3D打印氧化铝陶瓷的气氛脱脂热处理工艺研究

doi:10.15541/jim20210634

无机材料学报 ›› 2022, Vol. 37 ›› Issue (3): 333-337.DOI: 10.15541/jim20210634 CSTR: 32189.14.10.15541/jim20210634

3D打印氧化铝陶瓷的气氛脱脂热处理工艺研究

曾勇¹^,²^,³(), 张子佳¹^,²^,³, 孙立君¹^,²^,³, 姚海华¹^,²^,³, 陈继民¹^,²^,³

1.北京工业大学材料与制造学部, 北京 100124
2.北京市数字化医疗3D打印工程技术研究中心, 北京 100124
3.跨尺度激光成型制造技术教育部重点实验室, 北京 100124

收稿日期:2021-10-12 修回日期:2021-10-25 出版日期:2022-03-20 网络出版日期:2021-11-01
作者简介:曾勇(1987-), 男, 副教授. E-mail: zengyong@bjut.edu.cn
基金资助:
北京市教委科研计划(KM2020100050003)

Atmosphere Debinding Heat Treatment of 3D Printed Alumina Ceramics

ZENG Yong¹^,²^,³(), ZHANG Zijia¹^,²^,³, SUN Lijun¹^,²^,³, YAO Haihua¹^,²^,³, CHEN Jiming¹^,²^,³

1. Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100124, China
2. Beijing Engineering Research Center of 3D Printing for Digital Medical Health, Beijing 100124, China
3. Key Laboratory of Trans-scale Laser Manufacturing Technology, Ministry of Education, Beijing 100124, China

Received:2021-10-12 Revised:2021-10-25 Published:2022-03-20 Online:2021-11-01
About author:ZENG Yong (1987-), male, associate professor. E-mail: zengyong@bjut.edu.cn
Supported by:
Scientific Research Project of Beijing Education Committee(KM2020100050003)

摘要/Abstract

摘要：

脱脂热处理工艺对于3D打印陶瓷的成形质量具有重要的影响。目前光固化3D打印制备得到的氧化铝生坯经过在空气中的脱脂热处理工艺后烧结最终得到的氧化铝陶瓷存在的微观裂纹等缺陷, 将导致其力学性能较差。本工作研究了基于数字光处理(Digital light processing, DLP)技术的氧化铝陶瓷打印热处理工艺, 将3D打印制备得到的氧化铝陶瓷生坯分别在空气与氩气中脱脂后比较其宏观形貌, 发现在空气下脱脂的氧化铝生坯存在微观裂纹。再将脱脂后的生坯在空气下烧结得到氧化铝陶瓷, 并对其微观形貌和宏观性能进行表征, 发现在氩气下脱脂的氧化铝陶瓷平均晶粒尺寸要比直接在空气中脱脂得到的氧化铝陶瓷平均晶粒尺寸大, 而且晶粒结构致密, 无明显气孔和杂相, 而且具有更高的抗压强度。这说明在氩气中脱脂后烧结得到的氧化铝陶瓷性能更好。在氩气中脱脂的氧化铝致密度最高可达到96.72%, 抗压强度可达到761.7 MPa, 相比于只在空气中脱脂的氧化铝陶瓷性能得到显著提升。

关键词: 数字光处理技术(DLP), 氧化铝, 氩气脱脂, 空气脱脂

Abstract:

Debinding heat treatment process play an important role in forming quality of 3D printing ceramics. At present, the alumina green body prepared by light curing 3D printing is sintered after debinding in air. The final alumina ceramics may have defects such as micro cracks, resulting in poor mechanical properties. Direct heating and debinding in air may lead to cracks caused by reaction between resin and oxygen in green body. To avoid this situation, this work studies the printing heat treatment process of alumina ceramics based on digital light processing (DLP) technology. The alumina ceramic green body prepared by 3D printing was degreased either in air or in argon, and their macro morphologies were compared with each other. It is found that there are micro cracks in the alumina green body debinding in air. After being sintered in air, the alumina ceramics was obtained and their micro morphology and macro properties were characterized. Average grain size of alumina ceramics debinding in argon was larger than that directly debinding in air, while the grain structure was dense without obvious pore and impurity. Moreover, in terms of mechanical properties, alumina ceramics debinding in air have higher compressive strength. The highest density of alumina debinding in argon reaches 96.72%, and the compressive strength reaches 761.7 MPa, significantly improved as compared with the one debinding in air.

Key words: digital light processing (DLP), alumina, argon debinding, air debinding

中图分类号:

TQ174

曾勇, 张子佳, 孙立君, 姚海华, 陈继民. 3D打印氧化铝陶瓷的气氛脱脂热处理工艺研究[J]. 无机材料学报, 2022, 37(3): 333-337.

ZENG Yong, ZHANG Zijia, SUN Lijun, YAO Haihua, CHEN Jiming. Atmosphere Debinding Heat Treatment of 3D Printed Alumina Ceramics[J]. Journal of Inorganic Materials, 2022, 37(3): 333-337.

图/表 6

图1 氩气脱脂后在空气中烧结工艺曲线

Fig. 1 Sintering process curve in air after debinding in argon

图2 氧化铝生坯在不同气氛中脱脂得到的样品照片

Fig. 2 Photos of alumina green body obtained after debinding in different atmospheres (a) In air; (b) In argon

图3 氧化铝粉末和不同气氛下脱脂后烧结氧化铝陶瓷的SEM 照片

Fig. 3 SEM images of surface modified alumina powder and sintered alumina ceramics after debinding in different atmospheres (a) Surface modified alumina powder; (b) Sintered alumina ceramics after debinding in air; (c) Sintered alumina ceramics after debinding in argon

图4 氧化铝粉末和不同气氛脱脂后烧结氧化铝陶瓷的XRD图谱

Fig. 4 XRD patterns of alumina powders and sintered alumina ceramics after debinding in different atmospheres

表1 不同脱脂后烧结样品的收缩率和致密度

Table 1 Shrinkage and density of sintered samples after debinding in different atmospheres

Atmosphere	Shrinkage/%			Densification/%
Atmosphere	X	Y	Z	Densification/%
Air	4.81	4.55	9.23	95.39
Ar	5.62	5.48	11.54	96.72

图5 不同气氛下脱脂后烧结氧化铝陶瓷的应力-应变曲线

Fig. 5 Stress-strain curves of sintered alumina ceramics after debinding in different atmospheres

参考文献 22

[1]	CHEN Z W, LI Z Y, LI J J, et al. 3D printing of ceramics: a review. Journal of the European Ceramic Society, 2019, 39(4): 661-687. DOI URL
[2]	WANG J L, LI F L, HU B Q. Present situation and development of fine alumina in China. Ceramic, 2021(6): 12-14.
[3]	ZHU Z B, GUO Z J, LIU Y, et al. Development and application of alumina ceramics. Ceramic, 2003(1): 5-8.
[4]	SABAH A M, AZMAH H M A, JAAFAR C N A, et al. Effect of Cu metal of nanoscale particle size on the porosity and mechanical properties of porous alumina ceramics using yeast as a pore agent. Research Journal of Applied Sciences, Engineering and Technology, 2017, 14(5): 187-195.
[5]	MEZA L R, DAS S, GREER J R. Strong, lightweight, and recoverable three-dimensional ceramic nanolattices. Science, 2014, 345(6202): 1322-1326. DOI URL
[6]	ZHANG K Q, HE R J, DING G J, et al. Effects of fine grains and sintering additives on stereolithography additive manufactured Al₂O₃ ceramic. Ceramics International, 2021, 47(2): 2303-2310. DOI URL
[7]	BENGISU M. Engineering Ceramics. Berlin: Springer Science & Business Media, 2013: 115-126. 2013: 115-126.
[8]	PINARGOTE N W S, SMIRNOV A, PERETYAGIN N, et al. Direct ink writing technology (3D printing) of graphene-based ceramic nanocomposites: a review. Nanomaterials, 2020, 10(7): 1300. DOI URL
[9]	JI H C, ZHANG X J, PEI W C, et al. Research progress of ceramic 3D printing technology and materials. Material Engineering, 2018, 46(7): 19-28.
[10]	LIANG D, HE R J, FANG D N. Research status of manufacturing technology of ceramic materials and structural additives. Advanced Ceramics, 2017, 38(4): 231-247.
[11]	YANG W J, AN J, CHUA C K, et al. Acoustic absorptions of multifunctional polymeric cellular structures based on triply periodic minimal surfaces fabricated by stereolithography. Virtual and Physical Prototyping, 2020, 15(2): 242-249. DOI URL
[12]	AZARMI F, AMIRI A. Microstructural evolution during fabrication of alumina via laser stereolithography technique. Ceramics International, 2019, 45(1): 271-278. DOI URL
[13]	WEI Y H, ZHAO D Y, CAO Q L, et al. Stereolithography-based additive manufacturing of high-performance osteoinductive calcium phosphate ceramics by a digital light- processing system. ACS Biomaterials Science & Engineering, 2020, 6(3): 1787-1797.
[14]	LEE Y H, LEE J W, YANG S Y, et al. Dual-scale porous biphasic calcium phosphate gyroid scaffolds using ceramic suspensions containing polymer microsphere porogen for digital light processing. Ceramics International, 2021, 47(8): 11285-11293. DOI URL
[15]	YVES-CHRISTIAN H, JAN W, WILHELM M, et al. Net shaped high performance oxide ceramic parts by selective laser melting. Physics Procedia, 2010, 5: 587-594. DOI URL
[16]	LIU K, SUN H J, TAN Y L, et al. Additive manufacturing of traditional ceramic powder via selective laser sintering with cold isostatic pressing. The International Journal of Advanced Manufacturing Technology, 2017, 90(1-4): 945-952. DOI URL
[17]	KRUTH J P, MERCELIS P, van VAERENBERGH J, et al. Binding mechanisms in selective laser sintering and selective laser melting. Rapid Prototyping Journal, 2005, 11(1): 26-36. DOI URL
[18]	CHEN F, ZHU H, WU J M, et al. Preparation and biological evaluation of ZrO₂ all-ceramic teeth by DLP technology. Ceramics International, 2020, 46(8): 11268-11274. DOI URL
[19]	ENNETI R K, PARK S J, GERMAN R M, et al. Review: thermal debinding process in particulate materials processing. Materials and Manufacturing Processes, 2012, 27(2): 103-118. DOI URL
[20]	XING H Y, ZUO B, LI S S, et al. Study on surface quality, precision and mechanical properties of 3D printed ZrO₂ ceramic components by laser scanning stereolithography. Ceramics International, 2018, 43(18): 16340-16347. DOI URL
[21]	LIAN Q, WU X Q, LI D C, et al. Accurate printing of a zirconia molar crown bridge using three-part auxiliary supports and ceramic mask projection stereolithography. Ceramics International, 2019, 45(15): 18814-18822. DOI URL
[22]	WANG K, QIU M B, CHEN J, et al. Study on defect-free debinding green body of ceramic formed by DLP technology. Ceramics International, 2020, 46(2): 2438-244. DOI URL

3D打印氧化铝陶瓷的气氛脱脂热处理工艺研究

Atmosphere Debinding Heat Treatment of 3D Printed Alumina Ceramics

RichHTML

PDF (PC)

可视化

被引次数

摘要/Abstract

引用本文

使用本文

图/表 6

参考文献 22

相关文章 15

编辑推荐

Metrics

本文评价

[1]	武向权, 滕家琛, 季祥旭, 郝禹博, 张忠明, 徐春杰. 织构化多孔Al₂O₃-SiO₂复合陶瓷片-球混合浆料特性及光强分布仿真[J]. 无机材料学报, 2024, 39(7): 769-778.
[2]	程博, 安晓航, 李定华, 杨荣杰. ATH/ADP配比对EVA阻燃性能及机理转变的影响[J]. 无机材料学报, 2024, 39(5): 509-516.
[3]	刘文龙, 赵瑾, 刘娟, 毛小建, 章健, 王士维. 微波干燥自发凝固成型氧化铝湿坯[J]. 无机材料学报, 2023, 38(4): 461-468.
[4]	贾玉娜, 曹旭, 焦秀玲, 陈代荣. 无机酸铝体系氧化铝连续纤维的制备技术研究[J]. 无机材料学报, 2023, 38(11): 1257-1264.
[5]	王士维. 基于疏水作用的陶瓷浆料自发凝固成型研究进展[J]. 无机材料学报, 2022, 37(8): 809-820.
[6]	王新刚, 杨青青, 林根连, 高巍, 秦福林, 李荣臻, 康庄, 王小飞, 蒋丹宇, 闫继娜. 国产550级连续氧化铝陶瓷纤维的高温拉伸性能研究[J]. 无机材料学报, 2022, 37(6): 629-635.
[7]	周港怀, 刘耀, 石原, 刘绍军. 活性氧化铝催化剂载体的光固化浆料制备与成型[J]. 无机材料学报, 2022, 37(3): 297-302.
[8]	郝鸿渐, 李海燕, 万德田, 包亦望, 李月明. 莫来石/氧化铝预应力涂层增强氧化铝的弯曲强度和抗热震性能[J]. 无机材料学报, 2022, 37(12): 1295-1301.
[9]	彭飞, 姜勇刚, 冯坚, 蔡华飞, 冯军宗, 李良军. 耐高温氧化铝气凝胶隔热复合材料研究进展[J]. 无机材料学报, 2021, 36(7): 673-684.
[10]	郑雪, 江睿, 李谦, 王伟哲, 徐智谋, 彭静. 类阳极氧化铝纳米结构LED的研究[J]. 无机材料学报, 2020, 35(5): 561-566.
[11]	LI Xia,SHENASHEN Mohamed A,MEKAWY Moataz,TANIGUCHI Akiyoshi,EI-SAFTY Sherif A. 氢氧化铝纳米片: 结构依赖性癌症化疗药物的储运[J]. 无机材料学报, 2020, 35(2): 250-256.
[12]	李荣辉, 郏义征, 胡楠楠. 三维层级花状活性氧化铝纳米材料的制备及其除砷性能研究[J]. 无机材料学报, 2019, 34(5): 553-559.
[13]	陈文波, 陈伦江, 刘川东, 程昌明, 童洪辉, 朱海龙. 射频热等离子体制备球形氧化铝粉末的数值模拟及实验研究[J]. 无机材料学报, 2018, 33(5): 550-556.
[14]	杨景锋, 王齐华, 王廷梅. 氧化铝气凝胶的合成与性能[J]. 无机材料学报, 2018, 33(3): 259-265.
[15]	袁康, 廖其龙, 王辅, 代云雅, 黄金山. 烧结助剂(Y³⁺、La³⁺和Mg²⁺)对半透明氧化铝陶瓷的透光率的影[J]. 无机材料学报, 2017, 32(9): 1004-1008.