Al/Cr₂O₃复合粒子的制备及其多波段兼容隐身性能的研究

陈娇¹, 黄啸谷¹, 韩朋德¹, 王丽熙¹, 张其土^1,2

(南京工业大学 1. 材料科学与工程学院; 2. 江苏省无机及其复合新材料重点实验室, 南京 210009)

收稿日期:2010-03-23 修回日期:2010-05-24 出版日期:2010-12-20 网络出版日期:2010-11-24
基金资助:
国家部委科技资助项目(JPPT-1251)

Preparation and Multiple-band Stealth Properties of Al/Cr₂O₃ Composite Particles

CHEN Jiao¹, HUANG Xiao-Gu¹, HAN Peng-De ¹, WANG li-Xi ¹, ZHANG Qi-Tu ^{1, 2}

(1. College of Materials Science and Engineering, Nanjing University of Technology, Nanjing 210009, China; 2. Jiangsu Provincial Key Laboratory of New Materials of Inorganic and its Composites, Nanjing University of Technology, Nanjing 210009, China)

Received:2010-03-23 Revised:2010-05-24 Published:2010-12-20 Online:2010-11-24
Supported by:
National Ministries Funded Projects(JPPT-1251)

摘要/Abstract

摘要： 采用共沉淀法将Cr₂O₃包覆于片状金属铝粉表面制得Al/Cr₂O₃复合粒子. 借助于TG-DSC、XRD、SEM等测试手段系统研究了反应时间和煅烧温度分别对复合粒子的物相组成、包覆前后形貌的影响. 此外, 探讨了不同铝粉添加量下Al/Cr₂O₃粉末的红外辐射率和1.06 μm波长处的反射率性能. 结果表明: 当反应时间为2h、煅烧温度为400℃、铝粉添加量为50wt%时制得的Al/Cr₂O₃复合粒子包覆较为完整, 其外观呈墨绿色, 红外辐射率值为0.66, 1.06 μm波长处的反射率为0.41%, 具有良好的红外-激光-可见光兼容隐身性能.

关键词: Al/Cr₂O₃复合粒子, 共沉淀法, 复合隐身性能

Abstract: Al/Cr₂O₃ composite particles were prepared by co-precipitation method. Effects of reaction time and calcination temperature on phase composition and morphology were studied by TG-DSC, XRD and SEM. In addition, the infrared emissivity and the reflectivity of Al/Cr₂O₃ powders with different aluminum contents at the wavelength of 1.06 μm were also discussed. The results show that the Al/Cr₂O₃composite particles with 50wt% aluminum is well coated after reacted for 2h and calcined at 400℃.The optimized Al/Cr₂O₃ composite particles exhibit dark green appearance for visible light stealth, low emissivity of 0.66 for infrared stealth and low reflectivity of 0.41% for strong laser absorption at the wavelength of 1.06 μm.

Key words: Al/Cr₂O₃ composite particles, co-precipitation method, compound stealthy properties

中图分类号:

TQ637

陈娇, 黄啸谷, 韩朋德, 王丽熙, 张其土. Al/Cr₂O₃复合粒子的制备及其多波段兼容隐身性能的研究[J]. 无机材料学报, 2010, 25(12): 1298-1302.

CHEN Jiao, HUANG Xiao-Gu, HAN Peng-De, WANG li-Xi, ZHANG Qi-Tu. Preparation and Multiple-band Stealth Properties of Al/Cr₂O₃ Composite Particles[J]. Journal of Inorganic Materials, 2010, 25(12): 1298-1302.

参考文献

[1] 刘默伟, 李航. 红外隐身技术的发展分析. 舰船电子工程, 2009, 29(5): 25-27. [2] Bechtold W. Production of camouflage material effective in visible, infrared and radar spectra comprises manufacturing textile support, removing surfactants and applying metal coating, primer and camouflage lacquer in my patents list. CH 692761. 2002. [3] 邹振宁, 冷锋, 周芸. 光电对抗技术和装备现状评析. 电光与控制, 2004, 11(3): 30-34. [4] Zhou Y, Kang Y Q, Fang X Y, et al. Mechanism of enhanced dielectric properties of SiC/Ni nanocomposites. Chin. Phys. Lett., 2008, 25(5): 1902-1904. [5] Zou G Z, Cao M S, Zhang L, et al. A nanoscale core-shell of β-SiCP-Ni prepared by electroless plating at lower temperature. Surface & Coatings Technology, 2006, 201(1/2): 108-112. [6] 邹桂真, 曹茂盛, 张亮, 等(ZOU Gui-Zhen, et al). 化学镀制备Ni包覆纳米SiC核壳颗粒及其介电响应. 无机材料学报(Journal of Inorganic Materials), 2006, 21(4): 797-802. [7] Zou G Z, Cao M S, Lin Haibo, et al. Nickel layer deposition on SiC nanoparticles by simple electroless plating and its dielectric behaviors. Powder Technology, 2006, 168(2): 84-88. [8] Kang Y Q, Cao M S, Shi X L, et al. The enhanced dielectric from basalt fibers/nickel core-shell structures synthesized by electroless plating. Surface & Coatings Technology, 2007, 201(16/17): 7201-7206. [9] 李凤生, 杨毅. 纳米/微米复合技术及应用. 北京: 国防工业出版社, 2002. [10] 赖文忠, 董校捷, 黄婧, 等(LAI Wen-Zhong, et al). Co/Co9S8/ZnO核壳结构纳米微球的制备与表征. 无机材料学报(Journal of Inorganic Materials), 2010, 25(3): 265-270. [11] Kang Y Q, Cao M S, Yuan J, et al. Orientation-dependent electromagnetic properties of basalt fibre/nickel core-shell heterostructures. Chin. Phys. B, 2007, 19(1): 017701. [12] 徐扬子, 胡鹤(XU Yang-Zi, et al). ZnS包覆SiO2核壳和空腔结构纳米球制备研究. 无机材料学报(Journal of Inorganic Materials), 2007, 22(5): 847-852. [13] Masala O, Seshadri R. Spinel ferrite/MnO core/shell nanoparticles: chemical synthesis of all-oxide exchange biased architectures. J. Am. Chem. Soc., 2005, 127(26): 9354-9355. [14] 武晓威, 冯玉杰, 韦韩, 等(WU Xiao-Wei, et al). Ni-P化学镀制备钡铁氧体基红外-微波一体化隐身材料. 无机材料学报(Journal of Inorganic Materials), 2009, 24(1): 97-102. [15] 周建华, 王涛, 王道军, 等(ZHOU Jian-Hua, et al). 葡萄糖基碳包覆ZnFeO的合成及其红外发射率的研究. 无机材料学报(Journal of Inorganic Materials), 2009, 24(5): 1045-1048. [16] Hubbard, Ronald N. Radio frequency transparent infrared reflective coating materials and methods of making the same. US 5506053. 1996. [17] 魏美玲, 任卫, 程之强, 等. 超细陶瓷粉及铁粉的表面化学包覆改性的研究. 现代技术陶瓷, 2000(1): 3-6. [18] Kang Y Q, Cao M S, Yuan J, et al. Preparation and microwave absorption properties of basalt fibre/nickel core-shell heterostructures. Journal of Alloys and Compounds, 2010, 495(1): 254-259. [19] 杨毅, 刘永峙, 李凤生, 等. 纳米氧化亚镍包覆铝复合粒子的制备. 化工学报, 2005, 56(11): 2228-2232. [20] 杨丽君. 氧化铬晶体的结构及制备和用途. 渝西学院学报(自然科学版), 2003, 2(4): 9-11. [21] 闵乃本. 晶体生长的物理基础. 上海: 上海科学技术出版社, 1982. [22] 蔡森, 张松, 李永. 军用装备用太阳热反射涂料发展现状及趋势. 装备环境工程, 2009, 6(2): 9-13. [23] Aspnes D E. Optical response of microscopically rough surface. Phys. Rev. B, 1990, 41(10): 10334-10343. [24] 黄芸, 何伟, 许仲梓, 等. 掺铝氧化锌粉末的制备及其性能研究. 功能材料, 2009, 40(3): 494-497.

Al/Cr₂O₃复合粒子的制备及其多波段兼容隐身性能的研究

Preparation and Multiple-band Stealth Properties of Al/Cr₂O₃ Composite Particles

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	刘子玉, TOCI Guido, PIRRI Angela, PATRIZI Barbara, 冯亚刚, 陈肖朴, 胡殿君, 田丰, 吴乐翔, VANNINIMatteo, 李江. 固体激光用Nd:Lu₂O₃透明陶瓷的制备和光学性能研究[J]. 无机材料学报, 2021, 36(2): 210-216.
[2]	黄新友, 刘玉敏, 刘洋, 李晓英, 冯亚刚, 陈肖朴, 陈鹏辉, 刘欣, 谢腾飞, 李江. 醇水共沉淀法制备Yb:YAG透明陶瓷及其性能研究[J]. 无机材料学报, 2021, 36(2): 217-224.
[3]	李晓英, 刘强, 胡泽望, 姜楠, 石云, 李江. 碳酸氢铵与金属阳离子摩尔比对共沉淀法合成铽镓石榴石纳米粉体及陶瓷性能的影响[J]. 无机材料学报, 2019, 34(7): 791-797.
[4]	韦家蓓, TOCIGuido, PIRRIAngela, PATRIZIBarbara, 冯亚刚, VANNINIMatteo, 李江. 共沉淀纳米粉体制备Yb:CaF₂激光陶瓷及其性能研究[J]. 无机材料学报, 2019, 34(12): 1341-1348.
[5]	伍青峰, 崔亚娟, 张海龙, 周怡, 兰丽, 王健礼, 陈耀强. 改进共沉淀法以提高三效催化剂中铈锆复合氧化物的热稳定性[J]. 无机材料学报, 2017, 32(3): 331-336.
[6]	曲婷, 黄强, 赵振波. Bi₂MoO₆/Ni-Fe LDH复合材料的制备及可见光催化性能[J]. 无机材料学报, 2015, 30(8): 825-832.
[7]	彭诚, 张楚鑫, 吕明, 李智鸿, 吴建青. 共沉淀法制备硅酸锆包裹炭黑及其高温稳定性[J]. 无机材料学报, 2013, 28(8): 847-852.
[8]	王凯风, 刘伟, 王金淑. 铝酸盐的组成对钡钨阴极性能的影响[J]. 无机材料学报, 2013, 28(12): 1354-1358.
[9]	刘超峰, 张鸿, 夏俊霄, 李根, 李志成. La_9.33Si₆O₂₆基氧离子导电复合材料的制备与导电性[J]. 无机材料学报, 2011, 26(10): 1043-1048.
[10]	张东炎,张惠敏,靳先静,常爱民. Co_0.8Mn_0.8Ni_0.9Fe_0.5O₄ 纳米粉体的制备及热敏特性研究[J]. 无机材料学报, 2009, 24(5): 1008-1012.
[11]	周鼎,施鹰,云平,谢建军. 不同沉淀剂对Nd³⁺∶Lu₂O₃纳米粉体性能的影响[J]. 无机材料学报, 2009, 24(4): 764-768.
[12]	杨修春,卢振光,康晓春,韦亚南. ZrO₂对NiO/CeO₂/γ-Al₂O₃复合催化剂结构的影响[J]. 无机材料学报, 2009, 24(1): 187-191.
[13]	张志萍,刘红飞,程晓农. 共沉淀法合成ZrO₂-ZrW₂O₈复合材料的工艺研究[J]. 无机材料学报, 2008, 23(5): 991-995.
[14]	施鹰,陈启伟,施剑林. 沉淀剂对共沉淀法制备 Lu₂O₃发光粉体形貌的影响[J]. 无机材料学报, 2008, 23(4): 824-828.
[15]	刘银,丘泰. 纳米晶 Ni_1-x Zn_xFe₂O₄铁氧体粉料的制备及其磁性能研究[J]. 无机材料学报, 2007, 22(3): 391-394.