铜离子掺杂Y2Ba2O5高近红外反射颜料的制备和光学性能研究

doi:10.15541/jim20150562

摘要/Abstract

摘要：

采用溶胶-凝胶法制备一系列环境友好型绿色近红外反射纳米颜料, 结构通式为Y₂Ba_(2-_x₎Cu_xO₅(x=0、0.25、0.50、0.75和1.0), 通过X射线衍射(XRD)、扫描电子显微镜(SEM)、UV-vis-NIR分光光度仪和高精度分光测色仪对制备颜料的结构、形貌和光学性能进行了表征。研究结果表明, 铜离子掺杂进入Y₂Ba₂O₅晶格中, Y₂Ba₂O₅晶粒尺寸由62.1 nm降低至54.7 nm。Cu²⁺取代Y₂Ba₂O₅中的部分Ba²⁺, 粉末颜色由白色变为绿色(a*=-21.61), 禁带宽度由2.30 eV 减少到2.04 eV; 粉末呈现不规则球形结构, 粒径分布在150~300 nm范围内。掺杂Cu²⁺使粉末的近红外反射率降低, 但Cu²⁺掺杂量为x=0.50时仍然表现出较高的近红外反射率(68.80%)和太阳光反射率(45.95%)。因此, Y₂Ba_(2-_x₎Cu_xO₅系列高近红外反射绿色粉末作为“冷”颜料在建筑涂料方面具有巨大的应用潜能。

关键词: 溶胶-凝胶, 绿色颜料, 近红外反射率, 禁带宽度

Abstract:

A series of environmentally benign near-infrared reflective green nano-pigments were synthesized via Sol-Gel method with a general formula of Y₂Ba_(2-_x₎Cu_xO₅(x=0, 0.25, 0.50, 0.75 and 1.0). The crystal structure, morphology and optical properties of the synthesized pigments were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), UV-Vis-NIR diffuse reflectance spectra, and high accuracy spectrophotometer. Analysis results demonstrated that Cu ion was successfully introduced into the Y₂Ba₂O₅lattice of which grain size decreased from 62.1 nm to 54.7 nm. The systematic substitution of Cu²⁺for Ba²⁺in Y₂Ba₂O₅ changed color from white to green (a*=-21.61) and decreased band gap from 2.30 eV to 2.04 eV. These pigment samples revealed the uniform spherical-like morphology with an average size of 150-300 nm. When Cu²⁺ was introduced, the infrared reflectance of pigment sample was decreased. However, the pigment still displayed high near infrared reflectance (68.80%) and solar reflectance (45.95%), while the doping of Cu²⁺ up to x=0.50. Therefore, such green high near-infrared reflectance from these Y₂Ba₍₂_-x₎Cu_xO₅ powders have great potential in serving as cool pigments for building coatings.

Key words: Sol-Gel, green pigment, near-infrared reflectance, band gap

中图分类号:

TQ174

姜峻, 姚伯龙, 高旭瑞, 王利魁, 李洪萍, 邓丽朵. 铜离子掺杂Y₂Ba₂O₅高近红外反射颜料的制备和光学性能研究[J]. 无机材料学报, 2016, 31(6): 641-646.

JIANG Jun, YAO Bo-Long, GAO Xv-Rui, WANG Li-Kui, LI Hong-Ping, DENG Li-Duo. Synthesis and Optical Properties of Copper Doped Y₂Ba₂O₅Pigments with High Near-infrared Reflectance[J]. Journal of Inorganic Materials, 2016, 31(6): 641-646.

图/表 10

图1 Y2Ba(2-x)CuxO5(x=0~1.0)粉末的XRD图谱(a)及其2θ在28.0º~31.3º范围内的放大图谱(b)

Fig. 1 Powder X-ray diffraction patterns of Y2Ba(2-x)CuxO5(x=0-1.0) (a) and the expanded XRD patterns in the 2θ range of 28.0°-31.3° (b)

表1 Y2Ba(2-x)CuxO5(x=0~1.0)粉末的晶胞参数和晶粒尺寸

Table 1 Lattice parameters and crystallite size of the Y2Ba(2-x)CuxO5(x=0-1.0) powder

Pigment composition Y₂Ba_(2-_x)Cu_xO₅	Lattice parameter/nm			Crystallite size /nm
Pigment composition Y₂Ba_(2-_x)Cu_xO₅	a	b	c	Crystallite size /nm
x=0	0.4377 1.2210 1.2201 1.2183 1.2176	0.4377	1.1852	62.1 61.0 59.8 56.5 54.7
x=0.25		0.5602	0.7121
x=0.50		0.5629	0.7124
x=0.75		0.5642	0.7129
x=1.0		0.5655	0.7130

图2 绿色颜料Y2Ba(2-x)CuxO5(x=0~1.0)的拉曼光谱

Fig. 2 Raman spectra of Y2Ba(2-x)CuxO5(x=0-1.0) green pigments

图3 Y2Ba2O5(A)、Y2Ba1.5Cu0.5O5(B)和Y2BaCuO5(C)的FESEM照片

Fig. 3 FESEM images of Y2Ba2O5 (A), Y2Ba1.5Cu0.5O5 (B) and Y2BaCuO5 (C)

图4 粉末颜料Y2Ba(2-x)CuxO5(x=0~1.0)的数码照片

Fig. 4 Photographs of Y2Ba(2-x)CuxO5(x=0-1.0) powder pigments

表2 粉末颜料Y2Ba(2-x)CuxO5(x=0~1.0)色度坐标和禁带宽度

Table 2 Color coordinates and band gap of the Y2Ba(2-x)CuxO5(x=0-1.0) powder pigments

Pigment Y₂Ba_(2-_x₎Cu_xO₅	Color coordinates				Band gap /eV
Pigment Y₂Ba_(2-_x₎Cu_xO₅	L*	a*	b*	C*	Band gap /eV
x=0	90.83	-1.76	12.68	12.76	2.30 2.16 2.08 2.04 2.04
x=0.25	58.13	-13.83	11.37	17.90
x=0.50	56.40	-17.09	10.29	19.95
x=0.75	54.03	-18.67	11.53	21.94
x=1.0	51.86	-21.61	4.50	22.07

图5 粉末颜料Y2Ba(2-x)CuxO5 (x= 0~1.0)的紫外-可见漫反射光谱图

Fig. 5 UV-Vis diffuse reflectance spectra of Y2Ba(2-x)CuxO5 (x= 0-1.0) powder pigments

表3 粉末颜料Y2Ba(2-x)CuxO5(x=0~1.0)近红外反射率和太阳光反射率

Table 3 Values of NIR reflectance and solar reflectance of Y2Ba(2-x)CuxO5(x=0-1.0) powder pigments

Pigment Y₂Ba_(2-_x₎Cu_xO₅	x=0	x=0.25	x=0.50	x=0.75	x=1.0
NIR reflectance/%	85.87	70.53	68.80	67.32	56.38
Solar reflectance, R*/%	63.78	47.49	45.95	42.07	38.83

图6 粉末颜料Y2Ba(2-x)CuxO5(x =0~1.0)近红外反射光谱图

Fig. 6 NIR reflectance spectra of Y2Ba(2-x)CuxO5 (x=0-1.0) powder pigments

图7 粉末颜料Y2Ba(2-x)CuxO5(x =0~1.0)近红外太阳光反射谱图

Fig. 7 NIR solar reflectance spectra of Y2Ba(2-x)CuxO5 (x= 0-1.0) powder pigments

参考文献 21

[1]	VISHNU V S, REDDY M L.Near-infrared reflecting inorganic pigments based on molybdenum and praseodymium doped yttrium cerate: Synthesis, characterization and optical properties.Solar Energy Materials and Solar Cells, 2011, 95(9): 2685-2692.
[2]	JOSE S, REDDY M L.Lanthanum-strontium copper silicates as intense blue inorganic pigments with high near-infrared reflectance.Dyes and Pigments, 2013, 98(3): 540-546.
[3]	WANG D, SU D, ZHONG M.Chromatic and near-infrared reflective properties of Fe3+ doped KZnPO4.Solar Energy, 2014, 110: 1-6.
[4]	MASUI T, HONDA T, IMANAKA N.Novel and environmentally friendly (Bi, Ca, Zn) VO4 yellow pigments.Dyes and Pigments, 2013, 99(3): 636-641.
[5]	KE S, WANG Y, PAN Z.Synthesis of Nd2Si2O7 ceramic pigment with LiCl as a mineralizer and its color property.Dyes and Pigments, 2014, 108: 98-105.
[6]	GEORGE G, VISHNU V S, REDDY M L P. The synthesis, characterization and optical properties of silicon and praseodymium doped Y6MoO12 compounds: environmentally benign inorganic pigments with high NIR reflectance.Dyes and Pigments, 2011, 88(1): 109-115.
[7]	GEORGE G, KUMARI L S, VISHNU V S, et al.Synthesis and characterization of environmentally benign calcium-doped Pr2Mo2O9 pigments: applications in coloring of plastics.Journal of Solid State Chemistry, 2008, 181(3): 487-492.
[8]	VISHNU V S, GEORGE G, DIVYA V, et al.Synthesis and characterization of new environmentally benign tantalum-doped Ce0.8Zr0.2O2 yellow pigments: applications in coloring of plastics.Dyes and Pigments, 2009, 82(1): 53-57.
[9]	SREERAM K J, KUMERESAN S, RADHIKA S, et al.Use of mixed rare earth oxides as environmentally benign pigments.Dyes and Pigments, 2008, 76(1): 243-248.
[10]	RAJ A K V, RAO P P, SAMEERA S, et al. Pigments based on terbium-doped yttrium cerate with high NIR reflectance for cool roof and surface coating applications. Dyes and Pigments, 2015, 122: 116-125.
[11]	KRUAEHONG T.Electrical properties and crystal structure of Y123, Y358 and Y257/Y211 composite bulk superconductors.International Journal of Physical Sciences, 2014, 9(16): 360-367.
[12]	SHI Y, HASAN T, BABU N H, et al.Synthesis of YBa2Cu3O7-δ and Y2BaCuO5 nanocrystalline powders for YBCO superconductors using carbon nanotube templates.ACS Nano, 2012, 6(6): 5395-5403.
[13]	NAMBURI D K, SHI Y, PALMER K G, et al.An improved top seeded infiltration growth method for the fabrication of Y-Ba-Cu-O bulk superconductors.Journal of the European Ceramic Society, 2016, 36(3): 615-624.
[14]	GEORGE G.The structural and optical studies of titanium doped rare earth pigments and coloring applications.Dyes and Pigments, 2015, 112: 81-85.
[15]	RAJ A K V, RAO P P, SAMEERA S, et al. Pigments based on terbium-doped yttrium cerate with high NIR reflectance for cool roof and surface coating applications.Dyes and Pigments, 2015, 122: 116-125.
[16]	HAN A, YE M, ZHAO M, et al.Crystal structure, chromatic and near-infrared reflective properties of iron doped YMnO3 compounds as colored cool pigments.Dyes and Pigments, 2013, 99(3): 527-530.
[17]	VISINESCU D, PARASCHIV C, IANCULESCU A, et al.The environmentally benign synthesis of nano-sized CoxZn1-xAl2O4 blue pigments.Dyes and Pigments, 2010, 87(2): 125-131.
[18]	RADHIKA S, SREERAM K J, NAIR B U.Effective synthesis route for red-brown pigments based on Ce-Pr-Fe-O and their potential application for near infrared reflective surface coating.Journal of Chemical Sciences, 2014, 126(1): 65-73.
[19]	DILAWAR N, MEHROTRA S, VARANDANI D, et al.A Raman spectroscopic study of C-type rare earth sesquioxides.Materials Characterization, 2008, 59(4): 462-467.
[20]	ABRASHEV M V, TODOROV N D, GESHEV J.Raman spectra of R2O3 (R-rare earth) sesquioxides with C-type bixbyite crystal structure: a comparative study.Journal of Applied Physics, 2014, 116(10): 103508.
[21]	THONGKANLUANG T, KITTIAUCHAWAL T, LIMSUWAN P.Preparation and characterization of Cr2O3-TiO2-Al2O3-V2O5 green pigment.Ceramics International, 2011, 37(2): 543-548.

铜离子掺杂Y₂Ba₂O₅高近红外反射颜料的制备和光学性能研究

Synthesis and Optical Properties of Copper Doped Y₂Ba₂O₅Pigments with High Near-infrared Reflectance

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

图/表 10

参考文献 21

相关文章 15

编辑推荐

Metrics

本文评价

[1]	沈斌, 张旭, 熊怀, 李海元, 谢兴龙. 溶胶-凝胶SiO₂减反膜的制备与光学性能研究[J]. 无机材料学报, 2024, 39(5): 525-530.
[2]	戴乐, 刘洋, 高轩, 王书豪, 宋雅婷, 唐明猛, 刘丽莎, 汪尧进. 浓度梯度掺杂实现BiFeO₃薄膜自极化[J]. 无机材料学报, 2024, 39(1): 99-106.
[3]	贾玉娜, 曹旭, 焦秀玲, 陈代荣. 无机酸铝体系氧化铝连续纤维的制备技术研究[J]. 无机材料学报, 2023, 38(11): 1257-1264.
[4]	满鑫, 吴南, 张牧, 贺红亮, 孙旭东, 李晓东. Lu₂O₃-MgO纳米粉体合成及其复相红外透明陶瓷制备[J]. 无机材料学报, 2021, 36(12): 1263-1269.
[5]	杨丛纲, 米乐, 冯爱虎, 于洋, 孙大志, 于云. KH-560改性SiO₂绝缘薄膜的制备及性能研究[J]. 无机材料学报, 2021, 36(12): 1343-1348.
[6]	朱本必,张旺,张志坚,章建忠,IMRAN Zada,张荻. 光热增强光催化性能二氧化钛(B)/玻纤布复合研究[J]. 无机材料学报, 2019, 34(9): 961-966.
[7]	张少丹, 包维维, 马海萍. Cu ²⁺、Tb ³⁺共掺杂BaZrO₃高近红外反射颜料的制备及其性能研究[J]. 无机材料学报, 2019, 34(6): 599-604.
[8]	刘茜, 周真真. 低温活化合成含硅氮氧化物材料研究进展[J]. 无机材料学报, 2018, 33(2): 129-137.
[9]	赵慧月, 王晓栋, 冯建斌, 刘源, 黄吉辰, 沈军. NH₃/HTMS气相法改性SiO₂增透膜的耐环境稳定性[J]. 无机材料学报, 2018, 33(11): 1219-1224.
[10]	何飞, 李亚, 骆金, 方旻翰, 赫晓东. 具有气凝胶结构特征的C/SiO₂和C/SiC复合材料研究进展[J]. 无机材料学报, 2017, 32(5): 449-458.
[11]	路淑娟, 王唱, 赵博文, 汪浩, 刘晶冰, 严辉. PEG改性氧化钨薄膜的电致变色特性[J]. 无机材料学报, 2017, 32(2): 185-190.
[12]	陈婷, 查剑锐, 张筱君, 江伟辉, 江莞, 刘健敏, 吴倩. 硅烷偶联剂对制备硅酸锆薄膜及其抗氧化性能的影响[J]. 无机材料学报, 2017, 32(11): 1154-1158.
[13]	郑磊, 李劲, 刘洪波. AEP作用下溶胶-凝胶法制备纤维素基炭气凝胶及其对水溶液中Cu²⁺吸附性能[J]. 无机材料学报, 2017, 32(11): 1159-1164.
[14]	马鹏飞, 李日红, 张龙. 溶胶-凝胶法制备高比表面积铝磷钙生物活性玻璃[J]. 无机材料学报, 2017, 32(1): 107-112.
[15]	胡亚华, 顾牡, 张致远, 刘小林, 黄世明, 刘波, 张娟楠. Lu₂O₃纳米线阵列的超声辅助溶胶-凝胶模板法制备与表征[J]. 无机材料学报, 2016, 31(8): 807-811.