Fabrication and Characterization of Highly Ordered Zinc Oxide Nanowire/Tube Arrays by Sol-Gel Template Method

Abstract

Abstract: Highly ordered zinc oxide nanowire/tube arrays were prepared by a sol-gel method in the pores of anodic alumina membranes (AAM). The morphology and crystalloid structure of zinc oxide nonawire/tube arrays were characterized by scanning electron microscope(SEM), transmission electron microscope (TEM) and X-ray diffraction (XRD). The results show that zinc oxide nonawires are very uniformly assembled and parallel to each other in the pores of the AAM template. The length and diameter of nanowires are dependen on the thickness and hole diameter of AAM. Zinc oxide nanotube arrays can be controlled by changing immersing time, temperature and concentration of the sol.

Key words: anodic alumina membrane, sol-gel, zinc oxide nanowire/tube arrays

CLC Number:

O614
TB383

YU Mei,LIU Jian-Hua,LI Song-Mei,WEI Wei. Fabrication and Characterization of Highly Ordered Zinc Oxide Nanowire/Tube Arrays by Sol-Gel Template Method[J]. Journal of Inorganic Materials.

References

[1] Hu J T, Odom T W, Lieber C M. Ace. Chem. Res., 1999, 32: 435.
[2] 赵启涛, 候立松, 黄瑞安. 物理化学学报(Acta Chim. Sinica), 2003, 61 (10): 1671-1674.
[3] Chu S Z, Wada K, Inoue S, et al. Electrochimica Acta, 2003, 48: 3147-3153.
[4] Rahman I Z, Razeeb K M, Rahman M A, et al. J. Magnetism and Magnetic Mater., 2003, 262: 166-169.
[5] Forrer P, Schlottig F, Siegenthaler H, et al. J. Appl. Electrochem., 2000, 30: 533-541.
[6] Xu Hui, Qin Dong-Huan, Yang Zhi, et al. Mater. Chem. and Phys., 2003, 80: 524-528.
[7] Limmer S J, Seraji S, Wu Yun. Adv. Func. Mater., 2002, 1: 59-64.
[8] Zheng M J, Zhang L D, Li G H, et al. Chemical Physics Letters, 2002, 363: 123-128.
[9] Li Y, Cheng G S, Zhang L D. J. Mater. Res., 2000, 15 (11): 2305-2308.
[10] 苏轶坤, 王臻, 力虎林. 高等学校化学学报(Chem. J. Chinese Universities), 2002, 23 (5): 944-946.
[11] 周晓红, 赵秀琴. 安庆师范学院学报 (自然科学版)(Journal of Anqing Teachers College (Nature Science)), 2003, 9 (2): 4-6.
[12] 沈茹娟, 贾殿赠, 梁凯, 等. 无机化学学报(Chinese Journal of Inorganic Chemistry), 2000, 16 (6): 906-910.
[13] 彭忠东, 杨建红, 邓朝阳, 等. 中国有色金属学报(the Chinese Journal of Nonferrous Metals), 2000, 10 (4): 579-583.
[14] 刘建华, 孙杰, 李松梅, 等. 复合材料学报(Acta Matariae Compositae Sinica), 2003, 20 (6): 121-124.
[15] 陈尔凡, 田雅娟, 程远杰, 等. 高等学校化学学报(Chemical Journal of Chinese University), 2000, 21 (2): 172-176.
[16] 宋旭春, 徐铸德, 陈卫祥, 等(SONG Xu-Chun, et al). 无机?化学学报(Chinese Journal of Inorganic Chemistry), 2004, 20 (2): 186-190.
[17] 何顺爱, 周双喜, 张兰, 等. 桂林工学院学报(Journal of Guilin Institute of Technology), 2004, 24 (1): 80-83.
[18] Brinda B L, Peter K D, Charles R M. Chem. Mater., 1997, 9: 857-862.
[19] Hiheki M, Kenji F. Science, 1995, 268: 1466-1468.
[20] Hideki M, Haruki Y, Masahiro S, et al. Appl. Phys. Lett., 1997, 71 (19): 2770-2772.
[21] Brinda B L, Charles J P, Charles R M. Chem. Mater., 1997, 9: 2544-2550.