Abstract: Chemical uniform, high-purity spray-grade zirconia powders doped with variable ratios of yttria for
ceramic thermal barrier coatings were prepared by an internal gelation process. Both the morphology and particle size of the powders can be
controlled by varying the emulsification conditions. Scanning electron microscopic and optical microscopic observations revealed the materials
thus obtained to have a predominantly spherical morphology and the requisite size distribution (5～50μm). The dense, calcined
micro-spheres showed good flowability. Differential Thermal Analysis (DTA) of 4.7mol% Y₂O₃-ZrO₂ powders (dried at 80℃) indicated that m→’ transformation was happened at 468℃.
X-ray diffraction results showed that the crystalline phase of such powders after calcination at 800℃ was 100% nontransformable tetragonal.

Key words: yttria-stabilized zirconia (YSZ) powders, plasma spraying, internal gelation, emulsification, nontransformable tetragonal phase