胆酸钴凝胶超分子自模板法制备一维纳米α-Co(OH)2及其电化学电容行为

doi:10.3724/SP.J.1077.2013.12484

无机材料学报 ›› 2013, Vol. 28 ›› Issue (7): 739-744.DOI: 10.3724/SP.J.1077.2013.12484 CSTR: 32189.14.SP.J.1077.2013.12484

胆酸钴凝胶超分子自模板法制备一维纳米α-Co(OH)₂及其电化学电容行为

蔡龙成¹, 李娟¹, 黄建滨^1,2

(1. 新疆大学化学化工学院, 乌鲁木齐830046; 2. 北京大学化学与分子工程学院, 北京100871)

收稿日期:2012-07-13 修回日期:2012-09-19 出版日期:2013-07-20 网络出版日期:2013-06-19
作者简介:蔡龙成(1985–), 男, 硕士研究生. E-mail:317cailongcheng@163.com
基金资助:
新疆大学博士启动基金 (BS110112)

Electrochemical Capacitance Performance of One-dimensional Nano-α-Co(OH)₂ Employing Cobalt-cholate Supramolecular Nanofibers Self-template Method

CAI Long-Cheng¹, LI Juan¹, HUANG Jian-Bin^{1, 2}

(1. College of Chemistry and Chemical Engineering, Xinjiang University, Urumqi 830046, China; 2. College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, China)

Received:2012-07-13 Revised:2012-09-19 Published:2013-07-20 Online:2013-06-19
About author:CAI Long-Cheng. E-mail:317cailongcheng@163.com
Supported by:
Doctoral Scientific Research Staring Foundation of Xinjiang University (BS110112)

摘要/Abstract

摘要： 以Co(NO₃)₂•6H₂O和胆酸钠溶液混合制备了超分子自组装凝胶纳米纤维, 以此凝胶纳米纤维为自模板, NH₃•H₂O为沉淀剂, 在温和条件下制备了纳米α-Co(OH)₂。X射线衍射(XRD)、红外光谱(FT-IR)、扫描电子显微镜(SEM)及透射电子显微镜(TEM)测试表征了其组成和微观结构。实验结果表明所得材料为纯相一维纳米纤维交错形成疏松网状结构的α-Co(OH)₂, 其直径在100~200 nm之间。用循环伏安和恒电流充放电等测试方法对α-Co(OH)₂电化学电容行为进行了研究, 结果表明: 所得α-Co(OH)₂在6 mol/L KOH溶液中, 0~0.5 V(vs Hg/HgO)电位范围内, 电流密度为1 A/g时, 其单电极比容量达到1200 F/g, 经过800周循环, 比容量稳定保持在初始容量的75%。其独特的纳米结构使其易于浸入电解液, 具有快速的电化学响应特性, 提高了电极材料的有效利用率, 这种自模板法为制备纳米电容器电极材料提供了简易的途径。

关键词: 自模板, α-Co(OH)₂, 电化学电容

Abstract: Nano-α-Co(OH)₂ was prepared via a facile strategy, in which the cobalt-cholate self-assembled spramolecular nanofibers as self-template were obtained by mixing sodium cholate solution with cobalt nitrate solution, and then the samples were obtained by adding depositing reagents NH₃•H₂O under ambient conditions. The composition and microstructure of the as-prepared samples were investigated by X-ray diffraction (XRD), infrared spectroscope (FT-IR), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results indicate that the as-prepared materials are pure phase α-Co(OH)₂ with one-dimensional nanofiber crossing loose network–like struture whose diameter is 100-200 nm. The electrochemical capacitive properties of the products were investigated using cyclic voltammetry and impedance spectroscopy in 6 mol/L KOH aqueous solution. The specific capacitance is up to 1200 F/g at a constant current charge/discharge test of 1 A/g within 0-0.5 V potential region, and stably keep 75% of initial capacitance after over 800 charge-discharge cycles. Its special nanostructure, with fast electrochemical response property, allows easy penetration of electrolyte and effective utilization of electrode material. This self-templating approach is therefore believed to provide a simple and convenient route to fabricate nanomaterials for application in supercapacitors.

Key words: self-Template, α-Co(OH)₂, electrochemical capacitance

中图分类号:

O646

蔡龙成, 李娟, 黄建滨. 胆酸钴凝胶超分子自模板法制备一维纳米α-Co(OH)₂及其电化学电容行为[J]. 无机材料学报, 2013, 28(7): 739-744.

CAI Long-Cheng, LI Juan, HUANG Jian-Bin. Electrochemical Capacitance Performance of One-dimensional Nano-α-Co(OH)₂ Employing Cobalt-cholate Supramolecular Nanofibers Self-template Method[J]. Journal of Inorganic Materials, 2013, 28(7): 739-744.

参考文献

[1] Winter M, Brodd R J. What are batteries, fuel cells, and supercapacitors? Chemical Reviews, 2004, 104(10): 4245–4269.

[2] Zhang Y, Feng H, Wu X B, et al. Progress of electrochemical capacitor electrode materials: a review. International Journal of Hydrogen Energy, 2009, 34(11): 4889–4899.

[3] Wang G P, Zhang L, Zhang J J. A review of electrode materials for electrochemical supercapacitors. Chemical Society Reviews, 2012, 41(2): 797–828.

[4] Frackowiak E, Delpeux S, Jurewicz K, et al. Enhanced capacitance of carbon nanotubes through chemical activation. Chemical Physics Letters 2002, 361(1/2): 35–41.

[5] Burke A, Ultracapacitors: why, how, and where is the technology. Journal of Power Sources, 2000, 91(1): 37–50.

[6] Nohara S, Asahina T, Wada H, et al. Hybrid capacitor with activated carbon electrode, Ni(OH)2 electrode and polymer hydrogel electrolyte. Journal of Power Sources, 2006, 1579(1): 605–609.

[7] Hu C C, Chang K H, Lin M C, et al. Design and tailoring of the nanotubular arrayed architecture of hydrous RuO2 for next generation supercapacitors. Nano Letters, 2006, 12(6): 2690–2695.

[8] Gupta V, Kusahara T, Toyama H, et al. Potentiostatically deposited nanostructured a-Co(OH)2:A high performance electrode material for redox-capacitors. Electrochemistry Communications, 2007, 9(9): 2315–2319.

[9] Ahn H J, Kima W B, Seong T Y. Co(OH)2-combined carbon-nanotube array electrodes for high-performance micro- electro-chemical capacitors. Electrochemistry Communications, 2008, 10(9): 1284–1287.

[10] Hu Z A, Xie Y L, Wang Y X, et al. Synthesis of α-cobalt hydroxides with different intercalated anions and effects of intercalated anions on their morphology, basal plane spacing, and capacitive property. The Journal of Physical Chemistry C, 2009, 113(28): 12502–12508.

[11] Liang Y Y, Cao L, Kong L B, et al. Synthesis of Co(OH)2/USY composite and its application for electrochemical supercapacitors. Journal of Power Sources, 2004, 136(1): 197–200.

[12] Ni X M, Zheng H G, Xiao X K, et al. Citrate-assisted fab rication of ?owery α-Co(OH)2 architectures with improved electrochemical properties. Journal of Alloys and Compounds, 2009, 484(1/2): 467–471.

[13] Qiao Y, Wang Y J, Yang Z Y, et al. Self-templating of metal-driven supramolecular self-assembly:a general approach toward 1D inorganic nanotubes. Chemistry of Materials, 2011, 23(5): 1182–1187.

[14] LIU Ai-Dong. Synthesis of nanomaterials in the control of biotemplate. Journal of Yunnan University, 2005, 27(3A): 109–194.

[15] Liu Z, Ma R, Osada M, et al. Selective and controlled synthesis of α and β-cobalt hydroxides in highly developed hexagonal platelets. Journal of the American Chemical Society, 2005, 127(40): 13869–13874.

[16] Qiao Y, Lin Y Y, Yang Z Y, et al. Unique temperature-dependent supramolecular self-assembly: from hierarchical 1D nanostructures to super hydrogel. The Journal of Physical Chemistry B, 2010, 114(36): 11725–11730.

[17] Miki K, Masui A, Kasai N, et al. New channel-type inclusion compound of steroidal bile acid. structure of a 1:1 complex between cholic acid and acetophenone. Journal of the American Chemical Society, 1988, 110(19): 6594–6596.

[18] Qiao Y, Lin Y Y, Wang Y J, et al. Metal-driven hierarchical self-assembled one-dimensional nanohelices. Nano Letters, 2009, 9(12): 4500–4504.

[19] ZHANG Luo-Jiang, GAO Bo, ZHANG Xiao-Gang. Pyrolysis preparation of nickel oxide and its electrochemical capacitance. Journal of Inorganic Materials, 2012, 28(5): 979–982.

[20] Palmas S, Ferrara F, Vacca A, et al. Behavior of cobalt oxide electrodes during oxidative processes in alkaline medium. Electrochimica Acta, 2007, 53(2): 400–406.

胆酸钴凝胶超分子自模板法制备一维纳米α-Co(OH)₂及其电化学电容行为

Electrochemical Capacitance Performance of One-dimensional Nano-α-Co(OH)₂ Employing Cobalt-cholate Supramolecular Nanofibers Self-template Method

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 13

编辑推荐

Metrics

本文评价

[1]	鲍艳, 王彤. 中空SiO₂微球的制备及其在缓/控释应用中的新进展[J]. 无机材料学报, 2016, 31(12): 1269-1278.
[2]	赵立平, 王宏宇, 齐力. 二硫化钼用作不对称型电化学电容器的负极材料[J]. 无机材料学报, 2013, 28(8): 831-835.
[3]	肖兴中, 易清风. MnO₂/SMWCNT/PANI三元复合材料的合成及其电化学电容性能[J]. 无机材料学报, 2013, 28(8): 825-830.
[4]	鲍艳, 杨永强, 马建中. 模板法制备中空结构材料的研究进展[J]. 无机材料学报, 2013, 28(5): 459-468.
[5]	高兆辉, 张浩, 曹高萍, 韩敏芳, 杨裕生. 模板法制备介孔VN纳米电极材料及其电容性能[J]. 无机材料学报, 2012, 27(12): 1261-1265.
[6]	章罗江, 高博, 张校刚. NiO 的热分解制备及其电化学电容性质[J]. 无机材料学报, 2011, 26(4): 398-402.
[7]	吕岩, 王志永, 张浩, 房进, 曹高萍, 施祖进, 王碧燕. 电弧法制备石墨烯的孔结构和电化学性能研究[J]. 无机材料学报, 2010, 25(7): 725-728.
[8]	时志强,赵朔,陈明鸣,王妹先,王成扬. 预炭化对KOH活化石油焦的结构及电容性能的影响[J]. 无机材料学报, 2008, 23(4): 799-804.
[9]	王虹,唐致远,李中延. Ni²⁺掺杂对V₂O₅结构及电化学性能的影响[J]. 无机材料学报, 2008, 23(3): 583-586.
[10]	李强,李开喜,谷建宇,范慧,吕春祥. 电化学电容器复合电极材料铜氧化物/多孔炭的制备及电化学性[J]. 无机材料学报, 2007, 22(5): 894-900.
[11]	刘献明,张校刚. 热解温度对MnO₂电容行为的影响[J]. 无机材料学报, 2003, 18(5): 1022-1026.
[12]	王晓峰,王大志,梁吉. 碳纳米管表面沉积氧化镍及其超电容器的电化学行为[J]. 无机材料学报, 2003, 18(2): 331-336.
[13]	王晓峰,孔祥华. 新型氧化镍超电容器电极材料的研究[J]. 无机材料学报, 2001, 16(5): 815-820.