膜厚对SnO2厚膜型气敏器件灵敏度的影响

傅军   

  1. 海南师范学院物理系; 海口 571158
  • 收稿日期:1999-03-01 修回日期:1900-01-01 出版日期:1999-12-20 网络出版日期:1999-12-20

Effects of Film Thickness on the Gas Sensitivity of SnO2 Thick Film Sensors

FU Jun   

  1. Department of Physics; Hainan Normal University; Haikou 571158; China
  • Received:1999-03-01 Revised:1900-01-01 Published:1999-12-20 Online:1999-12-20

PDF (PC)

1094

摘要： 本文通过制备不同膜厚的纳米SnO2厚膜型气敏器件试样，测量试样对乙醇气体的灵敏度和试样的阻温曲线并进行复阻抗分析，研究了试样的膜厚对灵敏度的影响．SnO2纳米材料由化学沉淀法制备，采用平面丝网印刷技术制作不同膜厚的气敏试样．结果表明，试样膜厚在65μm左右对乙醇气体具有最大灵敏度．膜厚对灵敏度的影响可能与膜层的晶粒接触状态如接触面积、气孔率、气孔宽度和深度等发生变化有关．

关键词: SnO2厚膜, 气体灵敏度, 复阻抗分析, 丝网印刷

Abstract: The effects of film thickness on the gas-sensing properties of SnO2 thick film sensors were explored by
measuring the ethanol gas sensitivity, the variations in resistance with temperature and analyzing the complex impedance plots. The nanoparticles
were synthesized by chemical precipitation method and films were prepared by standard screen printing technology. The results showed that the sample
having 65μm thickness gave the maximum sensitivity. Changes in sensitivity with thickness might be caused by changes in the state of films, such as the
number and the width and depth of the pores.

Key words: SnO2 thick film sensor, gas sensitivity, complex impedance, screen printing