Preparation, Microstructure, and Conductive Properties of BaPbO3 Thin Films

  • LU Yu-Dong ,
  • WANG Xin ,
  • ZHUANG Zhi-Qiang
Expand
  • College of Materials Science and Engineering, South China University of Technology, Guangzhou 510640, China

Received date: 2006-02-17

  Revised date: 2006-04-04

  Online published: 2007-01-20

Fold

Abstract

Crackfree and small grain size perovskite-type ceramic BaPbO3 conductive thin films were deposited onto Al2O3 substrates by a modified sol-gel method using ethylene diamine tetra-acetic acid (EDTA), citric acid, and tartaric acid as the complex chelate agent. XRD, SEM, and EDS tests, together with resistivity date,
show a good correlation among the Pb to Ba ratio, grain size, and sheet
resistance. Experimental results demonstrate that BaPbO3 thin films with
homogeneous composition can be prepared by the method mentioned above.
Sheet resistance of BaPbO3 thin films decreases with Pb to Ba ratio or grain size increases. The influence of heat treatment on sheet resistance is related with the thickness of BaPbO3 thin films. The best electrical properties were obtained upon a rapid thermal anneal (RTA) at 700℃ for 10 min. Perovskite BaPbO3 films with sheet resistance of 5.86Ω﹒□-1 were derived from 20 spin-coating layers and annealed at 700℃ for 10min.

Key words： BaPbO3; ceramic; thin film; sol-gel; sheet resistance

Cite this article

LU Yu-Dong , WANG Xin , ZHUANG Zhi-Qiang . Preparation, Microstructure, and Conductive Properties of BaPbO3 Thin Films[J]. Journal of Inorganic Materials, 2007 , 22(1) : 138 -142 . DOI: 10.3724/SP.J.1077.2007.00138

References

[1] 王歆, 陆裕东, 庄志强(WANG Xin, et al). 材料导报(materials Review), 2005, 19 (7): 24--28.
[2] Shannon R D, Bierstedt P E. J. Am. Ceram. Soc., 1970, 11 (53): 635--636.
[3] Sleight A W, Gillson J L, Bierstedt P E. Solid State Commun., 1975, 17 (1): 27--28.
[4] Cava R J, Batlogg B, Karjewski J J, et al. Nature, 1988, 336 (6196): 814--817.
[5] Luo Y R, Wu J M. Appl. Phys. Lett., 2001, 79 (22): 3669--3671.
[6] Liang C S, Wu J M, Chang M C. Appl. Phys. Lett., 2002, 81 (4): 3624--3626.
[7] Luo Y R, Wu J M. Jpn. J. Appl. Phys., 2003, 42 (1): 242--246.
[8] Hiremath B V, Newnham R E, Cross L E. J. Am. Ceram. Soc., 1992, 75 (11): 2953--2958.
[9] Kao W H, Haberrichter S L, Bullock K R. J. Electrochem. Soc., 1992, 139 (11): L105--L107.
[10] 刘远良, 杜丕一, 翁文剑, 等(LIU Yuan-Liang, et al). 无机材料学报(Journal of Inorganic Materials), 2005, 20 (1): 151--157.
[11] 陆裕东, 王歆, 庄志强(LU Yudong, et al). 稀有金属(Chinese Journal of Rare Earth), 2005, 29 (5): 643--646.
Options
Outlines

/

〈 〉