2002, 28(7): 767-772.

[10] Lach R, Gyurova L Antonova, Grellmann W. Application of indentation fracture mechanics approach for determination of fracture toughness of brittle polymer systems. Polym. Test., 2007, 26(1): 51-59.

[11] Gong Jianghong. Determining indentation toughness by incorporating true hardness into fracture mechanics equations. J. Euro. Ceram. Soc., 1999, 19(8): 1585-1592.

[12] Ebisu T, Horibe S. Analysis of the indentation size effect in brittle materials from nanoindentation load–displacement curve. J. Euro. Ceram. Soc., 2010, 30(12): 2419-2426.

[13] Miyazaki Hiroyuki, Hyuga Hideki, Yoshizawa Yuichi, et al. Crack profiles under a vickers indent in silicon nitride ceramics with various microstructures. Ceram. Int., 2010, 36(1): 173-179.

[14] Chicot D, Mercier D, Roudet F, et al. Comparison of instrumented Knoop and Vickers hardness measurements on various soft materials and hard ceramics. J. Euro. Ceram. Soc., 2007, 27(4): 1905-1911.

[15] Lawn B R, Evans A G. A model for crack initiation in elastic/ plastic indentation fields. J. Mater. Sci., 1977, 12(11): 2195-2199.

[16] Giannakopoulos A E, Larsson P L, Vestergaard R. Analysis of vickers indentation. Int. J. Solids. Struct., 1994, 31(19): 2679-2708.

[17] Anton R J, Subhash G. Dynamic vickers indentation of brittle materials. Wear, 2000, 239(1): 27-35.

[18] Pajares A, Guibertea F, Cumbrera F L, et al. Analysis of kidney- shaped indentation cracks in 4Y-PSZ. Acta. Mater., 1996, 44(11): 4387-4394.

[19] Lube Tanja. Indentation crack profiles in silicon nitride. J. Euro. Ceram. Soc., 2001, 21: 211-218.

[20] Jones S L, Norman C J, Shahani R. Crack-profile shapes formed under a vickers indent pyramid. J. Mater. Sci. Lett., 1987, 6(6): 721-723.

[21] Sglavo Vincenzo M, Pancheri Paolo. Crack decorating technique for fracture toughness measurement in alumina. J. Euro. Ceram. Soc., 1997, 17(14): 1697-1706.

[22] Cook Robert F, Pharr George M. Direct observation and analysis of indentation cracking in glasses and ceramics. J. Am. Ceram. Soc., 1990, 73(4): 787-817.

[23] Lawn Brian. Fracture of Brittle Solids, 2nd edition. London, Cambridge University Press & Beijing, Higher Education Press, 2010: 228-240.