TeO2-ZnCl2-BaO-NaF玻璃系统的结构及中红外透过特性的研究

doi:10.3724/SP.J.1077.2007.00277

摘要/Abstract

摘要： 制备了一种新型的氧卤碲酸盐玻璃: (80-x)TeO₂-15ZnCl₂-xBaO-5NaF(x=30、20、10、0mol%), 对玻璃的机械强度、热稳定性、拉曼光谱、紫外吸收光谱、红外透过光谱等特性进行了研究. 通过拉曼光谱分析研究了玻璃组分含量的变化对玻璃结构和红外透过性能的影响. 结果表明, 随着BaO含量的增加, 玻璃在红外波段透过率显著增加, 并且红外透过截止波长向长波方向移动, 本文对这一实验结果进行了机理性的研究探讨. 同时, 通过在熔制过程中通入高纯O₂, 以及引入适量的卤化物有效地除去玻璃中的[OH]基团, 使玻璃的红外透过性能得到进一步的提高. 这种新型的氧卤碲酸盐玻璃在中红外区域有较高的透过(≥80%), 中红外波段透过截止波长达6.5μm, 是一种红外透过性能优良的光学玻璃材料.

关键词: 氧卤碲酸盐玻璃, 红外透过, 拉曼光谱

Abstract: Oxyhalide tellurite glasses: (80-x)TeO₂-15ZnCl₂-xBaO-5NaF(x=30,20,10,0mol%) were prepared. The mechanical strength performance, thermal properties, Raman spectra, UV absorption spectra and Infrared transmission spectra of the samples were investigated. The effects of composition content change on the structure and infrared transmission properties of glasses were investigated by means of Raman scattering. The results show that the transmission in mid-infrared region significantly increases and the IR cut-off shifts towards longer wavelength with increasing BaO, the mechanism was also discussed. The addition of halide to the glasses and the treatment with pure O₂ during melting are useful for the decrease of OH^-1 absorption bands, meanwhile the infrared transmittance is increased. The presented oxyhalide tellurite glass is a kind of optical material with high infrared transmission. It exhibits a high transmittance (≥80%) in the mid-infrared regions and possesses an infrared cut-off edge up to 6.5μm.

Key words: oxyhalide tellurite glass, infrared transmission, Raman spectra

中图分类号:

TQ171

吴家禄,张军杰,赖杨琼,胡丽丽,姜中宏. TeO₂-ZnCl₂-BaO-NaF玻璃系统的结构及中红外透过特性的研究[J]. 无机材料学报, DOI: 10.3724/SP.J.1077.2007.00277.

WU Jia-Lu,ZHANG Jun-Jie,LAI Yang-Qiong,HU Li-Li,JIANG Zhong-Hong. Properties of Structure and Mid-infrared Transmission in TeO₂-ZnCl₂-BaO-NaF Glass System[J]. Journal of Inorganic Materials, DOI: 10.3724/SP.J.1077.2007.00277.

参考文献

[1] Burger H, Vogel W, et al. Infrared Phys, 1985, 25 (1-2): 397--406.
[2] Keiji Kobayasbhi. J. Non-Cryst. Soids, 2003, 316: 404--405.
[3] O'Donnell M D, Miller C A, Furniss D, et al. J. Non-Cryst. Solids, 2003, 331: 48--57.
[4] Higby P L, Aggarwl I D. J. Non-Cryst. Solids, 1997, 210: 130--135.
[5] Sanghera J S, Bayya S S, Wojcik J. et al. Proc. 12th. Int. Symp. On Non-Oxide Glasses and Advanced Materials, Brazil, 2000. 15--20.
[6] Hu H, Lin F, Yuan Y, et al. Mater. Sci. Forum., 1988, 32--33: 370--374.
[7] Seddon A B , Cardoso A V. Phys. Chem. Glasses, 1994, 35 (3): 137--144.
[8] 曹国喜. 博士论文. 上海: 中国科学院上海光学精密机械研究所, 2003.
[9] Zhang Xiang Hua, Fonteneau G, Lucas J. J. Non-Cryst. Solids, 1988, 104: 38.
[10] Lucas Jacques. Current Opinion in Solid State & Materials Science, 1999, 4: 181--187.
[11] 汪国年, 杨建虎, 徐时清, 等(WANG Guo-Nian, et al). 无机材料学报(Journal of Inorganic Materials), 2004, 19 (5): 998--1001.
[12] 周跃芬, 刘粤惠, 戴世勋, 等(ZHOU Yue-Fen, et al). 无机材料学报(Journal of Inorganic Materials), 2003, 18 (3): 513--518.
[13] Neindre L L, Jiang S B, Hwang B C, et al. J. Non-Cryst. Solids, 1999, 255: 97--104.
[14] Yoshida S, Matsuoka J, Soga N. J. Non-Cryst Solids., 2001, 279: 44.
[15] Watanabe T, Benino Y, Komatsu T. J. Non-Cryst. Solids, 2001, 286: 141.
[16] Shelby J E, LaCourse W C, Clare A G. Engineered Materials Handbook. ASM International. 1991.
[17] Neov S, Kozhukharov V, Trapalis C, et al. Phys. Chem. Glasses, 1995, 36: 89.
[18] Sabadel J C, Armand P, et al. J. Solid State Chem., 1997, 132: 411.
[19] Sekiya T, Mochida N, et al. J. Non-Cryst. Solids, 1994, 168: 106.
[20] Sabadel J C, Armand P, et al. J. Non-Cryst. Solids, 1999, 244: 143.
[21] Sakida Shinichi. Studies on Structure of Tellurite Glasses. Kyoto University, 1999. 67--106.
[22] Worrell C A, Henshall T. J. Non-Cryst. Solids, 1978, 29: 283.
[23] Pan Z, Morgen S H. J. Non-Cryst. Solid, 1997, 210: 133.
[24] Tikhomirov V K, Jha A, Perakis A. J. Non-Cryst. Solids, 1999, 256-257: 89.
[25] Wang Guonian, Zhang Junjie, Dai Shixun, et al. Physics Letters A, 2005, 341: 287--288.
[26] 干福熹. 现代玻璃科学技术(上册). 上海: 上海科学技术出版社, 1988. 139.
[27] Sekiya T, Mochida N, Ohtsuka A, et al. J. Non-Cryst. Solids, 1992, 144: 128--129.
[28] Wang Y, Osaka A. Mater. Sci. Forum, 1988, 32: 161.
[29] Zhang Junjie, Qiu Jianbei, Kawamoto Yoji. Materials Letters, 2002, 55: 80--81.
[30] Kosuge T, Benino Y, et al. J. Non-Cryst. Solids, 1998, 242: 158--161.
[31] Himei Y, Osaka A, Nanba T, et al. J. Non-Cryst. Solids, 1994, 177: 164--168.
[32] Higazy A A, Bridge B. J. Mater. Sci., 1985. 2354--2355.
[33] El-Mallawany R A. Infrared Phys., 1989, 29 (2-4): 783--785.
[34] Bridge B, Higazy A A. J. Phys. Chem. Glasses, 1986, 27 (1): 1--3.

TeO₂-ZnCl₂-BaO-NaF玻璃系统的结构及中红外透过特性的研究

Properties of Structure and Mid-infrared Transmission in TeO₂-ZnCl₂-BaO-NaF Glass System

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	张守超, 陈洪雨, 刘洪飞, 杨羽, 李欣, 刘德峰. 6H-SiC中子辐照肿胀高温回复及光学特性研究[J]. 无机材料学报, 2023, 38(6): 678-686.
[2]	产思义, 屠菊萍, 黄珂, 邵思武, 杨志亮, 刘鹏, 刘金龙, 陈良贤, 魏俊俊, 安康, 郑宇亭, 李成明. 2英寸MPCVD光学级均匀金刚石膜的制备研究[J]. 无机材料学报, 2023, 38(12): 1413-1419.
[3]	程国峰, 阮音捷, 孙玥, 尹晗迪. 纯相BiFeO₃的热稳定和热膨胀性质研究[J]. 无机材料学报, 2019, 34(10): 1128-1133.
[4]	凌云鹏, 闵嘉华, 梁小燕, 张继军, 杨柳青, 温旭亮, 张滢, 李明, 刘兆鑫, 王林军, 沈悦. 溶剂熔区移动法生长Cd_0.9Zn_0.1Te晶体的工艺优化研[J]. 无机材料学报, 2017, 32(9): 980-984.
[5]	乔北京, 陈飞飞, 聂秋华, 戴世勋, 黄益聪. TiO₂掺杂Ge-Sn-Se微晶玻璃的结构与光学特性研究[J]. 无机材料学报, 2015, 30(11): 1189-1194.
[6]	姜金龙, 王琼, 黄浩, 张霞, 王玉宝, 耿庆芬. 紫外光辐照下钛硅共掺杂类金刚石薄膜微结构的演化[J]. 无机材料学报, 2014, 29(9): 941-946.
[7]	尹冬梅, 屠德阳, 车丙晨, 张芳芳, 林常规, 戴世勋. Sn对Ge-Se-Te玻璃结构与光学特性的影响[J]. 无机材料学报, 2014, 29(3): 279-283.
[8]	魏文猴, 方亮, 杨志勇, 沈祥. Sb对GeSb_xSe_7-_x硫系玻璃的结构和物性的影响[J]. 无机材料学报, 2014, 29(11): 1218-1222.
[9]	汪刘应, 徐卓, 华绍春, 刘安明, 郭秦, 刘顾. 不同管径CNTs/Al₂O₃-TiO₂复合吸波涂层的拉曼光谱特征及吸波性能研究[J]. 无机材料学报, 2013, 28(2): 136-140.
[10]	毛茂, 黄婉霞, 张雅鑫, 颜家振, 罗轶, 施奇武, 蔡靖涵. 钨掺杂二氧化钒薄膜的THz波段相变性能的研究[J]. 无机材料学报, 2012, 27(8): 891-896.
[11]	张磊, 黄利, 丁佳, 陈辉宇, 陈伟, 胡丽丽. 酸碱处理对磷酸盐激光玻璃表面的侵蚀研究[J]. 无机材料学报, 2012, 27(6): 627-632.
[12]	李法荟, 林红, 李俊峰, 雷牧云, 李祯, 李建保. LiF对镁铝尖晶石透明陶瓷红外透过率的影响[J]. 无机材料学报, 2012, 27(4): 417-421.
[13]	于美, 刘鹏瑞, 孙玉静, 刘建华, 安军伟, 李松梅. 石墨烯-银纳米粒子复合材料的制备及表征[J]. 无机材料学报, 2012, 27(1): 89-94.
[14]	徐亚东, 介万奇, 王涛, 俞鹏飞, 杜园园, 何亦辉. CdZnTe 晶体中微米级富 Te 相与 PL 谱的对应关系[J]. 无机材料学报, 2011, 26(4): 359-363.
[15]	张荣军, 杨延清, 王晨, 沈文涛, 罗贤. 三级化学气相沉积法制备SiC纤维的微观组织结构[J]. 无机材料学报, 2010, 25(12): 1281-1285.