Magnetic Field Induced Chain Alignment of Ferroparticles in Magnetic Fluid

LI Yan-Qin^1,2, BU De-Cai^1,2, LI Xue-Hui²

(1. School of Physics and Optoelectronic Technology, Dalian University of Technology, Dalian 116024, China; 2.College of Physical Science and Technology, Dalian University, Dalian 116622, China)

Received:2012-09-10 Revised:2012-12-30 Published:2013-07-20 Online:2013-06-19
About author:LI Yan-Qin. E-mail: liyanqin_dlu@126.com
Supported by:
National Natural Science Foundation of China(51077006, 50677005)

摘要/Abstract

摘要： 研究了磁性液体在有、无外加磁场作用时磁性液体中纳米磁性颗粒的微观排列结构, 发现无外加磁场作用时磁性颗粒随机均匀分布在载液中, 有外加均匀磁场作用时, 磁性颗粒沿磁场方向排列成均匀链状结构。当外加均匀磁场强度为11.1 kA/m, TEM照片清晰显示磁性颗粒排列成一条链状结构, 随着外加均匀磁场强度逐渐增强到28.6 kA/m, 更多磁性颗粒沿磁场方向紧密排列成链状结构。在外加梯度磁场作用下, 铁芯中心处磁场强度为28.7 kA/m时, 大量磁性颗粒聚集于线圈中心轴附近形成复杂链状团簇结构; 沿r轴方向磁场强度较弱的地方, 较少磁性颗粒排列成链状结构。当磁场梯度从1.73 kA/m²逐渐增加到5.11 kA/m²时, 磁场梯度轴线上的磁性颗粒团簇结构由稀疏逐渐变成为密集。磁场诱导磁性颗粒链状排列结构的研究对磁性液体在机械工程、生物工程、热力工程等领域的应用有重要意义。

关键词: 磁性液体, 透射电子显微镜, 链状结构, 磁偶极子

Abstract: Chain alignment of suspended-ferroparticles in a carrier fluid exposed to the external magnetic field was investigated theoretically and experimentally. The results show that without the external magnetic field the ferroparticles were randomly distributed and when exposed to uniform magnetic field the turned out to be a chained-alignment pattern along the external magnetic field orientation at intensity of 11.1 kA/m. With the external uniform magnetic field intensity up to 28.6 kA/m, more ferroparticles closely aggregated to a chained-alignment pattern along the magnetic field direction. When the magnetic field intensity reached 28.7 kA/m in the gradient magnetic field, a large number of ferroparticles gathered around the coils and formed complex clusters, while a small number of ferroparticles demonstrated a chain-alignment pattern along r direction with weaker magnetic field intensity. When the magnetic field gradient was gradually increasing from 1.73 kA/m² to 5.11 kA/m², the cluster pattern of ferroparticles turned out to be dense along the axis. This research may enhance the applications of magnetic fluid in the fields of mechanical engineering, bioengineering and thermodynamic engineering.

Key words: magnetic fluid, transmission electron microscopy, chained-alignment, magnetic dipole

中图分类号:

TM271

李艳琴, 部德才, 李学慧. 磁性液体纳米磁性颗粒磁场诱导链状结构研究[J]. 无机材料学报, 2013, 28(7): 745-750.

LI Yan-Qin, BU De-Cai, LI Xue-Hui. Magnetic Field Induced Chain Alignment of Ferroparticles in Magnetic Fluid[J]. Journal of Inorganic Materials, 2013, 28(7): 745-750.

参考文献

[1] Rosensweig R E. Magnetic fluids. Annual Reviews Fluid Mechanics, 1987, 19: 437–463.

[2] GUO Guang-Sheng, WANG Zhi-Hua, YU Shi, et al. Preparation of iron-nitride magnetic fluid by vapor-liquid chemical reaction. Journal of Inorganic Materials, 2000, 15(5): 921–925.

[3] Burcan Jan, Burcan-Piotrowicz Ewa, S?awinńska Anna. Investigation on magnetic fluids as lubricant. Indian Journal of Engineering and Materials Sciences, 2004, 11(4): 338–342.

[4] ZOU Ji-Bin, ZOU Ji-Ming, HU Jian-Hui. Design and pressure control of high-pressure differential magnetic fluid seals. IEEE Transactions on Magnetics, 2003, 39(5): 2651–2653.

[5] ZHANG Bo, Nakajima Arira. Dynamics of magnetic fluid support grinding of Si3N4 ceramic balls for ultraprecision bearings and its importance in spherical surface generation. Precision Engineering, 2003, 27(1): 1–8.

[6] Thurm S, Odenbach S. Magnetic separation of ferrofluids. Journal of Magnetism and Magnetic Materials, 2002, 252: 247–249.

[7] LIU Rui-Ting, LIU Jie, TONG Jie-Qiong, et al. Heating effect and biocompatibility of bacterial magnetosomes as potential materials used in magnetic fluid hyperthermia. Progress in Natural Science: Materials International, 2012, 22(1): 31–39.

[8] Lira S A, Miranda J A. Adhesion properties of chain-forming ferrofluids. Physical Review E, 2009, 79(4): 046303–1–8.

[9] Gonzales-Weimuller Marcela, Zeisberger Matthias, Krishnan Kannan M. Size-dependant heating rates of iron oxide nanoparticles for magnetic fluid hyperthermia. Journal of Magnetism and Magnetic Materials, 2009, 321(13): 1947–1950.

[10] PU Sheng-Li, DAI Min, SUN Guo-Qing. Longitudinal field-induced polarized light transmittance of magnetic fluids. Optics Communications, 2010, 283(20): 4012–4016.

[11] LI Qiang, XUAN Yi-Min, WANG Jian. Experiment investigations on transport properties of magnetic fluids. Experimental Thermal and fluid Science, 2005, 30(2): 109–116.

[12] Yoshihisa Enomoto, Katsumi Oba, Masafumi Okada. Simulation study on microstructure formations in magnetic fluids. Physica A, 2003, 330(3/4): 496–506.

[13] Ivanov Alexey O, Kantorovich So?a S, Mendelev Valentin S, et al. Ferro?uid aggregation in chains under the influence of a magnetic field. Journal of Magnetism and Magnetic Materials, 2006, 300(1): e206–e209.

[14] Cerdá J J, Kantorovich S, Holm C. Aggregate formation in ferrofluid monolayers: simulations and theory. Journal of Physics: Condensed Matter, 2008, 20(20): 204125–1–5.

[15] Pyanzina E, Kantorovich S, CerdáJuan J, et al. Structure factor of ferro?uids with chain aggregates: theory and computer simulations. Journal of Magnetism and Magnetic Materials, 2011, 323(10): 1263–1268.

[16] Hong Chin-Yih, Jang I J, Horng H E, et al. Ordered structures in Fe3O4 kerosene-based ferro?uids. Journal of Applied Physics, 1997, 81(8): 4275–4277.

[17] Horng H E, Hong Chin-Yih, Yang S Y, et al. Novel properties and applications in magnetic fluids. Journal of Physics and Chemistry of Solids, 2001, 62(9/10): 1749–1764.

[18] LI Yan-Qin, LI Xue-Hui, AN Hong, et al. Preparation using plasma and research of surface tension coefficient for magnetic fluid. Metallic Functional Materials, 2009, 16(6): 8–10.

[19] 李学慧, 刘志升, 李艳琴, 等. 交变电场/温度场协同合成纳米磁性润滑油的方法及装置. 中国发明专利, ZL200910011126.8, 2011.12.7.

[20] 李艳琴, 李学慧, 徐萍. 磁场中磁性液体透射电子显微镜观测样品制备方法. 中国发明专利, ZL20120204709.4, 2012.6.21.

[21] LI Qiang, XUAN Yi-Min, LI Bin. Simulation and control scheme of microstructure in magnetic fluids. Science in China Series E: Technological Sciences, 2007, 50(3): 371–379.

[22] WANG Shi-Bin, DU Lin, SUN Cai-Xin, et al. Agglomeration of aqueous ferrofluid subjected to the magnetic field by 3-D dissipative particle dynamics simulation. Journal of Functional Materials, 2011, 42(2): 298–301.

[23] Yang S Y, Tse W S, Hrong H E, et al. Optical anisotropy induced by external magnetic fields on magnetic fluid films. Journal of Magnetism and Magnetic Material, 2001, 226-230: 1992–1994.

[24] WANG Zuo-Wei, Holm Christian, Müller Walter Hanns. Boundary condition effects in the simulation study of equilibrium properties of magnetic dipolar fluids. Journal of Chemical Physics, 2003, 119(1): 379–387.

[25] Barrett Matthew, Deschner Andreas, Embs Jan P, et al. Chain formation in a magnetic fluid under the influence of strong magnetic fields studied by small angle neutron scattering. Soft Matter, 2011, 7(14): 6678–6683.

磁性液体纳米磁性颗粒磁场诱导链状结构研究

Magnetic Field Induced Chain Alignment of Ferroparticles in Magnetic Fluid

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 5

编辑推荐

Metrics

本文评价

[1]	吴秋琴, 姚奋发, 金传洪, 郑遗凡. 碳纳米管内填充生长超细一维亚化学计量比氧化钨纳米线[J]. 无机材料学报, 2022, 37(4): 413-419.
[2]	朱信华, 李爱东, 刘治国. 扫描透射电子显微镜(STEM)在新一代高K栅介质材料的应用[J]. 无机材料学报, 2014, 29(12): 1233-1240.
[3]	卢焕明,叶志镇,黄靖云,汪雷,赵炳辉. 硅基LiNbO₃薄膜的微结构研究[J]. 无机材料学报, 2005, 20(4): 971-975.
[4]	王其祥,宋宝珍,李洪钟. H₂+H₂O还原法制备超细金属磁记录粉[J]. 无机材料学报, 2001, 16(5): 861-866.
[5]	郭广生,王志华,余实,杨福明. 气-液化学反应制备氮化铁磁性液体[J]. 无机材料学报, 2000, 15(5): 921-925.